Cr，Ni奥氏作焊缝结晶模式判断关系式的建立

在分析和归纳现有大量实验数据的基础上建立了判断Ｃｒ，Ｎｉ奥氏体焊缝结晶模式的Ｃｒ，Ｎｉ当量关系式。当Ｃｒｅｑ≥１．５７８Ｎｉｅｑ—０．４４时，焊缝以ＦＡ模式结晶，焊缝中不易出现凝固裂纹；当Ｃｒｅｑ≤１．５７８Ｎｉｅｑ－１．３６时，焊缝则以先析出奥氏体的ＰＡ模式结晶，热裂倾向性较大。用实验数据验证了判断关系式。上述判断关系式的建立，提供了焊缝热裂敏感性预测的手段。     

Cr,Ni奥氏体焊缝结晶模式判断关系式的建立

在分析和归纳现有大理实验数据的基础了建立了判断Ｃｒ，Ｎｉ奥氏体焊缝结晶模式的Ｃｒ，Ｎｉ当量关系式。当Ｃｒｅｑ≥１．５７８Ｎｉｅｑ－０．４４时，焊缝中不易出现凝固裂纹；当Ｃｒｅｑ≤１．５７８Ｎｉｅｑ－１．３６时，焊缝则以先析出奥氏体的ＰＡ模式结晶，热裂倾向性较大。用实验数据验证了判断关系。上述判断关系式的建立，提供了焊缝热裂敏感性预测的手段。     

30CrMo钢和40CrNi钢埋弧自动焊焊缝金属的强韧化研究

对３０ＣｒＭｏ和４０ＣｒＮｉ钢埋弧自动焊焊缝金属的强韧化进行了初步研究。结果表明控制好焊缝金属的合金化程度,能细化针状铁素体,阻止Ｍ－Ａ组元脆化、使焊缝金属达到良好的强韧性配合,并且能有效地防止焊拉结晶是裂纹的生产。     

我国热作模具钢性能数据集（续Ⅳ）

(4 )　 3Ｃｒ2ＭｏＷＶＮｉ钢3Ｃｒ2ＭｏＷＶＮｉ钢降低碳的含量 ,增加了钨和钒的含量 ,设想在提高钢的韧性同时 ,又能提高钢的热稳定性和耐磨性 ,也有助于减弱第二类回火脆性的敏感性。实测 3Ｃｒ2ＭｏＷＶＮｉ钢 60 0℃以上的高温性能除伸长率较低、80 0 90 0℃的变形抗力比 5ＣｒＮｉＭｏ钢高 ,热稳定性与 5ＣｒＭｎＭｏＳｉＶ钢相当外 ,其它高温性能 (强度、硬度、冲击韧性、抗氧化性、抗热疲劳性、耐热磨损性 )均优于 5ＣｒＮｉＭｏ钢、4 5Ｃｒ2ＮｉＭｏＶＳｉ钢和5ＣｒＭｎＭｏＳｉＶ钢。该钢有二次硬化效应和较高的热稳定性 ,因此使…     

30CrMo＆40CrNi钢焊接冷裂纹敏感性研究

对３０ＣｒＭｏ＆４０ＣｒＮｉ钢的焊接冷裂敏感性进行了研究,确定了采用手工电弧焊焊接３０ＣｒＭｏ＆４０ＣｒＮｉ钢的焊接材料。用透射电镜观察了ＨＡＺ组织的精细结构。结果表明,１００℃预热,２５０℃×２ｈ紧急后热影响区粗晶区可得到对防止冷裂纹有利的,以位错板条马氏体和下贝氏体为主,带有少量孪晶片状马氏体的显微组织。这不仅为评定３０ＣｒｅＭｏ和４０ＣｒＮｉ的抗裂性能提供了理论依据,而且对实际焊接生产具有重     

PIC—D型防渗碳剂的研制

采用反应防渗，致密层覆盖隔绝气氛防渗及氧化还原防渗机理，开发研制的ＰＩＣ－Ｄ型防渗碳剂，成本低廉价，无毒，无臭，无公害。具有良好的低、高温性能，适用于２０ＣｒＭｎＴｉ钢以及２０Ｃｒ钢、３０ＣｒＭｎＴｉ钢、２０钢等常用渗碳钢的防渗处理，对其它渗碳及碳氮共渗钢也有一定的防渗效果。     

超低碳贝氏体WDB620钢及其焊接性

介绍了超低碳贝氏体WDB620钢的力学性能，用几种传统的焊接性试验方法对该钢焊接接头的力学性能及抗裂性进行了研究。结果表明，超低碳贝氏体WDB620钢具有良好的强韧性；当焊接热输入量小于35kJ／cm时，焊接接头性能良好。该钢具有很低的焊接冷裂纹敏感性。     

