某铜钼矿铜钼分离工艺试验研究

介绍了某铜钼矿石铜钼分离的药剂试验成果，在硫化钠用量15．5kg／t、水玻璃用量0．55kg／t，闭路试验指标：当铜钼混合精矿中含铜17．85％，钼0．251％时，获得的钼精矿品位46．77％，钼回收率85．72％，其中含铜0．205％，铜精矿品位17．93％，铜回收率99．995％。     

某斑岩型铜钼矿等可浮浮选分离研究

对某斑岩型铜钼矿进行了选矿试验研究。采用钼铜等可浮浮选再分离-强化选铜工艺流程,采用CSU31作等可浮浮选捕收剂,在原矿含铜0．49％、含钼0．0115％的条件下,获得了含铜26．71％、总铜回收率86．11％的铜精矿及含钼48．03％、钼回收率83．53％的钼精矿,实现了铜、钼矿物与脉石的有效分离,获得了良好的技术指标。     

某铜钼矿石铜钼分离工艺试验研究

介绍某铜钼矿石铜钼分离的药剂试验结果。硫化钠用量15．5kg／t、水玻璃用量0．55kg／t，闭路试验指标：当铜钼混合精矿中含铜17．85％、钼0．251％时，获得的钼精矿品位46．77％，钼回收率85．72％(其中含铜0．205％)，铜精矿品位17．93％，铜回收率99．995％。     

某高次生铜易泥化铜钼混合精矿铜钼分离新工艺研究

针对某铜钼混合精矿中次生铜含量较高且含泥量大,导致在铜钼分离浮选过程中次生铜矿物难以被抑制,产出的钼精矿不能满足质量要求等问题,进行了预先分选—铜钼分离工艺研究。结果表明:在铜钼混合精矿铜品位为24. 40%、钼品位为0. 46%及最佳的试验条件下,采用预先分选、一次粗选、两次扫选、八次精选、中矿循序返回的浮选流程,可获得钼品位51. 56%、铜品位1. 05%、钼作业回收率74. 29%的钼精矿,铜品位24. 55%、钼品位0. 12%、铜作业回收率99. 97%的铜精矿,实现了高次生铜易泥化铜钼混合精矿中铜钼的有效分离。     

铜钼混合精矿分离浮选试验研究

对国内某大型铜钼矿浮选厂的铜钼混合精矿进行了分离浮选试验研究.在分离前对精矿进行强化脱药,采用组合抑制剂YF851和YF212进行分段抑制,可显著改善铜钼分离效果,获得了较好试验指标:钼精矿品位为49.91%、含铜0.69%,钼回收率为84.45%;铜精矿品位为32.90%,含钼0.07%,铜回收率为99.98%.     

乌山铜钼矿高次生铜矿石铜钼分离关键技术研究与应用

针对乌山铜钼矿矿石中次生铜矿物含量高,及其选矿厂设备选型配置、工艺流程结构不合理等问题,进行了技术研究和流程改造。通过对其工艺参数及技术条件的优化,对现场分离设备重新选型和设计,解决了流程无法实现连续稳定生产等突出问题,使设备选型和流程结构满足了生产要求,为铜钼成功分离奠定了良好的基础。经工艺流程的改造优化,铜钼分离钼精矿品位和钼回收率均达到投产以来最好水平,其中钼精矿品位累计为48.48%,累计含铜1.49%,钼回收率由改造前的30.58%提高到81.82%;且铜钼分离流程运行稳定,经济效益显著。     

低品位铜钼精矿三级流动性脱药铜钼分离试验研究

甲玛铜钼混合精矿因药剂、微细粒泥和辉钼矿紧密吸附,导致钼品位及回收率很难提高,针对这一技术难题,对该含泥铜钼精矿进行了详细的试验研究,最终获得流动性摩擦脱药高浓度浮选新工艺在铜钼混合浮选-抑铜浮钼中应用。采用此工艺进行试验,在铜钼混合精矿钼品位0.52%,铜品位23.37%的情况下,可获得钼精矿钼品位45.19%、作业回收率82.05%,铜精矿铜品位23.58%、作业回收率99.95%的生产指标,为该含泥低品位铜钼矿石的选矿提供了技术依据。该技术理念可作为铜、铅、锌、金、银、钼、硫、铁等依次浮选设计资源依据。     

