Pd负载型介孔ZrO2-TiO2复合材料的设计合成及其CO催化氧化性能研究

以介孔结构的复合ZrO₂-TiO₂为载体负载活性组分, 制备了具有高CO催化氧化活性的Pd/ZrO₂-TiO₂与PdCu/ZrO₂-TiO₂负载型催化剂。XRD、TEM研究结果表明: 活性组分Pd、Cu物种可均匀分散于介孔载体中。系统考察了不同的催化剂载体、制备方法和助催化剂等对该介孔复合材料CO催化氧化性能的影响, 结果表明: 以ZrO₂-TiO₂为载体的催化剂其CO催化氧化活性明显优于以介孔Al₂O₃或介孔SBA-15为载体的催化剂; 一步法制备的介孔Pd/ZrO₂-TiO₂催化剂其CO催化氧化的低温活性较浸渍法制备的Pd/ZrO₂-TiO₂有很大提高; 并且Pd和Cu物种共负载的介孔ZrO₂-TiO₂复合催化剂具有最优的CO催化氧化活性, 其CO的完全催化氧化温度可降至170℃, O₂-TPD分析说明Pd和Cu之间的相互作用使得PdCu/ZT催化剂在更低温度具有氧化还原活性。     

W掺入对Ti0.8Zr0.2Ce0.2O2.4/Al2O3-TiO2-SiO2催化脱硝性能的优化

以Al₂O₃-TiO₂-SiO₂(ATS)为载体、Ti_0.8Zr_0.2Ce_0.2O_2.4(TZC)为催化活性组分, 采用挤出成型法制备系列整体式TZC/ATS及W掺入催化剂样品。研究了W掺入对催化剂TZC/ATS 的氨气选择性催化还原(NH₃-SCR)脱除NO活性及抗K₂O、CaO等毒性的影响, 比较了Ti_0.8Zr_0.2Ce_0.2W_0.08O_2.64/ATS(TZCW_0.4/ATS)催化剂与V₂O₅(WO₃)/TiO₂催化剂的抗K₂O、CaO等中毒性能, 并采用N₂-BET、XRD、SEM和NH₃-TPD等技术手段分别表征了催化剂的比表面积、固相结构、微观形貌及表面酸性。结果表明, 当活性组分中Ti/Zr/Ce/W元素摩尔比为4:1:1:0.4时, TZCW_0.4/ATS催化剂NH₃-SCR脱除NO的效率最高、稳定性最好。W掺入显著增强了催化剂的抗K₂O及CaO毒性能力, 且TZCW_0.4/ATS催化剂抗K₂O及CaO的中毒能力明显强于V₂O₅(WO₃)/TiO₂催化剂。分析表明, W掺入提高了TZCW_0.4/ATS催化剂的比表面积, 增加了催化剂的表面酸量, 从而优化了催化剂的脱硝性能。     

尖晶石型AFe2O4催化剂的制备及其催化燃烧甲苯的研究

通过溶胶-凝胶-自蔓延燃烧法制备尖晶石型AFe₂O₄(A=Cu, Co, Ni, Mg, Zn)催化剂, 以甲苯为VOCs模拟气, 考察AFe₂O₄催化剂对VOCs的催化燃烧活性, 并采用XRD、N₂吸附-脱附、SEM、TEM、H₂-TPR、XPS对催化剂进行表征分析。结果表明: AFe₂O₄表现出较好的催化燃烧活性, 其中CuFe₂O₄的催化燃烧活性最佳, 起燃温度(T50)和完全燃烧温度(T90)分别为188℃、239℃。AFe₂O₄具有明显的片状尖晶石晶体, 并形成以介孔为主的多级孔结构, 该特点为催化剂提供了大量表面活性位。A位元素种类对其催化燃烧活性影响较大, 当A位元素为Cu时, Cu的H₂还原峰面积远大于其他元素, H₂还原温度仅为289℃, 表面亲电子氧和氧空位浓度占氧元素总量(O_ele/O_1S)的36%。CuFe₂O₄为片状反尖晶石晶型, 晶格体积仅为0.294 nm³, 并伴有CuO和α-Fe₂O₃物种。以介孔为主的多级孔结构、特有的片状反尖晶石晶型以及该晶型与CuO和α-Fe₂O₃的协同作用是CuFe₂O₄催化燃烧活性提高的主要原因。     

