Tailoring of misfit along interfaces between ZnxMn3−xO4 and Ag

This work is aimed at examining how the tetragonality of Zn_xMn_3−xO₄ spinel structures depends on the chemical composition when Zn_xMn_3−xO₄ is embedded in a metal matrix. The paper focuses on a wide range of Zn_xMn_3−xO₄ precipitates in a Ag matrix with x varying between 0 and 1.5. This variation of x has been obtained by internal oxidation of Ag–2at.%Mn–4at.%Zn in air followed by annealing in vacuo at different temperatures. It will be demonstrated that the Zn concentration x in Zn_xMn_3−xO₄ has a major influence on the interfacial misfit and orientation relation between Ag/Zn_xMn_3−xO₄. The degree of mismatch of 10.4% of 1 1 1 Ag–Mn₃O₄ and 2.4% of Ag–Zn_1.5Mn_1.5O₄ was visualized using the Bragg filtering technique on HRTEM micrographs of those interfaces. It was possible to identify misfit dislocations qualitatively with this technique at 1 1 1 Ag–Zn_xMn_3−xO₄ interfaces with different degree of mismatch.     

Power factor of La1−xSrxFeO3 and LaFe1−yNiyO3

The electrical conductivity (σ), Seebeck coefficient (S), and power factor (σS²) of perovskite-type LaFeO₃, La_1−xSr_xFeO₃ [0.1 ≤ x ≤ 0.4] and LaFe_1−yNi_yO₃ [0.1 ≤ y ≤ 0.6] were investigated in the temperature range of 300–1100 K to explore their possibility as thermoelectric materials. The electrical conductivity of LaFeO₃ showed semiconducting behavior, and its Seebeck coefficient changed from positive to negative around 650 K with increasing temperature. The electrical conductivity of LaFeO₃ increased with the substitutions of Sr and Ni atoms, while its Seebeck coefficient decreased. The Seebeck coefficient of La_1−xSr_xFeO₃ was positive, whereas that of LaFe_1−yNi_yO₃ changed from positive to negative with increasing Ni content. The substitutions of Sr and Ni were effective in increasing the power factor of LaFeO₃; 0.0053 × 10⁻⁴ Wm⁻¹ K⁻² for LaFeO₃ (1050 K), 1.1 × 10⁻⁴ Wm⁻¹ K⁻² for La_1−xSr_xFeO₃ (x = 0.1 at 1100 K) and 0.63 × 10⁻⁴ Wm⁻¹ K⁻² for LaFe_1−yNi_yO₃ (y = 0.1 at 1100 K).     

Subsolidus phase relation and crystal structure of the PrBa2−xSrxCu3O7±δ system

The PrBa_2−xSr_xCu₃O_7±δ solid solution was investigated by means of X-ray powder diffraction in combination with Rietveld analysis. The Sr-doped Pr123 single phase could be synthesized at 950 °C in air. The solubility of PrBa_2−xSr_xCu₃O_7±δ solid solution is 0.2≤x≤0.6. The structure of PrBa_2−xSr_xCu₃O_7±δ is orthorhombic for x=0.2. The structure transforms into tetragonal for 0.3≤x≤0.6. In the PrBa_2−xSr_xCu₃O_7±δ structure, Sr ions can replace Ba ions, the highest value is x=0.6 under our experimental condition. But Sr ions could not replace Pr ions. Furthermore Pr ions could not occupy the sites of Ba ions in the PrBa_2−xSr_xCu₃O_7±δ system. Both ionic radii and chemical properties play an important role in the mutual substitution of Pr, Ba and Sr ions in the Pr123 structure of the PrBa_2−xSr_xCu₃O_7±δ system.     

The characteristics of Li(CoxNi1 − x)O2 cathode powders formed from the fine-sized Co3O4/NiO precursor powders

Li(Co_xNi_1 − x)O₂ (0 ≤ x ≤ 1) cathode powders were prepared by solid state reaction method using Co₃O₄/NiO precursor powders obtained by spray pyrolysis. The effect of the ratios of cobalt and nickel components on the characteristics of Co₃O₄/NiO precursor and Li(Co_xNi_1 − x)O₂ cathode powders were investigated. The Co₃O₄/NiO precursor powders with the ratios of cobalt and nickel components as 1/0, 0.75/0.25 and 0.5/0.5 had submicron size and regular morphologies. On the other hand, the Co₃O₄/NiO powders with the high contents of nickel component had aggregated morphologies of submicron size primary powders. The fine-sized precursor powders formed the fine-sized LiCoO₂ and Li(Co_0.75Ni_0.25)O₂ cathode powders by solid state reaction with LiOH powders. However, the high contents of the nickel component of the Co₃O₄/NiO precursor powders formed the Li(Co_xNi_1 − x)O₂ (0 ≤ x ≤ 0.5) cathode powders with aggregated morphologies and large sizes. The discharge capacities of the powders increased with increasing the nickel content into the Li(Co_xNi_1 − x)O₂ cathode powders up to 188 mAh/g.     

