Reinforcing properties of poly(trimethyleneterephthalate) by a thermotropic liquid crystal polymer

A thermotropic liquid crystalline copolymer (TLCP) having a trimethylene terephthalate (TT) unit and a triad terephthaloyl mesogenic unit was synthesized and its blends with poly(trimethylene terephthalate) (PTT) were prepared for TLCP‐reinforced fiber spinning. The TLCP, PTT, and their blends were characterized in terms of their thermal, mechanical, and morphological properties. In the hot‐drawn fibers of 20 wt % TLCP/PTT blend, the well‐oriented fibrils were observed at higher temperature (>T_m) than the PTT melt by polarizing optical microscope. With scanning electron microscopy images of cryogenically fractured surfaces of the blends, the TLCP were well dispersed in 0.3 to 0.5 µm in domain size. Interfacial adhesion between the TLCP and PTT seemed fairly good. The TLCP acted effectively as a reinforcing material in PTT matrix, it led to an increase of initial modulus and tensile strength of the blend fibers as TLCP's content increased. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 41408.     

The Influence of NBR-g-GMA Compatibilizer on the Morphology and Mechanical Properties of Poly (ethylene terephthalate)/Polycarbonate/NBR Ternary Blends

The work aims to study the role of NBR-g-GMA compatibilizer on the morphology and mechanical characteristics of PET/PC/NBR ternary blends. The compatibilizer content and amount of constitutive polymers are changed to correlate morphology development with mechanical properties. Various ternary samples are prepared using a twin-screw extruder whereat weight percent of rubbery dispersed phase (NBR+NBR-g-GMA) is changed. Analyzing the morphology of produced samples and interpretation of mechanical properties corroborated the role of the mentioned factors on the type of morphology and also the size of both individual and composite domains in these sorts of ternary blends. Based on this attempt, the mechanical properties of 50/50 blends of NBR/NBR-g-GMA, showed maximum toughness value compared to pure PET specimen. Also, the results revealed that by increasing the rubber content, the rodlike structures were disappeared; besides, toughness was increased. On the contrary, by increasing PC content, rodlike structures have seen by morphological study; however, core-shell droplets formed in the blend structure caused enhancing the impact strength and reducing Young's modulus. Ultimately, the ternary blend of 63/7/30 of PET/PC/ (NBR+NBR-g-GMA) revealed the best mechanical properties due to proper interaction between the PET matrix and rubbery domains in the presence of reactive compatibilizer.     

Characteristics of hydroxybenzoic acid-ethylene terephthalate copolymers and their blends with polystyrene,polycarbonate, and polyethylene terephthalate

We present a basic study of the thermal, dielectric, Theological, and mechanical properties of hydroxybenzoic acid-ethylene terephthalate copolymers (PHB-PET). It is argued that they have two-phase structures, one rich in ethylene terephthalate (PET) and one rich in hydroxybenzoic acid (PHB). Polystyrene (PS) is immiscible in 60% PHB-PET (60-PHB-PET) blends. Polycarbonate (PC) is partially miscible with the high PET phase of 60-PHB-PET. PET seems completely miscible with this high PET phase. Shear viscosity measurements on blends indicate that 60-PHB-PET gives rise to large reductions of viscosity. Extrudates and melt-spun fibers have been prepared. The phase morphologies of low PHB-PET blends as determined by scanning electron microscopy indicate ellipsoids or long fibrils of the, 60-PHB-PET in PS or PC matrices. High extrusion rates and melt spinning produce fibrillar structures. The mechanical properties of films, extrudates, and melt-spun fibers were studied. Blends with 10% 60-PHB-PET exhibited significant increases in Young's modulus and tensile strength.     

