铝锂合金激光填丝焊接接头组织性能研究

利用激光填丝焊接方法对5A90铝锂合金薄板焊接头的组织性能进行了研究。结果表明:激光填丝焊接头的主要组织特征为细晶层和焊缝区大范围等轴晶,与激光焊接头类似,而不同之处表现为激光填丝焊接头的显微组织相对细化,柱状晶区范围相对减小。激光填丝焊缝区硬度HV0.2(925.7MPa)略低于激光焊缝区硬度(956.5MPa),但前者硬度分布更加均匀。激光填丝焊接头的抗拉强度稍低于激光焊接头,分别达母材的79.22%和73.03%,但其断后延伸率却显著高于后者,分别达母材的38.65%和20.38%。综上所述,5A90铝锂合金激光填丝焊接头的组织性能略优于激光焊接头,若使激光填丝焊接头的综合力学性能达到使用要求,不仅需要焊后热处理强化,还需要与母材匹配性更好的焊丝。     

薄板铝合金激光填丝焊组织性能分析

实现了薄板5A06铝合金的激光填丝焊.并采用扫描电镜和能谱分析仪对比分析了激光填丝焊和非填丝焊接头的显微组织及其成分分布,对比分析了这两种接头显微硬度和拉伸性能.结果表明,薄板5A06铝合金的激光填丝焊焊缝的成分主要取决于焊丝成分,由于激光焊冷却速度快,焊缝的成分和组织均匀性均较激光焊未填丝的低.其激光填丝焊接头的抗拉强度和断后伸长率均高于激光焊的接头,可以达到与母材等强,焊缝硬度低于激光焊焊缝.     

TC4钛合金窄间隙激光填绞股焊丝焊接接头组织及性能

采用实心绞股焊丝,通过窄间隙激光填丝焊对TC4钛合金进行焊接,分析了激光填丝焊接头各区域的微观组织及形貌,并测试了焊接接头的显微硬度、室温拉伸性能及冲击性能等力学性能。结果表明,焊缝截面整体成形良好,无明显未熔合和气孔等缺陷;母材由等轴α+β相组成,热影响区晶粒比母材稍大,热影响区由针状α′马氏体+初生α相组成,焊缝由粗大的原始β柱状晶和内部网篮状α′马氏体组成;焊接接头的抗拉强度平均值达940 MPa,拉伸断裂在母材,断口韧窝较浅,主要表现为韧性断裂特征;焊缝的显微硬度平均值为375 HV,高于母材及热影响区。 创新点： 采用高熔敷效率的绞股焊丝作为填充金属,对 20 mm 厚 TC4 钛合金板进行激光填丝焊,探究了厚板钛合金焊接接头的组织与性能分布规律,为厚板钛合金焊接结构的实际应用提供基础数据支撑。     

超高强度钢35CrMnSi惯性摩擦焊接头组织与性能

对35CrMnSi超高强度钢进行了惯性摩擦焊试验研究,对热处理前后焊接接头组织、显微硬度进行分析测试,并对热处理后焊接接头进行了拉伸性能、冲击性能及拉伸断口分析。结果表明:焊后接头焊缝组织为板条马氏体与残余奥氏体,热力影响区组织为细小的马氏体、索氏体、珠光体和铁素体混合组织;热处理后焊缝组织为回火马氏体与少量铁素体;摩擦焊接头焊缝区的硬度高于热力影响区和母材,热处理后焊接接头硬度趋于一致,焊接接头抗拉强度大于1 890 MPa,断后伸长率大于7. 5%,焊缝区拉伸断口为混合断口;焊接接头冲击吸收能量大于18. 5J。     

高氮奥氏体焊丝焊接超高强钢接头组织和性能

为解决超高强钢焊接冷裂纹问题,采用强度低于母材的高氮奥氏体丝材进行GMAW工艺试验,研究在不同坡口角度下超高强钢焊接接头组织性能. 结果表明,采用该焊丝获得的接头焊缝成形良好,焊缝截面未见裂纹缺陷. 熔合线附近组织主要为针状和板条状马氏体,焊缝组织主要为奥氏体及被奥氏体基体所包围的铁素体树枝晶. 熔合线附近马氏体区硬度平均值为530 HV;焊缝区硬度平均值为275 HV. 相对于60°坡口接头,90°坡口接头熔合线附近马氏体组织硬度更高. 90°坡口接头的抗拉强度平均达到850 MPa,最高达887 MPa,而60°坡口接头抗拉强度平均仅为690 MPa.     

