Tensile and thermomechanical properties of short carbon fiber reinforced polyamide 6 composites

In this study, carbon fiber (CF) reinforced polyamide 6 (PA6) composites were prepared by using melt mixing method. Effects of fiber length and content, on the mechanical, thermal and morphological properties of CF reinforced PA6 composites were investigated. Fiber length distributions of composites were also determined by using an image analyzing program. It was seen that the maximum number of fibers were observed in the range of 0–50 μm. Mechanical test results showed that, increasing CF content increased the tensile strength, modulus and hardness values but decreased strain at break values of composites. DSC results showed that T_g and T_m values of composites were not changed significantly with increasing CF content and length. However, heat of fusion and the relative degree of crystallinity values of composites decreased with ascending CF content. DMA results revealed that storage modulus and loss modulus values of composites increased with increasing CF content.     

Soybean oil-based thermosets with N-vinyl-2-pyrrolidone as crosslinking agent for hemp fiber composites

Soybean oil-based thermosets from acrylated epoxidized soybean oil (AESO) with a highly reactive vinyl monomer, N-vinyl-2-pyrrolidone (NVP), as crosslinking agent to replace styrene (St) were formulated for the fabrication of hemp fiber composites. The theoretical miscibility of NVP–AESO and St–AESO systems were discussed based on the group contribution method. The AESO resin with 30 wt% NVP exhibited a slightly higher viscosity than the counterpart with St, while the maximum curing temperature of the former was considerably lower than that of the latter. The composites from 20 wt% NVP resin gained comparable mechanical properties and higher glass transition temperature (T_g) to the composites with 30 wt% St. Further increase in NVP usage to 40 wt% resulted in the composites with higher tensile strength, tensile modulus, flexural strength, flexural modulus, storage modulus, and T_g of 29.6%, 22.4%, 22.5%, 20.6%, 21.6%, and 47.2%, respectively, when compared to those of the St-based composites.     

Flammability and tensile properties of polylactide nanocomposites with short carbon fibers

Nanocomposites of polylactide (PLA) with aluminum hydroxide (ATH), short carbon fibers (CF), and montmorillonite (MMT) were prepared via direct melt blending. The exfoliated and intercalated clay structures with some aggregations in the PLA matrix were observed. The tensile strength and elongation at break of the PLA composite caused by the high content of the retardant ATH were improved by adding modified MMT and CF to replace a portion of ATH in the PLA matrix. The thermal degradation temperatures and char residue of the PLA/ATH/MMT/CF nanocomposites as determined by thermogravimetric analysis were higher than without MMT. Furthermore, a novel method was proposed to analyze the flammability of composite using an infrared camera, which could capture the apparent thermal image of the sample during UL 94 V test. It was found that, with addition of the MMT and short CF, a more effective insulation layer could be formed on the ablating surface of the PLA/ATH composite, and the high thermal conductivity of the CF might increase the release rate of heat from the surface composite during burn, thus the PLA/ATH/MMT nanocomposite containing short carbon fibers having a V-0 rating without flaming dripping could be obtained.     

Effects of grafted chain length on mechanical and electrical properties of nanocomposites containing polylactide-grafted carbon nanotubes

We herein report the effects of interfacial reinforcement on mechanical and electrical properties of nanocomposites based on polylactide (PLA) and multi-walled carbon nanotube (MWCNT). For this purpose, a series of MWCNTs grafted with PLA chains of various lengths (MWCNT-g-PLAs) were prepared by ring-opening polymerization of l-lactide with carboxylic acid-functionalized MWCNT (MWCNT-COOH). MWCNT-g-PLAs were then mixed with commercial PLA to obtain PLA/MWCNT-g-PLA nanocomposites with 1.0 wt.% MWCNT content. It was revealed that morphological, mechanical, and electrical properties of PLA/MWCNT-g-PLA nanocomposites were strongly dependent on the PLA chain length of MWCNT-g-PLAs. FE-SEM images exhibited that the nanocomposites containing MWCNT-g-PLA with longer PLA chain length exhibited better dispersion of MWCNTs in the PLA matrix. Initial moduli and tensile strengths of PLA/MWCNT-g-PLA composites increased with the increment of chain length of PLA grafted on MWCNTs, which attributes to the improved interfacial adhesion between the grafted PLA chains of MWCNT-g-PLA and the PLA matrix. As a result, the experimental initial modulus (2775 ± 193 MPa) of the nanocomposite including MWCNT-g-PLA with PLA chains of average molecular weight of 530 g/mol was quite close to the theoretical value (2911 MPa) predicted for the nanocomposite with perfect interfacial adhesion. Unexpectedly, electrical resistivities of PLA/MWCNT-g-PLA nanocomposites were found to increase from ∼10⁴ to ∼10¹² Ω/sq with increasing the PLA chain length of MWCNT-g-PLA, which is due to the fact that the PLA chains grafted on MWCNTs prevent the formation of the electrical conduction path of MWCNTs in the PLA matrix.     

