对应用于LCD的不同于传统管状背光源的新型面状场发射背光源(FE-BLU)的制备技术进行了研究.将表面改性碳纳米管(CNTs)丝网印刷于金属Ag精细电极上形成碳纳米管阴极,利用透射电镜与扫描电镜表征了CNTs及阴极的表面形貌.采用有机溶剂高压气流法对阴极进行表面处理,并真空封装成25.4 cm(10 in)的CNTs FE-BLU器件.测试结果表明,表面处理后阴极场发射电流密度得到明显提高,器件亮度可达5 860 cd/m2,均匀性为82%,持续发射35 h后,发射电流无明显衰减.     

碳纳米管薄膜的电泳沉积与场发射性能

采用电泳法在Si基片上沉积碳纳米管(CNTs)薄膜。研究了电泳极间距、电泳时间及电泳电压等对沉积的薄膜形貌结构与场发射性能的影响。SEM、高倍光学显微镜和场发射性能测试结果表明,保持阴阳极间距为2cm,在100V的直流电压下电泳2min所获得的CNTs薄膜均匀、连续、致密且具有最好的场发射性能,其开启电场强度仅为1.19V/μm,当外加电场强度为2.83V/μm时,所获得的最大发射电流密度可达14.23×10–3A/cm2。     

薄膜型平栅极FED背光源的制备及性能研究

利用磁控溅射和光刻技术在玻璃基底上制备薄膜型平栅极场发射阴极阵列,采用电泳工艺将碳纳米管(CNTs)发射材料转移到薄膜型平栅结构的阴极电极表面,借助光学显微镜和扫描电镜观测薄膜型平栅极场发射阴极阵列。利用Ansys软件模拟阴栅间距对阴极表面电场分布的影响,优化其结构参数,对其场发射特性进行了讨论。实验结果表明,CNTs能均匀地分散在平栅型结构的阴极表面,当电场强度为2.4 V/μm时,器件发射电流密度达到1.8 mA/cm2,亮度达3 000cd/m2,均匀性为90%,能稳定发射28 h,且具有较好的栅控作用。该薄膜型平栅极背光源技术简单、成本低,为将来制备新一代大面积场发射背光源提供了可行性方案。     

碳纳米管场发射阴极电泳法制备及场发射特性研究

采用电泳沉积法在玻璃基板上成功制备出碳纳米管场发射阴极,采用扫描电子显微镜观察薄膜表面形貌,并对制备的碳纳米管阴极进行场发射测试.实验结果表明电泳2 min沉积的碳纳米管薄膜均匀连续且具有较好的场发射特性,其开启电场为3.1 V/μm,当外加电场强度为11.5 V/μm时场发射电流密度达到11.33 mA/cm2,经过10 V/μm的电场激活处理后样品具有较好的场发射稳定性.     

电流法改善碳纳米管阴极场发射特性

针对丝网印刷碳纳米管阴极,提出电流法进行表面后处理,有效改善碳纳米管阴极场发射特性.利用扫描电子显微镜表征电流法处理前后CNTs阴极表面形貌变化,并对处理前后CNTs阴极进行场发射特性测试.结果表明,电流法处理后CNTs阴极表面残留有机物被破坏,开启电场从2.4 V/μm降低到1.6 V/μm,同样面积的薄膜(印制面积为1 cm×1 cm)在2.6 V/μm场强下的发射电流由30 μA提高到了800 μA,说明电流处理对于提高薄膜的场发射特性有明显作用.该方法在碳纳米管场发射显示器的制作中具有很好的实际应用价值.     

CuCr合金催化剂制备条件对大电流CNTs阴极的影响

通过改变溅射功率以磁控溅射法制备了Cu/Cr合金催化剂,研究了化学气相沉积法制备的碳纳米管(CNTs)作为大电流密度场发射阴极的场发射性能。采用扫描电镜和场发射测试仪分别对不同功率催化剂制备的CNTs进行了形貌及性能分析。结果表明,根据溅射功率与催化剂颗粒的关系,可以通过调节溅射功率改变CNTs的长径比及密度,在250WCu/Cr催化剂制备的CNTs薄膜具备了良好的场发射性能,阴极电子发射的开启电场仅为1.47V/μm,当电场为3.23V/μm,发射电流密度可高达3259μA/cm2。     

