宽带钢热连轧精轧机组成套辊形配置技术研究与应用

为了实现热轧宽带钢板形的高精度控制,根据宽带钢热连轧精轧机组上游机架控制凸度与下游机架控制平坦度的特性,在首钢迁钢1580 mm热连轧生产线的精轧机组开发并应用了成套辊形配置技术.在F1机架工作辊采用负凸度辊形,加强带钢轧制过程的对中;在F2到F4机架工作辊应用低轴向力CVC辊形,对带钢进行凸度调控;在F5到F7机架工作辊上采用负凸度辊形,辅以长行程的工作辊周期性窜辊,均匀轧辊磨损,控制带钢的平坦度;在所有机架的支撑辊上采用VCR变接触式辊形,增加机架的横向刚度.采用此辊形配置后,带钢的板形控制精度达95％以上,同时,改善了带钢轧制稳定性,延长了轧制计划长度,实现了一定范围的自由规程轧制.     

马钢CSP热连轧机末机架平辊轧制的研究与应用

为了提高马钢CSP带钢产品的板形质量,在马钢CSP热连轧机板形控制模型中常规工作辊窜辊策略的基础上,结合平辊轧制技术的相关理论,提出了马钢CSP热连轧机末机架平辊轧制方案。试验结果表明,在末机架使用平辊,并结合变行程变步长的窜辊策略,有效地改善了轧辊磨损状况,提高了带钢产品的板形质量。     

LVC工作辊综合辊形预测模型和应用

 在热轧带钢板形在线控制模型中,综合辊形的计算精度直接影响板形控制模型设定的准确性。建立了LVC工作辊初始辊形、热辊形和磨损辊形的计算模型,并在此基础上建立了综合辊形的等效模型和特征参数。该综合辊形等效模型已成功应用于鞍钢2150 mm热连轧在线板形控制模型中。生产数据表明,采用该模型后板形设定模型计算出的弯辊力和窜辊量能够自动适应轧制规格、轧辊磨损和热胀的变化,带钢头部凸度和平坦度的命中率均达到95%以上。     

变接触支持辊辊形及辊形配置技术在宽带钢热连轧粗轧机组的应用

首钢迁钢2 250 mm热连轧生产线在2006年底投产后1年多的时间里,带钢的板形控制精度较低,需要进一步提高。粗轧后中间坯存在镰刀弯、负凸度和楔形大的板形问题,导致精轧控制稳定性差,造成板形控制精度较低。为了解决粗轧中间坯板形的问题,在粗轧R2机架上设计并应用了6次多项式变接触支持辊辊形和负凸度工作辊辊形,取代了原来采用的平辊形。此支持辊辊形可以使辊间接触长度随所轧制带钢宽度变化,消除了有害接触区,使得辊间接触应力均匀化,并提高了辊缝横向刚度,改善了轧辊的磨损辊形,并提高了板形调控能力。工作辊负辊形弥补了工作辊的热凸度,增强了板坯轧制过程的对中和稳定性。此支持辊辊形与工作辊辊形配置使用,大幅改善了中间坯的凸度、楔形和镰刀弯等板形质量,使得热轧产品的板形质量有10%左右的提高。     

1580mm热连轧支撑辊磨损对带钢板形的影响

以鞍钢1580 mm热连轧机支撑辊为研究对象,通过耦合金属塑性变形和辊系弹性变形模型,建立起带钢板形数值分析系统,定量分析了热连轧机支撑辊磨损对带钢断面形状和前张应力分布的影响。模拟计算和生产实践结果表明,随着支撑辊轧制吨数的增加,辊身磨损的不断加剧,带钢板凸度相应增大,双边浪趋势逐渐增强。采用工作辊辊型匹配支撑辊轧制吨数的方法,收到了很好的板形控制效果。     

2250mm宽带钢热连轧生产线凸度控制优化

 首钢迁钢2250mm热连轧生产线在达产初期出现了带钢凸度控制稳定性差的问题,甚至出现负凸度现象。对此热轧生产线的生产数据进行了分析,同时对轧辊温度与辊形进行了实际测量。究其原因为CVC辊形对热凸度和磨损辊形较为敏感,工作辊冷却水能力不足引起的轧辊热凸度过大破坏了CVC辊形曲线的板形控制能力。由于改造轧辊冷却水系统费用较高,需要停产,为了解决凸度控制稳定性问题,采用了辊形优化设计的方法。对精轧机组的CVC工作辊辊形进行了优化,空载辊缝凸度调控范围从［－0.7mm,0.7mm］增大到［－1.2mm,12mm］。同时,为了改善CVC工作辊与支撑辊辊间接触状态,设计并应用了CVC支撑辊辊形。此CVC辊形配置解决了首钢迁钢2250mm热轧线凸度控制稳定性差的问题,板形控制精度由原来的67%提高到了93％以上。     

热轧薄带平整机支撑辊辊型优化的研究与应用

某热轧薄带平整机轧辊长度为1 800 mm,带钢宽度为1 320 mm,两者相差太大,造成工作辊与支撑辊间有害接触区长度过大,在轧辊自身挠度作用下,辊间应力峰值集中于带钢边部位置.随轧制公里数延长,工作辊边部磨损加剧,不利于后期板形控制,同时会缩短轧辊使用寿命.针对热轧薄带平整机工作辊磨损不均匀问题,设计优化支撑辊辊型...     