Hybrid effect of nanoparticles with carbon fibers on the mechanical and wear properties of polymer composites

Polyetheretherketone (PEEK) composites reinforced with carbon fibers (CFs) and nano-ZrO₂ particles were prepared by incorporating nanoparticles into PEEK/CF composites via twin-screw extrusion. The effects of nanoparticles on the mechanical and wear properties of the PEEK/CF composites were studied. The results showed that the incorporation of nano-ZrO₂ particles with carbon fiber could effectively enhance the tensile properties of the composites. The tensile strength and Young’s modulus of the composites increased with the increasing nano-ZrO₂ content. The enhancement effect of the particle was more significant in the hybrid reinforced composites. The compounding of the two fillers also remarkably improved the wear resistance of the composites under water condition especially under high pressures. It was revealed that the excellent wear resistance of the PEEK/CF/ZrO₂ composites was due to a synergy effect between the nano-ZrO₂ particles and CF. CF carried the majority of load during sliding process and prevented severe wear to the matrix. The incorporation of nano-ZrO₂ effectively inhibited the CF failures through reducing the stress concentration on the carbon fibers interface and the shear stress between two sliding surfaces. It was also indicated that the wear rates of the hybrid composites decreased with the increasing applied load and sliding distance under water lubrication. And low friction coefficient and low wear rate could be achieved at high sliding velocity.     

Morphology,thermal and mechanical properties of PVC/MMT nanocomposites prepared by solution blending and solution blending + melt compounding

Two types of montmorillonite (MMT), natural sodium montmorillonite (Na-MMT) and organically modified montmorillonite (OMMT), in different amounts of 1, 2, 5, 10 and 25 phr (parts per hundred resin), were dispersed in rigid poly (vinyl chloride) by two different methods: solution blending and solution blending + melt compounding. The effects on morphology, thermal and mechanical properties of the PVC/MMT nanocomposites were studied by varying the amount of Na-MMT and OMMT in both methods. SEM and XRD analysis revealed that possible intercalated and exfoliated structures were obtained in all of the PVC/MMT nanocomposites. Thermogravimetric analysis revealed that PVC/Na-MMT nanocomposites have better thermal stability than PVC/OMMT nanocomposites and PVC. In general, PVC/MMT nanocomposites prepared by solution blending + melt compounding revealed improved thermal properties compared to PVC/MMT nanocomposites prepared by solution blending. Vicat tests revealed a significant decrease in Vicat softening temperature of PVC/MMT nanocomposites prepared by solution blending + melt compounding compared to unfilled PVC.     

Enhanced conductivity behavior of polydimethylsiloxane (PDMS) hybrid composites containing exfoliated graphite nanoplatelets and carbon nanotubes

Polydimethylsiloxane (PDMS) hybrid composites consisting of exfoliated graphite nanoplatelets (xGnPs) and multiwalled carbon nanotubes functionalized with hydroxyl groups (MWCNTs-OH) were fabricated, and the effects of the xGnP/MWCNT-OH ratio on the thermal, electrical, and mechanical properties of polydimethylsiloxane (PDMS) hybrid composites were investigated. With the total filler content fixed at 4 wt%, a hybrid composite consisting of 75% × GnP/25% MWCNT-OH showed the highest thermal conductivity (0.392 W/m K) and electrical conductivity (1.24 × 10⁻³ S/m), which significantly exceeded the values shown by either of the respective single filler composites. The increased thermal and electrical conductivity found when both fillers are used in combination is attributed to the synergistic effect between the fillers that forms an interconnected hybrid network. In contrast, the various different combinations of the fillers only showed a modest effect on the mechanical behavior, thermal stability, and thermal expansion of the PDMS composite.     

