超声振动对EA4T钢激光熔覆质量和性能的影响

采用超声振动辅助激光熔覆对EA4T钢表面进行修复,利用光学显微镜(OM)、扫描电镜(SEM)和X射线衍射仪(XRD),对比分析超声振动对EA4T钢激光熔覆成形质量、微观组织和物相组成的影响,通过显微硬度仪对熔覆层和基体的显微硬度进行测试。结果表明:超声振动作用下,熔覆层成形质量得到提高,原来方向性较强的枝晶组织被打断、打碎,枝晶偏析程度显著减轻;与此同时,施加超声振动晶粒得到细化,促进Cr₂₃C_6碳化物在枝晶上析出,但并未改变熔覆层物相组成;相比较未施加超声振动,超声振动作用下的熔覆层显微硬度分布更加均匀,平均显微硬度提高126.2HV_0.2,热影响区平均显微硬度下降31.2HV_0.2。     

激光熔覆镍基合金层的组织与高温耐磨性能

为了改善304不锈钢工件的高温耐磨性能,利用CO2激光器在其表面熔覆了Ni基高温合金层。研究了熔覆层的物相组成、显微组织、成分分布,测试了其显微硬度、高温耐磨性能等,并与基材进行了对比。结果表明:Ni基合金熔覆层的组织从熔池底部到表层为胞状晶—柱状枝晶—树枝晶;熔覆层的主要组成相是Ni3Cr2,NbC,Mo2C与Cr23C6;Ni基合金粉末中添加难熔元素Cr,Mo,Nb等对熔覆层的组织起到了固溶强化、硬质相强化和弥散强化作用;熔覆层的平均显微硬度达到了405 HV,高温耐磨性能是基体的2倍多。     

Ti811合金表面激光熔覆Ti2Ni+TiC+Al2O3+CrxSy复合涂层的组织和性能

以TC4+Ni45+Al₂O₃+MoS₂+Y₂O₃混合粉末为熔覆材料,采用同轴送粉技术在Ti811合金表面进行激光熔覆制备复合涂层,使用SEM、EDS和XRD等手段分析了涂层的微观组织,测试了涂层的显微硬度和摩擦磨损性能。结果表明,在激光熔覆过程中Ti811合金中的Ni和C分别与Ti发生反应,原位生成金属间化合物Ti₂Ni和硬质增强相TiC;MoS₂分解后S与Cr发生硫化反应生成了软质润滑相Cr_xS_y。网状形态的Ti₂Ni、近球状和枝晶形态的TiC以及点状的Al₂O₃,均匀分布在熔覆层中。硬质相强化和软质相润滑的共同作用,使激光熔覆层具有较高的显微硬度和较优良的耐磨性能。激光功率为900 W的熔覆层其平均显微硬度值达1303.5HV_0.5,其耐磨性能最佳。     

耐磨耐蚀Fe基激光熔覆层的组织和性能研究

目的 采用同步送粉激光熔覆技术制备兼具耐磨与耐蚀性能的Fe基熔覆层,获取熔覆层的物相组织、硬度与耐蚀性,并研究热处理对熔覆层性能的影响。方法 采用Fe-B-C-Cr-Ni-Mo-Nb-V多组元合金粉末,在304不锈钢基体上制备Fe基耐磨耐蚀熔覆层,并模拟淬火加高温回火的热处理工艺,进行熔覆层热处理试验。采用XRD、SEM表征熔覆层的物相组成和微观组织,采用显微硬度计测试熔覆层的硬度,通过极化曲线和阻抗谱对熔覆层的电化学腐蚀性能进行测试。结果 所制备的激光熔覆层同基体具有良好的冶金结合,熔覆层物相包含奥氏体g相、马氏体α''相和Cr23(C,B)6相。熔覆层的微观组织为亚共晶结构,由尺寸细小的树枝晶和枝晶间层片状共晶组织构成,热处理后还形成了大量微纳尺度的析出相。激光熔覆层的硬度相对于基体硬度提高了2.5~2.7倍,热处理后试样最高硬度达521.4HV。激光熔覆层的自腐蚀电位为−0.428 V,腐蚀电流密度为1.41×10⁻⁵ A/cm²,热处理后的熔覆层自腐蚀电位降低,腐蚀电流密度增大,阻抗值明显减小,耐蚀性降低。结论 利用激光熔覆Fe-B-C-Cr-Ni-Mo-Nb-V多组元合金粉末可制备致密、无缺陷的Fe基熔覆层,细晶强化以及大量硬质共晶组织的存在使熔覆层的硬度得到显著提升。高Cr、Ni含量保证了熔覆层具有良好的耐蚀能力,淬火加高温回火的热处理工艺使熔覆层的硬度提升,但耐蚀能力有一定程度的下降。该Fe基熔覆层在耐磨耐蚀涂层技术领域具有较好的应用前景。     

