大比例掺用铁尾矿制备轻质保温墙体材料

以水泥为胶凝剂、黄石市灵乡铁矿尾矿为主要原料制备轻质保温墙体材料,研究了轻骨料膨胀珍珠岩、铁尾矿及其碱性激发剂掺量和水灰比对试件抗压强度、容重、导热系数的影响。结果表明：试验用碱性激发剂对铁尾矿的活性有显著的激发作用,从而可提高铁尾矿的掺用比例、减少水泥用量;当水泥、铁尾矿、激发剂、膨胀珍珠岩的质量比为1∶2.5∶0.25∶0.63,水灰比为0.8时,试件28 d的抗压强度＞5 MPa、容重＜900 kg/m3、导热系数<0.231 W/（m·k）,满足轻质保温墙体材料的性能要求。     

气化炉渣对铁尾矿烧结墙体材料性能的影响

为了降低铁尾矿烧结墙体材料体积密度和提高保温隔热性能,在尾矿中添加部分气化炉渣,采用挤出成型方法制备了铁尾矿烧结墙体材料.结果表明,在950℃烧结时,添加20%气化炉渣可以制备出密度低于1.45g/cm3导热系数低于0. 23 W/(m·K)、抗压强度高于30 MPa的墙体材料,为利用尾矿制备具有节能、利废、保温、隔热、低密度的新型墙体材料提供了一条新的途径.     

铁尾矿和废石制备建筑外墙防火保温陶瓷材料

利用河北某铁尾矿和废石为原料制备了建筑外墙防火陶瓷保温材料。对铁尾矿和废石进行了ICP-AES分析、化学成分分析、X射线衍射物相分析、TG-DSC热分析和放射性检测。在此基础上研究了原料配比、原料粉磨细度、发泡剂用量、发泡剂粒度、烧成制度与建筑外墙陶瓷保温材料性能之间的关系。结果表明,以放射性合格的铁尾矿和废石制备建筑外墙防火陶瓷保温材料技术可行。合适的物料配比为铁尾矿用量为40%~55%,废石用量为45%~60%,发泡剂外掺量为0.5%;原料粉磨细度控制在7.45μm(D50)左右;发泡剂粉磨细度为0.037mm(D90);烧成温度1160℃,烧成时间60 min;制备的建筑外墙防火陶瓷保温材料干密度为350 kg/m3,吸水率为0.48%,导热系数为0.09 W/(m·K),抗压强度为2.20 MPa,抗折强度为1.46 MPa,防火等级为A级。     

利用邯郸铁矿尾矿制备轻质隔热墙体材料

以邯郸铁矿尾矿为原料,采用淀粉糊化固化法制备轻质隔热墙体材料。研究了淀粉添加量、烧成温度、加水量等工艺条件对轻质隔热墙体材料气孔率和耐压强度的影响。结果表明,随着淀粉添加量的增加,制品的气孔率增高,耐压强度降低;随着烧成温度的提高,制品的气孔率降低,耐压强度增高;水分添加量对制品性能的影响没有烧成温度和淀粉添加量明显。用本方法可以制备体积密度不超过0.85 g/cm3、耐压强度大于0.5 MPa、导热系数不超过0.18 W/(m.K)的轻质隔热墙体材料,为铁尾矿的综合利用提供了新途径。     

利用铁尾矿制备发泡水泥

为提高铁尾矿的利用率,以普通硅酸盐水泥为基质材料,铁尾矿为掺和料,通过化学发泡法制备发泡水泥。研究了铁尾矿掺量、发泡剂用量、水灰比、硬脂酸钙等因素对发泡水泥抗压强度和密度的影响,并确定最佳原料配比。结果表明,原料最佳配比为:铁尾矿55%,普通硅酸盐水泥45%,发泡剂8%,硬脂酸钙0.35%,聚丙烯纤维0.3%,在水胶比为0.43的条件下,发泡水泥7 d和28 d抗压强度分别为1.35 MPa和1.65 MPa,干密度为698.25 kg/m~3。     

烧成温度对铁尾矿墙体材料性能的影响

研究了以90.8%的某铁尾矿、4.2%的水泥、5%的黏土为原料生产的新型墙体材料试样的物理性能、结构特征、化学成分受烧成温度的影响;比较了900 ℃下烧成的新型墙体材料试样与目前市场上的墙体材料的体积密度、隔热性能、耐压强度等重要性能指标。研究表明,900 ℃下烧成的试样基本具备新型轻质隔热墙体材料的性能。     