Mechanical and thermal properties of chicken feather fiber/PLA green composites

Chicken feather fiber (CFF)/reinforced poly(lactic acid) (PLA) composites were processed using a twin-screw extruder and an injection molder. The tensile moduli of CFF/PLA composites with different CFF content (2, 5, 8 and 10 wt%) were found to be higher than that of pure PLA, and a maximum value of 4.2 GPa (16%↑) was attained with 5 wt% of CFF without causing any substantial weight increment. The morphology, evaluated by scanning electron microscopy (SEM), indicated that an uniform dispersion of CFF in the PLA matrix existed. The mechanical and thermal properties of pure PLA and CFF/PLA composites were compared using dynamic mechanical analysis (DMA), thermomechanical analysis (TMA) and thermogravimetric analysis (TGA). DMA results revealed that the storage modulus of the composites increased with respect to the pure polymer, whereas the mechanical loss factor (tan δ) decreased. The results of TGA experiments indicated that the addition of CFF enhanced the thermal stability of the composites as compared to pure PLA. The outcome obtained from this study is believed to assist the development of environmentally-friendly composites from biodegradable polymers, especially for converting agricultural waste – chicken feather into useful products.     

Effects of poly(oxyethylene)-block structure in polyetheramines on the modified carbon nanotube/poly(lactic acid) composites

The hybrids of multi-walled carbon nanotube and poly(lactic acid) (MWCNT/PLA) were prepared by a melt-blending method. In order to enhance the compatibility between the PLA and MWCNTs, the surface of the MWCNTs was covalently modified by Jeffamine® polyetheramines by functionalizing MWCNTs with carboxylic groups. Different molecular weights and hydrophilicity of the polyethermaines were grafted onto MWCNTs with the assistance of a dehydrating agent. The results showed that low-molecular-weight Jeffamine® polyetheramine modified MWCNTs can effectively improve the thermal properties of PLA composites. On the other hand, high-molecular-weight and poly(oxyethylene)-segmented polyetheramine could render the modified MWCNTs of well dispersion in PLA, and consequently affecting the improvements of mechanical properties and conductivity of composite materials. With the addition of 3.0 wt% MWCNTs, the increment of E′ of the composite at 40 °C was 79%. For conductivity, the surface resistivity decreased from 1.27 × 10¹² Ω/sq for neat PLA to 8.30 × 10⁻³ Ω/sq for the composites.     

Enhanced mechanical,thermal and flame retardant properties by combining graphene nanosheets and metal hydroxide nanorods for Acrylonitrile–Butadiene–Styrene copolymer composite

Three metal hydroxide nanorods (MHR) with uniform diameters were synthesized, and then combined with graphene nanosheets (GNS) to prepare acrylonitrile–butadiene–styrene (ABS) copolymer composites. An excellent dispersion of exfoliated two-dimensional (2-D) GNS and 1-D MHR in the ABS matrix was achieved. The effects of combined GNS and MHR on the mechanical, thermal and flame retardant properties of the ABS composites were investigated. With the addition of 2 wt% GNS and 4 wt% Co(OH)₂, the tensile strength, bending strength and storage modulus of the ABS composites were increased by 45.1%, 40.5% and 42.3% respectively. The ABS/GNS/Co(OH)₂ ternary composite shows the lowest maximum weight loss rate and highest residue yield. Noticeable reduction in the flammability was achieved with the addition of GNS and Co(OH)₂, due to the formation of more continuous and compact charred layers that retarded the mass and heat transfer between the flame and the polymer matrix.     