45钢表面Ni基激光熔覆层的耐蚀性能

为改善45钢表面的力学性能和耐蚀性,在相同功率下采用不同扫描速率在其表面激光熔覆制备了Ni基(Ni35A)复合涂层。利用金相显微镜、X射线衍射仪、显微硬度计和电化学腐蚀测试系统对熔覆试样进行组织形貌、相组成、显微硬度和耐蚀性能分析。结果表明:熔覆试样由熔覆层、结合区和基体3部分组成;熔覆层组织细密并与基体冶金结合,扫描速率过大时易形成裂纹;熔覆层主要由FeNi3和Ni3B相组成,不同速率所得熔覆层显微硬度均超过400 HV;扫描速率为500 mm/min时熔覆试样自腐蚀电位提高了40 mV。     

AZ31B镁合金表面激光熔覆Ni60合金粉末组织及性能EI北大核心

利用5kW横流连续CO2激光器,采用预置粉末法对AZ31B镁合金表面进行激光熔覆Ni60合金粉末试验。利用光学显微镜,SEM,XRD,显微硬度仪,电化学腐蚀设备等仪器对熔覆层和基体的组织及性能进行了测试分析。结果表明,熔覆层与基体呈冶金结合,熔覆层组织为细小的树枝晶和等轴晶;XRD结果表明在熔覆层表面形成了Mg2Ni,Mg-Ni2等新相,熔覆层的显微硬度由HV45~50提高到HV150~350,约为基体的3~7倍。在3.5%(质量分数)NaCl的溶液中进行电化学腐蚀试验表明,熔覆层表面的自腐蚀电位较原始镁合金提高约0.379V,其抗腐蚀性较原始镁合金显著提高。     

基底材料对NiCrBSiC合金激光熔覆层组织和磨损性能的影响

采用横流CO2激光在45钢和TC4钛合金表面熔覆NiCrBSiC合金涂层,利用XRD,SEM和TEM分析了激光熔覆层的微观组织,测试了激光熔覆层的硬度和摩擦磨损性能.结果表明,NiCrBSiC合金激光熔覆层的组织和性能与基底材料的种类密切相关.45钢表面激光熔覆层由γ-Ni,Ni3B,Cr7C3和CrB相组成,硬度在HV800～900之间;TC4合金表面激光熔覆层由γ-Ni,Ni3B,TiC和TiB2相组成,硬度在HV900～1100之间.TC4合金表面NiCrBSiC激光熔覆层的摩擦系数和质量磨损率分别低于45钢表面NiCrBSiC激光熔覆层的摩擦系数和质量磨损率.     

Y2O3对钛基激光熔覆层组织及性能的影响

针对Ti811钛合金硬度低、耐磨性差的问题,以TC4粉、Ni45A粉和Y₂O₃粉为原料,采用同轴送粉激光熔覆技术在Ti811钛合金表面进行了激光熔覆制备耐磨复合涂层的实验,分析了熔覆层的组织和相组成,测试了熔覆层的显微硬度和摩擦磨损等力学性能。研究表明:复合涂层组织由枝晶TiC、依附生长于枝晶TiC表面的纳米颗粒TiC、生长于基体表面的等轴球形（近球形）TiC、金属间化合物Ti₂Ni、增强相TiB、TiB₂及基体α-Ti组成,所有生成相呈均匀弥散分布状态;涂层中等轴球形（近球形）TiC和Y₂O₃构成了复合相结构,经二维点阵错配度计算表明,Y₂O₃的（111）晶面与TiC的（110）晶面的二维点阵错配度δ=6.54%,因此Y₂O₃可作为TiC的有效异质形核核心细化晶粒;涂层的显微硬度处于HV_0.5 655~700之间,较Ti811基材提高了约1.6~1.8倍;涂层的磨损机制主要为磨粒磨损,摩擦磨损性能较基材显著提升。      

