Preparation of 0.7Pb(Mg1/3Nb2/3)O3–0.3PbTiO3 Thin Films Via a Polyvinylpyrrolidone-Assisted Aqueous Sol–Gel Process and Dielectric Properties

Pb(Mg_1/3Nb_2/3)O₃–PbTiO₃ (PMN–PT) thin films were prepared by spin coating using aqueous solutions of metal salts containing polyvinylpyrrolidone, where niobium oxide layers and lead—magnesium–titanium oxide layers were laminated on Pt(111)/TiO _x /SiO₂/Si(100) substrates and fired at 750° or 800°C. 250 ± 20 nm thick 0.7PMN–0.3PT thin films of a single-phase perovskite could be prepared, and the film fired at 750°C had dielectric constants and dielectric loss of 1900 ± 350 and 0.13 ± 0.03, respectively, exhibiting polarization-electric field hysteresis with a remanent polarization of 5.1 μC/cm² and a coercive field of 21 kV/cm.     

In-Plane Polarized 0.7Pb(Mg1/3Nb2/3)O3–0.3PbTiO3 Thin Films

Ferroelectric 0.7Pb(Mg_1/3Nb_2/3)O₃–0.3PbTiO₃ (PMN-PT) thin films were deposited on ZrO₂/SiO₂/silicon substrates using a chemical-solution-deposition method. Using a thin PZT film as a seed layer for the PMN-PT films, phase-pure perovskite PMN-PT could be obtained via rapid thermal annealing at 750°C for 60 s. The electrical properties of in-plane polarized thin films were characterized using interdigitated electrode arrays on the film surface. Ferroelectric hysteresis loops are observed with much larger remanent polarizations (∼24 μC/cm²) than for through-the-thickness polarized PMN-PT thin films (10–12 μC/cm²) deposited on Pt/Ti/Si substrates. For a finger spacing of 20 μm, the piezoelectric voltage sensitivity of in–plane polarized PMN-PT thin films was ∼20 times higher than that of through-the-thickness polarized PMN-PT thin films.     

Synthesis and Dielectric Properties of Solution Sol-Gel-Derived 0.9Pb(Mg1/3Nb2/3)O3–0.1PbTiO3 Ceramics

A solution sol-gel method has been developed to prepare 0.9Pb(Mg_1/3Nb_2/3)O₃-0.1PbTiO₃ (0.9PMN-0.1PT) ceramics. During the processing the gel first converted to cubic pyrochlore phase at a calcination temperature of 600°C followed by the formation of pure perovskite phase at 775°C. The ceramics sintered at 1250°C for 4 h showed ≈98% of the theoretical density. The room-temperature dielectric constant of the pellets sintered at 1250°C showed a maximum value of 25035 at 1 kHz. Sintering studies at different temperatures revealed that the dielectric constant increased with increasing grain size in these ceramics.     

Processing and Electrical Properties in Lead-Based (Pb(Mg1/3Nb2/3)O3, Pb(Yb1/2Nb1/2)O3, PbTiO3) Systems

Lead-based ferroelectric (FE) ceramics exhibit superior electromechanical properties; therefore, there has been an increased focus on developing new lead-based FE materials with high Curie temperature ( T _c) and enhanced properties. The aim of this study was to investigate new compositions in the Pb(Mg_1/3Nb_2/3)O₃–Pb(Yb_1/2Nb_1/2)O₃–PbTiO₃ ( PMN–PYbN–PT) system to enhance the electromechanical properties while increasing the T _c and lowering the sintering temperature. The 0.575[0.5PMN–0.5PYbN]–0.425PT composition at PMN/PYbN (50/50) mole ratio were prepared by reactive sintering PMNT and PYbNT powder mixtures at 950°–1200°C for 4 h. PMNT and PYbNT powders were calcined via the columbite method. Samples were prepared by cold isostatic pressing at 80 MPa. Dense and fully perovskite 0.575[0.5PMN–0.5PYbN]–0.425PT ceramics were fabricated at 975°C for 4 h, and these samples displayed a remnant polarization ( P _r) of 32 μ C/cm², coercive field ( E _c) of 17 kV/cm, and a piezoelectric charge coefficient ( d ₃₃) of 475 pC/N. It is proposed that this ternary system can be tailored for various applications.     