铜、钼分离浮选试验研究

为了充分回收利用钼资源,对某选矿厂产出的含钼铜精矿进行了铜、钼分离浮选试验研究。通过对含钼铜精矿进行阶段磨矿、抑制铜等金属硫化矿、有效抑制脉石矿物,获得了钼精矿品位47.35%、含铜0.62%、钼回收率86.45%的较好闭路试验指标。     

福建某低品位铜钼多金属矿选矿工艺研究

福建某低品位铜钼多金属矿含Mo 0.051%、Cu 0.16%,矿石中钼、铜主要以辉钼矿、黄铜矿形态赋存,同时嵌布连生关系复杂,不利于铜钼分离。结合工艺矿物学分离结果确定了硫化矿混合浮选—混合精矿再磨—铜钼与硫分离—铜钼分离的选矿工艺流程,在经优化后的药剂制度条件下全流程闭路试验获得了钼精矿、铜精矿、硫精矿三个产品,钼精矿中Mo回收率达到了80.26%,铜精矿中Cu回收率达到了87.03%,实现了对该低品位铜钼多金属矿中金属资源的综合回收。     

某低品位钼铜矿石选矿试验研究

某钼铜矿石是一种以钼为主、并伴生铜矿物的低品位钼铜矿石,原矿含钼仅0.045%、含铜0.025%,无其它有价值的金属元素,试验采用先优先混合浮选将钼铜金属矿物同时富集后,再进行钼铜分离的选矿工艺,取得了钼精矿钼品位53.25%～50.4%(含铜0.30%～1.514%,取决于精选作业次数)、混合浮选开路作业回收率70.09%、分离浮选开路作业回收率55.89%～82.42%、开路作业总回收率为39.17%～57.77%;铜精矿含铜品位22.23%(含钼2.36%)、混合浮选作业回收率46.82%、分离浮选回收率90.45%、开路总回收率为42.35%的较好指标。如果条件允许能够进行闭路浮选试验,可能会取得更好的技术经济指标。     

陕西某低品位铜钼矿选矿试验研究

The copper grade the low-grade copper-molybdenum ore in Shaanxi is 0.32% and the molybdenum grade is 0.048%.The copper and molybdenum minerals mainly exist in the form of sulfide ore. The properties are complex that there are many kinds of minerals in the ore, which are closely distributed and fine dissemination size. According to the properties of the ore, the technological process of bulk flotation and separation of copper and molybdenum was adopted in the experiment. With lime as regulator and reagent L03 as collector, the mixed concentrate of copper and molybdenum was obtained by the bulk flotation which flow-sheet is one roughing, three refining and two scavenging process. Then regrinding the mixed concentrate, use sodium sulfide as inhibitor of copper minerals, sodium silicate as slurry dispersant and inhibitor of silicate gangue minerals , kerosene as collector, can separate copper and molybdenum with the flow-sheet which one roughing, five refining and three scavenging. The copper concentrate with copper grade of 18.82% and copper recovery rate of 85.35% and molybdenum concentrate with molybdenum grade of 47.14% and molybdenum recovery rate of 79.24% were obtained by the final closed-circuit flotation test process, the indicator is nearly ideal.     