合金成分对镍基合金激光熔覆涂层组织与性能的影响

为了研究激光熔覆镍基合金涂层显微组织与性能之间的关系,本文选用Ni25、Ni45、Ni60镍基自熔性合金粉末作为熔覆材料,在同一工艺参数下在45#钢基体上制得Ni25、Ni45、Ni60合金激光熔覆涂层。利用扫描电子显微镜(SEM)、能谱仪(EDS)、X射线衍射仪(XRD)、显微硬度计等方法对涂层的显微组织、物相组成、显微硬度等进行了研究。结果表明从Ni25到Ni60合金涂层,随着合金元素含量的提高,涂层微观组织逐渐由亚共晶转变为过共晶,γ-Ni奥氏体枝晶所占体积分数减少,尺寸细化,枝晶间的共晶组织和硬质相所占的体积分数增大,涂层和基体之间结合带的宽度越来越窄,熔覆层的显微硬度越来越高。Ni25、Ni45合金涂层的平均显微硬度分别为250HV和550HV左右,而Ni60合金涂层的平均硬度却高达750HV左右,为Ni25合金涂层的3倍。     

等离子熔覆Ni—Cr合金涂层的组织与性能研究

采用等离子熔覆技术在40Cr钢基材表面熔覆Ni-Cr合金涂层,研究了熔覆层的组织特征、成分和显微硬度分布特点.结果表明:等离子熔覆层与基体的结合面是由等轴晶构成的,熔覆层与基体呈现良好的冶金结合状态;熔覆层中部分布着沿逆热流方向生长的排列较规则的枝晶组织;熔覆层表层是细小的枝晶组织.能谱分析表明在结合面处Ni,Cr含量发生显著变化,等离子熔覆可以实现低稀释率.熔覆层的显微硬度呈梯度过渡到基体,熔覆层外层硬度值最高,在结合面附近硬度出现显著的变化.     

升温时效处理7075铝合金在含SRB模拟海水中的应力腐蚀行为

7系铝合金是一种可热处理强化的铝合金,通过改变热处理工艺的方法可以提高铝合金的抗应力腐蚀性能.本文研究了不同升温时效处理下,铝合金在含硫酸盐还原菌(SRB)模拟海洋溶液中的应力腐蚀行为,并通过应力-应变曲线和断口形貌,对比分析了铝合金在无菌溶液和SRB溶液中的应力腐蚀行为差异.研究表明,升温时效处理可以提高合金的自腐蚀电位,降低腐蚀电流密度和合金的应力腐蚀敏感性.硫酸盐还原菌(SRB)通过代谢促进了合金的腐蚀,改变了合金应力腐蚀开裂的机理,使合金的应力腐蚀开裂主要机理由阳极溶解转变为氢致开裂.     

45钢表面激光熔覆CoCrNi中熵合金涂层组织与性能

为探究CoCrNi中熵合金在激光熔覆领域中的应用,以CoCrNi合金粉末作为熔覆粉末,在45钢表面采用同轴送粉法制备合金涂层。利用扫描电镜、X射线衍射仪、显微硬度仪、摩擦磨损实验机和电化学工作站等设备研究了熔覆层微观组织、硬度、耐磨性和耐腐蚀性能。结果表明：熔覆层成形良好,组织均匀致密,组成相主要为FCC单相固溶体;熔池与基体交界处为平面晶,底部靠近中心为柱状晶,顶部分别为胞状晶和等轴晶,3种元素在熔覆层深度方向上的比例几乎相同;熔覆层平均硬度为250HV,摩擦系数、磨损量较基体分别降低了11.7%和36.7%;自腐蚀电流密度略有降低,CoCrNi熔覆层的钝化区域为-150到1 100 mV,表明熔覆层显著提高45钢的耐腐蚀性能。     

