三元体系M(NO3)n-CH3CONHCONH2-H2O相平衡的研究

研究了题述２个（Ｍ＝Ｚｎ,ｎ＝２,Ｍ＝Ｌａ,ｎ＝３）三元体系在３０℃的相平衡,测定了饱和溶液的党妥度及其折光指数,给制了相应的溶度图和折光指数－组成关系图。Ｌａ（ＮＯ３）３体系溶度曲线及折光指数曲线均由３支组成,分别与Ｌａ（ＮＯ３）．６Ｈ２Ｏ、Ｌａ（ＮＯ３）３．３Ｈ２Ｏ和ＣＨ３ＣＯＮＨＣＯＮＨ２相对应。２个共饱点的组成分别为：Ｌａ（ＮＯ３）３５８．３４％,ＣＨ３ＣＯＮＨＣＯＮＨ２１６．５３％和Ｌａ     

四元体系Na2B4O7—Na2CO3—NaCl—H2O在0℃时的等温溶度研究

第一次用等温方法测定了含硼酸盐的三元边界体系Ｎａ２Ｂ４Ｏ７－ＮａＣｌ－Ｈ２Ｏ和四元体系Ｎａ２Ｂ４Ｏ７－Ｎａ２ＣＯ３－ＮａＣｌ－Ｈ２Ｏ在０℃时的溶度。结果发现它们都是低共饱型体系。在三元体系中共饱点组成为ＮａＣｌ２６．１９％,Ｎａ２Ｂ４Ｏ７０．３６％（质量）;四元体系中共饱点组成为ＮａＣｌ２３．５５％,Ｎａ２Ｂ４Ｏ７０．６２％,Ｎａ２ＣＯ３４．０７％（质量）,并且绘出了四元体系中的溶度图和等水线。     

三元体系LaX3—PIAP—H2O（30℃,X^—=NO^—3,Cl^—）相平衡研究

测定了三元体系ＬａＸ３－ＰＩＡＰ－Ｈ２Ｏ（Ｘ－＝ＮＯ－３，Ｃｌ－）在３０℃时的溶度和饱和溶液的折光率，给出了相应的溶度图和饱和溶液的折光率－组成图．这两个体系在３０℃时均为简单共饱型．     

Ce（NO3）3.3H2O—18C6—CH3CN三元体系相平衡的研究

采用半微量相平衡方法研究了三元体系Ｃｅ（ＮＨ３）３．３Ｈ２Ｏ－１８Ｃ６－ＣＨ３ＣＮ在３０３．１５Ｋ的溶解度,测定了饱和溶液的折光率。该体系中仅生成一种化学计量的配合物Ｃｅ（ＮＯ３）３．１８Ｃ６．３Ｈ２Ｏ,其存在的相区较大,初步排除了其它组成配合物存在的可能性。     

Gd（NO_3）_3／Er（NO_3）_3－Gly－H_2O三元体系的研究（25

测定了Ｇｄ（ＮＯ_３）_３／Ｅｒ（ＮＯ_３）_３－Ｇｌｙ－Ｈ_２Ｏ三元体系在２５℃时的溶度和饱和溶液折光率。各体系的溶度和饱和溶液折光率曲线均由４支组成，分别与ＲＥ（ＮＯ_３）_３·ｎＨ_２Ｏ（ＲＥ＝Ｇｄ，ｎ＝６；ＲＥ＝Ｅｒ，ｎ＝５）、配合物ＲＥ（Ｇｌｙ）_２（ＮＯ_３）_３·２Ｈ_２Ｏ，ＲＥ（Ｇｌｙ）_４（ＮＯ_３）_３·Ｈ_２Ｏ及Ｇｌｙ相对应。     

Gd（NO3）3／Er（NO3）3—Gly—H2O三元体系的研究（25℃）

测定了Ｇｄ（ＮＯ３）３／Ｅｒ（ＮＯ３）３－Ｇｌｙ－Ｈ２Ｏ三元体系在２５℃时的溶度和饱和溶液折光率。各体系的溶度和饱和溶液折光率曲线均由４支组成，分别与ＲＥ（ＮＯ３）３；ｎＨ２Ｏ配合物ＲＥ（Ｇｌｙ）２（ＮＯ３）３．２Ｈ２Ｏ，ＲＥ（Ｇｌｙ）４（ＮＯ３）３；Ｈ２Ｏ及Ｇｌｙ相对应。     

0℃时SmI3—（CH2）6N4.HI—H2O体系的相平衡研究

合成出ＳｍＩ３．９Ｈ２Ｏ和（ＣＨ２）６Ｎ４．ＨＩ,并测定了０℃时ＳｍＩ３－（ＣＨ２）６Ｎ４．ＨＩ－Ｈ２Ｏ体系的相平衡数据,作出该体系的相图、发现了新的配合物Ｓｍｉ３．「（ＣＨ２）６Ｎ４．ＨＩ」．１４Ｈ２Ｏ。     