Microstructure and tribological properties of LaxCeyO1 − x − y composite nanofilms

A series of La_xCe_yO_{1 − x − y} films (x = 0–0.54, y = 0–0.58) with thickness of 35–45 nm was deposited by unbalanced magnetron sputtering. High-resolution transmission electron microscope observation shows that La_0.24Ce_0.34O_0.42 film has polycrystalline structure. La₂O₃ and CeO₂ are formed within the La_xCe_yO_{1 − x − y} films confirmed by the X-ray diffraction and X-ray photoelectron microscopy. The friction coefficient and residual compressive stress of five kinds of three-element compound films exhibit symmetric distribution with the relative equilibrium of La and Ce atomic concentration within the films. The critical load of all deposited films is between 28 and 33 mN. The friction coefficient of two kinds of rare earth complex oxide films is in the range of 0.08–0.09, which is lower than that of only one kind of rare earth oxide films, and the friction mechanism is discussed.     

Electrical, magnetic and elastic properties of La1.2(Sr1−xCax)1.8Mn2O7 (0.0 ≤ x ≤ 0.4)

Polycrystalline bulk samples of double layered manganite system La_1.2(Sr_1−xCa_x)_1.8Mn₂O₇ (0.0 ≤ x ≤ 0.4) were prepared by sol–gel method. After characterizing the samples using XRD and SEM, their electrical, magnetic and elastic properties were investigated. The lattice parameters and cell volume show a monotonous decrease with increase of Ca content, whereas the grain size is found to increase with increasing Ca content. The value of T_IM is found to decrease with Ca content up to x = 0.3 and then a slight increase of T_IM is observed. The low temperature upturn of resistivity is attributed to the spin-glass-like behavior, which is also evidenced by the irreversibility observed between ZFC and FC magnetizations. The conduction mechanism above T_IM can be explained by Mott VRH model. The present magnetization and ultrasonic studies indicate that the system shows a secondary transition at T^*, which decreases with increasing Ca content. Further, the T^* seems to be intrinsic to the present double layered manganite system.     

Nanocrystalline LaNi4−xMn0.75Al0.25Cox electrode materials prepared by mechanical alloying (0≤x≤1.0)

Polycrystalline hydrogen storage alloys based on lanthanum (La) are commercially used as negative electrode materials for the nickel–metal hydride (Ni–MH_x) batteries. In this paper, mechanical alloying (MA) was used to synthesize nanocrystalline LaNi_4−xMn_0.75Al_0.25Co_x (x=0, 0.25, 0.5, 0.75 and 1.0) hydrogen storage materials. XRD analysis showed that, after 30 h milling, the starting mixture of the elements decomposed into an amorphous phase. Following the annealing in high purity argon at 700 °C for 0.5 h, XRD confirmed the formation of the CaCu₅-type structures with a crystallite sizes of about 25 nm. The nanocrystalline materials were used as negative electrodes for a Ni–MH_x battery. Cobalt substituting nickel in LaNi₄Mn_0.75Al_0.25 greatly improved the discharge capacity and cycle life of the LaNi₅ material. For example, in the nanocrystalline LaNi_3.75Mn_0.75Al_0.25Co_0.25 powder, discharge capacities up to 258 mA h g⁻¹ (at 40 mA g⁻¹ discharge current) were measured. Mechanical alloying is a suitable procedure to obtain LaNi₅-type alloy powders for electrochemical energy storage.     

Preparation and structures of the La1−xKxCo1−xNbxO3 (x = 0–l) system

The La_1−xK_xCo_1−xNb_xO₃ system was performed by conventional solid state reaction technique using metal oxides. By DSC analysis, the activation energy of crystallization of the powders with x = 0.3 is 388.4 kJ/mol. The crystal structure of the compound reveals a transition from rhombohedral to cubic, and then to orthorhombic structure as the amount of the potassium niobate (KNbO₃) increases. It is found that the structure of the samples with x < 0.3 is similar to that of lanthanum cobaltate (LaCoO₃), while at the compositions with 0.7 ≥ x ≥ 0.3, the structure transforms to cubic. Finally, with x ≥ 0.7, the structures were similar to that of KNbO₃. According to the results of selected-area-diffraction (SAD) patterns and X-ray diffraction (XRD) identifications, the lattice parameters were calculated. The direction of superlattice structure along [2 1 0] was found for x = 0.5 as identified from SAD patterns. The dielectric constants were measured with cubic structure. Dielectric constant (K) decreases with increasing x.     

