SiOx/PET复合薄膜的力学性能及阻隔性能

目的基于氧化硅(SiO_x)镀层优异的性能,研究不同厚度的SiO_x层对SiO_x/PET复合薄膜力学性能和阻隔性能的影响,以期得到性能较优的SiO_x/PET复合薄膜。方法以自制的聚对苯二甲酸乙二醇酯(PET)薄膜为基材,采用等离子体增强化学气相沉积法沉积得到SiO_x层厚度分别为40,150,230,320 nm的SiO_x/PET复合薄膜,并进行傅里叶变换红外线光谱分析、力学性能和阻隔性能测试,以及薄膜表观形貌分析。结果沉积SiO_x层后,SiO_x/PET复合薄膜拉伸强度和断裂伸长率随SiO_x层厚度的增大先增大后减小,氧气透过率和水蒸气透过率则出现明显衰减而后逐渐平缓的趋势。SiO_x层厚度达150~230 nm时,复合薄膜的力学性能和阻隔性能表现较优,拉伸强度、断裂伸长率、氧气透过率以及水蒸气透过率分别提高了约25.0%,20.9%,79.3%,77.3%。结论适宜厚度的SiO_x层可以使得SiO_x/PET复合薄膜同时具备较优的力学性能和阻隔性能。     

氟化乙丙烯共聚物薄膜驻极体电荷存储性能与电晕产生模式相关性

采用在直流稳态、高频脉冲和交变电场作用下的电晕放电对氟化乙丙烯共聚物(FEP)薄膜材料进行注极,通过等温表面电位测量和热刺激放电技术考察了FEP驻极体的电荷存储特性,依据电晕放电等离子体鞘层模型对实验结果进行了分析,研究了电晕产生模式对FEP薄膜驻极体电荷存储性能的影响。结果表明,电晕注极FEP薄膜驻极体的表面电位稳定性与电晕产生模式、电晕极性有关,但是电荷存储机制只与电晕极性有关。脉冲电晕注极时的稳定性优于稳态电晕注极,但其初始表面电位值较低。交变电场电晕注极获得的驻极体,呈现负极性。不同电晕放电模式在材料表面形成的等离子体鞘层的组成和厚度不同,是FEP驻极体性质不同的主要原因。     

凹印塑料水墨在聚氯乙烯薄膜上的印刷

塑料印刷与塑料、电子、物理、高分子化学、色彩、光学、流体力学和表面化学等现代科学有着密切的关系。而塑料印刷以塑料薄膜印刷和塑料片材、板材的印刷为主，最常见的塑料薄膜有聚乙烯薄膜和聚氯乙烯薄膜。因聚乙烯的极性较差，通常为提高其印刷色牢度，一般需要采用电晕放电处理以提高其印刷色牢度。而聚氯乙烯多了个-cl键，极性增强通常情况下可不用电晕处理。墙纸的印刷属于聚氯乙烯表面印刷的范畴。     

聚酰亚胺/二氧化钛纳米复合薄膜制备与耐电晕性

采用原位聚合法制备不同TiO₂组分聚酰亚胺(PI)/纳米TiO₂复合薄膜, 薄膜厚度50μm。 测试结果表明, TiO₂呈球状颗粒, 直径约为100 nm, 聚酰亚胺呈片状, 尺寸约为2μm×1μm。随着TiO₂含量的增加, 复合薄膜介电常数和介电损耗增大, 击穿场强先增加后降低; 在40 kV/mm电场强度下, 复合薄膜耐电晕老化寿命增加, 纯PI薄膜寿命为3 h, 20wt%TiO₂含量薄膜寿命达到25 h; TiO₂颗粒耐电晕能力强, 与聚合物形成界面相, 改变材料陷阱能级, 有利于空间电荷的扩散和热量的传输, 在薄膜表面形成放电阻挡层, 降低局部放电对薄膜内部的侵蚀, 显著提高薄膜耐电晕老化寿命。     

薄膜印刷前不同方式预处理各有何作用?

<正>等离子体处理通过放电装置将电离的等离子体中的电子或离子打到承印物表面,一方面,可以打开材料的长分子链,出现高能基团;另一方面,经打击使薄膜表面出现细小的针孔,同时还可使表面杂质离解、重解。电离时放出的臭氧有强氧化性,附着的杂质被氧化而除去,使承印物表面自由能提高,达到改善印刷性能的目的。电晕处理利用高频(中频)高压电源,在放电刀架和刀片的间隙产生一种电晕释放现象,用这种方法对塑料薄膜在印刷前进行表面处理,叫电     

脉冲电晕对气调包装薄膜透气性能影响研究

采用脉冲电晕对非极性的食品包装薄膜聚乙烯(PE)和聚丙烯(PP)进行表面处理,研究了电晕处理时的4 种因素(即放电功率、电极与薄膜间的距离、走膜速率和导辊温度)对薄膜透气率的影响,探讨了电晕处理后薄膜的透气率和薄膜的表面张力值之间的关系,建立了电晕处理对薄膜透气率的影响规律。结果表明,电晕处理对薄膜的表面张力和薄膜的透气率有明显的影响,为建立电晕处理与薄膜透气率之间的数学模型和气调包装设计提供了可靠的薄膜透气率数值计算。     

