油酸钠与微细粒黑钨矿的作用机理

通过浮选实验、溶液化学计算、吸附量测试、动电位和红外光谱分析等方法,系统研究了油酸钠对微细粒黑钨矿的浮选捕收机理.结果表明:黑钨矿可浮性与油酸钠吸附量正相关,微细粒黑钨矿可浮性较好的pH区间为7.0～9.0,溶液中油酸离子和离子-分子缔合物组分对黑钨矿浮选过程起主要作用.溶液化学计算表明:油酸钠的吸附量和黑钨矿的可浮性与金属阳离子形成的油酸盐组分浓度有直接关系;油酸钠的添加使荷负电的黑钨矿动电位负移.红外光谱分析表明油酸钠在黑钨矿表面发生化学吸附,生成金属油酸盐,进而增强了黑钨矿的可浮性.     

油酸钠直接浮选孔雀石的机理研究

研究了油酸钠直接浮选孔雀石的浮选行为及作用机理.采用浮选试验、Zeta电位测试、傅里叶红外光谱测试、溶液化学计算及热力学计算进行吸附机理分析.浮选试验表明:当捕收剂油酸钠用量为160 mg/L、pH值范围7~10时,孔雀石浮选回收率可以达到70%以上;当pH=9.5时,回收率为88.67%,达到最高;动电位及溶液化学表明:油酸钠在矿浆中的组分为C_(17)H_(33)COOH·C_(17)H_(33)COO~-,C_(17)H_(33)COO~-和(C_(17)H_(33)COO)_2~(2-),油酸钠在孔雀石表面主要发生了化学吸附;根据吉布斯自由能的计算和红外光谱测试分析表明:在合适的p H值范围,油酸钠与孔雀石表面的铜离子作用生成油酸铜盐沉淀,改变了孔雀石的表面性质使它表面疏水从而容易浮选回收.     

用磁处理油酸钠溶液浮选钛铁矿及增效机理研究

研究了磁处理油酸钠溶液对钛铁矿和钛辉石浮选的影响.研究发现磁处理油酸钠溶液使钛辉石回收率由75.0%降至60.6%,钛铁矿回收率由75.2%降至69.3%;磁处理后的油酸钠溶液中钛铁矿和钛辉石的Zeta电位均正移,且钛辉石正移幅度较大,说明磁处理后油酸钠对钛铁矿的选择性增加.通过研究磁处理后油酸钠溶液的电导率、表面张力和光谱性质的变化揭示磁处理影响浮选的机理.磁处理后油酸钠溶液的电导率和表面张力增加,溶液中氢键作用减弱,促进了油酸根离子的释放,数量增多且得以释放的油酸根离子选择性吸附在钛铁矿表面,使钛铁矿和钛辉石之间的可浮性差异扩大.     

六偏磷酸钠在铝土矿浮选中的作用

通过浮选试验、吸附量测试、动电位测试,研究了六偏磷酸钠对一水硬铝石和高岭石2种矿物浮选行为的影响以及其作用机理.结果表明六偏磷酸钠对这2种矿物均有抑制作用,当捕收剂用量增大时,被六偏磷酸钠抑制的一水硬铝石的可浮性逐渐变好,而高岭石则变化不大．其主要原因在于六偏磷酸钠与捕收剂油酸钠在这2种矿物表面存在竞争吸附,而油酸钠在一水硬铝石表面的吸附能力强于在高岭石表面的吸附,使得在一定捕收剂用量下,六偏磷酸钠抑制高岭石的上浮而不抑制一水硬铝石,这为2种矿物的浮选分离提供了依据;此外,六偏磷酸钠对矿物表面的动电位影响较大,增大了矿物之间的静电排斥力,有利于矿泥的分散,增强了浮选分离的选择性．     

钛铁矿海滨砂矿尾矿的浮选试验研究

对广西北海地区的钛铁矿砂矿尾矿进行了系统浮选试验研究,钛铁矿砂矿尾矿由原矿经过重选和磁选得到.研究表明,Pb(NO_3)_2对钛铁矿有活化作用,主要是由于Pb2+与钛铁矿发生特性吸附,提高了油酸钠对钛铁矿的捕收能力.以硫酸和水玻璃作为调整剂,Pb(NO_3)_2作为活化剂,油酸钠作为捕收剂进行浮选,在硫酸用量900 g/t,水玻璃用量400 g/t,Pb(NO_3)_2用量30 g/t,油酸钠用量450 g/t的药剂制度条件下,经过一次粗选、两次精选的闭路浮选流程,可得到TiO_2品位为39.55%,回收率为54.61%的钛精矿.     

