石灰干化污泥对土壤重金属稳定化处理的效果

以采自湖南省嘉禾县重金属复合污染土壤为研究对象,采用城市污水处理石灰干化污泥作为稳定剂,对污染土壤进行稳定化处理,并采用TCLP和BCR连续提取法对稳定化效果进行分析和评价。研究结果表明,单独使用石灰干化污泥,TCLP浸出浓度随着干化污泥质量分数的增加而显著减少,干化污泥的质量分数为40%时,稳定化率最大为Zn-98.92%、Cd-99.06%、Pb-96.84%;但是干化污泥的高pH值导致稳定后土壤中As的浸出增加。为了恢复植物生长功能,经过亚铁盐和磷酸调节pH后,石灰干化污泥稳定过的土壤pH有效降低,同时亚铁盐和磷酸有利于促进Pb和Zn的稳定效果;但是对Cd的稳定有负面影响;另外,亚铁盐的加入同时可以减少As的浸出浓度。经处理后土壤中重金属形态由不稳定态转为稳定态,使重金属的浸出浓度明显降低,减少了土壤重金属的浸出毒性。该研究结果表明,石灰干化污泥可以作为资源回收利用,应用于重金属污染土壤的修复中,并能改善稳定后土壤适宜植物生长的理化性质。     

金矿区高浓度砷污染土壤的稳定化处理

以粉煤灰、干化污泥、粉碎花生壳、硫酸亚铁(Fe_2SO_4)和磷酸二氢钾(KH_2PO_4)为稳定剂对矿区高浓度As污染土壤进行处理,通过土壤理化性质、重金属形态和浸出浓度变化等综合评估稳定剂对高浓度砷污染土壤的稳定化处理效果。结果表明,添加稳定剂可以提高土壤pH值、有机质含量和阳离子交换量。粉煤灰、干化污泥、粉碎花生壳、硫酸亚铁对土壤中的As有较好的稳定化作用,其中硫酸亚铁对土壤中As的稳定效果最好。同时添加10%粉煤灰、10%干化污泥和1%硫酸亚铁后,土壤中可交换态As、碳酸盐结合态As、铁锰氧化物结合态As、有机结合态As含量显著降低,降幅分别为62.3%、55.2%、29.6%、58.2%,残渣态As含量增加8.1%。添加粉煤灰、干化污泥、硫酸亚铁能显著降低土壤中As的浸出浓度,而添加KH_2PO_4会使土壤中As浸出浓度增加,移动性增强。当同时添加10%粉煤灰、10%干化污泥、1%粉碎花生壳和1%硫酸亚铁后,As浸出浓度最低(0.93 mg·L~(-1)),稳定效果最好,稳定化效率达到了74.8%。土壤中As的浸出浓度与可交换态As和碳酸盐结合态As呈显著正相关,与残渣态As呈显著负相关,可交换态As、碳酸盐结合态As和残渣态-As含量是影响土壤中As浸出浓度变化的主要因素。     

含砷污泥的粉煤灰固化研究

硫酸废水处理系统的中和污泥属于有害废渣,其中As浸出率超标.采用固化的方法处理某冶炼厂硫酸废水中和污泥,发现以水泥∶粉煤灰∶污泥=1∶1∶2的配比固化后,固化块浸出液浓度达到国标规定(1.5 mg/L).研究表明,粉煤灰替代水泥50%可达到较好的固化效果,浸泡24 d后浸出浓度达到稳定值,pH值为7时浸出浓度最小,外加剂对固化有负影响,采用湿养护可获得更好的效果.     