聚乙烯薄膜表面放射线改性

聚乙烯薄膜表面放射线改性聚乙烯薄膜价格便宜，用途广泛。但由于没有极性基团不能粘接和印刷。用电晕放电方法进行表面改性，印刷性能有所改善，但仍不尽人意。近年来采用放射线照射进行表面改性，粘接性能明显提高。改性用的聚乙烯薄膜，可用线型低密度薄膜（ＬＬＤ），...     

亚胺化工艺对聚酰亚胺/纳米Al_2O_3三层复合薄膜耐电晕性能的影响

以均苯四甲酸二酐和4,4’-二氨基二苯醚作为原材料,N,N-二甲基乙酰胺作为溶剂,采用原位聚合法通过不同的亚胺化工艺分别制备了3组掺杂量为12%(质量分数)的PI/纳米Al_2O_3三层复合薄膜。采用红外光谱(FT-IR)对复合薄膜的第1层进行了表征,并计算了不同工艺下第1层复合薄膜的亚胺化率。采用扫描电子显微镜(SEM)对三层复合薄膜的断面结构进行了表征。同时,利用光激放电(photon-stimulated discharge,PSD)测试了复合薄膜的陷阱状态,并对纯膜及复合薄膜的电老化阀值和耐电晕时间进行了测试。结果表明,随着亚胺化温度与时间的增加,第1层复合薄膜的亚胺化程度随之增加,即亚胺化率增大;随着亚胺化率的增加,复合薄膜的层间结合程度逐渐变好,复合薄膜内部陷阱密度降低,电老化阀值增加,耐电晕时间增加。     

Y2O3溶胶复合薄膜的抗近红外/紫外性能研究

以表面具有螯合官能团的高分子材料Poly(BA-co-GMA-IDA)为高分子液体模板,制备了Y2O3功能性溶胶复合薄膜.测试结果显示,Y2O3功能性混和溶胶薄膜具有优异的抗近红外/紫外性能,其薄膜对320nm以下的中短紫外光阻隔率＞97%(300nm以后可完全隔绝紫外),对320～380nm的长波紫外线的阻隔率也＞60%;近红外阻隔率可以达到70%以上.以高分子模板制备复合薄膜的抗近红外/紫外性能明显优于未用高分子模板制备的同类型薄膜.     

聚乙烯醇复合薄膜的抗紫外线性能

目的研究聚乙烯醇(PVA)复合薄膜(添加紫外线阻隔剂)的紫外线透过率和透明性能。方法将不同种类、不同质量分数的紫外线阻隔剂与PVA原料混合制备复合薄膜,检测其紫外线透过率、透光率、雾度。结果添加有机紫外线吸收剂UV-284后,薄膜能够有效阻隔大部分紫外线,但影响薄膜的外观,复合薄膜呈黄色。无机的紫外线阻隔剂在PVA薄膜中容易发生颗粒团聚,当Nano-Ti O2的质量分数为2.5%时,复合薄膜的平均紫外线透过率达到2%左右,若再增加质量分数则紫外线透过率变化不大。结论紫外线阻隔剂有效降低了PVA薄膜的紫外线透过率,但同时复合薄膜的透光率降低,雾度上升。综合比较,PVA薄膜中添加Nano-Ti O2的紫外线阻隔效果,比加入相同质量分数的UV-284或Nano-Zn O的复合薄膜要好。     

MPECVD中氧化硅阻隔层性能的研究

介绍了用磁增强等离子体化学气相沉积技术在连续(Roll-to-Roll)系统中,在PET薄膜表面沉积纳米SiOx阻隔层薄膜的工艺。研究了不同工艺条件下,薄膜的阻隔性能、颜色变化及其影响因素。实验得到:在单体和氧气的混合反应气体中,提高氧气的比例有利于增加薄膜透明性,并且得到的氧化硅膜由黄褐色趋近于无色透明。通过红外光谱仪对薄膜的成分进行了分析,用分光光度计和紫外可见分光光度计测量了薄膜颜色和透明性变化,分析了其影响产生的机理。     

Determination of antioxidant activity of surface‐treated PET films coated with rosemary and clove extracts