某铁尾矿和废石制备建筑外墙防火保温陶瓷材料

利用河北某铁尾矿和废石为原料制备了建筑外墙防火陶瓷保温材料。对铁尾矿和废石进行了ICP-AES分析、化学成分分析、X射线衍射物相分析、TG-DSC热分析和放射性检测。在此基础上研究了原料配比、原料粉磨细度、发泡剂用量、发泡剂粒度、烧成制度与建筑外墙陶瓷保温材料性能之间的关系。结果表明：以放射性合格的铁尾矿和废石制备建筑外墙防火陶瓷保温材料技术可行。合适的物料配比为铁尾矿用量为40~55%,废石用量为45~60%,发泡剂外掺量为0.5%;原料粉磨细度控制在7.45μm(D₅₀)左右;发泡剂粉磨细度为0.037mm(D90);烧成温度1160℃,烧成时间60min;制备的建筑外墙防火陶瓷保温材料干密度为350kg/m₃,吸水率为0.48%,导热系数为0.09W/(m?K),抗压强度为2.20MPa,抗折强度为1.46MPa,防火等级为A级。     

萝北某石墨尾矿铁含量对制备发泡陶瓷性能影响研究

通过磁选工艺降低石墨尾矿混合原料的铁含量,研究了铁含量对制备发泡陶瓷的性能影响。结果表明,磁选工艺可以显著降低石墨尾矿的铁含量;当磁选给矿?0.074 mm含量为71.64%、磁场磁感应强度为0.8 T、矿浆质量浓度为15%时,石墨尾矿TFe₂O₃含量从6.37%降低到2.18%。通过发泡陶瓷制备试验发现,磁选后的混合原料的TFe₂O₃含量从4.65%降低到1.81%,制备的发泡陶瓷外观颜色明显改善,抗压强度从7.2 MPa提高到7.9 MPa,导热系数从0.33 W/(m·K)提高到0.36 W/(m·K);抗压强度有所提高,保温性能有所降低,整体上磁选前后发泡陶瓷的性能差异较小。      

铁尾矿基陶粒混凝土的制备及性能研究

随着矿冶行业的快速发展,尾矿堆积量逐年增多,特别是铁尾矿已成为国内研究者关注的焦点。先用铁尾矿制备轻质高强陶粒,然后以该陶粒作为轻骨料制备陶粒混凝土。采用正交试验研究水灰比、减水剂用量、砂用量、增稠剂用量对陶粒混凝土抗压强度及陶粒上浮的影响。通过试验确定该铁尾矿基陶粒混凝土的最佳方案为水灰比0.25、减水剂用量0.5%、砂用量20%、增稠剂用量0.12%。最终制得28 d抗压强度为67.33 MPa、抗折强度为8.1 MPa、体积密度1 940 kg/m3的高性能陶粒混凝土。研究中解决了轻骨料陶粒混凝土中陶粒上浮问题,实现了资源二次开发。      

铁尾矿干压免烧砖的制备

以陕西某铁尾矿为主要原料,添加少量水泥及适量当地河砂,制备MU15级干压免烧砖,研究了铁尾矿与河砂的质量比、水泥用量、拌和用水量、成型压力以及化学外加剂对尾矿免烧砖抗压强度的影响。结果表明：在成型压力为15 MPa条件下,铁尾矿与河砂的质量比为1.25∶1.00,水泥在固体干料总量中占10%,拌和用水量为固体干料总量的8%,萘系高效减水剂掺量为水泥量的0.8%,葡萄糖酸钠缓凝剂掺量为水泥量的0.03%时,可制得28 d抗压强度达到16.4 MPa的铁尾矿免烧砖,其各项性能指标符合JC/T 422-2007《非烧结垃圾尾矿砖》标准的规定。     

China rare earth market review

正November 21~30,2014Due to weak demand from downstream industries,transactions of rare earth in Chinese domestic market were inactive.It was difficult to sell any rare earth products except for dysprosium oxide and terbium oxide.Suppliers lost confidence in recent market.Demand for rare earth products was soft.Consumers continued to take a wait-and-see attitude.Rare earth export market remained slow.     