含重金属污泥制砖毒性的浸出

污泥中的重金属是影响污泥处置利用的重要因素,污泥制砖可以有效固结重金属。采用污水厂污泥与页岩按一定配比混合制备烧结砖,通过毒性浸出实验,研究烧结砖对重金属的固化程度以及重金属浸出稳定性,从而评定烧结制砖的安全性。结果表明,在浸出液为中性和酸性条件下,Cu、Cr、As和Pb的浸出浓度基本保持稳定,浸出时间的影响不大,而Zn的初始浸出浓度相对较大,最终逐渐降低;碱性条件下,Cr、Cu和Pb的浸出浓度随时间变化不大,而Zn和As的浸出浓度则在浸提时间内无明显变化规律;但不同p H浸出液下的重金属浸出浓度均远低于国家限值,污泥制砖重金属固化效果好,安全可靠。     

改性污泥替代垃圾填埋场覆土的研究

以市政污泥为研究对象，采用固化剂对污泥进行改性，通过分析不同固化剂添加比例下固化产物的抗压强度和渗透系数，比较不同养护时间下污泥固化产物浸出液的COD、氨氮和重金属性质，探讨市政污泥固化产物作为垃圾填埋场覆土可行性。实验结果表明：固化剂添加比例为30％的固化产物抗压强度高于50kPa，其渗透系数达到10^-7cm／s数量级，基本满足覆土材料的标准要求。污泥固化产物重金属的最大浸出量远远低于《污水综合排放标准》（GB8978-88）中一级排放标准。随养护时间延长，固化产物浸出液COD和氨氮浸出浓度亦呈下降趋势，重金属Pb、Cd浸出量明显减少，浸出比例小于1％。养护有利于降低固化产物的浸出污染程度，30％的污泥固化产物养护3d后可作为垃圾填埋场日覆盖材料。     

硫酸锰废渣的浸出毒性及处理研究

研究了硫酸锰废渣的主要金属元素组成及浸出毒性,并采用锰渣加石灰混合的方法进行无害化处理,研究结果表明,硫酸锰废渣浸出液中Mn、Cd超标,锰渣加石灰混合处理的方法能有效降低废渣的浸出毒性,锰渣与石灰的重量比为25:2最佳.     

硫酸锰废渣的浸出毒性及处理研究

研究了硫酸锰废渣的主要金属元素组成及浸出毒性,并采用锰渣加石灰混合的方法进行无害化处理,研究结果表明,硫酸锰废渣浸出液中Mn、Cd超标,锰渣加石灰混合处理的方法能有效降低废渣的浸出毒性,锰渣与石灰的重量比为25：2最佳.     

造纸污泥固化/稳定化处理技术研究

为了能更好地无害化处理造纸污泥,对造纸污泥的固化/稳定化处理技术进行了研究。以水泥、粉煤灰和煤渣作为固化剂对造纸污泥进行固化/稳定化处理。通过抗压强度评价污泥固化块的力学性质;并对固化块浸出液的COD浓度与重金属质量浓度进行了检测。当水泥、粉煤灰和煤渣的掺量分别为0.12、0.02和0.10 kg/kg,养护时间为6 d时,固化块抗压强度达到360 kPa。结果表明,水泥和煤渣对提高造纸污泥固化块的抗压强度具有促进作用,而它们与粉煤灰对造纸污泥中的有机质和重金属均具有一定的固化作用。在以上条件下,固化块浸出液中COD浓度约为115.7 mg/L,重金属浓度符合国家标准。经养护后的固化块含水率均保持在35%~40%,符合填埋场的进场标准。     

城市河涌受污染底泥的固化/稳定化处理

为了给河涌疏浚底泥的资源化提供技术支持,以广州市车陂涌表层受污染底泥为研究对象,用水泥、石灰、粉煤灰、膨润土等材料对底泥进行固化/稳定化处理实验。通过无侧限抗压强度、污染物在模拟自然条件下(中性)的释放特征、毒性浸出实验(酸性条件)对固化/稳定化处理效果进行综合分析。结果表明:经合适的处理后,固化体抗压强度能高于300 kPa;固化体自然条件下重金属的释放量明显减少,固化/稳定化处理能够有效减缓和减少固化体的二次污染;毒性浸出实验结果表明,河涌底泥经固化/稳定化处理后其重金属浸出能力显著降低。     