不同晶型Fe2O3催化H2O2湿法脱硝的实验研究

研究了以α-Fe₂O₃、β-Fe₂O₃和γ-Fe₂O₃为催化剂的类Fenton试剂溶液氧化吸收NO的过程,分析了3种Fe₂O₃的晶相结构和表面性质对NO脱除效率的影响机理。脱硝性能测试结果表明：γ-Fe₂O₃的活性最好,在H₂O₂浓度为1.5 mol/L、催化剂浓度为20 mmol/L、pH值为5以及反应温度为55℃等条件下,γ-Fe₂O₃的脱硝率可达87.5%。机理研究表明：3种Fe₂O₃催化H₂O₂分解湿法脱除NO的反应发生在催化剂表面,反应过程中存在氧化还原循环,H₂O₂催化分解的主要产物是·OH。活性差异分析结果表明：Fe₂O₃的晶相结构和表面性质对NO的脱除效果具有显著的影响,γ-Fe₂O₃的活性最高是由于比表面积大、分散性高和表面的Fe²⁺含量更多,而β-Fe₂O₃的活性高于α-Fe₂O₃是由于表面的氧空位含量更多。     

纳米金刚石负载Fe2O3的制备及其对高氯酸氨的热分解催化作用

对纳米金刚石（ND）进行羧基化处理以提高其分散性,然后采用沉淀法制备了羧基化ND负载Fe₂O₃的催化剂。利用XRD、TG、BET和TEM对该负载型催化剂进行表征,通过DSC研究其对高氯酸铵(AP)热分解的催化作用。结果表明:ND经过羧基化处理后,在水中的分散性大幅度提高。沉淀法制备了直径5 nm、长50 nm的Fe₂O₃包裹或附着于ND的负载型复合催化剂,该催化剂对AP高温热分解的催化效果优于单一的Fe₂O₃或ND。当Fe₂O₃和ND的质量比为5∶1、在AP中添加质量分数2%的复合催化剂时,AP的高温分解峰温降低约30 ℃,ND负载Fe₂O₃催化剂具有一定的协同催化作用。     

石墨烯基介孔锰铈氧化物催化剂:制备和低温催化还原NO

锰铈氧化物由于较强的氧化还原活性、优良的低温脱硝性能,已被广泛用于选择性催化还原(SCR)脱硝反应,但是锰铈氧化物存在活性组分易团聚、比表面积较低等问题,限制其催化剂活性的提高。本研究以介孔结构的石墨烯基SiO₂(G@SiO₂)纳米材料为模板,采用水热法制备了系列石墨烯基介孔锰铈氧化物(G@MnO_x-CeO₂)催化剂,并考察了该催化剂在低温下(100～300℃)的SCR脱硝性能。结果表明,与石墨烯基铈氧化物(G@CeO₂)相比,G@MnO_x-CeO₂催化剂具有较高脱硝活性。当Mn、Ce与模板G@SiO₂质量比分别为0.35、0.90时, G@Mn(0.35)Ce(0.9)催化剂的脱硝活性最佳, 220℃下NO转化率达到最高(80%)。添加适量MnO_x,提高了G@MnO_x-CeO₂催化剂的比表面积、孔容,降低了催化剂的结晶度;并且MnO_x<...     

ZrO2颗粒状态对SiC/金刚石复相陶瓷结构、性能的影响

本文用不同水解时间辅以氨水沉淀制备了不同颗粒尺寸的纳米(9nm ) ZrO₂ (Y₂O₃) 粉体。以其为增韧相, 在高温(1350℃) 超高压(5GPa) 条件下烧结ZrO₂ (Y₂O₃) + SiC+ 金刚石超硬复相陶瓷, 用TEM、SEM、XRD、冲击韧性测定和磨耗比测定研究了ZrO₂ (Y₂O₃) 颗粒形状特征及对超硬复相陶瓷相结构及机械性能的影响。结果表明, ZrO₂ (Y₂O₃) 制备的水解时间≥50h, ZrO₂ (Y₂O₃) 颗粒均一, 在复相陶瓷内均一分布, 以100% t 相存留, 断裂过程中t →m 转变量≥20vo l% , 使超硬复相陶瓷具备较高韧性及耐磨性。      