西藏某难选铜铅多金属矿石铜铅浮选分离试验研究

西藏某难选铜铅多金属矿石中多种金属矿物密切共生,硫化物之间嵌连关系较为复杂,且含有大量的次生硫化铜及氧化铜矿物,铜铅分选极为困难。针对该矿石特点,进行了铜铅混合浮选—混合精矿分离、优先浮钼、优先浮铜—再浮铅等多种工艺流程探索试验。结果表明:优先浮铜—再浮铅工艺流程可获得较好指标,闭路试验获得铜品位25.01%、铜回收率81.92%、含铅6.71%的铜精矿,铅品位45.89%、铅回收率70.09%、含铜1.69%的铅精矿,实现了矿石中铜铅的有效分离。     

钨矿伴生硫化矿铜铋分选工艺试验

以江西某钨矿伴生硫化矿为试料,试验采用重-浮-重流程,铜铋分离试验采用优先浮选-浮铜抑铋工艺流程,小型闭路试验结果为:铜精矿品位为25.03%,回收率为93.93%,铜精矿中铋的损失率7.08%;铋精矿中铋品位15.08%,回收率为79.42%,铋精矿中铜的损失率1.84%。     

某高品位钼铋硫化矿选矿试验研究

内蒙古某钼铋多金属硫化矿,含钼0.65 %,含铋1.12 %,钼铋品位较高,有较大的工业回收价值.采用“混合浮选—钼铋分离”的选矿工艺回收该矿石中的有用矿物,以乙硫氮和煤油作为捕收剂进行混合浮选,以硫化钠和亚硫酸钠作为组合抑制剂,煤油为捕收剂进行钼铋分离,最终实验室小型闭路试验可以获得含钼47.31 %,钼回收率89.52 %的钼精矿以及含铋42.64 %,铋回收率86.04 %的铋精矿,较好地实现了钼铋分离.      

某难选氧硫混合型铜矿浮选试验研究

针对某难选氧硫混合型铜矿的特点,利用铜矿物之间可浮性的差异,采用“先硫后氧,先浮选易选氧化铜矿,再浮选难选氧化铜矿”的异步浮选的流程,对含铜3.99%的原矿,在条件优化试验的基础上,开展闭路试验,可以获得浮选硫化铜精矿含铜50.66%,铜回收率25.17%,氧化铜精矿含铜19.68%,回收率54.05%,浮选综合铜精矿回收率达到79.23%。     

超声波强化铜钼浮选过程的研究

斑岩型铜钼矿具有矿石性质复杂、嵌布粒度细、辉钼矿与黄铜矿可浮性相近等特点,导致在浮选过程中铜钼分离困难。利用超声波改变矿浆性质、矿物表面性质及药剂溶液性质。通过对某铜钼矿石采用超声波技术处理强化铜钼浮选分离,纯矿物浮选研究表明,采用超声波处理可以有效实现黄铜矿与辉钼矿的分离。实际矿石分选表明:在磨矿浓度为66.7%、矿浆pH=10.0、石灰用量为450 g/t、水玻璃用量为1 kg/t、YC药剂+丁基黄药用量为160 g/t+50 g/t、2#油30 g/t、磨矿细度 < 0.074 mm占77.2%时,获得混合铜钼精矿钼品位为2.96%,钼回收率为87.44%;铜品位为0.76%,铜回收率为92.77%。对铜钼混合精矿,在矿浆浓度10%下,经超声功率2 000 W处理时间20 min,浮选条件为矿浆pH=10、煤油用量为80 g/t、2#油用量为15 g/t、硫化钠用量为300 g/t,获得最终钼精矿Mo品位为22.19%,作业回收率为95.95%,钼总回收率为83.90%;铜精矿Cu品位为11.88%,作业回收率为98.27%,铜总回收率为91.16%,实现了铜钼矿物良好分离。      

某锡矿石伴生钼铋铜的综合回收

针对某锡矿石伴生钼铋铜的综合回收试验研究,根据钼、铋、铜矿的密切共生关系及可浮性特点,制定了钼铋铜混合浮选,混合精矿再磨脱药,最后进行抑铜浮钼铋,钼铋分离的选矿工艺流程,获得钼精矿品位46.07%、回收率75.04%,铋精矿品位16.27%、回收率32.62%,铜精矿品位24.65%、回收率63.03%的良好选矿指标.