油酸钠浮选体系中褐铁矿与方解石的分离及机理

对油酸钠浮选体系中褐铁矿和方解石的可浮性及钙离子的影响及机理进行研究.以焦磷酸钠为调整剂,在油酸钠质量浓度为146.1 mg/L,焦磷酸钠质量浓度为45.7 mg/L,pH=9.5的条件下,进行褐铁矿与方解石的人工混合矿反浮选分离试验.研究结果表明:油酸钠是褐铁矿和方解石的良好捕收剂,钙离子对褐铁矿浮选有强烈抑制作用,而对方解石可浮性基本无影响;红根栲胶是方解石的有效抑制剂,而焦磷酸钠是褐铁矿的有效抑制剂;褐铁矿回收率达到91％以上,且TFe质量分数由混合原矿的28.5％提高到49.5％;钙离子强烈抑制褐铁矿是因为Ca2+消耗了部分Ol-(油酸根)生成油酸钙沉淀,减少了Ol-(油酸根)在褐铁矿表面的吸附以及竞争吸附在褐铁矿表面的钙离子与油酸根生成的油酸钙脱落;方解石在浮选体系中的部分溶解可解除焦磷酸钠对方解石的抑制作用.     

Study on the accelerant to the sodium oleate during bauxite flotation

The conventional collector for diasporemineral is oleic acid(OLA),which is highly insoluble and must be used in high dosage in bauxite flotation.Firstly flotation experiments with every reagent(sodium oleate,tween-20)were carried out and it was shown that sodium oleate was an effective diaspore collector,whereas nonionic surfactant tween-20 showed little collectivity.Then experiments were carried out with sodium oleate as the main collector with the addition of tween-20 to study the influences of potentiator on diaspore flotation.It could be seen from the experiments that potentiator had a marked influence on the recovery of diaspore,which was raised by more than 12% and that addition sequence also affected the flotation behavior.It gave the best results with the reagents mixed thoroughly before added and the best ratio of collector oleic acid and potentiator tween-20 stood at 10:1.From the calculation of the ingredients in the sodium oleate solution,at the pH 9,sodium oleate acted with surface of themineral with the acid-soap polymer [HOL·OL-].Zeta potential test showed that the potentiator promoted the absorption of collector on themineral surface,which lowered zeta potential.As could be seen from surface tension experiments,the addition of potentiator tween-20 lowered the CMC(critical micelle concentration) value of oleic acid solution,which was equivalent to raise the power of the agents.By the adsorptive capability tests,with the addition of tween-20,the adsorption of oleic acid on diaspore got more.     

TX-100对油酸钠体系下菱镁矿与白云石浮选分离的影响

菱镁矿与白云石具有相似的晶体结构、化学成分及溶解特性,导致浮选分离难度较大.本文通过浮选试验、表面张力测定、红外光谱测试及X射线光电子能谱测试,研究油酸钠体系下曲拉通X-100(TX-100)对菱镁矿与白云石浮选分离的影响.结果表明,TX-100具有强化油酸钠对菱镁矿与白云石浮选分离的效果,油酸钠以化学方式吸附于菱镁矿与白云石表面,在白云石表面可能与TX-100有竞争吸附.TX-100降低了油酸钠的表面张力,促进了油酸钠的溶解和分散,同时通过增溶作用提高了生成油酸钙沉淀所需的钙离子浓度,使得油酸钠在白云石表面的吸附减弱,对白云石有选择性的抑制作用.     

复合改性剂对氢氧化镁的表面改性研究

采用硬脂酸钠/油酸钠/聚乙二醇6 000复配表面活性剂为改性剂,对氢氧化镁进行改性研究.通过改性前后氢氧化镁粉体的吸油值及其在液体石蜡中的吸光度等性能来评价氢氧化镁的改性效果,从而确定最佳改性条件,同时采用红外谱图研究了表面改性分子与氢氧化镁表面的作用机理.正交实验结果表明,在表面改性剂的质量分数为9％,硬脂酸钠/油酸钠/聚乙二醇6 000的配料比为2：2：1（质量比）,改性温度为60℃,改性时间为100 min条件下制备的产品性能优良,在石蜡中分散性良好,红外光谱显示表面改性剂分子在氢氧化镁表面发生化学吸附.