含重金属水处理污泥的固化和浸出毒性研究

工业危险固体废物在进行安全填埋前需要进行固化稳定处理。针对电镀厂和皮革厂含重金属的水处理污泥，用不同比例的水泥、粉煤灰进行固化稳定处理。考虑酸雨环境，浸出实验采用TCLP标准。电镀厂污泥单独固化时，其浸出液中铜离子浓度由78．0mg／L下降到1．5mg／L；镍离子浓度由224．5mg／L下降到22．2mg／L，高于危险废物允许进入填埋区15mg／L的控制限值。电镀厂污泥与皮革厂污泥混合后固化，浸出液毒性明显降低。铜离子的浸出浓度降低到1．98mg／L，镍离子降低到4．10mg／L，总铬降低到0．40mg／L，各项指标均低于国家危险废物允许进入填埋区的控制限值，可安全填埋。     

SGA对垃圾焚烧飞灰中重金属的固化性能研究

根据EPA1311、HJ／T299—2007、HJ／T300—2007和HJ557—2009等国内外不同标准，研究了深圳某垃圾焚烧发电厂垃圾焚烧飞灰的浸出毒性，探讨了六硫代胍基甲酸（sixthioguanidineacid，SGA）、二甲基二硫代氨基甲酸盐（sodiumdimethyldithiocarbamate，SDD）和Ca（OH）2浓度对垃圾焚烧飞灰中重金属的固定性能的影响。研究结果表明，随着浸提液pH的降低，该厂焚烧飞灰中大部分金属元素的浸出量增大，焚烧飞灰浸出液中的cd、Ni、Ph和zn浓度分别超过国家危险废物鉴别标准（GB5085．3—2007）规定值的4．75倍、1．47倍、6．72倍和2．20倍，属于危险废弃物，必须进行稳定化处理。当固化剂SGA加入量为0．1mol／kg时，稳定化后的重金属浸出浓度已经低于危险废物鉴别标准，且对Cd、Cr、Cu和Pb的固化性能优于SDD和Ca（OH）2；当固化剂SGA、SDD和Ca（OH）2加入量为0．5mol／kg时，稳定化后的焚烧飞灰重金属浸出浓度均低于国家危险废物鉴别标准（GB5085．3-2007）中的规定值。与SDD和Ca（OH）：相比，SGA对垃圾焚烧飞灰中重金属的固化处理更具有优势。     

SGA对垃圾焚烧飞灰中重金属的固化性能研究简

根据EPA 1311、HJ/T 299-2007、HJ/T 300-2007和HJ 557-2009等国内外不同标准，研究了深圳某垃圾焚烧发电厂垃圾焚烧飞灰的浸出毒性，探讨了六硫代胍基甲酸（sixthio guanidine acid，SGA）、二甲基二硫代氨基甲酸盐（sodium dimethyl dithio carbamate，SDD）和Ca（OH）₂浓度对垃圾焚烧飞灰中重金属的固定性能的影响。研究结果表明，随着浸提液pH的降低，该厂焚烧飞灰中大部分金属元素的浸出量增大，焚烧飞灰浸出液中的Cd、Ni、Pb和Zn浓度分别超过国家危险废物鉴别标准（GB5085.3-2007）规定值的4.75倍、1.47倍、6.72倍和2.20倍，属于危险废弃物，必须进行稳定化处理。当固化剂SGA加入量为0.1 mol/kg时，稳定化后的重金属浸出浓度已经低于危险废物鉴别标准，且对Cd、Cr、Cu和Pb的固化性能优于SDD和Ca（OH）₂；当固化剂SGA、SDD和Ca（OH）₂加入量为0.5 mol/kg时，稳定化后的焚烧飞灰重金属浸出浓度均低于国家危险废物鉴别标准（GB 5085.3-2007）中的规定值。与SDD和Ca（OH）₂相比，SGA对垃圾焚烧飞灰中重金属的固化处理更具有优势。     

Stabilization of APC residues from waste incineration with ferrous sulfate on a semi-industrial scale