限流电阻层改善碳纳米管场发射显示器发光均匀度的研究

针对碳纳米管(CNT)场发射阴极薄膜中,CNT个体差异及其与衬底的不良接触对发光均匀性的影响,引入反馈限流电阻层以改善阴极薄膜的场发射发光均匀性.采用丝网印刷工艺在衬底上制备氧化锌作为电阻限流层,在其上制备CNT阴极薄膜.对CNT薄膜阴极的发射电流稳定性和均匀性进行了测试,给出了电阻限流层对场发射特性曲线的影响效果.SEM分析表明,氧化锌电阻层有利于消除CNT阴极的尖端屏蔽效应,并且使得CNT与衬底具有更加紧密的接触.场发射特性和场发射发光照片表明,虽然随着限流层厚度增加,阈值电压有所增加,发射电流有所减小,然而限流层的存在有效地改善了发射电流的稳定性,使得发射电流和场发射发光点分布更加均匀.     

限流电阻层改善碳纳米管场发射显示器发光均匀度的研究

针对碳纳米管(CNT)场发射阴极薄膜中,CNT个体差异及其与衬底的不良接触对发光均匀性的影响,引入反馈限流电阻层以改善阴极薄膜的场发射发光均匀性.采用丝网印刷工艺在衬底上制备氧化锌作为电阻限流层,在其上制备CNT阴极薄膜.对CNT薄膜阴极的发射电流稳定性和均匀性进行了测试,给出了电阻限流层对场发射特性曲线的影响效果.SEM分析表明,氧化锌电阻层有利于消除CNT阴极的尖端屏蔽效应,并且使得CNT与衬底具有更加紧密的接触.场发射特性和场发射发光照片表明,虽然随着限流层厚度增加,阈值电压有所增加,发射电流有所减小,然而限流层的存在有效地改善了发射电流的稳定性,使得发射电流和场发射发光点分布更加均匀.     

薄膜衬底电极CNT阴极制备及场发射性能研究

采用电泳沉积(EPD,electrophoretic deposition)法在不同薄膜衬底电极上制备碳纳米管(CNT,carbon nanotube)场发射阴极.采用场发射扫描电子显微镜(FESEM)对其进行表面形貌表征,结果表明,EPD可以制得CNT均匀分布的场发射阴极.场发射测试结果表明衬底电极对CNT阴极的场发...     

热累积效应对碳纳米管场发射特性的影响

为进一步提高碳纳米管阴极的场发射能力,分析了不同条件下碳纳米管的场发射测试结果,研究了热累积效应对碳纳米管场发射性能的影响。实验结果表明,通过抑制场发射测试过程中阳极的热累积,可获得更大的发射电流和发射电流密度。该研究为进一步提高碳纳米管阴极场发射能力提供了参考。     

电泳法制备场发射阴极的性能优化研究

电泳法是一种新型的大面积碳纳米管场发射阴极制备方法。文章在成功地用电泳法制备了适用于场发射显示器的碳纳米管阴极基础上,通过选用不同的碳纳米管原料、改变电泳条件等方法,进一步优化碳管阴极的性能。使用不同方法制备的碳纳米管配置电泳液,由于制备方法和碳管本身的特性,管子在电泳溶液中呈现不同的分散性。碳管管径较粗时由于表面自由能相对小,所以碳管在溶液中不易形成团聚物,电泳沉积的阴极会均匀平整;管径小的碳管则由于容易团聚,需要加入表面活性剂来改善其在电泳溶液中的分散性。场发射特性和发光显示图实验结果发现,即使得到相同均匀平整的阴极,但是由于碳管本身的发射能力的差异性最终导致电泳沉积得到的阴极的场发射特性的不同。另外,电泳的实验条件也会对沉积的阴极的场发射性能和形貌产生影响。在不同电泳直流电压条件下,碳管薄膜的密度分布和厚度不同,呈现出不同的场发射能力,结果表明当电压值在25V时可以得到性能最佳的场发射阴极。     

Low turn-on voltage field emission triodes with selective growth ofcarbon nanotubes