LVC工作辊辊形窜辊补偿研究与应用

在热连轧带钢板形控制中,磨损和热胀会影响LVC工作辊的辊缝形状,进而影响到其板形调控性能,本文应用二维变厚度有限元法分析了不同轧制过程中LVC工作辊承载辊缝形状和承载辊缝凸度的变化情况,针对原有窜辊公式不能反映辊缝随轧制过程变化的缺点,建立了新型的LVC工作辊窜辊补偿公式以及相应的窜辊补偿策略,并将其成功应用在鞍钢ASP2150热连轧板形自动控制模型中,从而实现板形预设定的高精度控制.从现场轧制的带钢板形工艺数据可以发现,使用LVC辊形加窜辊补偿可以明显改善带钢板形质量,具有较强的实用性.     

宽带钢热连轧机的粗轧辊系配置方案与应用

为解决粗轧轧制稳定性,减少轧辊异常报废损失,设计并应用了变接触支撑辊辊形和负凸度工作辊辊形。该辊系配置使得辊间接触长度与轧制带钢的宽度基本相等,消除了有害接触区,使辊间接触应力均匀化,并提高了 辊缝横向刚度,改善了轧辊的磨损,增强了板坯轧制过程的对中和稳定性。     

1700 热 连 轧 机 CVC 轧 辊 的 磨 损

 研究了国内某厂1700热连轧机CVC轧辊磨损模型,分析了影响轧辊磨损的各种因素。确定了模型中主要系数数值,编制离线仿真程序,计算某一换辊周期CVC工作辊磨损,得到轧制带钢长度与工作辊中心磨损的关系及CVC轧辊磨损曲线。计算结果表明,轧制带钢长度是影响轧辊中心磨损量的一个重要因素;CVC轧辊磨损规律与普通轧辊相同,轧辊磨损对其辊形影响不大。将计算得到的CVC轧辊磨损曲线与采用高精度磨床测量得到的实际磨损曲线比较,两者吻合较好,表明此轧辊磨损计算模型具有较高的计算精度,可用于轧辊磨损在线预报。     

1 580 mm精轧机组大凹辊控制硅钢板形的研究及实践

热轧硅钢断面轮廓对冷轧横向厚差有重要影响,尽可能减小热轧硅钢边降有利于减小冷轧成品横向同板差。为了改善热轧硅钢边降较大、轧制周期短的问题,在1 580 mm精轧机下游F5～F7机架尝试使用大凹辊辊型,总结了大凹辊辊型应用前后热轧硅钢断面板形指标、冷轧横向同板差和工作辊磨损改善情况,分析了大凹辊辊型对硅钢边降和轧辊磨损的影响。实践发现使用大凹辊辊型可有效延长轧制千米数,减小轧制末期硅钢边降,改善冷轧成品横向同板差。     

热连轧精轧高速钢轧辊重复上机初始辊形预报

针对热连轧精轧高速钢轧辊重复上机时存在残留磨损辊形和残留热辊形影响初始辊形的问题,分析了残留磨损辊形和残留热辊形对板形控制精度的影响及难点,得出轧辊温度场是高速钢轧辊重复上机初始热辊形最佳表征方式的结论,提出高速钢轧辊下机后空冷过程温度场建模思路,并建立轧辊空冷过程温度场计算模型。在此基础上,基于热连轧生产线二级系统框架,研究形成了高速钢轧辊重复上机初始辊形预报技术设计方案,并在首钢京唐公司1 580 mm热连轧生产线应用。应用结果表明,该技术对实现热连轧精轧高速钢轧辊更高效应用和提高板形控制精度有显著效果。     

Roll Wear Evaluation of HSS,HiCr and IC Work Rolls in Hot Strip Mill

While it is acknowledged that roll wear is one of the most challenges to hot strip mills (HSM), very few studies which detail an exact prediction model have been published. The aim of this work is to evaluate and compare two prediction models with measured roll wear. The first prediction model, model 1, developed for a plate mill, was modified to use in strip rolling process. The second prediction model, model 2, is a simplified on‐line model. Data of two hot strip mills were used to investigate the influence of different rolling schedules. The rolls and strip properties were described and the rolling conditions were detailed. The influence of hot rolling factors, such as strip strength, roll grades, rolling temperature, rolling force, reduction and contact length, were also studied. When rolling with different work roll materials and strip grades, the modified prediction model has better prediction accuracy than the simplified model. The accuracy of both models becomes better at higher roll wear > 150 μm. HSS work rolls were confirmed to exhibit improvement of roll wear in comparison with HiCr rolls, the wear resistance was 3 to 4 times better. The influence of strip grade on roll wear was shown to be significant, with higher accuracy of the regression statistics for rolling with similar strip grades and lower regressed accuracy for rolling with mixed strip grades. The roll wear was evaluated at the centre of the barrel.     