The effect of recycling number on the mechanical,chemical, thermal,and rheological properties of PBT/PC/ABS ternary blends: With and without glass‐fiber

The recycling possibilities of poly(butylene terephthalate)/polycarbonate/acrylonitrile–butadiene–styrene (PBT/PC/ABS) ternary blend with and without glass‐fiber content were investigated using repeated injection molding process. In this study, PBT/PC/ABS ternary blends were reprocessed at five times and the results were presented after each recycling process. The recycling possibility of PBT/PC/ABS ternary blend was evaluated by measuring the mechanical, chemical, thermal, and rheological properties. Mechanical properties were determined by the tensile strength, yield strength, strain at break, elastic modulus, impact strength, flexural strength, and flexural modulus. Chemical and thermal properties were evaluated by Fourier transform infrared spectroscopy, differential scanning calorimetry, thermal gravimetric analysis, and scanning electron microscopy. Rheological properties of the ternary blends were studied by melt flow index measurement. From the results, it was found that mechanical properties of recycled composites were better than virgin PBT/PC/ABS ternary blends. POLYM. COMPOS., 35:2074–2084, 2014. © 2014 Society of Plastics Engineers     

PET/PC blends: Effect of chain extender and impact strength modifier on their structure and properties

Methylene diphenyl diisocyanate (MDI) affects the morphology, rheological, mechanical, and relaxation properties, as well as tendency to crystallize of PET in PET/PC/(PP/EPDM) ternary blends produced by the reactive extrusion. Irrespective of the blend phase structure, the introduction of MDI increases the melt viscosity (MFI dropped), resulting from an increase in the molecular weight of the polymer chains; the PET crystallinity was also reduced. MDI favors compatibility of PET with PC in PET/PC/(PP/EPDM) blends. This is explained by intensified interphase interactions on the level of segments of macromolecules as well as monomer units. The presence of MDI causes a substantial rise in the dynamic shear modulus within the high‐elastic region of PET (for temperature range between T_g,PET and that of PET cold crystallization); the processes of PET cold crystallization and melt crystallization become retarded; the glass‐transition temperatures for PET and PC become closer to each other. MDI affects insignificantly the blend morphology or the character of interactions between the disperse PP/EPDM blend and PET/PC as a matrix. PP/EPDM reduces the intensity of interphase interactions in a PET/PC/(PP/EPDM), but a rise in the degree of material heterogeneity. MDI does not change the mechanism of impact break‐down in the ternary blends mentioned above. Increased impact strength of MDI‐modified materials can be explained by higher cohesive strength and resistance to shear flow at impact loading. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Toughening of recycled poly(ethylene terephthalate)/glass fiber blends with ethylene–butyl acrylate–glycidyl methacrylate copolymer and maleic anhydride grafted polyethylene–octene rubber

The aim of this study was to improve the toughness of recycled poly(ethylene terephthalate) (PET)/glass fiber (GF) blends through the addition of ethylene–butyl acrylate–glycidyl methacrylate copolymer (EBAGMA) and maleic anhydride grafted polyethylene–octene (POE‐g‐MAH) individually. The morphology and mechanical properties of the ternary blend were also examined in this study. EBAGMA was more effective in toughening recycled PET/GF blends than POE‐g‐MAH; this resulted from its better compatibility with PET and stronger fiber/matrix bonding, as indicated by scanning electron microscopy images. The PET/GF/EBAGMA ternary blend had improved impact strength and well‐balanced mechanical properties at a loading of 8 wt % EBAGMA. The addition of POE‐g‐MAH weakened the fiber/matrix bonding due to more POE‐g‐MAH coated on the GF, which led to weakened impact strength, tensile strength, and flexural modulus. According to dynamic rheometer testing, the use of both EBAGMA and POE‐g‐MAH remarkably increased the melt storage modulus and dynamic viscosity. Differential scanning calorimetry analysis showed that the addition of EBAGMA lowered the crystallization rate of the PET/GF blend, whereas POE‐g‐MAH increased it. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Effect of blending sequence on the morphology and impact toughness of poly(ethylene terephthalate)/polycarbonate blends