Single-Calcination Synthesis of Pyrochlore-Free 0.9Pb(Mg1/3Nb2/3)O3–0.1PbTiO3 and Pb(Mg1/3Nb2/3)O3 Ceramics Using a Coating Method

A coating approach for synthesizing 0.9Pb(Mg_1/3Nb_2/3)O₃–0.1PbTiO₃ (0.9PMN–0.1PT) and PMN using a single calcination step was demonstrated. The pyrochlore phase was prevented by coating Mg(OH)₂ on Nb₂O₅ particles. Coating of Mg(OH)₂ on Nb₂O₅ was done by precipitating Mg(OH)₂ in an aqueous Nb₂O₅ suspension at pH 10. The coating was confirmed using optical micrographs and zeta-potential measurements. A single calcination treatment of the Mg(OH)₂-coated Nb₂O₅ particles mixed with appropriate amounts of PbO and PbTiO₃ powders at 900°C for 2 h produced pyrochlore-free perovskite 0.9PMN–0.1PT and PMN powders. The elimination of the pyrochlore phase was attributed to the separation of PbO and Nb₂O₅ by the Mg(OH)₂ coating. The Mg(OH)₂ coating on the Nb₂O₅ improved the mixing of Mg(OH)₂ and Nb₂O₅ and decreased the temperature for complete columbite conversion to ∼850°C. The pyrochlore-free perovskite 0.9PMN–0.1PT powders were sintered to 97% density at 1150°C. The sintered 0.9PMN–0.1PT ceramics exhibited a dielectric constant maximum of ∼24 660 at 45°C at a frequency of 1 kHz.     

High Piezoelectric and Dielectric Properties of La-Doped 0.3Pb(Zn1/3Nb2/3)O3–0.7Pb(ZrxTi1−x)O3 Ceramics Near Morphotropic Phase Boundary

La-doped 0.3Pb(Zn_1/3Nb_2/3)O₃–0.7Pb(Zr _x Ti_{1− x} )O₃ ( x =0.5–0.53) piezoelectric ceramics with pure perovskite phase were synthesized by a two-step hot-pressing route. The piezoelectric properties of various compositions near the morphotropic phase boundary (MPB) were systematically investigated. Not only was the exact MPB of this system determined via X-ray diffractometry analysis, but also the peak of piezoelectric properties was found near the MPB. The optimum piezoelectric properties of this series were observed in the specimen with Zr/Ti=51/49. The piezoelectric coefficient ( d ₃₃) and electromechanical coupling factor ( k _p) were 845 pC/N and 0.70, respectively, which have not been reported in this system so far. Large permittivity (ɛ_r=4088) and permittivity maximum (ɛ_m=29 500) were also obtained for the poled specimens. The temperatures ( T _max) of the permittivity maxima ranged from 206° to 213°C with various Zr/Ti ratios.     

Preparation and Characterization of Relaxor Ferroelectric 0.65Pb(Mg1/3Nb2/3)O3–0.35PbTiO3 by a Polymerizable Complex Method

A modified polymerizable complex (PC) method for the preparation of the relaxor ferroelectric 0.65Pb(Mg_1/3Nb_2/3)O₃–0.35PbTiO₃ (PMN–PT) ceramics has been developed using a novel water-soluble Nb precursor. The effects of Pb content and sintering temperature on the structure, morphology, composition, and electrical properties of PMN–PT powders and ceramics were investigated systematically. It was found that the modified PC method could effectively reduce the initial crystallization temperature of the perovskite phase to 500°C. For PMN–PT samples with 15% excess Pb content sintered at 600°C for 2 h, the 87% perovskite phase can be achieved, which is much higher than that in conventional solid-state reactions and other solution-based methods at the same temperature. On further increasing the sintering temperature to 1100°C, the perovskite phase content basically remains constant. This is attributed to the Pb-deficient pyrochlore phase formation. On increasing the sintering temperature to 1250°C, the dielectric constant and remnant polarization of PMN–PT ceramics significantly improved due to the larger grain sizes, enhanced density, and the decreasing pyrochlore phase. PMN–PT ceramics with a 98.5% content of the perovskite phase have been fabricated at 1250°C. It displays typical ferroelectric relaxor characteristics with a remnant polarization of 18 μC/cm², a coercive field of 9.6 kV/cm, a piezoelectric coefficient of d ₃₃=360 pC/N, and room-temperature and maximum dielectric constants of 3600 and 10 500 at 1 kHz, respectively.     

Solid-State Epitaxial Effects in Structurally Diphasic Xerogel of Pb(Mg1/3Nb2/3)O3

Lead magnesium niobate (PMN), Pb(Mg_1/3Nb_2/3)O₃, with perovskite structure has been prepared using structurally diphasic PMN gels. The diphasic gels were made using various concentrations of perovskite PMN seeds. The unseeded gel calcined at 775°C for 2 h gave ∼98% of perovskite PMN phase. The use of 1% PMN perovskite seed not only led to a pure perovskite phase but also lowered the crystallization temperature of these gels by about 75°C. These results show that isostructural seeding helps to lower the crystallization temperature of perovskite PMN phase.     