宽带钢热连轧机组均压支承辊辊形开发与应用

 CVC工作辊辊形自发明以来在全球150多条热连轧生产线上得到应用,以控制带钢的板形。实际应用中,与CVC工作辊配对使用的支承辊无论采用平辊还是CVC辊形均存在非均匀磨损甚至轧辊剥落失效的问题,主要原因是CVC支承辊辊形和平支承辊与CVC工作辊配置时存在接触压力集中。为了解决此问题,设计并应用了一种均压支承辊辊形与CVC工作辊配置使用。此辊形是变接触支承辊辊形（VCR）与CVC支承辊辊形的组合,具有变接触辊形的优点,同时又能更好地与CVC工作辊配置使用。均压支承辊辊形应用后,改善了CVC工作辊与支承辊辊间接触状态,解决了轧辊剥落问题,并改善了带钢凸度质量。     

冷轧平整机板形问题的特点及对策

对某冷轧厂1700mm单机架平整机的板形问题进行了综合研究，发现该轧机在辊形加工、轧辊磨损及弯辊使用等方面存在的问题，并通过有限元模型研究了辊形对板形的作用，分析了平整上弯辊对板厚的影响，指出平整机板形问题的特殊性。针对平整板形的设备工艺特点，提出了新的辊形配置方案并正式投入生产。结果表明，改进后的辊形配置对降低弯辊调整量、改善板形、提高生产过程稳定性效果显著。     

热连轧机工作辊局部不均匀磨损的形成原因与控制方法

针对宽带钢热连轧机工作辊严重的“猫耳朵”磨损和局部低点磨损的现象,分析了局部不均匀磨损的特点、形成原因以及对板形的影响。通过1800mm热连轧机不同窜辊方式对不均匀磨损的作用分析,提出了适合热连轧机的窜辊方式,经过现场应用证明,该窜辊方式可以减小局部磨损,改善带钢板形质量。     

Profile and Flatness Control Technology With a Long Shifting Stroke on Wide Non-Oriented Electrical Steel Sheets

 In order to solve the difficult profile and flatness control problem of wide non-oriented electrical steel sheets, the factors such as the relationship between strip crown control and strip width, the relationship between the maximum wearing value of work roll and the number of a rolling campaign and the wear contour change of work roll were analyzed on the basis of industrial test. Through analyzing the rolling process characteristics of non-oriented electrical steel sheets, the ASR (asymmetry self-compensating work rolls) shape control technology and its roll shifting strategy of the wider non-oriented electrical steel sheets was proposed and developed. When the technology was applied, the number of the wide non-oriented electrical steel (23 mm×1280 mm) in one rolling campaign rose from 40 coils of the trial production to 70 coils of the industrial production, the ratio of the measured strip crown less than 45 μm was increased from 500% to 949%, and the ratio of the measured strip crown more than 60 μm was decreased from 200% to 07%.     

武钢2250热轧平整机窜辊策略的研究

为了抑制或均匀武钢2250热轧带钢平整机在轧制服役过程中所表现出严重的W形工作辊磨损,降低磨损峰值,改善工作辊出现褶皱、光带等辊面缺陷,提高带钢的板形质量。根据现场轧制工艺条件及生产实际,通过建立热轧平整机工作辊的磨损预报模型,对工作辊的窜辊方式、窜辊步长和窜辊节奏等主要影响因素进行了研究,提出了改进的工作辊窜辊策略。通过现场试验发现,工作辊磨损峰值小于40μm,较改进前减小约20%;板形调控特性得到改善,弯辊力调节量较改进前减小约30%;降低了辊耗,延长轧辊服役时间,单位磨损量减小约20%。     

Three-Dimensional Model for Strip Hot Rolling

Steel stripis widely usedin many fields such asautomobile ,building,transportation and householdappliance ,etc·. Withthei mprovement in productiv-ity and automation of strip processing,the require-ments for crown and flatness of strip have been in-creasingly severe ,and“crown free”steel strips arerequired for some special applications such as for au-tomobile parts andtinplate cans .In order toi mprovethe strip quality , an effective three-di mensionalmodel is needful to further study on the…