The morphology of PET/PC/E‐GMA‐MA blends made by different mixing sequences was studied by transmission electron microscopy (TEM). The results suggest that migration of the E‐GMA‐MA copolymer from the PET phase to the PC phase occurred during the mixing of the (PET/E‐GMA‐MA) pre‐blend with the PC at 10% copolymer content. As a result of the migration, the E‐GMA‐MA particles are located in the PC phase rather than in the PET phase. This finding is not in agreement with the prediction made previously by others based on the possible reaction between the epoxy group of GMA and carboxyl group of PET. Core‐shell (PC/E‐GMA‐MA) particles formed in situ during blending and the size of the core‐shell particles was controlled by the blending sequence used. Mechanical properties of the ternary blends were tested at various temperatures. Although the blending sequence does not have a noticeable effect on the yield strength and modulus of the blends, it has a strong influence on the morphology formed, which determines the impact toughness. For blends made under optimum processing conditions, the brittle‐ductile transition occurred at a lower temperature and lower elastomer content. A study of the toughening mechanism suggested that the major toughening events were cavitation plus matrix shear yielding. It is postulated that the very high impact toughness found with the (PC/E‐GMA‐MA)/PET blend (at 10% E‐GMA‐MA) originated from the bimodal particle size distribution of the core‐shell particles formed in situ.     

Effect of composition and molecular structure on the LC phase of PHB-PEN-PET ternary blend

Poly(p-hydroxybenzoic acid) (PHB)–poly(ethylene terephthalate) (PET) 8/2 thermotropic liquid crystalline copolyester, poly(ethylene 2,6-naphthalate) (PEN), and PET were mechanically blended to pursue the liquid crystalline (LC) phase of ternary blends. The torque values of blends with increasing PHB content abruptly decreased above 40 wt % of PHB content because the melt viscosity of ternary blends dropped. Glass transition temperature and melting temperature of blends increased with increasing PHB content. The tensile strength and initial modulus of blends were low at 10 and 20 wt % PHB. However, the blends containing above 30 wt % PHB were improved with increasing PHB content due to the formation of fibrous structure. The blend of 20 wt % PHB formed irregularly dispersed spherical domains, and the blends of 30–40 wt % PHB showed LCP ellipsoidal domains and fibrils. In the polarized optical photographs, the blends of 40 wt % PHB showed pseudo LC phases. The degree of transesterification and randomness of blends were increased with blending time. © 1998 John Wiley & Sons, Inc. J. Appl. Polym. Sci. 70: 1065–1073, 1998     

Self‐reinforcing elastomer composites based on polyolefinic thermoplastic elastomer and thermotropic liquid crystalline polymer

In situ reinforcing elastomer composites based on Santoprene thermoplastic elastomer, a polymerized polyolefin compound of ethylene–propylene–diene monomer/polypropylene, and a thermotropic liquid crystalline polymer (TLCP), Rodrun LC3000, were prepared using a single‐screw extruder. The rheological behavior, morphology, mechanical, and thermal properties of the blends containing various LC3000 contents were investigated. All neat components and their blends exhibited shear thinning behavior. With increasing TLCP content, processability became easier because of the decrease in melt viscosity of the blends. Despite the viscosity ratio of dispersed phase to the matrix phase for the blend system is lower than 0.14, most of TLCP domains in the blends containing 5–10 wt % LC3000 appeared as droplets. At 20 wt % LC3000 or more, the domain size of TLCP became larger because of the coalescence of liquid TLCP threads that occurred during extrusion. The addition of LC3000 into the elastomer matrix enhanced the initial tensile modulus considerably whereas the extensibility of the blends remarkably decreased with addition of high TLCP level (>.20 wt %). The incorporation of LC3000 into Santoprene slightly improved the thermal resistance both in nitrogen and in air. Dynamic mechanical analysis results clearly showed an enhancement in dynamic moduli for the blends with 20–30 wt % LC3000. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

PET/PTT共混体系的相容特性及力学性能研究

通过熔融共混法制备了聚对苯二甲酸乙二醇酯(PET)与聚对苯二甲酸醇酯(PTT)的共混物,采用差示扫描量热仪、动态热机械分析仪、万能电子试验机等对共混体系的热性能、动态力学性能及拉伸性能进行了测试。测得PET/PTT共混体系只有1个玻璃化转变温度(Tg)和损耗峰,表明在非晶区完全相容,其中纯PET的Tg为84℃,纯PTT的Tg低于50℃; 而双重熔融峰及热结晶峰宽化现象的出现表明,共混体系在晶区是部分相容,各组分倾向于分别进行有序化排列、单独结晶,其中纯PET的熔点为256℃,纯PTT的熔点为229 ℃;共混体系的拉伸模量和拉伸强度随PTT含量的增加呈上升趋势;但当共混比例接近时体系的拉伸模量和拉伸强度有所下降,共混比为5/5时的拉伸模量和拉伸强度分别低达1098MPa和51MPa。     