Current situation and future trend of China rare earth luminescent materialindustry(continued)

<正>Developing ecological lighting source The world is facing the big problem of energy shortage today and the contradiction between economy development and environmental protection is worsened.Therefore,people are more likely to choose an ecological light source that is more energy efficient and environmental friendly.The choice provides great opportunity for the development of rare earth optical material industry in China.The concept of green lighting positions rare earth luminescent material as a leading player in illumination market.The light source of both rare earth luminescent lamp and LED lamp is ecological and energy saving.This is why     

Galaxy Magnets achieved the net profit of 34.02 million yuan in the first six months of 2014

正Galaxy Magnet announced its financial results for the first half of 2014 on August 14.For the first six months ended on 30 June 2014,Galaxy Magnet achieved operation income of RMB 182.3 million,up8.40% over the same period of 2013,and the net profit attributable to the shareholders of the listed company of 34.02 million yuan,increasing 35.49% over the same period of last year.Stable performance increase was led by development of new customers and application market of magnets.     

Rare Earth Application in Steel in China

<正>China has rich rare earth resources.Output of rare earth and steel in China ranks the top first in the world.However,there is still certain distance between the steel produced in China and developed countries from the point of varieties and quality.China still has to import some types of steel.Improving the quality should be emphasiZed in future development of steel industry in China.Rare earth can be used to upgrade traditional steel     

稀散金属产业的观察与思考

分析了近年来国内外稀散金属产业的生产、应用、资源与市场状况.铟锡氧化物靶材、砷化镓晶片、锗红外材料、铼高温合金和硒在电解锰及玻璃的应用等已成为稀散金属的主要应用领域.稀散金属的产量快速增长达到历史高位而导致了市场的失衡.以GaInP_2/GaAs/Ge,CIGS和CdTe为代表的非硅系太阳能电池是稀散金属的新兴应用领域,将给稀散金属带来日益增长的需求.     

Brief news

正Corun invested another 50 million yuan in power battery for HEV Hunan Corun announced on 27 June that they had signed the cooperation agreement to jointly built Corun(Shaoxing)Autos Power Battery System Co.,Ltd.in Shaoxing Binhai New City.According to the announcement,total registered     

铜熔炼中锍品位对杂质元素分配行为的影响

借助于多相、多成分系统中平衡计算的手段，开发出微量元素砷、锑、铋及伴生元素铅、锌等在铜熔炼中分配行为的计算机模型。利用该模型对铜熔炼过程进行计算机模拟，分析了冰铜品位对砷、锑、铋、铅和锌等杂质元素的分压、活度系数及它们在冰铜、炉渣和气相中分配率的影响，并讨论其热力学分析结果对生产实践的指导意义。     

减震防磨损溜槽在山东京杭水铁联运中的应用

溜槽作为煤炭运输中连接运输设备和储煤设施的重要部件，其设计的合理性直接影响到整个生产系统。尤其落差大的溜槽在使用过程中，不仅噪声大，磨损快，而且还会对下一级胶带冲击很大。实际生产中，溜槽维护成本高，严重影响煤炭运输正常作业。结合山东京杭水铁联运项目中溜槽运量大、落差高的特点，阐述了常用的防冲击、减震防磨损的方法以及在实际使用中的优缺点。并结合设计经验，提出了新的应用设计，通过计算机头落煤曲线，得出机头溜槽物料大概落煤点，设计堆煤网格，形成集料槽；在溜槽底板设置阻尼层，并用螺栓固定，起到缓冲减震降噪的作用。同时也起到了保护下一级胶带和落煤点缓冲托辊的作用。     

重型结构件快速标准化定位在液压支架生产中的应用

随着工业自动化的快速发展,机器人在加工过程中的利用率越来越高。但由于工业机器人对定位精度的要求非常高,往往会因为不能准确定位而对机器人接下来的加工操作造成一定的误差影响。而这种误差导致的最直接的结果就是焊接机器人无法准确定位到正确的焊缝位置,出现焊偏、焊漏或者熔深不够等焊接缺陷。以液压支架生产过程中对重型结构件的定位为实例,对旧式的定位块进行改进,在一定程度上增加了定位方式的灵活程度和精确程度。经过测试,新的定位方法极大地提高了定位的精确度,降低了定位过程中的操作难度,缩短了定位活件的时间。     

庐枞矿集区地震资料干扰波分析与压制研究

庐枞矿集区地表条件及地质构造非常复杂,导致地震资料波场关系复杂,有效反射信号弱,干扰波种类多及特征在时间与空间方向上差异大。通过对干扰波特征及压制技术的分析研究,确定了适合矿集区复杂地表条件下的干扰波压制方法和流程。庐枞矿集区地震资料处理的实际应用显示,使用该方法压制干扰波效果明显,提高了资料的信噪比。