Large-scale synthesis of Pb1−xLaxTiO3 ceramic powders by molten salt method

The ferroelectric perovskite type lanthanum doped lead titanate (PLT) ceramic powders were synthesized in one step with the starting materials of PbC₂O₄, La₂O₃ and TiO₂ in NaCl–KCl molten salts in the temperature range of 700–950 °C. It was found that molten salt method was a large scale and easy preparation way to produce PLT powders with high dispersity. Tetragonal phase Pb_1−xLa_xTiO₃ ceramic powders were identified by XRD in the composition range 0 ≤ x ≤ 0.3 and mono-dispersed particles with spheric shape and less than 100 nm size were observed by SEM. The grain sizes of Pb_1−xLa_xTiO₃ ceramic powders increased with the increase of La content and decreased with calcination temperature. The grain growth progress and the possible reaction mechanism in molten salts and its influencing factors were discussed in this work. The grain growth process was the main influencing factor of the grain size, which depended on the solubility in the flux.     

Study of the structural, thermodynamic and electrochemical properties of LaNi3.55Mn0.4Al0.3(Co1−xFex)0.75 (0 ≤ x ≤ 1) compounds used as negative electrode in Ni-MH batteries

This study concerns the influence of iron for cobalt substitution on the structural, thermodynamic and electrochemical properties of the hydrides of poly-substituted LaNi_3.55Mn_0.4Al_0.3(Co_1−xFe_x)_0.75 (0 ≤ x ≤ 1) alloys used as material for negative electrode in Ni-MH batteries. The Fe substitution leads to an increase of the cell parameter, this increase is linear according to the rate of substitution, and a decrease of the equilibrium pressure in agreement with the geometric law. Nevertheless, it is observed that the Fe substitution leads to a deviation from the linear variation between the logarithm of the pressure and the cell volume observed for Co, Mn and Al for Ni substitution. The Fe for Co substitution leads also to a decrease of the solid–gas and electrochemical capacity.     

Phase behavior and some properties of LaMn1−xRhxO3 solid solution

Structure and magnetic and electrical properties of the polycrystalline compounds LaMn_1−xRh_xO₃ (0 < x ≤ 1) have been investigated. The samples were characterized by X-ray diffraction and Rietveld refinement which confirmed the space group Pnma (No. 62) for all compositions at room temperature. A transformation from O′- to O-type orthorhombic structure is seen near x = 0.6 tending to make the phase unstable. The electrical conductivity measurement shows semiconducting property above room temperature with a rather low activation energy for Mn-rich compositions. Compounds in the region 0.1 ≤ x ≤ 0.9 show ferromagnetic property but the substitution of Rh³⁺ ion for Mn³⁺ ion suppresses the ferromagnetism that results in reducing the Curie temperature, T_C.     

Roles of lithium ions and La/Li-site vacancies in sinterability and total ionic conduction properties of polycrystalline Li3xLa2/3−xTiO3 solid electrolytes (0.21 ≤ 3x ≤ 0.50)

The Li_0.33La_0.55TiO₃ solid electrolyte has a maximum grain ionic conductivity of 1.13 × 10⁻³ S cm⁻¹ among the Li_3xLa_2/3−xTiO₃ oxides (0.21 ≤ 3x ≤ 0.50), but the total ionic conductivity of its polycrystalline phase is not the highest. Owing to the grain-boundary resistances controlling the total resistances of bulk samples, an excellent solid electrolyte is mainly characterized by the grain-boundary resistances. With regard to the role of lithium ions, the substitution of La³⁺ ions by the Li⁺ ions weakens the strength of inter-ionic forces, leading to the decrease in the sintering temperature. The presence of La³⁺/Li⁺-site vacancies promotes the densification and grain growth and further results in rapid decreases in porosity and grain-boundary resistances. Li_0.21La_0.60TiO₃ with a larger amount of La³⁺/Li⁺-site vacancies can therefore exhibit the highest total ionic conductivity through rapidly decreasing its grain-boundary resistances by changing its microstructure, and it becomes a better polycrystalline solid electrolyte than Li_0.33La_0.55TiO₃ in the Li_3xLa_2/3−xTiO₃ system studied, in spite of its lower grain ionic conductivity.     