RuO2/ZrO2/TaON复合光催化材料的制备及光解水制氢性能

采用控制水解法制备了细颗粒的ZrO₂/Ta₂O₅复合氧化物粉体, 在氨气流量为90 mL/min、850℃下氮化10 h获得ZrO₂/TaON, 用浸渍法制备含助催化剂RuO₂的复合光催化剂。用XRD、SEM、TEM和UV-Vis漫反射光谱等对所制备的光催化材料进行了表征, ZrO₂、RuO₂的晶粒尺寸约为10 nm,TaON的晶粒尺寸约为25 nm, 复合光催化剂可以吸收波长≤500 nm的可见光。ZrO₂的引入降低了氮化生成TaON的缺陷密度, 提高了TaON的比表面积。光电流及光催化分解水制氢反应定量评价了复合材料的光催化性能, RuO₂含量为2.0wt%时复合光催化剂活性最高, 0.6 V偏压下光电流密度为0.6 mA/cm², 产氢速率为6.0 μmol/h。     

低毒单体DMAA用于ZrO2/Al2O3坯体注凝成型

采用低毒的单体N, N-二甲基丙烯酰胺(DMAA)制备了氧化锆增韧氧化铝(ZrO₂/Al₂O₃)坯体。讨论了分散剂的用量、 ZrO₂/Al₂O₃浆料的pH值、 粉体中ZrO₂含量、 粉体所占浆料的固相体积分数、 球磨时间、 预混液中DMAA的浓度(质量分数)对ZrO₂/Al₂O₃浆料黏度的影响。并研究了注凝成型ZrO₂/Al₂O₃坯体的性能和显微结构。结果表明, 当浆料pH值为9, 分散剂的添加量为ZrO₂/Al₂O₃粉体质量的0.6%, 球磨时间为6 h, ZrO₂/Al₂O₃浆料具有最小的黏度。固相体积分数的提高和DMAA加入量的增大都会提高ZrO₂/Al₂O₃浆料的黏度, ZrO₂的加入会降低浆料的黏度。用DMAA制备得到的ZrO₂/Al₂O₃坯体结构均匀, 抗弯强度达到25 MPa。      

ZrW2O8 / ZrO2 可控热膨胀复合材料的制备

采用分步加热固相法成功制备了纯度较高的各向同性负热膨胀材料ZrW₂O₈ 。将ZrW₂O₈ 与ZrO₂ 按一定比例混合, 在1200 ℃烧结24 h 制备了热膨胀系数可控的ZrW₂O₈ / ZrO₂ 复合材料。研究结果表明, 通过改变ZrW₂O₈ 的体积分数, ZrW₂O₈ / ZrO₂ 复合材料的热膨胀系数可以控制为负、正或零。当ZrW₂O₈ 的体积分数为37 %时, 复合材料的热膨胀系数接近零。为了得到致密的ZrW₂O₈ / ZrO₂ 复合陶瓷, 采用Al₂O₃ 作为烧结剂, 取得了较好的效果。0. 35 wt % Al₂O₃ 的加入可以在不影响复合材料热膨胀性能的前提下, 显著提高复合材料的致密度。      

Microstructure and mechanical performances of ZTA/LaAl11O18 composite prepared by a heterogeneous precipitation method

Al₂O₃ composite combinatively strengthened by ZrO₂ and in situ formed LaAl₁₁O₁₈ was prepared by a heterogeneous precipitation method. The sintering temperature was significantly lowered in comparison with monolithic Al₂O₃. ZrO₂ and LaAl₁₁O₁₈ inhibited Al₂O₃ grain growth, forming fine and uniform microstructure in the material. SEM showed that increasing numbers of Al₂O₃ and LaAl₁₁O₁₈ grains fractured transgranularly, because of the strengthened grain boundary by residual thermal stress. X-ray diffraction revealed that ZrO₂ was exclusively in tetragonal symmetry (t-ZrO₂) and did not transformed to m-ZrO₂ under the fracture stress. The strength of the material was about 1 GPa, almost doubled over that of monolithic Al₂O₃.     