Commercial PET films were surface treated and subsequently coated with either rosemary (RME) or clove (CE) extracts. Surface treatments involved (1) corona treatment, (2) chemical modification, and (3) plasma treatment. Radical scavenging activity (RSA) of both pure plant extracts and coated film extracts were determined using the 1,1‐diphenyl‐2‐picrylhydrazyl (DPPH) method. RME‐coated films showed a % RSA of 25.6%, 22.4%, and 24.1% for plasma, chemical modification, and corona treatment, respectively, at an extract concentration of 1402 ppm, respectively, while pure RME showed a %RSA of 16.0%. Respective %RSA values for CE were 25.0% for plasma, 25.2% for chemically modified, and 25.2% for corona‐treated films at 1402 ppm, while pure CE showed a %RSA of 47.6%. Thiobarbituric acid (TBA) test, performed on ground fish muscle wrapped in all types of employed films, showed a remarkable decrease in the degree of fish oxidation ranging between 50.0 and 80.0% after 6 days of storage. Contact angle measurements confirmed that surface chemically modified films had the highest adhesion strength followed by corona and plasma‐treated films. Scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), and X‐ray photoelectron spectroscopy (XPS) data also supported contact angle measurements. Finally, the oxygen permeability of surface‐treated films did not differ from untreated films indicating that surface treatment did not affect film barrier properties.     

水性丝印荧光油墨色彩再现研究

目的为了更好地研究加色法成像机理,改善红色水性荧光丝印油墨的荧光性能,进而对三色荧光油墨的呈色性能进行研究。方法通过改变不同红色荧光材料的含量研究红色水性荧光丝印油墨的荧光性能,接着在此基础上,得出红、绿、蓝三色荧光油墨的色域,比较不同呈色方式对三色油墨荧光性能的影响,并探讨2种不同的承印物对三色油墨呈色性能的影响。结果当荧光粉质量分数为6%时,红色水性丝印荧光油墨的荧光强度最好。三色荧光油墨的色域范围比s RGB范围略小,可以满足色彩再现的研究需要。丝印时,网点并列比网点叠合更有利于荧光油墨彩色信息的真实再现。不含荧光剂的承印物有利于荧光油墨的色彩再现,纸张比pc膜色调再现能力好。结论最终制备的水性丝印荧光油墨具备优良的荧光性能,可以再现s RGB色域内的大部分色彩。     

铝掺杂对非晶SiOx薄膜电致发光的影响

为提高硅基薄膜（SiOx）发光材料的发光效率，采用双离子束溅射法制备了不同铝含量的Al—Si—SiOx薄膜。对所制备样品的电致发光（EL）测试表明：由于金属（Al）的掺入，使得在同样的电压下。薄膜中的电流随着铝含量的增加而增加；并且铝含量增大使得通过薄膜的电流增强，因而得到较高强度的电致发光。所以当硅基薄膜中掺入铝时，薄膜的发光效率得以提高；并且，随着铝含量的增加，薄膜的发光效率亦相应提高。     

铝基SiOx膜层滑动磨损及其机理研究

本文采用低温常压CVD方法制备铝基SiOx陶瓷膜层.以黄铜为对磨材料,使用销-盘式磨损试验机对比研究纯铝表面与SiOx膜层的滑动磨损性能,通过SEM分析磨损的表面形貌并分析其磨损机理.结果表明纯铝表面发生粘着磨损,存在大量塑性变形和折叠,导致片状脱落,磨损率高;SiOx薄膜硬度较高,存在孔隙,表面发生塑性变形、崩塌和磨粒磨损;因薄膜孔隙具有储存润滑剂(水)的作用,磨损率明显低于对比纯铝样品;随沉积时间增加,SiOx膜层变厚,承载能力提高,磨损量减小.     

电晕放电处理对高密度聚乙烯表面作用的研究

本文研究了高密度聚乙烯(HDPE)经电晕放电处理后表面形态及性能的变化,通过接触角测定、多重内反射红外光谱、扫描电镜、重量分析等手段,证实了多种气体均能在较短的时间内使HDPE的润湿性明显提高,含氧气体或非含氧气体都能对HDPE表面进行刻蚀,但它们有不同的刻蚀机理,含氧气体的放电处理可把含氧基团引入HDPE表面,且改变了HDPE表面的刻蚀过程。     

The power source effect on SiOx coating deposition by plasma enhanced chemical vapor deposition

SiOx coatings were prepared by capacitively coupled plasma enhanced chemical vapor deposition on polyethyleneterephtalate substrates in 23 kHz middle-frequency and radio frequency power supplies, respectively, where hexamethyldisiloxane was used as gas source. The influences of discharge conditions on gas phase intermediate species and active radicals for SiOx formation was investigated by mass spectrometry as real-time in-situ diagnosis. The deposited SiOx coating chemical structures were also analyzed by Fourier transform infrared spectroscopy. Meanwhile, the film barrier property, oxygen transmission rate, was measured at 23 °C and 50% humidity circumstance. The better barrier property was obtained in the MF power source depositing SiOx coated PET.     

纸张表面效率对印刷品色彩再现的影响

纸张的表面效率对色彩再现有很大影响,相同的彩色油墨印在不同的纸上,会产生不同效果.测量出几种不同纸张的表面效率和它们对同种油墨呈色性.分析纸张表面效率与印刷色彩再现之间关系,为印刷厂提高印品质量,选择纸张提供理论依据.