Magnetic phase transitions in Nd1−xYxMn2Ge2 (0 ≤ x ≤ 0.6)

The structure and magnetic properties of Nd_1−xY_xMn₂Ge₂ (0.0≤x≤0.6) were studied by X-ray powder diffraction and magnetization measurements. All compounds crystallize in the ThCr₂Si₂-type structure with space group I4/mmm. Substitution of Y for Mn led to a linear decrease in the lattice constants and the unit cell volume. Increasing substitution of Y for Nd in NdMn₂Ge₂ shows a depression of ferromagnetic ordering and the gradual development of antiferromagnetic ordering.     

Ba4In2−x(CO3)1+xO6−2.5x and Ba4In0.8Cu1.6(CO3)0.6O6.2—new indium oxycarbonates closely related to n=3 Ruddlesden–Popper phases

Investigations of phase relations in the Ba-rich part of the In₂O₃–BaO(CO₂)–CuO pseudo-ternary system at 900 °C have revealed the existence of new indium–copper oxycarbonate – Ba₄In_0.8Cu_1.6(CO₃)_0.6O_6.2. Rietveld refinement of the X-ray powder diffraction data combined with infrared studies gives evidence that this phase is a oxycarbonate crystallising in the tetragonal structure (space group I4/mmm) with unit cell parameters: a=4.0349(1) Å and c=29.8408(15) Å. In the binary part of the In₂O₃–BaO(CO₂) system we have identified the occurrence of Ba₄In_2−x(CO₃)_1+xO_6−2.5x oxycarbonate solid solution showing a crystal structure also described by I4/mmm space group, but with the unit cell parameters: a=4.1669(1) Å and c=29.3841(11) Å for x=1. The existence range of this phase, −0.153<x<0.4, includes chemical compositions of earlier found phases: Ba₅In_2+xO_8+0.5x with 0≤x≤0.45 (known as the -solid solution), as well as the binary Ba₄In₂O₇ phase. The crystal structures of both new oxycarbonates are isomorphic and related to n=3 member of the Ruddlesden–Popper family.     

X-ray diffraction and Mössbauer study of (Fe1−xNix)4N (0.2 ≤ x ≤ 0.6) films

Single phase (Fe_1−xNi_x)₄N compounds (0.2 ≤ x ≤ 0.6) have been synthesized by reactive evaporation and investigated by X-ray diffraction and Mössbauer spectrometry. The lattice parameters of the nitrides decrease from 3.796 to 3.774 Å with increasing Ni concentration. The fitting results of Mössbauer spectra indicate that the average hyperfine field have the same changing tendency with lattice parameter and the nickel atoms have a tendency to be located at the corner site.     

On the crystal structure of new series of compounds, RPt2+xSb2−y (x = 0.125, y = 0.25; R = La, Ce, Pr)

A new compound CePt_2+xSb_2−y (x = 0.125, y = 0.25) was synthesized by arc-melting of the elements. The chemical and structural characterizations were carried out at room temperature on as-cast samples using X-ray diffractometry, metallographic analysis and EDS-microanalysis. According to the results of X-ray single crystal diffraction this antimonide crystallizes in I4cm space group (no. 108), Z = 32, ρ = 12.19 Mg/m³, μ = 89.05 mm⁻¹ (a = 12.5386(3) Å, c = 21.4692(6) Å (crystal I) and a = 12.5455(2) Å, c = 21.4791(5) Å (crystal II)). The structure and composition were confirmed by powder X-ray diffraction (a = 12.4901(2) Å, c = 21.3620(4) Å) and EDS-microanalysis respectively. Isotypic compounds were observed with La and Pr from X-ray powder diffraction of as-cast alloys at room temperature (a = 12.6266(4) Å, c = 21.4589(6) Å for LaPt_2+xSb_2−y and a = 12.5184(5) Å, c = 21.4178(7) Å for PrPt_2+xSb_2−y). The CePt_2+xSb_2−y structure is derived from CaBe₂Ge₂ (a = 2a₀ − 2b₀, b = 2a₀ + 2b₀, c = 2c₀) and comprises a new atomic arrangement with both vacancy on 4(b) pyramidal site and substitution of antimony atoms (X) by platinum (B) in the B–XX–B layers (referring to the subcell structure) forming two B––1/2B1/2XX–3/4B and two X–BB–X layers per cell. The structure of CePt_2+xSb_2−y is compared with those reported before for URh_1.6As_1.9 and CeNi_1.91As_1.94.     