新型高温用渗碳轴承钢的接触疲劳寿命

研究了新型高温用渗碳轴承钢（１０Ｃｒ４Ｎｉ４Ｍｏ４Ｖ）及高温用完全化轴承钢（Ｃｒ４Ｍｏ４Ｖ）的接触疲劳寿命及其组织。结果表明，１０Ｃｒ４ＮｉＭｏ４Ｖ钢的接触疲劳寿命高于Ｃｒ４Ｍｏ４Ｖ钢，１０Ｃｒ４Ｎｉ４Ｍｏ４Ｖ钢渗碳层中存在较高的残留压应力，渗层组织中碳化物细小且呈均匀弥散分布。     

冷处理对Cr12MoV钢硬度的影响

通过测定不同热处理条件下Ｃｒ１２ＭｏＶ钢的硬度值和残余奥氏体量,并通过金相和透射电观察发现,钢中的残余奥氏体和下贝氏体组织对冷作模具钢的耐磨性能有不利的影响,采用冷处理工艺抑制下贝氏体转变,显著提高Ｃｒ１２ＭｏＶ钢的硬度和耐磨性能。     

金属材料J—R曲线及条件起裂值的单试样三曲线法

用单试样三曲线法测定了１２Ｃｒ１ＭｏＶ，１．２５Ｃｒ０．５ＭｏＳｉ，１６ＭｎＲ三种钢材和一利焊缝金属的Ｊ积分阻力曲线及其条件其条件直起值，与标准的多度样测定结果基本吻合。实验表明，单试样三曲线的关联分析反裂纹三点弯曲试样的宏观断裂物理过程，延性裂纹的扩展符合幂函数规律。     

不同类型的贝氏体组织对低碳钢力学性能的影响

低碳贝氏体钢是高强度、高韧性、多用途的新型钢种,它的出现是社会需求和现代冶金技术发展的必然结果.目前,低碳贝氏体钢已经在工程机械上得到广泛应用.然而,实际生产中得到的低碳贝氏体钢并不是由单一贝氏体组织组成,往往是多种显微组织并存,因此并不能直接体现钢的力学性能与贝氏体组织之间的对应关系.针对这一情况,以低碳Mn-B-Cr-Mo-Nb钢为研究对象,在国内某钢铁公司进行控轧控冷试验.通过对终冷温度的控制,分别得到由全部粒状贝氏体,全部板条贝氏体以及粒状贝氏体+板条贝氏体组成的3种不同类型的低碳贝氏体钢.经过对这3种不同类型的贝氏体钢进行拉伸和冲击试验后发现:在化学成分相同的条件下,粒状贝氏体钢的强度最低,韧塑性最好;板条贝氏体钢板的强度最高,韧塑性最差:由粒状贝氏体+板条贝氏体组成的钢,其强度、韧塑性居中.由此可知,终冷温度对热轧钢板的显微组织和力学性能影响很大,通过对中温转变组织的控制,就可以进一步提高低碳贝氏体钢的综合力学性能.     

焊接凝固裂纹驱动力的分析与模拟

分析了焊接构件中熔池变形及凝固收缩对熔池尾部应力应变场的影响,建立了不锈钢焊接凝固裂纹应力应变场的数值模拟模型,并对凝固裂纹的驱动力进行了计算.通过单元再生方案,消除了焊接构件中熔池变形对熔池尾部应力应变场的影响;通过增大材料的线膨胀系数,考虑了凝固收缩对熔池尾部应力应变场的影响,最终得到了各种条件下的焊接应力-应变场.     

HG80钢及其焊接接头的疲劳裂纹扩展

为适应大型工程机械焊接用钢需要，对低合金高强度钢HG80及其焊接接头的疲劳裂纹扩展速率进行了研究。结果表明，疲劳裂纹扩展速率对钢板的轧制方向不敏感，焊缝及热影响区疲劳裂纹扩展速率明显低于基材。在排除焊接残余应力导致的裂纹闭合效应后，焊缝及热影响区疲劳裂纹扩展速率与基材相当。     

核级手动截止阀Ω焊缝凝固缺陷成因研究

采用显微硬度测量、金相和扫描电镜(SEM)观察对不锈钢手动截止阀焊接接头各微区的硬度进行测量;对Ω焊缝、热影响区(HAZ)和母材的显微组织进行观察;对接头的断口形貌进行观测分析。结果表明:接头各区域的硬度分布差异不大,分布较为均匀,而2#试样HAZ的硬度高于1#。Ω焊缝金属柱状晶粗大,晶粒(柱状和胞状晶)的方向性强,晶间存在偏析,焊缝已形成沿晶界开裂。主要原因是:Ω焊缝装配间隙部位在冷却结晶时因液态填充不够,形成缩松、缩孔。在焊接应力/应变场作用下,拉伸应变或应变率超过此时材料的临界塑性和临界应变率时则产生焊接凝固裂纹。     