填充焊丝对6A02铝合金光纤激光焊接接头组织性能的影响

采用ER4043焊丝开展了1.0 mm厚6A02铝合金的光纤激光填丝焊接,对比分析了是否填丝对焊缝横截面形貌、接头组织、显微硬度分布和拉伸性能的影响.结果表明,激光填丝焊缝成形饱满,能够显著提高焊前装配的最大间隙容忍裕度.与自熔激光焊接接头相比,激光填丝焊接接头熔合区附近的柱状晶组织和焊缝中心的混合组织（柱状晶+等轴晶）均相对粗化,接头软化现象更加明显,焊态时接头抗拉强度基本相当,仅达到母材水平的83.2%,但经历固溶时效热处理后,接头强度得以恢复,并高于母材水平,断后伸长率获得显著改善,可以达到21.29%,远高于前者的8.13%.     

不同焊丝对7075铝合金双脉冲MIG焊缝组织与性能的影响

用ER5556和ER5356焊丝对AA7075-T651铝合金板材双脉冲MIG焊缝组织与性能进行研究。结果表明:两种焊丝接头焊缝区均为铸态枝晶组织,与ER5556相比ER5356焊丝焊接接头热影响区的晶界有更多第二相析出;ER5556焊丝焊接接头最低硬度为90.6 HV,接头抗拉强度为342.5 MPa,伸长率为8.5%;ER5356焊丝焊接接头最低硬度为80.8 HV,接头抗拉强度为292.5 MPa,伸长率为3.5%;ER5556焊丝接头拉伸断口上有明显的撕裂棱。     

异种钢激光焊接接头热成型后的组织与性能

采用激光填丝的方法对带有Al Si镀层的22MnB5和6Mn6异种热成型钢进行了拼焊,并对焊缝进行了焊后热成型实验。通过金相显微镜、维氏硬度计和拉伸试验机对热成型前后焊缝截面的宏观形貌、显微组织、硬度和拉伸性能进行了观察和测试。结果显示,在本文所提供的焊接参数条件下,可以获得焊缝成形良好的接头,且在拉伸测试中均断裂于6Mn6母材一侧(热成型后)。焊缝组织在热成型前后均以粗大的板条马氏体为主。Al Si镀层在焊接过程中被卷入焊缝形成带状和块状的富铝相,并在热成型后形成条块状分布的δ铁素体,但未导致接头在拉伸测试中断于焊缝。焊后母材硬度均低于200 HV,焊缝则在500 HV左右;热成型后焊缝硬度下降至370 HV左右,22MnB5母材上升至500 HV左右,6Mn6母材则在250 HV左右。     

高碳钢片对铝硅镀层热成形钢激光焊接接头组织性能的影响

以45号碳钢薄片为夹层,利用CWX3000光纤激光器对1.5 mm厚的铝硅镀层热成形钢进行激光焊接试验,研究焊缝碳含量对焊接接头显微组织和力学性能的影响. 试验结果表明,碳钢薄片的加入使焊缝碳含量增加,奥氏体相区扩大,焊缝δ铁素体的体积分数由17.3%降低至4.5%,焊缝平均硬度由425 HV增加至557 HV,焊接接头的抗拉强度由980 MPa增加至1 280 MPa,杯突值由1.7 mm增加至3.2 mm,抗拉强度及成形性能均有所提升.     

薄板2524铝合金激光填丝焊接工艺及组织性能

2524铝合金是具有优异损伤容限的新型航空高强Al-Cu-Mg合金.采用高功率光纤激光器焊接1.6 mm厚2524铝合金,研究了填充5087焊丝情况下,激光功率、焊接速度和填丝速度对焊缝成形、热裂纹倾向和焊缝显微组织的影响,优化焊接工艺参数,考察接头静态拉伸性能.结果表明,采用填充材料后,焊缝柱状枝晶生长方向性明显减小、晶粒细化、晶界共晶增多、热裂纹倾向降低.当激光功率为2.5 kW,焊接速度为2 m/min,填丝速度为2 m/min时,可获得成形良好、无缺陷的焊缝,接头抗拉强度达到313~324 MPa,拉伸断裂于接头熔合线附近,断口处有大量韧窝,呈韧性断裂特征.     