Reactive blending of poly(ethylene terephthalate) with a liquid crystalline copolyester and polyhydroxyether

Poly(ethylene terephthalate) modified with a dianhydride (PET–anhydride) was melt‐blended with a liquid crystalline copolyester (Vectra A) in the presence of a small amount of a liquid crystalline polyhydroxyether. The mechanical properties of a blend consisting of PET–anhydride/Vectra A/polyhydroxyether were drastically improved compared to blends without polyhydroxyether or without anhydride. Melt‐spun fibers of PET–anhydride/Vectra A/polyhydroxyether in a 80/20/0.75 weight ratio displayed a much higher tensile modulus (17 GPa) and tensile strength (214 MPa) than did a 80/20 PET–anhydride/Vectra A blend (4 GPa and 60 MPa, respectively). A similar increase in modulus and strength was found for a 90/10/0.75 relative to a 90/10 blend. The tensile moduli of the blends can well be described by the Tsai–Halpin equation. A better fibril formation was observed, which was attributed to an improved viscosity ratio. Reactions between the various functional groups during melt processing were indicated by viscosity measurements. The polyhydroxyether may act as a reactive compatibilizer which improves the interfacial adhesion, chemically and/or physically. WAXD recordings of both blends showed a crystalline and highly oriented Vectra phase. The PET phase was unoriented and amorphous in a PET/Vectra blend and semicrystalline and weakly oriented in a PET/Vectra/polyhydroxyether blend. Postdrawing of the various blend fibers to λ = 4 increased the modulus by about 40% and the tensile strength by more than 100%, mainly through orientation of the PET phase. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 71: 1107–1123, 1999     

Deformation and morphology development of poly(ethylene terephthalate)/polyethylene and polycarbonate/polyethylene blends with high interfacial contact during elongation

Immiscible blends of poly(ethylene terephthalate) (PET)/polyethylene (PE) and polycarbonate (PC)/PE were examined to study the influence of the high interfacial contact (pseudo‐adhesion) on the mechanical properties and the morphology developed during elongation. The high interfacial contact resulted from the contraction difference of the two polymers during cooling from the processing temperature to room temperature. As a result of the pseudo‐adhesion, the tensile strength and modulus of the PET/PE and PC/PE blends increased steadily with the increase of PET and PC concentration. In PC/PE blends, numerous PC microfibers were formed in‐situ, while in PET/PE blends, slippage took place between the PET particles and the matrix. Moreover, the macroscopic morphology development of both blends upon elongation was quite different. For PET/PE blend, necking was initiated at one point close to the non‐gate end of the specimen, and then propagated uniformly from this point. For the PC/PE blend, necking‐initating sites and propagation were irregular, and consequently the whole tested zone was deformed. The recoil of partially elongated specimens indicated that the recoverability of the PC/PE blend is higher than that of the PET/PE blend. Polym. Eng. Sci. 44:1561–1570, 2004. © 2004 Society of Plastics Engineers.     

Morphology and mechanical properties of fibers from blends of a liquid crystalline polymer and poly(ethylene terephthalate)

The domain morphology and mechanical properties of fibers spun from blends of a thermotropic liquid crystalline polymer, Vectra A-900, and poly(ethylene terephthalate) (PET) have been studied across the entire composition range. The PET phase was removed by etching to reveal fibrillar LCP domains in the blends of all compositions. The 0.5μm fibril appeared to be the basic structural entity of the LCP domains. A primary effect of composition was the change from discontinuous fibrils when the composition was 35 and 60% by weight LCP to continuous fibrils when the composition was 85 and 96% LCP. This transition had major ramifications on the mechanical properties: the modulus increased abruptly between 60 and 85% LCP, and a change in the fracture mode from brittle fracture to a splitting mode was accompanied by an increase in fracture strength. Different models were required to describe the mechanical properties of the discontinuous and continuous fibril morphologies. Analytic models for short aligned fibers of Nielsen, and Kelly and Tyson were applicable when the LCP fibrils were discontinuous, while modulus and strength of blend fibers with continuous LCP fibrils were discribed by the rule of mixtures.     