Zn-Cl~--NH_3-CO_3~(2-)-H_2O 系的热力学分析

根据同时平衡原理和质量平衡原理,推导出Ｚｎ－Ｃｌ－－ＮＨ３－ＣＯ３２－－Ｈ２Ｏ系金属氧化物及碳酸盐在水溶液中热力学平衡的数学模型,计算并绘出该体系的浓度对数－ｐＨ图,研究了各配位体及ｐＨ值对该平衡体系的影响．当溶液有ＮＨ３和Ｃｌ－存在时,ＺｎＯ的溶解度增大;ＮＨ３的浓度对ＺｎＯ的溶解度的影响最大,因而不宜用氨水作为Ｚｎ２＋的沉淀剂．当溶液中有ＣＯ３２－存在时,Ｚｎ的溶解损失小;即使溶液中含有一些ＮＨ３,但溶液中Ｚｎ的总浓度还是比较小．当溶液中有ＣＯ３２－存在时不仅使Ｚｎ完全沉淀时的ｐＨ值降低了,而且ｐＨ值的范围也加宽了,因而可选用Ｎａ２ＣＯ３,（ＮＨ４）２ＣＯ３等作为Ｚｎ２＋的沉淀剂．根据溶液中［Ｃｌ－］Ｔ,［ＮＨ３］Ｔ,［ＣＯ３２－］Ｔ的不同,通过这些浓度对数－ｐＨ图可以在理论上初步选择Ｚｎ２＋沉淀的最佳ｐＨ值范围．     

极谱法测定Ce（Ⅲ）在NH4NO3—C2H5OH—H2O体系中的存在形式

报道了Ｃｅ（Ⅲ）在ＮＨ４ＮＯ３－Ｃ２Ｈ５ＯＨ－Ｈ２Ｏ体系中形成配合物的事实,测定其具体存在形式可表述为：（Ｃｅ（ＮＯ３）５Ｃ２Ｈ５ＯＨ）＾２－。     

RE（NO_3）_3－Ala－H_2O三无体系在25℃时的半微量相平衡研究

测定了ＲＥ（ＮＯ_３）_３－Ａｌａ－Ｈ_２Ｏ（ＲＥ＝Ｓｍ，Ｇｄ，Ｅｒ）三元体系在２５℃时的溶解度和饱和溶液折光率，绘制了相应的溶解度图与饱和溶液折光率曲线。各体系的溶解度曲线与折光率曲线均由４支组成，分别与ＲＥ（ＮＯ＿３）３．ｎＨ＿２Ｏ（ＲＥ＝Ｓｍ，Ｇｄ，ｎ＝６；ＲＥ＝Ｅｒ，ｎ＝５），ＲＥ（Ａｌａ）（ＮＯ＿３）３·Ｈ＿２Ｏ，ＲＥ（Ａｌａ）＿４（ＮＯ＿３）＿３·Ｈ＿２Ｏ和Ａｌａ的晶体相对应．     

高Bi_2O_3低B_2O_3含量的PbO－Bi_2O_3－B_2O_3系统研

通过传统熔体冷却方法确定了高Ｂｉ２Ｏ３低Ｂ２Ｏ３含量的ＰｂＯ－Ｂｉ２Ｏ３－Ｂ２Ｏ３系统形成玻璃的最少Ｂ２Ｏ３引入量；利用Ｘ射线衍射分析和红外光谱分析方法研究了由Ｐｂ３Ｏ４，Ｂｉ２Ｏ３单一氧化物、高Ｂｉ２Ｏ３含量的ＰｂＯ－Ｂｉ２Ｏ３二元系统及高Ｂｉ２Ｏ３低Ｂ２Ｏ３含量的ＰｂＯ－Ｂｉ２Ｏ３－Ｂ２Ｏ３三元系统经熔融冷却而获得物质的结构特点，探讨了少量Ｂ２Ｏ３的引入对该三元系统形成玻璃的作用和形成无定形结构的可能机制。     

SiO2-Al2O3-ZnO-SrO-La2O3系微晶玻璃性能的研究

SiO2-Al2O3-ZnO-SrO-La2O3为基本成分制备了微晶玻璃样品,在750℃下不同时间热处理。用微波微扰法测量其微波介电性能,结合扫描电镜和X射线衍射分析了其晶相。结果表明,随保温时间的延长,样品的主晶相经历了SrZrSi2O7→SrAl2Si2O8→新玻璃相La2ZrTiO7的变化。SrAl2Si2O8相是亚稳过渡相。反应生成的新玻璃相La2ZrTiO7的Q值高达1800,温度系数约为＋500×10^-6／℃。     

Fe2O3-MoO3-Sb2O3体系中的固相反应

通过混合焙烧的方法制备Fe2O3MoO3Sb2O3复合氧化物.采用X射线衍射(XRD)、同步热重差示扫描量热(TGDSC)和穆斯堡尔(Mssbauer)谱研究Fe2O3MoO3Sb2O3三组分体系在不同温度下的固相反应,并分别与Fe2O3MoO3和Fe2O3Sb2O3双组分体系的结果加以对比.结果表明,Sb2O3加入到Fe2O3MoO3体系中抑制了Fe2(MoO4)3的形成,而MoO3加入到Fe2O3Sb2O3体系,则可显著促进FeSbO4的生成.     