Effect of microstructure and chemical composition on cold crack susceptibility of high-strength weld metal

The effects of the microstructural constituents, chemical composition, and retained austenite on high-strength weld metal were studied using preheat-free steels and GMAW solid wires with a low hydrogen content. The cold cracking susceptibility of these GMAW wires was evaluated using the y-groove Tekken test. The results showed that acicular ferrite produced the greatest resistance to cold cracking and that the microstructure of the deposit was more important than the hardness and diffusible hydrogen content in low-hydrogen weld metal. Crack blunting and branching occurred when a crack propagated through fine acicular ferrite because of the fine interlocking nature of the microstructure. Alloying elements for nucleating acicular ferrite, such as Ti, Al, and V, are required for proper austenite grain size, and sequence of inclusion formation was identified in the present paper. Furthermore, the retained austenite was not found to play the role of a hydrogen trapping site and so had no effect on the cold cracking susceptibility at a low preheating temperature (≤100°C) and low heat input (≤1.5 KJ/mm) to the weld metal.     

Surface crack susceptibility of electrodischarge-machined steel surfaces

This study investigates the correlation between the surface cracking susceptibility of seven common engineering steels (JIS SKS93, SNCM439, SCM440, SKS2, SK2, SKH51, and SKD11) and the major electrodischarge machining processing parameters, namely the pulse current and the pulse-on duration. The results reveal that the susceptibility of the working materials to surface cracking can be reduced by increasing the pulse current or shortening the pulse-on duration. Furthermore, it is shown that steels with a lower carbon equivalent index or a higher thermal conductivity are more resistant to crack formation. Overall, the steels considered in this study can be ranked in terms of an increasing surface cracking susceptibility as follows: low alloy steel, carbon tool steel, high speed steel, and cold working steel.     

980MPa级低碳贝氏体高强钢MAG焊接接头不同试样的拉伸断裂机理

在980MPa级深海用低碳贝氏体高强钢MAG焊接接头上,制取5种不同形状和缺口位置的试样进行拉伸试验,原位观察了每种试样的动态断裂过程,并对其断裂机理进行了分析,确定了焊接接头的薄弱部位。结果表明:直缺口试样的断裂经历了塑性变形、裂纹起裂、裂纹扩展、裂纹尖端钝化,直至断裂的过程,并且在裂纹扩展过程中,裂纹尖端重复钝化、扩展、新裂纹产生、再钝化、再扩展;圆弧和平板试样以剪切方式断裂,经历了塑性变形、颈缩、出现微裂纹、微裂纹扩展,直至瞬间断裂的过程;所有试样的薄弱部位都为焊缝金属。     

焊接接头母材区断裂韧度COD特征值研究

采用三点弯曲试样对ＡＰＩＸ５２管线钢焊接接头母材金属区断裂韧度ＣＯＤ特征值进行了测试研究。研究结果表明，焊缝金属的力学性能对母材金属的起裂韧工，裂纹扩展阻力，撕裂模量及延伸区宽度有很大的影响，其影响程度取决于裂纹离焊缝的距离，离焊缝愈近，影响愈大，裂纹尖端的延伸区宽度和起裂韧度具有良好的线性关系。     

合金元素对高强钢焊缝金属贝氏体形成及力学性能影响的研究进展

高强钢焊接过程中焊缝金属与母材的强韧匹配问题一直难以解决,因此急需细化合金元素调控体系,完善高强钢焊缝金属的强化增韧机理。贝氏体是高强钢焊缝金属中的重要组织,对其强韧性有重要影响,因此介绍了典型贝氏体的形成机理及分析方法,重点综述了合金元素对高强钢焊缝金属微观组织和力学性能的影响,得出高强钢焊接中各合金元素推荐值,进而丰富高强钢焊缝金属合金元素调控体系。     

焊接缺陷磁光成像动态检测与识别

为了实现焊接缺陷的自动检测,研究一种交变磁场激励下焊缝表面及亚表面缺陷的磁光成像动态无损检测方法。分析了基于法拉第磁致旋光效应的焊接缺陷磁光成像机理,并结合交变磁场原理推导出励磁变化与动态磁光成像的关系。探索低碳钢板的亚表面焊缝磁光成像特征试验,验证了所提方法可用于检测焊缝亚表面的未熔合缺陷。最后对高强钢焊缝特征的动态磁光图像进行分析,采用主成分分析法和支持向量机(PCA-SVM)模式识别方法建立了焊接缺陷分类模型。试验结果表明,所提方法可以识别高强钢焊件中的焊缝特征(未熔透、裂纹、凹坑和无缺陷),缺陷分类模型的整体识别率达到92.6%,能够实现焊缝表面及亚表面缺陷的自动检测。