Preparation of Dense Lead Magnesium Niobate–Lead Titanate (Pb(Mg1/3Nb2/3)O3–PbTiO3) Ceramics by Spark Plasma Sintering

The effect of spark plasma sintering (SPS) on the densification behavior of Pb(Mg_1/3Nb_2/3)O₃–PbTiO₃ ceramics has been investigated. Specimens with a density of >99% of the theoretical density (TD) were obtained using SPS treatment at 900°C. Through normal sintering at 1200°C, however, the density of the specimen was only ∼92% of TD.     

B-Site Order–Disorder Transition in Pb(Mg1/3Nb2/3)O3–Pb(Mg1/2W1/2)O3 Triggered by Mechanical Activation

B-site cation order–disorder transition induced by mechanical activation was observed in Pb(Mg_1/3Nb_2/3)O₃–Pb(Mg_1/2W_1/2)O₃ (PMN–PMW) solid solution, which was examined using both XRD diffraction and Raman spectroscopic study. The order–disorder transition is composition dependent. Mechanical activation triggers the B-site disordering, which can be steadily recovered by thermal annealing at elevated temperature, i.e., at temperatures around 600°C. Raman spectroscopy demonstrated that there existed tiny ordered microdomains in 0.4PMN·0.6PMW subjected to up to 20 h of mechanical activation, although they cannot be shown by X-ray diffraction. This is a result of the equilibrium between the mechanical destruction and temperature-facilitated recovering at the collision points during mechanical activation. It is therefore unlikely that a complete disordering can be realized in PMN–PMW by mechanical activation. The disordering in PMN–PMW triggered by mechanical activation occurs simultaneously with the refinement in crystallite size at the initial stage of mechanical activation, suggesting that the fragmentation of crystallites is responsible for the order–disorder transition at least during the initial stage of mechanical activation.     

Hierarchical Domain Structure of Adaptive MB Phase in Pb(Mg1/3Nb2/3)O3–32%PbTiO3 Single Crystal

The domain structure in Pb(Mg_1/3Nb_2/3)O₃–32%PbTiO₃ single crystal has been investigated with analytical electron microscopy. It is revealed that the M_B phase is an adaptive phase composed of 71° rhombohedral nanodomains and that the nanodomain walls are parallel to {110} planes by a combination of convergent beam electron diffraction and through-focus high-resolution image series. The findings suggest and are supportive of the viewpoint that the M_A phase could also be an adaptive phase composed of 109° rhombohedral nanodomains with domain walls parallel to {001} planes.     

Effect of Excess PbO on the Sintering Characteristics and Dielectric Properties of Pb(Mg1/3Nb2/3)O3–PbTiO3-Based Ceramics

Additions of excess PbO to the perovskite Pb[(Mg_1/3Nb_2/3)_0.92Ti_0.08]O₃ solid solution enhanced the formation of a liquid phase at 840°C, which served as a densification aid for the ceramics. The liquid phase allowed elimination of pores and promoted grain growth during sintering. With additions of 1 to 2 wt% excess PbO, densities in excess of 97% of theoretical were obtained at a sintering temperature of 950°C. The peak dielectric constants of the resulting ceramics were over 18 000 at 30°C and dissipation factors less than 1%. Additions of PbO in excess of 2 wt% resulted in inferior dielectric properties due mainly to the dilution of the ferroelectric phase.     

Synthesis of Pb(Mg1/3Nb2/3)O3 in Excess Lead Oxide by Mechanical Activation

Twenty hours of mechanical activation of mixed oxides at room temperature led to the formation of Pb(Mg_1/3Nb_2/3)O₃ (PMN) in excess PbO. The crystallinity of the activation-derived perovskite PMN phase was further established when the activated PMN–PbO phase mixture was subjected to calcination at 800°C. Pyrochlores, such as Pb₃Nb₄O₁₃ and Pb₂Nb₂O₇, were not observed as transitional phases on mechanical activation and subsequent calcination, although 50% excess PbO was deliberately added. The perovskite PMN phase was recovered by washing off excess PbO using acetic acid solution at room temperature. It was sintered to a relative density of 98.9% of theoretical at 1200°C for 1 h and the sintered PMN exhibited a dielectric constant of ∼14 000 at 100 Hz and a Curie temperature of −11°C.     