Characterization and hydrogenation of CeNi5−xCrx (x = 0, 1, 2) alloys

The effect of partial substitution of Ni by Cr in CeNi₅ intermetallic compound has been studied by pressure–composition isotherm measurements for different temperatures. The samples were prepared of high purity materials using the standard arc melting technique in argon atmosphere. The structure and the elemental composition of different alloys have been investigated by means of XRD, SEM and EDX techniques. The unit cell volume of the alloy was found to increase with increasing Cr content. In order to calculate the hydrogen storage capacity pressure–composition isotherm has been investigated for CeNi_5−xCr_x (x = 1, 2) alloys in the temperature and pressure ranges of 293 ≤ T ≤ 333 K and 0.5 ≤ P ≤ 35 bar, respectively. The P–C–T isotherm for different alloys clearly shows the presence of three regions ,  + β and β. The enthalpy and entropy for the systems has also been calculated using Van’t Hoff plot. The variation of enthalpy and entropy with hydrogen content has also been studied.     

Bulk and lattice thermal expansion in Ce1−xSrxO2−x (0.0≤x≤0.10)

In this communication, we report on the bulk and lattice thermal expansion studies on a number of compounds, within the homogeneity range of solid solutions, in a series with the general composition Ce_1−xSr_xO_2−x (0.0≤x≤0.10). The XRD pattern of each product was refined to determine the solid solubility of SrO into the lattice of CeO₂, and the homogeneity range. The composition with maximum solid solubility limit of SrO in CeO₂ lattice, under the slow cooled conditions, was delineated as Ce_0.91Sr_0.09O_1.91 (i.e. 9 mol.% of SrO). The bulk thermal expansion measurements from ambient to 1123 K, as investigated by a dilatometer, revealed that the _l (293 to 1123 K) values for the compositions within the homogeneity range increase from 11.58×10⁻⁶ to 12.13×10⁻⁶ K⁻¹ on increasing the Sr²⁺ content from 0 mol.% (i.e. CeO₂) to 9 mol.%, i.e. the upper solubility limit of SrO into the lattice of CeO₂. A similar trend was observed in the lattice thermal expansion coefficients _a (293 to 1473 K) as obtained by a high temperature-XRD.     

Effect of partial substitution of Co with Fe on the properties of LaNi3.55Mn0.4Al0.3Co0.75−xFex (x=0, 0.15, 0.55) alloys electrodes

The effect of iron substitution on the electrochemical behaviour of LaNi_3.55Mn_0.4Al_0.3Co_0.75−xFe_x compounds (x=0, 0.15, 0.55) has been studied by chronopotentiometry and cyclic voltammetry techniques. The maximum capacity decreases linearly from 308 to 239 mAhg⁻¹ when the iron content increases from 0 to 7.3 wt.% (x=0.55). This decrease can be explained by the corrosion of the alloy in the aqueous KOH electrolyte. In spite of this decrease and of the long time needed for the activation, a good stability of discharge capacity was observed in LaNi_3.55Mn_0.4Al_0.3Co_0.75−xFe_x compounds. The reversibility of the electrochemical redox reaction of LaNi_3.55Mn_0.4Al_0.3Co_0.75−xFe_x alloy electrodes has been observed in the alloys least rich in iron. The hydrogen diffusivity in LaNi_3.55Mn_0.4Al_0.3Co_0.75−xFe_x alloy electrodes decreases when increasing the iron content. The obtained values of the hydrogen diffusion coefficient D_H, varies between 2.1×10⁻⁷ and 8.2×10⁻⁹ cm² s⁻¹ depending on the iron content of the electrode.     

Magnetocrystalline anisotropy of Nd3(Fe1−xCox)27.7Ti1.3Ny compounds

The effect of Co substitution for Fe in Nd₃(Fe_1−xCo_x)_27.7Ti_1.3N_y (0 ≤ x ≤ 0.4) compounds on the magnetocrystalline anisotropy has been investigated. The anisotropy constants K's and the anisotropy field H_A have been deduced from the magnetization curves measured on magnetically aligned powder (4–7 μm) samples. The obtained results show that at RT the anisotropy is uniaxial and H_A (about 10 T) does not change substantially upon the substitution. At 5 K the results for K's give evidence for the presence of easy-cone-type anisotropy. The cone angle as well as the anisotropy field decrease upon the substitution from 21.6° to 11.8° and from 22.8 to 18.6 T, respectively.