La2O3-Al2O3-SiO2 glass-infiltrated 3Y-TZP all-ceramic composite for the dental restorative application

The 3 mol％ yttria stabilized tetragonal zirconia polycrystals (3Y-TZP) powder had three particle size distributions,while the fine one was lower than 100 nm.The 3Y-TZP compact was prepared by dry-press...     

Relationship between luminescence and matrices in the system Al_2O_3-B_2O_3-C_2O_3

The system Al-2O-3-B-2O-3-Ce-2O-3, with Al/B ratio varying from 4.5 to 2 and Ce/(Al+B)=0.02, has been prepared at the temperature from 1 200 to 1 400℃. Relationship between luminescence and matrices in the system Al-2O-3-B-2O-3-Ce-2O-3 was investigated. It was found that some changes of the matrices occurred with Al/B ratio varying from 4.5 to 2. These results lead to a great change in luminescence properties, indicating variation of Ce-surroundings of crystal field. With the decrease of the ratio from 3 to 2, the excitation and emission peaks shift to shorter wavelengths. It was also found that a new type of rare earth luminescent materials was obtained with appropriate Al/B ratio.     

Ce~(3+)和Tb~(3+)掺杂的BaO-La_2O_3-B_2O_3-SiO_2玻璃的发光性质

采用传统熔体冷却技术制备Ce~(3+)和Tb~(3+)掺杂的BaO-La_2O~3-B_2O_3-SiO_2玻璃,并测试样品的吸收光谱和荧光光谱.实验结果表明:由于Ce~(3+)在5d-4f轨道之间的电子跃迁,基础玻璃掺Ce~(3+)后吸收截止边明显红移;掺Ce~(3+)的BaO-La_2O_3-B_2O_3-SiO_2玻璃的荧光发射光谱为峰值位于410 nm附近的宽带,对应于Ce~(3+)的5d-4f跃迁;由于SiO~2比B_2O_3的光碱度大,玻璃的荧光发射波长,体现出随硼硅比的降低而略有红移;还原性气氛有利十提高玻璃中Ce~(3+)的含量,从而增强发光强度;对Ce~(3+)和Tb~(3+)共掺玻璃,Ce~(3+)和Tb~(3+)在波长200-311 nm间有激发带重叠,因存在竞争吸收,导致以此区间波长激发时Tb~(3+)的发光有所减弱;Ce~(3+)和Tb~(3+)在311-444 nm间也有激发带(或激发带与发射带)部分重叠,因Ce~(3+)和Tb~(3+)之间存在的辐射和无辐射能量传递导致Ce~(3+)强烈敏化Tb~(3+)的发光.     

K2O-MgO-SiO2-Al2O3-B2O3-F玻璃陶瓷的烧结析晶

利用弯曲试验、X射线衍射分析和扫描电镜等手段,研究了烧结K2O-MgO-SiO2-Al2O3-B2O3-F玻璃陶瓷时烧结温度对材料密度、抗弯强度及析晶性能的影响.研究结果表明:在低温区(900℃)烧结时,玻璃陶瓷析晶少,密度和抗弯强度低;随烧结温度提高,烧结体密度、抗弯强度、析晶率不断提高,在1050℃时均达到最大值(密度约为2 39g/cm3,抗弯强度约为80MPa);温度继续升高到1100℃时,密度、抗弯强度和析晶率都有所降低.     

Preparation and radar-absorbing properties of Al_2O_3/TiO_2/Fe_2O_3/Yb_2O_3 composite powder

Al_2O_3/Ti O_2/Fe_2O_3/Yb_2O_3 composite powder was synthesized via the sol–gel method. The structure,morphology,and radar-absorption properties of the composite powder were characterized by transmission electron microscopy,X-ray diffraction analysis and RF impedance analysis. The results show that two types of particles exist in the composite powder. One is irregular flakes(100–200 nm) and the other is spherical Al_2O_3 particles(smaller than 80 nm). Electromagnetic wave attenuation is mostly achieved by dielectric loss. The maximum value of the dissipation factor reaches 0.76(at 15.68 GHz) in the frequency range of 2–18 GHz. The electromagnetic absorption of waves covers 2–18 GHz with the matching thicknesses of 1.5–4.5 mm. The absorption peak shifts to the lower-frequency area with increasing matching thickness. The effective absorption band covers the frequency range of 2.16–9.76 GHz,and the maximum absorption peak reaches-20.18 d B with a matching thickness of 3.5 mm at a frequency of 3.52 GHz.     

由FeO—V2O3和V2O3-SiO2二元相图提取活度

本文研究了在正规溶液的假设下,运用由二元相图提取活度的方法,分别计算了FeO—V2O3和V2O3-SiO2渣系相图在2500K温度下的活度。经加权平均计算,计算值和实验值的相对误差分别为13．34％和6．5％．这个精度处于Turkdogan提出的10％-30％的实验误差范围以内,可以作为进一步研究复杂含钒渣系时的热力学参考数据。