Dielectric-State Analysis in Solid-Solution Pb(Yb1/2Ta1/2)O3–Pb(Lu1/2Nb1/2)O3

The structure and temperature dependence of complex lead perovskite dielectrics were investigated for the system (1 − x )Pb(Yb_1/2Ta_1/2)O₃– x Pb(Lu_1/2Nb_1/2)O₃. Superlattice reflections for the compositions 0.8 < x < 1.0 were observed by X-ray diffractometry, and the temperature-composition dielectric-state diagram was determined. In the present study, the disordered middle composition, with 0.2 < x < 0.8, showed a diffuse paraelectric–ferroelectric phase transition, whereas the ordered end compositions, with 0 ≤ x < 0.2 and 0.8 < x ≤ 1.0, revealed successive sharp paraelectric–antiferroelectric and weak antiferroelectric–ferroelectric phase transitions. The dielectric state was confirmed by examining the variation of polarization ( P ) with electric field ( E ).     

Structure–Property Relations in xBaTiO3–(1−x)La(Mg1/2Ti1/2)O3 Solid Solutions

The microwave dielectric properties and microstructures of compounds in the solid solution series x BaTiO₃–(1− x )La(Mg_1/2Ti_1/2)O₃ (BTLMT) have been investigated. The structural phase transitions that occur as a function of x have been studied and are related to changes in the dielectric properties. For compounds where x ≤ 0.1, X-ray diffraction (XRD) showed evidence of 1:1 ordering between Mg and Ti cations. For x ≤ 0.3, XRD and electron diffraction revealed that compounds were tilted in both antiphase and in-phase. However, for 0.3 < x < 0.7, only antiphase tilting was present. The temperature coefficient of resonant frequency (τ_f) vs the relative permittivity (ɛ_r) was linear until x = 0.5 at which point in the solid solution the transition to a nontilted structure resulted in nonlinear behavior. τ_f values close to zero (−2 ppm/°C) were achieved at x = 0.5 (ɛ_r∼ 60), which had a quality factor ( Q · f _o) of 9600 GHz.     

Structure and Dielectric Properties of Pb(Sc2/3W1/3)O3–Pb(Zr/Ti)O3 Relaxors

The structure and dielectric properties of (1− x )Pb(Sc_2/3W_1/3)O₃–( x )Pb(Zr/Ti)O₃ ceramics have been investigated over a full substitution range. All compositions with x < 0.5 adopt a cubic perovskite structure; however, for x ≤ 0.25 a doubled cell results from a 1:1 ordered distribution of the B-site cations. The structural order in Pb(Sc_2/3W_1/3)O₃ (PSW) can be described by a random-site model with one cation site occupied by Sc³⁺ and the other by a random distribution of (Sc_1/3³⁺W_2/3⁶⁺). The ordering is destabilized in solid solutions of PSW with PbZrO₃ (PSW–PZ), but stabilized by PbTiO₃ in the (1− x )PSW–( x )PT system. The changes in order are accompanied by alterations in the dielectric response of the two systems. For PSW–PZ the temperature of the permittivity maximum ( T _ɛ,max) increases linearly with x ; however, for PSW–PT T _ɛ,max decreases in the ordered region (up to x = 0.25) and then increases rapidly as the order is lost. Similar effects were produced by modifying the degree of order of (0.75)PSW–(0.25)PT; when the order parameter was reduced from ∼1.0 to ∼0.65, T _ɛ,max increased by more than 60°C.     

Ferroelectric 90° Domain Evaluation in Tetragonal Pb(Mg1/3Nb2/3)O3–PbTiO3 Ceramics

The domain structure of ferroelectrics changes during poling has a direct influence on the macroscopic properties of the materials. The intensity variation of the different X-ray diffraction (XRD) pattern profiles was used to identify the percentage of 90° domain reorientation in the tetragonal phase of Pb(Mg_1/3Nb_2/3)O₃–PbTiO₃ (PMN–PT) ceramics after poling. The results are consistent with the change of piezoelectric properties. In addition, by using XRD patterns, a spatial distribution of polarization in a well-poled 0.62PMN–0.38PT ceramics has been determined and was found to be best described by the Cauchy function W _00l (φ)=1/(1+0.023φ²).     

Perovskite Phase Formation in the Relaxor System [Pb(Fe1/2Nb1/2)O3]1-x–[Pb(Zn1/3Nb2/3)O3]x

Phase formation and dielectric properties of the compositions in the system [Pb(Fe_1/2Nb_1/2)O₃]₁_ _x –[Pb(Zn_1/3Nb_2/3)O₃] _x were investigated as possible materials for multilayer ceramic capacitors. The formation of the phase with perovskite structure and dielectric properties of ceramics at room temperature in the entire composition range are presented. The undesirable pyrochlore phase can be suppressed up to x = 0.6 by adopting calcination of B-site oxides, followed by reaction with PbO. Compositions in the single-phase range can be sintered at less than 1000°C.