V_2O_5与Al_2O_3复合改性CaSiO_3陶瓷的烧结性能与微波介电性能

为降低CaSiO3陶瓷的烧结温度,通过在CaSiO3粉体中添加1wt%的Al2O3以及不同量的V2O5,探讨了V2O5添加量对CaSiO3陶瓷烧结性能、微观结构及微波介电性能的影响规律。结果表明:适量地添加V2O5除了能将V2O5-Al2O3/CaSiO3陶瓷的烧结温度从1 250℃降低至1 000℃外,还能抑制CaSiO3陶瓷晶粒异常长大并细化陶瓷晶粒。在烧结过程中,V2O5将熔化并以液相润湿作用促进CaSiO3陶瓷的致密化进程;同时,部分V2O5还会挥发,未挥发完全的V2O5将与基体材料反应生成第二相,第二相的出现将大幅降低陶瓷的品质因数。综合考虑陶瓷的烧结性能与微波介电性能,当V2O5添加量为6wt%时,V2O5-Al2O3/CaSiO3陶瓷在1 075℃下烧结2h后具有良好的综合性能,其介电常数为7.38,品质因数为21 218GHz。     

Al2O3/BaZrO3双陶瓷界面微观组织演化及机理

以Al₂O₃为背层(硅溶胶为粘结剂), 电熔BaZrO₃作为面层材料(钇溶胶为粘结剂), 1550℃烧结后制成50 mm×25 mm×5 mm的Al₂O₃/BaZrO₃双陶瓷试样。通过光学显微镜(OM)、扫描电子显微镜(SEM)、X射线衍射仪(XRD)和EDS等手段观察了BaZrO₃层和Al₂O₃/BaZrO₃界面的显微结构, 研究了BaZrO₃与Al₂O₃的界面反应。结果表明, 面层由BaZrO₃基体和分布其上的大小10 μm左右的Y稳定的ZrO₂晶粒组成; Al₂O₃/BaZrO₃界面发生反应形成厚约300 μm的过渡层, 界面反应生成物有BaOAl₂O₃、ZrO₂和BaO·Al₂O₃·2SiO₂。界面从单纯的BaZrO₃/Al₂O₃双陶瓷结构演变为BaZrO₃、ZrO₂、BaO·Al₂O₃、BaO·Al₂O₃·2SiO₂和Al₂O₃等多种物相组成的复杂结构。反应过程中Al元素基本不迁移扩散, BaZrO₃中Ba元素向Al₂O₃所在的位置扩散形成BaO·Al₂O₃, 残留物形成一层条状ZrO₂, 而BaO·Al₂O₃·2SiO₂围绕着EC95(Al₂O₃+5%SiO₂)粉体颗粒周围生成。     

ZrO_2增韧Al_2O_3陶瓷的力学性能和增韧机制

对通过热压烧结法制备的3种陶瓷99.5vol%Al2O3(AD995)、ZrO2(15vol%)/Al2O3和ZrO2(25vol%)/Al2O3的力学性能和增韧机制进行了实验和理论研究。基于复合材料细观力学理论并考虑ZrO2的相变特性,建立了描述ZrO2/Al2O3陶瓷力学性能的本构模型。结果表明:ZrO2的加入细化了基体Al2O3晶粒,ZrO2/Al2O3陶瓷的致密性得到提高;3种陶瓷试件的破坏呈现小变形到脆性破坏的特点,压缩加载下试件应力-应变曲线近似为线性关系;AD995陶瓷的断裂韧性为5.65 MPa·m1/2,ZrO2(25vol%)/Al2O3陶瓷的断裂韧性为8.42 MPa·m1/2,提高了近50%;随ZrO2增韧相含量的增加,ZrO2/Al2O3陶瓷的弹性模量降低而断裂韧性增加,这一变化趋势与实验结果有良好的一致性。     

残余应力对涂覆Al2O3涂层的ZrO2陶瓷的强度和裂纹扩展阻力的影响

本研究在ZrO₂基体表面涂覆一薄层Al₂O₃涂层, 利用基体与涂层之间热膨胀系数不匹配, 在Al₂O₃-ZrO₂预应力陶瓷(简称A_CZ_S预应力陶瓷)表层引入压应力。采用维氏压痕法评价残余应力对A_CZ_S预应力陶瓷的表层和基体中裂纹扩展阻力的影响。理论分析结合实验结果表明: 表层的压应力使得A_CZ_S预应力陶瓷的裂纹扩展阻力增大, 最终导致强度和损伤容限提高; 且A_CZ_S预应力陶瓷表层的压应力和裂纹扩展阻力随着基体截面积与涂层截面积比值的增加而增大。当ZrO₂基体表层的Al₂O₃涂层厚度为40 μm时, 表层压应力使A_CZ_S预应力陶瓷的弯曲强度达到(1207±20) MPa, 相比于同种工艺下制备的ZrO₂陶瓷强度提高了32%, 同时也是Al₂O₃强度的3倍。此外, A_CZ_S预应力陶瓷也表现出很好的抗热震性能。     