Studies on blends of polyethylene terephthalate with bisphenol-a-polycarbonate and polypropylene

Moldability and mechanical properties of polyethylene terephthalate (PET) under normal molding conditions were found to improve significantly when it was blended with bisphenol-A-polycarbonate (PC) and polypropylene (PP) to form ternary polymer blend systems. DSC results of these blends revealed that the PET and PC components formed a miscible blend while PP being incompatible with them, formed a separate phase. PP was also found to form a sleeve around the PET-PC miscible phase and, thereby, showed a skin-core type of morphology. Variations of mechanical properties with varying amounts of PP was measured keeping the ratio of PET and PC constant. Tensile and flexural properties of the blends decrease with the amount of PP. Notched impact strength increases up to a certain level of PP and then decreases, while the unnotched values decrease gradually. The effect of annealing on the mechanical properties of these blends have been discussed on the basis of the increased crystallinity of some of the components.     

Properties of a thermotropic liquid crystalline polymer blended with different thermoplastics

Thermal, rheological, morphological, and mechanical properties of a thermotropic liquid crystalline polymer, TLCP (copolyester Vectra A-950 from Hoechst), blended with a polycarbonate (PC), a polyethylene glycol terephthalate (PETG), and a blend of PC and PETG (20/80) are presented and discussed. Important supercooling effects are observed for the TLCP. For the blends the glass transition temperature of the matrix is shown to decrease slightly, suggesting partial miscibility of the components. A finer dispersion is observed for the TLCP/PC blends, at least for TLCP concentrations lower than 20%, for which the mechanical properties are quite good. For higher TLCP concentrations, as well as for the other two matrices, the mechanical properties follow more or less the mixing rule, and the morphology of the blends suggests poor adhesion. We were unable to obtain fibrillar structures by extruding the blends through a capillary rheometer; in the TLCP/PC blends, the TLCP domains were too small, and for the other blends the extrudates had not enough melt strength.     

Structural,rheological, and mechanical properties of ternary blends of PEN,PET, and liquid crystalline polymer

Structural, rheological, and mechanical properties of ternary blends of a liquid crystalline copolyester (LCP) composed of p-hydroxybenzoic acid and 2,6-hydroxynaphthoic acid, poly(ehtylene naphthalate)(PEN), and poly(ethylene terephtalate) (PET) were investigated using capillary rheometry, tensile testing, scanning electron microscopy, and X-ray diffraction. Viscosity-shear rate behavior of the ternary blends is very similar to that of pure polymers and their binary blends. The activation energy of flows of the ternary blends was smaller than those of PEN and PET. Tensile modulus and strength of extruded strands of the blends increased with increasing LCP content. The extruded strands of the blends consist of a crystalline and oriented LCP phase and an amorphous and unoriented PEN/PET blended phase. Tensile mechanical properties and structures of the ternary blends were discussed.     

Fabrication of High Performance PET/TLCP Fibers through the Synergistic Interfacial Enhancement and Compatibilization of Functional 1D and 2D Carbon Nanomaterials

The maleic anhydride functionalized graphene oxide (GO-MA) is fabricated by an efficient and solvent-free Diels–Alder reaction. Polyethylene terephthalate (PET)/thermotropic liquid crystal polyester (TLCP), PET/TLCP/GO-MA, PET/TLCP/aminated multi-walled carbon nanotubes (MWCNTs-NH₂), and PET/TLCP/GO-MA/MWCNTs-NH₂ composite fibers are systematically melt-spun. The structure and compatibilizing effects of GO-MA and MWCNTs-NH₂ on the mechanical, thermal, and crystallization properties of the composite fibers are indicated. The non-isothermal crystallization kinetics and X-ray diffraction (XRD) data show that TLCP and nanofillers can change the crystalline morphology of PET. The mechanical properties of the fibers rise with increasing TLCP content. The tensile strength 929 MPa and modulus 17.5 GPa of the fibers with 7 wt% TLCP and 0.25 wt% nanofillers (0.1 wt% GO-MA and 0.15 wt% MWCNTs-NH₂) are significantly higher than those with 7 wt% TLCP (tensile strength 622 MPa and modulus 16.1 GPa) and even higher than those with 15% TLCP (tensile strength 836 MPa, and modulus 18.0 GPa). When the GO-MA and MWCNTs-NH₂ co-exist, the anti-dripping phenomenon is improved. Therefore, the TLCP, GO, and MWCNTs synergistically strengthens the mechanical properties. This is promising for the industrial fabrication of high-strength fibers.     