Multiscale fiber reinforced composites based on a carbon nanofiber/epoxy nanophased polymer matrix: Synthesis, mechanical, and thermomechanical behavior

Vacuum assisted resin infusion molding (VARIM) was used to produce multiscale fiber reinforced composites (M-FRCs) based on carbon nanofibers dispersed in an epoxy resin. Flexural, interlaminar shear strength (ILSS) and thermomechanical tests are presented for the 0.1 wt% and 1 wt% M-FRCs and compared with the neat fiber reinforced composites (FRCs). Flexural strength and modulus increased (16–20%) and (23–26%), respectively for the 0.1 wt% and 1 wt% M-FRCs when compared to the neat FRCs. ILSS properties increased (6% and 25%) for the 0.1 wt% and 1 wt% M-FRCs, respectively when compared to neat FRCs. The glass transition temperatures (T_g) of both M-FRC samples were 25 °C higher than the neat FRC. Coefficients of thermal expansion (CTE) of the M-FRC samples improved compared to the neat FRC. The improved T_g and CTE properties in the M-FRC samples are attributed to synergistic interactions between the CNF/PNC matrix and glass fibers.     

Effect of cellulose nano fiber (CNF) on fatigue performance of carbon fiber fabric composites

The effect of cellulose nano fibers (CNF): micro-fibrillated cellulose and bacteria cellulose fibers were investigated on the fatigue life of carbon fiber (CF) fabric/epoxy (EP) composites. Epoxy used as the matrix was physically modified with CNF in advance before fabricating the laminates. The high cycle fatigue strength was significantly improved at 0.3 wt% CNF. There exists an appropriate CNF content which makes the fatigue life longest. An increase of adhesive strength between CF and matrix results due to physical modification with CNF. The adhesive strength much increases with increasing the CNF content. Almost no interfacial debonding occurs at 0.8 wt% CNF content when CF breakage takes place. On the other hand, some debonding occurs along CFs from the breaking point at 0.3 wt% CNF. Debonding is more significant in the case of no CNF addition to the matrix. An appropriate interfacial strength brought at 0.3 wt% CNF is the key of fatigue life extension.     

Manufacture and characterisation of thermoplastic composites made from PLA/hemp co-wrapped hybrid yarn prepregs

PLA/hemp co-wrapped hybrid yarns were produced by wrapping PLA filaments around a core composed of a 400 twists/m and 25 tex hemp yarn (Cannabis sativa L) and 18 tex PLA filaments. The hemp content varied between 10 and 45 mass%, and the PLA wrapping density around the core was 150 and 250 turns/m. Composites were fabricated by compression moulding of 0/90 bidirectional prepregs, and characterised regarding porosity, mechanical strength and thermal properties by dynamic mechanical thermal analysis (DMTA) and differential scanning calorimetry (DSC). Mechanical tests showed that the tensile and flexural strengths of the composites markedly increased with the fibre content, reaching 59.3 and 124.2 MPa when reinforced with 45 mass% fibre, which is approximately 2 and 3.3 times higher compared to neat PLA. Impact strength of the composites decreased initially up to 10 mass% fibre; while higher fibre loading (up to 45 mass%) caused an increase in impact strength up to 26.3 kJ/m², an improvement of about 2 times higher compared to neat PLA. The composites made from the hybrid yarn with a wrapping density of 250 turns/m showed improvements in mechanical properties, due to the lower porosity. The fractured surfaces were investigated by scanning electron microscopy to study the fibre/matrix interface.     

Enhanced thermal conductivity and retained electrical insulation for polyimide composites with SiC nanowires grown on graphene hybrid fillers

Polyimide (PI) composites containing one-dimensional SiC nanowires grown on two-dimensional graphene sheets (1D–2D SiC_NWs-GSs) hybrid fillers were successfully prepared. The PI/SiC_NWs-GSs composites synchronously exhibited high thermal conductivity and retained electrical insulation. Moreover, the heat conducting properties of PI/SiC_NWs-GSs films present well reproducibility within the temperature range from 25 to 175 °C. The maximum value of thermal conductivity of PI composite is 0.577 W/mK with 7 wt% fillers loading, increased by 138% in comparison with that of the neat PI. The 1D SiC nanowires grown on the GSs surface prevent the GSs contacting with each other in the PI matrix to retain electrical insulation of PI composites. In addition, the storage modulus and Young’s modulus of PI composites are remarkably improved in comparison with that of the neat PI.     