Cr对G520不锈钢焊缝组织及力学性能的影响

采用Cr含量分别为10%,18%,26%,34%(质量分数)的金属型药芯焊丝焊接G520沉淀硬化不锈钢,研究了药芯焊丝中Cr含量对G520沉淀硬化不锈钢焊接接头组织以及力学性能的影响. 结果表明,4组焊接接头焊缝区组织均为奥氏体和δ铁素体,随药芯焊丝中Cr含量的增加,δ铁素体由点块状转变为网状和条状. 固溶于基体组织中的Cr含量、δ铁素体及Cr₂₃C₆的含量、奥氏体晶粒平均尺寸的综合作用影响着焊接接头拉伸性能及室温冲击韧性. 焊丝中Cr含量为26%时,G520沉淀硬化不锈钢焊接接头的抗拉强度为969 MPa,断后伸长率为20.8%,冲击吸收能量为60.7 J,焊接接头力学性能最优.     

Microstructure and Fatigue Properties of Laser Welded DP590 Dual-Phase Steel Joints

In this paper, cold-rolled DP590 dual-phase steel sheets with 1.5 mm thickness were butt-welded by a fiber laser, and the evolution and effect on microhardness, tensile property and fatigue property of the welded joint microstructure were studied. The results showed that the base metal is composed of ferrite and martensite, with the martensite dispersed in the ferrite matrix in an island manner. The microstructure of the weld zone was lath-shaped martensite that can be refined further by increasing the welding speed, while the heat-affected zone was composed of ferrite and tempered martensite. The microhardness increased with increasing welding speed, and the hardness reached its highest value—393.8 HV—when the welding speed was 5 m/min. Static tensile fracture of the welded joints always occurred in the base metal, and the elongation at break was more than 16%. The conditional fatigue limits of the base metal and the weld joints were 354.2 and 233.6 MPa, respectively, under tension–tension fatigue tests with a stress rate of 0.1. After observation of the fatigue fracture morphology, it was evident that the fatigue crack of the base metal had sprouted into the surface pits and that its expansion would be accelerated under the action of a secondary crack. The fatigue source of the welded joint was generated in the weld zone and expanded along the martensite, forming a large number of fatigue striations. Transient breaking, which occurred in the heat-affected zone of the joint as a result of the formation of a large number of dimples, reflected the obvious characteristics of ductile fracture.     

Comparison of two types of low-transformation-temperature weld metals based on solidification mode

Two types of low-transformation-temperature weld metals were devised, one associated with primary austenite solidification, the other primary ferrite solidification. The martensite start temperature of both low-transformation-temperature weld metals was about 125°C. Experimental results showed that low-transformation-temperature weld microstructure associated with primary austenite solidification was martensite with 8.0% retained austenite, whereas that one related to primary ferrite solidification primarily consisted of martensite and δ-ferrite. Accordingly, both welded joints had little distinction between distortion and residual stress, indicating that weld metal associated with primary ferrite solidification played the same function as primary austenite solidification on residual stress reduction. Moreover, the low-transformation-temperature weld metal associated with primary ferrite solidification had higher tensile strength and hardness than that based on primary austenite solidification.     

中低温热处理对SUS304不锈钢TIG焊接接头组织及力学性能的影响

轨道交通车辆在冲击振动试验后,部分设备SUS304不锈钢焊接件出现断裂失效现象.为了提升SUS304不锈钢焊后机械性能,采用金相显微镜、扫描电镜、硬度测试及拉伸试验等方法,研究了中低温热处理工艺对2 mm厚SUS304不锈钢板TIG焊接接头的组织及力学性能的影响.研究发现,经400℃热处理30 min及焊接后未处理态焊...     