1Cr12Ni2W1Mo1V不锈钢表面等离子堆焊司太立熔覆层的组织及性能

为提高1Cr12Ni2W1Mo1V不锈钢的耐水蚀性能,采用等离子堆焊方法在其表面制备司太立熔覆层。研究了涂层的显微组织和显微硬度分布,分析了涂层的抗微粒冲蚀性能和耐水蚀性能。结果表明:司太立熔覆层与基体材料冶金结合良好,熔覆层组织细小、分布均匀,基体为枝晶状Co-Cr固溶体,枝晶间较均匀地分布着黑色碳化物,主要为M7C3和少量WC颗粒;司太立熔覆层的平均显微硬度(382.38 HV4.9 N)约为基材平均硬度(195.29HV4.9 N)的1.96倍,最高硬度值达到了421.00 HV4.9 N;堆焊第2层的硬度明显高于第1层的;司太立熔覆层合金的抗微粒冲蚀性能优于基材,其水蚀速度比基材小,在基材1Cr12Ni2W1Mo1V上堆焊司太立合金能有效提高其耐水蚀性能。     

Structure and composition of oxide film on 5083 alloy at brazing temperature

The structure and composition of the surface oxide film on the 5083 aluminium alloy at a brazing temperature of 500°C were investigated by transmission electron microscopy and X-ray photoelectron spectroscopy. The results showed that the original γ-Al₂O₃ film on the surface of the cold rolled 5083 aluminium alloy was transformed into a complex oxide film consisting of MgO, MgAl₂O₄, and free Al atoms after heating. The thickness of this oxide film, which could be divided into two distinct layers, was approximately 130 nm. The outer layer was mainly composed of an amorphous MgO phase, while the inner layer was MgO based, with a few free Al atoms and a small number of nanocrystalline MgAl₂O₄ particles distributed in it.     

Microstructure and properties of laser clad high-entropy alloy coating on aluminium

An AlCrFeNiCuCo high-entropy alloy (HEA) coating was synthesised on an aluminium substrate by laser cladding. Samples were characterised using an optical microscope, X-ray diffraction, scanning electron microscopy with energy-dispersive spectroscopy, a microhardness tester, and an electrochemical workstation. The results showed that the interface between the cladding layer and matrix was sound, while the HEA coating consisted of BCC and FCC solid solutions and an Al-rich phase resulting from substrate dilution. The microstructure of the clad layer comprised both columnar and equiaxed grains. The average microhardness of the coating was 550 HV_0.2, and it exhibited better corrosion resistance than the aluminium matrix in a 1?mol?L^?1 H₂SO₄ solution. The typical corrosion characteristic of the coating was pitting and localised corrosion.     

5083铝合金整体壁板耐腐蚀性能研究

铝合金整体壁板具有质量轻、耐腐蚀等特点,在国外已广泛应用在船舶建造上。本文研究了5083铝合金整体壁板的抗剥落腐蚀和应力腐蚀性能,对其耐腐蚀性能和机理进行了深入的探讨。结果表明,在铝合金整体壁板组织中β相沿加工方向成行,不连续分布,未在晶界上出现连续的β相网膜结构,因此整体壁板具有良好的耐腐蚀性能。     

机械镀Zn-Al合金镀层的耐腐蚀性能研究

为了增强机械镀镀层的耐腐蚀性能,采用机械镀方法,以含铝5%(质量分数)的Zn-Al合金粉为原料,在Q235钢材基体表面制备了Zn-Al合金镀层。利用扫描电镜(SEM)表征了合金镀层的截面和断面形貌;采用极化曲线、电化学阻抗谱(EIS)分析了合金镀层在3.5%NaCl溶液中的电化学行为;通过中性盐雾腐蚀实验分析了合金镀层的耐蚀性,并采用XRD分析了镀层的盐雾腐蚀产物。结果表明,Zn-Al合金镀层由葫芦状的Zn-Al合金颗粒交错互嵌堆积而成,镀层颗粒之间以类似隼接的连接方式搭接“卡锁”;与机械镀Zn层相比,Zn-Al合金镀层的腐蚀电位正移了209 mV,腐蚀电流密度仅为纯Zn镀层的7.1%左右,极化电阻为纯Zn镀层的14倍;Zn-Al合金镀层的容抗弧半径明显大于纯Zn镀层的弧半径,且Q_dl较纯锌层减小;纯Zn镀层出现白锈和红锈的时间分别为24和362 h,而Zn-Al合金镀层出现白锈和红锈的时间为48和504 h。Zn-Al合金镀层的耐中性盐雾腐蚀性能明显优于纯Zn镀层,合金镀层对电荷转移具有更好的抑制作用,且Zn-Al合金镀层的腐蚀产物结构致密,可增强物理屏蔽功能。     