Properties of poly(lactic acid)/montmorillonite/carbon nanotubes nanocomposites: determination of percolation threshold

Incorporation of rigid nanoparticles is the most effective means of improving polymer properties. Montmorillonite (MMT) and multi-walled carbon nanotubes (MWCNTs) are legendary in this field for their individual exceptional properties. A synergistic phenomenon is induced between these two particles when they are simultaneously incorporated into polymers. At a definite nanofillers concentration, called the percolation threshold, there is a sudden change in nanocomposite properties due to the formation of a 3D-structured network of the nanoparticles within the matrix. In this work, the properties of poly(lactic acid) (PLA) nanocomposites filled with different fractions of MMT/MWCNTs hybrid (0.5–2.0 wt%) were analyzed. In particular, the percolation threshold of the MMT/MWCNTs hybrid was uniquely identified by differential scanning calorimetry, thermogravimetric analysis and dynamic mechanical thermal analysis. The structural studies by X-ray diffraction and Fourier-transform infrared spectroscopy were also associated with the percolation threshold of MMT/MWCNTs in PLA. At 1.0 wt% MMT/MWCNTs concentration, the complete exfoliation of the particles was maintained, and the thermal characteristics such as glass transition, crystallization and melting temperatures reached their plateau at this hybrid concentration. Moreover, the thermal degradation and viscoelastic parameters showed their peak values at this critical point, which is correlated with the formation of the percolation threshold within the matrix. The morphological studies confirmed the homogeneous dispersion of MMT/MWCNTs in PLA up to a concentration of 1.0 wt%. At 2.0 wt% MMT/MWCNTs, few aggregations occurred in the PLA-based composite, confirming that the percolation threshold was formed at a lower concentration of MMT/MWCNTs nanoparticles.

     

The effect of alkaline and silane treatments on mechanical properties and breakage of sisal fibers and poly(lactic acid)/sisal fiber composites

The main goals of this work were to study the effect of different chemical treatments on sisal fiber bundles tensile properties as well as on tensile properties of composites based on poly(lactic acid) (PLA) matrix and sisal fibers. For this purpose, sisal fibers were treated with different chemical treatments. After treating sisal fibers the tensile strength values decreased respect to untreated fiber ones, especially when the combination of NaOH + silane treatment was used. Taking into account fiber tensile properties and fiber/PLA adhesion values, composites based on silane treated fibers would show the highest tensile strength value. However, composites based on alkali treated and NaOH + silane treated fibers showed the highest tensile strength values. Finally, experimental tensile strength values of composites were compared with those values obtained using micromechanical models.     

Effect of the SiO2/TiO2 ratio on the solid acidity of SiO2-TiO2/montmorillonite composites

SiO₂-TiO₂/montmorillonite composites with varying SiO₂/TiO₂ molar ratios were synthesized and the effect of the SiO₂/TiO₂ ratio on the solid acidity of the resulting composites was investigated. Four composites with SiO₂/TiO₂ molar ratios of 0, 0.1, 1 and 10 were synthesized by the reaction of colloidal SiO₂-TiO₂ particles prepared from alkoxides with sodium-montmorillonite at room temperature. The composites showed slight expansion and broadening of the XRD basal reflection, corresponding to the intercalation of fine colloidal SiO₂-TiO₂ particles into the montmorillonite sheets and incomplete intercalation to form disordered stacking of exfoliated montmorillonite and colloidal SiO₂-TiO₂ particles. The colloidal particles crystallized to anatase in the low SiO₂/TiO₂ composites but remained amorphous in the high SiO₂/TiO₂ composites. The specific surface areas (S_BET) of the composites measured by N₂ adsorption ranged from 250 to 370 m²/g, considerably greater than in montmorillonite (6 m²/g). The pore size increased with decreasing SiO₂/TiO₂ molar ratio of the composites. The NH₃-TPD spectra of the composites consisted of overlapping peaks, corresponded to temperatures of about 190 and 290 °C. The amounts of solid acid obtained from NH₃-TPD were 186-338 μmol/g in the composites; these values are higher than in the commercial catalyst K10 (85 μmol/g), which is synthesized by acid-treatment of montmorillonite. The present sample with SiO₂/TiO₂ = 0.1 showed the highest amount of acid, about four times higher than K10.     