焊后热处理对Al-Zn-Mg-Cu合金MIG焊接接头组织与性能的影响

采用ER5356焊丝对Al-4.6Zn-1.5Mg-0.15Cu合金板材进行熔化极钨极氩弧焊试验,并对焊接接头进行了不同的焊后热处理。借助光学显微镜(OM)、扫描电镜(SEM)研究不同焊后热处理试样的组织变化规律,并进行了显微硬度测试与拉伸试验。结果表明:经固溶加时效处理后,焊接接头抗拉强度与显微硬度得到明显提升,抗拉强度与焊缝硬度均值分别提高至304 MPa与85 HV,相比焊后未处理的263 MPa与66 HV,增幅分别达15.6%与28.8%。焊接接头经时效处理后,组织的不均匀性及强化相的分布得到改善;而经重新固溶后,第二相发生回溶,再经时效处理将使得一部分不稳定的过饱和固溶体重新析出且弥散分布。     

10Ni3CrMoV钢CO2激光多层焊的接头组织与性能

与传统电弧焊相比,激光焊接厚板优势明显。采用纯激光焊和激光电弧复合焊等多道焊接技术实现了28 mm厚10Ni3CrMoV钢的高效焊接,采用光学显微镜分析焊缝、热影响区和焊缝重叠区的组织,激光复合焊缝组织主要为针状铁素体,纯激光焊缝、粗晶区和细晶区组织主要为板条马氏体,激光复合焊缝重叠区组织为粒状贝氏体+马氏体,纯激光焊缝和激光复合焊缝重叠区组织为马氏体+少量粒状贝氏体。测试了焊接接头的力学性能,结果表明,激光复合焊缝金属的冲击韧性较高,焊接接头的抗拉强度和屈服强度与母材相当,延伸率略小于母材,焊接接头的最大硬度小于360 HV,弯曲性能合格。     

振动条件下硬铝合金TIG焊接的工艺优化

采用Al-Si系焊丝对Al-Cu-Mg硬铝合金进行半自动TIG焊，焊接过程中施加机械振动.采用正交试验方法对工艺参数进行优化，并对不同工艺参数下硬铝合金的焊接接头进行拉伸性能、硬度、显微组织和物相分析，分析振动参数和焊接参数对焊接接头组织性能的影响规律和作用机理.结果表明，最佳工艺匹配参数为:焊接电流I=110 A、振动幅度D=0.05 mm、振动频率f=50 Hz，此时接头的性能为:抗拉强度R_m=289.68 MPa，断后伸长率A=4.95%，焊缝平均硬度H为108.0 HV；合适参数的振动可以细化焊缝区显微组织、抑制孔状缺陷，并使焊缝显微组织为细小的等轴树枝晶和胞状树枝晶为主，进而提高焊接接头综合力学性能.     

ULCB钢电子束穿透焊组织与性能

为了进一步探索ULCB钢的焊接性能,采用真空电子束穿透焊不同束流强度对14 mm钢板对接接头进行了焊接,通过焊缝形貌比较,束流强度为100 mA时,接头焊缝成形最好,选取该接头做了拉伸、硬度、冲击试验及金相组织分析.结果表明,拉伸试样的断裂区域在母材区,抗拉强度为761 MPa、屈服强度为669 MPa,硬度范围在270~330 HV;冲击试样的断裂区域在热影响区,焊缝区平均冲击功为288 J,热影响区平均冲击功为273 J;接头显微组织中,焊缝区和热影响区产生了α'马氏体相,使焊缝区和热影响区产生相变强化,导致焊接接头的强度和硬度均高于母材.     

中厚板钛合金激光-CMT复合焊接工艺特性分析

通过采用激光-CMT焊接的方法对10 mm厚TC4钛合金实现了不开坡口单面焊双面成形,并对焊缝的组织、力学性能及腐蚀性能进行了测试分析. 结果表明,该最优参数下形成的焊接接头中主要由大量的α'马氏体及初生的α相构成,且存在网篮状组织,焊缝区域的显微硬度大于母材区域,可达380 HV,且由于激光作用区拥有更大的冷却速度,焊缝底部生成了更多的α'马氏体,导致焊缝底部硬度比电弧作用区更高. 焊接接头抗拉强度可达到916 MPa,断后伸长率达到16.08%,拉伸断裂结果为韧性断裂,焊缝组织的性能明显优于母材.焊缝处的抗腐蚀性能优于母材,这是因为焊缝组织有更细小的晶粒及大量位错,提升了钝化能力并阻碍了Cl?的扩散.