2195铝锂合金搅拌摩擦焊接头盐雾腐蚀行为研究

本文研究了厚度为8 mm的2195铝锂合金母材及搅拌摩擦焊接头在3.5wt.％NaCl介质中的盐雾腐蚀行为,计算了不同腐蚀周期下的腐蚀速率,并通过OM、SEM、TEM观察分析母材与焊核区的腐蚀微观形貌.结果 表明:2195铝锂合金母材及搅拌摩擦焊接头在3.5％ NaCl腐蚀介质中的主要腐蚀形式为点蚀,随时间的延长发展为晶间腐蚀并剥落.2195铝锂合金搅拌摩擦焊接头耐蚀性优于母材,是因为大量高电化学活性的T1相的存在降低了母材区的耐蚀性能,在焊核区T1相完全溶解,焊核区的耐腐蚀性能强于母材区.在腐蚀初期腐蚀速率最大,随腐蚀时间的延长腐蚀速率逐渐降低,并最终趋于平稳.这是由于腐蚀产物在2195铝锂合金基体表面不断积累,对基体产生了一定保护.     

7B04铝合金-CFRP300在模拟海洋大气环境下的电偶腐蚀行为

为了有效地从腐蚀防护角度为飞机异种金属选材提供指导,针对飞机特定的服役环境,通过有限元仿真和腐蚀实验研究飞机典型搭接结构的腐蚀行为。对铝合金、复合材料及搭接件进行了实验室的周浸实验,然后通过极化曲线测量实验、宏微观形貌的观察、疲劳测试、XRD等表征手段研究7B04铝合金与CCF300/QY9511复合材料搭接件的电偶腐蚀规律,并以极化曲线测得的电化学参数为边界条件,建立了搭接件的腐蚀仿真模型。结果表明,在周浸实验0周期和10周期后,铝合金的自腐蚀电位和自腐蚀电流密度分别为-802 mV和2.357×10^-7 A/cm²,-872 mV和1.477×10^-6 A/cm²,复合材料则分别为-240 mV和6.217×10^-7 A/cm²,-98 mV和2.286×10^-7 A/cm²,随着腐蚀周期的延长7B04铝合金材料呈现自腐蚀速率加快、自腐蚀电位负移的变化趋势,而复合材料呈现自腐蚀电位正移、自腐蚀速率缓慢增大的变化趋势;搭接件腐蚀产物逐渐增多,腐蚀程度越来越严重;疲劳寿命随着腐蚀周期的延长而降低;随着腐蚀周期延长,腐蚀坑深度逐渐增大;腐蚀的产物包括Al（OH）₃,Al₂O₃,AlCl₃;搭接件仿真结果与加速腐蚀实验后的结果具有良好的一致性。该研究给出了飞机典型搭接结构的易腐蚀部位,揭示了电偶腐蚀规律,为飞机结构的腐蚀防护指明了方向。     

Research on explosive welding of aluminum alloy to steel with dovetail grooves

In order to explore a new method for the explosive welding of aluminum alloy to steel, a 5083 aluminum alloy plate and a Q345 steel plate with dovetail grooves were respectively employed as the flyer and base plates. The parameters adopted in the explosive welding experiment were close to the lower limit of weldable window of 5083 aluminum alloy to Q345 steel. The bonding properties of 5083/Q345 clad plate were studied through mechanical performance tests and microstructure observations. The results showed that the aluminum alloy and steel plates were welded under the actions of metallurgical bonding and meshing of dovetail grooves. The tensile shear strength of 5083/Q345 clad plate met the requirements of the bonding strength of Al/Fe clad plate. The interfaces between aluminum alloy and the upper and lower surfaces of dovetail grooves were mainly welded through direct bonding, and discontinuous molten zone emerged in the local region; while the interface between aluminum alloy and the inclined surface of dovetail grooves was bonded by continuous molten layer. The brittle intermetallic compounds FeAl₂ and Al₅Fe₂ were generated at the bonding interfaces of 5083/Q345 clad plate. The fracture surface of the tensile specimen exhibited ductile and quasi-cleavage fractures.