原位气相生长法制备碳纳米管/Al2O3陶瓷复合材料

以Al₂O₃陶瓷成型体为基体,通过化学气相反应在陶瓷体内原位生长碳纳米管（CNTs）,制备出CNTs/Al₂O₃陶瓷复合材料。结果表明,Al₂O₃陶瓷体中均匀分布有可观量的多壁CNTs,碳管根部嵌于Al₂O₃晶粒间并从晶粒表面生长出。在Al₂O₃陶瓷成型体中原位生长CNTs需严格控制生长条件,尤其是生长温度（850℃）,温度过高和过低都难以长出CNTs,此外造孔剂、碳源和催化剂也影响CNTs的原位生长。对原位生长的CNTs/Al₂O₃复合体进一步高温烧结获得致密化的复合材料,其导电率达3.7 S/m,较纯Al₂O₃提高13个数量级。在陶瓷成型体中原位生长CNTs是一步法制备CNTs/陶瓷复合材料的新方法,可用于发展高性能的结构陶瓷和具有导电导热等多功能特性的新型陶瓷复合材料。     

Al2O3颗粒形貌对注凝成型ZrO2/Al2O3陶瓷性能的影响

采用3种不同形貌的Al₂O₃原料对注凝成型制备ZrO₂/Al₂O₃（ZTA）陶瓷工艺中悬浮体的流变性能进行了研究。以低毒的单体N,N-二甲基丙烯酰胺（DMAA）制备了ZrO₂/Al₂O₃坯体和陶瓷。讨论了3种不同形貌的Al₂O₃原浆料的分散剂用量、球磨时间和固含量对浆料流变性的影响。Al₂O₃粉体呈扁平状有利于降低浆料的黏度,Al₂O₃粉体呈棒状对生坯强度的提高有利。制得的3种ZrO₂/Al₂O₃坯体颗粒间结合紧密,抗弯强度分别达到21.45,19.87,25.90 MPa。Al₂O₃粉体呈颗粒状有利于最终陶瓷力学性能的提高,陶瓷的抗弯强度及断裂韧性分别为680 MPa和7.49 MPa·m^1/2,453.1 MPa和6.8 MPa·m^1/2,549.4 MPa和6.34 MPa·m^1/2。     

Bi2O3助熔剂对CaO-B2O3-SiO2/Al2O3玻璃陶瓷复合材料性能的影响

以CaO-B₂O₃-SiO₂(CBS)玻璃粉体和Al₂O₃陶瓷粉体为原料,通过在CBS与Al₂O₃的质量比固定为50:50的玻璃-陶瓷复合材料中添加适量的Bi₂O₃作为烧结助熔剂,探讨了Bi₂O₃助熔剂对CBS/Al₂O₃复合材料的烧结性能、介电性能、抗弯强度和热膨胀系数的影响规律.研究表明:Bi₂O₃助熔剂能通过降低CBS玻璃的转变温度和黏度促进CBS/Al₂O₃复合材料的致密化进程,于880 ℃下烧结即能获得结构较致密、气孔较少的CBS/Al₂O₃复合材料.然而,过量添加Bi₂O₃将使玻璃的黏度过低,从而恶化CBS/Al₂O₃复合材料的烧结性能、介电性能及抗弯强度.当Bi₂O₃的添加量为CBS/Al₂O₃复合材料的1.5wt%时,于880 ℃下烧结即能获得最为致密的CBS/Al₂O₃复合材料,密度为2.82 g·cm^-3,这一材料具有良好的介电性能(介电常数为7.21,介电损耗为1.06×10^-3),抗弯强度为190.34 MPa,0~300 ℃的热膨胀系数为3.52×10^-6 K^-1.