A stabilization method for air pollution control (APC) residues from municipal solid waste incineration (MSWI) involving mixing of the residue with water and FeSO4 has been demonstrated on a semi-industrial scale on three types of APC residues: a semidry (SD) APC residue, a fly ash (FA), and an FA mixed with sludge (FAS) from a wet flue gas cleaning system. The process was performed in batches of 165-175 kg residue. It generates a wastewater that is highly saline but has a low content of heavy metals such as Cd, Cr, and Pb. The stabilized and raw residues have been subject to a range of leaching tests: the batch leaching test, the pH-static leaching test, the availability test, and the column test. These tests showed that the stabilized residues have remarkably improved leaching properties, especially with respect to Pb but also with respect to Cd, Cu, and Zn. The release of Pb was reduced by a factor of 250-36,000.     

Stabilization of APC Residues from Waste Incineration with Ferrous Sulfate on a Semi-Industrial Scale

Abstract

A stabilization method for air pollution control (APC) residues from municipal solid waste incineration (MSWI) involving mixing of the residue with water and FeSO₄ has been demonstrated on a semi-industrial scale on three types of APC residues: a semidry (SD) APC residue, a fly ash (FA), and an FA mixed with sludge (FAS) from a wet flue gas cleaning system. The process was performed in batches of 165-175 kg residue. It generates a wastewater that is highly saline but has a low content of heavy metals such as Cd, Cr, and Pb. The stabilized and raw residues have been subject to a range of leaching tests: the batch leaching test, the pH-static leaching test, the availability test, and the column test. These tests showed that the stabilized residues have remarkably improved leaching properties, especially with respect to Pb but also with respect to Cd, Cu, and Zn. The release of Pb was reduced by a factor of 250-36,000.     

Remediation of metal contaminated soil with mineral-amended composts

This study examined the use of two composts derived from green waste and sewage sludge, amended with minerals (clinoptilolite or bentonite), for the remediation of metal-contaminated brownfield sites to transform them into greenspace. Soils contaminated with high or low levels of metals were mixed with the mineral-enhanced composts at different ratios and assessed by leaching tests, biomass production and metal accumulation of ryegrass (Lolium perenne L.). The results showed that the green waste compost reduced the leaching of Cd and Zn up to 48% whereas the composted sewage sludge doubled the leachate concentration of Zn. However, the same soil amended with composted sewage sludge showed an efficient reduction in plant concentrations of Cd, Cu, Pb or Zn by up to 80%. The results suggest that metal immobilisation and bioavailability are governed by the formation of complexes between the metals and organic matter. The amendment with minerals had only limited effects.     

Remediation of metal-contaminated soils with the addition of materials - part II: leaching tests to evaluate the efficiency of materials in the remediation of contaminated soils

The effect of the addition of materials on the leaching pattern of As and metals (Cu, Zn, Ni, Pb, and Cd) in two contaminated soils was investigated. The examined materials included bentonites, silicates and industrial wastes, such as sugar foam, fly ashes and a material originated from the zeolitization of fly ash. Soil + material mixtures were prepared at 10% doses. Changes in the acid neutralization capacity, crystalline phases and contaminant leaching over a wide range of pHs were examined by using pH_stat leaching tests. Sugar foam, the zeolitic material and MX-80 bentonite produced the greatest decrease in the leaching of pollutants due to an increase in the pH and/or the sorption capacity in the resulting mixture. This finding suggests that soil remediation may be a feasible option for the reuse of non-hazardous wastes.     

垃圾焚烧飞灰浸出特性及固化试验的研究

垃圾焚烧飞灰残留有重金属元素和二恶英等物质而被认为是危险废物,必须对之进行稳定化处理.通过试验研究分析了国内首家自主开发成功的广东省东莞市某回转窑垃圾焚烧发电厂垃圾焚烧飞灰的化学成分及矿物组成,研究了飞灰的浸出毒性,考察了水泥固化焚烧飞灰的效果,并与熔融/玻璃固化进行了比较.研究表明,该焚烧飞灰中重金属Cd的浸出毒性严重超标,并且随pH值的减小而增大,水泥固化效果随龄期的增大而更加显著.熔融/玻璃固化的效果优于水泥固化,但其经济性有待提高.     