A low turn-on voltage, field emission triode array has been fabricated using the selective deposition of carbon nanotubes (CNTs) in a microwave plasma chemical vapor deposition (MPCVD) system. The field emission triodes exhibited a low turn-on voltage of 13 V and a large emission current of 23 μA with the gate voltage at 60 V. Short-term stress reveals a 10% current fluctuation within 1800 sec. The excellent electric properties suggest that the array shows potential for application in field emission displays and vacuum microelectronics     

Stable field emission from planar-gate electron source with MWNTs by electrophoretic deposition

A planar-gate electron source with multi-wall carbon nanotubes (MWNTs) has been successfully fabricated by conventional magnetron sputtering, lithography and electrophoretic deposition (EPD). The optical microscopy showed that he MWNTs purified in H₂SO₄/HNO₃ solution were selectively deposited on cathode. High resolution transmission electron microscopy (HRTEM) images and Raman spectra demonstrated that some MWNTs was destroyed and generated some defect. Field emission results indicated that the emission current of this triode structure is completely controlled by gate voltage. The turn-on voltage of electrophoretic deposited MWNTs cathode at current density of 1 μA/cm² was lower than that of screen printed MWNTs cathode besides better emission uniformity. In addition, the emission current fluctuation was less than 3% for 400 min. All the results indicate that the fabricated electron emission source has a good field emission performance and long lifetime.     

Gated carbon nanotube emitter with low driving voltage

By approaching the counter electrode to the carbon nanotubes (CNT) emitter, remarkable reduction of the cathode operating voltage has been accomplished in the under-gate CNT cathode structure. The peak emission current density of 2.5 mA/cm/sup 2/, which is sufficient for high brightness CNT field emission display, was obtained at the cathode-to-gate voltage of 57 V when the CNT-to-counter electrode gap was 2.2 /spl mu/m. The gate current was less than 10% of the anode current. The CNT cathode with low driving voltage can help the cost-effective field emission display implemented.     

碳纳米管场致发射阴极浆料的研制

通过筛选阴极浆料中的载体、不同种类的粘结剂和添加剂,开发出具有优良场致发射性能的大面积、低成本丝网印刷复合阴极浆料并烧结制成阴极。结果表明:在电场强度为3.2V/μm下其电流密度约为42×10–3A/cm2,场发射均匀性很好,二极管型发光板发光亮度为625cd/m2。该阴极适用于制作大面积的CNT-FED阴极和液晶显示器的背光源。     

阳极氧化条件对多孔硅冷阴极场发射特性的影响

研究了多孔硅的制备条件对多孔硅冷阴极场发射特性的影响,实验表明多孔硅的制备条件如电解电流密度、电解时间等多孔硅冷阴极的场发射特性有较大的影响。     

Improvement of the field emission properties of carbon nanotubes by CNT/Fe_3O_4 composite electrophoretic deposition

A simple CNT/Fe_3O_4 composite electrophoretic deposition method to improve the field emission cathode properties of carbon nanotubes(CNTs) is proposed.It is found that CNT/Fe_3O_4 composite electrophoretic deposition leads to better field emission performance than that of single CNT electrophoretic deposition.The result is investigated using SEM,J-E and FE.After the process,the turn-on electric field decreases from 0.882 to 0.500 V/μm at an emission current density of 0.1 mA/cm~2,and the latter increase...     

Effect of diamond-like carbon coating on the emissioncharacteristics of molybdenum field emitter arrays

We have studied the electron emission characteristics of Mo field emitter arrays (FEAs) using a diamond-like carbon (DLC) film deposited by a layer-by-layer technique using plasma enhanced chemical vapor deposition. The turn-on voltage was lowered from 55 to 30 V by a 20 nm thick hydrogen-free DLC coating and maximum emission current was increased from 166 to 831 μA. Also the gate voltage required to get the anode current of 0.1 (μA/emitter) decreases from 77 to 48 V. Furthermore, the emission current from DLC coated Mo FEAs is more stable than that of noncoated Mo FEAs     

碳纳米管薄膜的电泳沉积及其场发射性能研究

利用电泳沉积法在铝片上制备了碳纳米管薄膜冷阴极。通过扫描电镜、Raman光谱观察分析了表面形貌和结构,并对场发射性能进行了测试。经过研磨处理的碳纳米管薄膜样品,开启电场为2V／μm,当电场强度为4V／μm时电流密度达到2600μA／cm^2,发光点密度大于10^4／cm^2。