The effect of silane treated- and untreated-talc on the mechanical and physico-mechanical properties of poly(lactic acid)/newspaper fibers/talc hybrid composites

This paper evaluates the effect of the addition of silane treated- and untreated- talc as the fillers on the mechanical and physico-mechanical properties of poly(lactic acid) (PLA)/recycled newspaper cellulose fibers (RNCF)/talc hybrid composites. For this purpose, 10 wt% of a talc with and without silane treatment were incorporated into PLA/RNCF (60 wt%/30 wt%) composites that were processed by a micro-compounding and molding system. PLA is utilized is a bio-based polymer that made from dextrose, a derivative of corn. Talc is also a natural product. The RNCF and talc hybrid reinforcements of PLA polymer matrix were targeted to design and engineer bio-based composites of balanced properties with added advantages of cost benefits besides the eco-friendliness of all the components in the composites. In this work, the flexural and impact properties of PLA/RNCF composites improved significantly with the addition of 10 wt% talc. The flexural and impact strength of these hybrid composites were found to be significantly higher than that made from either PLA/RNCF. The hybrid composites showed improved properties such as flexural strength of 132 MPa and flexural modulus of 15.3 GPa, while the unhybridized PLA/RNCF based composites exhibited flexural strength and modulus values of 77 MPa and 6.7 GPa, respectively. The DMA storage modulus and the loss modulus of the PLA/RNCF hybrid composites were found to increase, whereas the mechanical loss factor (tan delta) was found to decrease. The storage modulus increased with the addition of talc, because the talc generated a stiffer interface in the polymer matrix. Differential scanning calorimetry (DSC) thermograms of neat PLA and of the hybrid composites showed nearly the similar glass transition temperatures and melting temperatures. Scanning electron microscopy (SEM) micrographs of the fracture surface of Notched Izod impact specimen of 10 wt% talc filled PLA/RNCF composite showed well filler particle dispersion in the matrix and no large aggregates are present. The comparison data of mechanical properties among samples filled with silane-treated- and untreated- talc fillers showed that the hybrid composites filled with silane treated talc displayed the better mechanical prosperities relative to the other hybrid composites. Talc-filled RNCF-reinforced polypropylene (PP) hybrid composites were also made in the same way that of PLA hybrid composites for a comparison. The PLA hybrid bio-based composites showed much improvement in mechanical properties as compared to PP-based hybrid counterparts. This suggests that these PLA hybrid bio-based composites have a potential to replace glass fibers in many applications that do not require very high load bearing capabilities and these recycled newspaper cellulose fibers could be a good candidate reinforcement fiber of high performance hybrid biocomposites.     

Multi-step microwave reduction of graphite oxide and its use in the formation of electrically conductive graphene/epoxy composites

The multi-step MW reduction technique was developed in this study to obtain reduced graphene oxides; EG, RGO-1, and RGO-2 with MW irradiation time of 1, 2, and 3 min, respectively. Results of TGA, IR, and elemental analysis demonstrated that the degree of reduction of GO increased with increasing the MW irradiation time. Overall, 3 min of MW irradiation of GO in 3 steps was sufficient to obtain highly reduced GO (C/O ratio 10.38 by elemental analysis). The electrical percolation threshold of composites was observed as 1 wt% and 0.3 wt% for RGO-1 and RGO-2, respectively. Even at 0.5 wt% loading of RGO-2 in epoxy, the T_g value of the composite increased by 10 °C, indicating a strong interfacial interaction between graphene and epoxy resin.     

Magnetically-sensitive shape memory polyurethane composites crosslinked with multi-walled carbon nanotubes

Magnetically-sensitive polyurethane composites, which were crosslinked with multi-walled carbon nanotubes (MWCNTs) and were filled with Fe₃O₄ nanoparticles, were synthesized via in situ polymerization method. MWCNTs pretreated with nitric acid were used as crosslinking agents. Because of the crosslinking of MWCNTs with polyurethane prepolymer, the properties of the composites with a high content of Fe₃O₄ nanoparticles, especially the mechanical properties, were significantly improved. The composites showed excellent shape memory properties in both 45 °C hot water and an alternating magnetic field (f = 45 kHz, H = 29.7 kA m⁻¹). The shape recovery time was less than one minute and the shape recovery rate was over 95% in the alternating magnetic field.