Arsenic contaminated site at an abandoned copper smelter plant: waste characterization and solidification/stabilization treatment

A preliminary survey of an arsenic contaminated site from an abandoned copper smelting facility and feasibility study of using solidification/stabilization (S/S) process to treat the contaminant waste were undertaken. It was found that the waste, located in the three-flue gas discharge tunnels, contained 2-40% arsenic. The pH of the contaminated waste is extremely low (ranging from 1.8 to 3.6). The X-ray diffraction evidence indicates that the arsenic particles present in the flue gas mainly exist as As(III), or As(2)O(3). The total amount of arsenic contaminated waste is estimated to be 700 ton in the studied area. About 50% of the particle sizes are less than 2 mm. Arsenic is easily extracted from wastes with a variety of leaching solutions. In order to meet the arsenic leaching standard of the toxicity characteristic leaching procedure (TCLP), an extremely high cement dosage is required in the S/S process (cement/waste weight ratio>6). The waste with lower particle size having higher specific surface area exhibits somewhat positive effect on the S/S performance. The use of fly ash from municipal waste incinerators, in conjunction with the reduced amount of cement, is able to meet the TCLP arsenic and lead standards. The use of lime alone could meet the TCLP arsenic standard, but lead leaching concentrations exceeded leaching Pb standard. The results of semi-dynamic leaching tests of some solidified samples indicate higher accumulated arsenic leaching concentrations after only a few leachant renewals.     

The leachability and chemical speciation of selected trace elements in fly ash from coal combustion and refuse incineration

A laboratory leaching test has been used to predict the potential mobility of As, Se, Pb and Cd in landfilled fly ash produced by coal combustion and refuse incineration. These waste residues also formed the basis of a speciation study in which the valency states of As and Se and the chemical forms of Pb and Cd have been determined. Selenium displayed the greatest leachability in each ash type, despite being present at relatively low concentrations in both materials. Substantial amounts of other trace elements were also leached, particularly Pb and Cd from refuse ash and As from coal ash. Chemical associations of Pb and Cd were examined by a sequential extraction procedure. In coal fly ash, both elements were mostly present in the residual fraction, while in refuse ash these elements were mainly associated with the exchangeable fraction. Water-soluble extracts of coal fly ash contained As exclusively as As(V); high background interference prevented the detection of water-soluble As in refuse ash. Selenium was present largely as Se(IV) in aqueous extracts of both ash types. The value of speciation techniques and leaching tests as predictors of environmental behaviour is discussed in conjunction with results of routine trace element determinations and plant uptake studies.     

Screening of heavy metal containing waste types for use as raw material in Arctic clay-based bricks

In the vulnerable Arctic environment, the impact of especially hazardous wastes can have severe consequences and the reduction and safe handling of these waste types are therefore an important issue. In this study, two groups of heavy metal containing particulate waste materials, municipal solid waste incineration (MSWI) fly and bottom ashes and mine tailings (i.e., residues from the mineral resource industry) from Greenland were screened in order to determine their suitability as secondary resources in clay-based brick production. Small clay discs, containing 20 or 40% of the different particulate waste materials, were fired and material properties and heavy metal leaching tests were conducted before and after firing. Remediation techniques (washing in distilled water and electrodialytical treatment) applied to the fly ash reduced leaching before firing. The mine tailings and bottom ash brick discs obtained satisfactory densities (1669–2007 kg/m³) and open porosities (27.9–39.9%). In contrast, the fly ash brick discs had low densities (1313–1578 kg/m³) and high open porosities (42.1–51. %). However, leaching tests on crushed brick discs revealed that heavy metals generally became more available after firing for all the investigated materials and that further optimisation is therefore necessary prior to incorporation in bricks.