Mechanical,chemical, thermal,and rheological properties of recycled PA6/ABS binary and PA6/PA66/ABS ternary blends

The effects of multiple injection molding cycles on the chemical and mechanical properties of PA6/ABS and PA6/PA66/ABS blends are investigated. The chemical structures of both PA6/ABS binary and PA6/PA66/ABS ternary blends do not alter after recycling process. For PA6/ABS binary blend, it is found that the tensile strength, strain at break, elastic modulus, impact strength, flexural strength, and modulus of recycled blend decrease by 6.49%, 15.19%, 21.00%, 9.41%, 7.09%, and 8.25%, respectively, while MFI increases by 23.59% as compared with the virgin blend. After five recycling process for PA6/PA66/ABS ternary blend, the tensile strength, strain at break, and impact strength of recycled blend decrease by 18.00%, 50.80%, and 87.27%, respectively. However, flexural strength and modulus of PA6/PA66/ABS blend increase slightly. For virgin PA6/PA66/ABS blend, MFI value was 7.7 g/10 min and with recycling this value showed an important increase to 31.56 g/10 min after five cycles. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 40810.     

Study of the Processing and Mechanical Properties of In Situ Composite Materials of Thermoplastics with Thermotropic Liquid Crystalline Polymers

By blending thermoplastics (TPs)—polycarbonate (PC) and polyethersulfone (PES)—with thermotropic liquid crystalline polymers (TLCPs)—KU9221 and KU9231—and then extruding the blends to form fibers, the in situ reinforcing characteristics were studied. The injection experiment of blends was compared with the extrusion experiment. According to the experimental results, in situ reinforcing characteristics of these processes were analyzed theoretically. These researches have come to some important conclusions. TLCP domains can be transformed to form fibers that are oriented in the direction of flow during processing; these TLCP microfibers result in improved mechanical properties of the TP/TLCP blends. The extruding flow is more effective in orienting TLCP domains and results in better in situ reinforcement than that of injection molding, and the extruded fibers have better mechanical properties. The mechanical properties of the blend fibers are improved greatly with increasing tensile ratio of melt drawing and the content of TLCPs.     

Melt rheology and interfacial properties of binary and ternary blends of PS,EOC, and SEBS

This works systematically investigates the interfacial properties of the binary and the ternary blends based on polystyrene (PS), ethylene octene copolymer (EOC), and styrene–ethylene–butylene–styrene (SEBS) by analyzing the melt linear rheological behavior of the blends and neat components. Moreover, the relationship between rheology, phase morphology, and mechanical properties of PS/EOC ternary blends with various quantities of SEBS were studied. The surface shear modulus (β) and interfacial tension values obtained by Palierne model indicated that the EOC/SEBS blend has the best interfacial properties, while the lowest interaction was found for PS/EOC blend. Based on the Palierne model and Harkin's spreading coefficients a core–shell type morphology with EOC phase encapsulated by the SEBS shell dispersed in the PS matrix was determined for the ternary blends. Scanning electron microscopy results revealed that both fibrillar and droplet forms of dispersed phase could be developed during the blending of PS and EOC in presence of SEBS. The extent of fibrillar morphology and interfacial interactions in PS/EOC/SEBS ternary blends was dependent on the SEBS content. The improvement of the mechanical properties of PS/EOC blends in the presence of SEBS was evidenced by the tensile and impact resistance experiments. The tensile strength reinforcement was more pronounced for the ternary blends with more fibrillar dispersed phase. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2020 , 137, 48791.