Interface temperature measurement of M2C and M6C eutectic carbides in the Fe–Mo–C system

The High speed cast iron, which is used for hot rolling parts, needs high fracture toughness and wear resistance. To improve these properties, the control of eutectic carbides, M₃C, M₇C₃,M₆C and MC is important by adding elements such as Cr, W, V and Mo.

The aim of this study is to estimate which carbide will solidify under certain solidification conditions and compositions. This prediction criterion can be gained by measuring the interface temperature of each carbide in various samples with different solute elements, composition and growth rate.

In this report, the solidified temperature of γ + M₂C and γ + M₆C eutectic carbide in the Fe–Mo–C ternary system in the composition range near to the eutectic monovariant line, was measured during the unidirectional solidiication process. The relationship between solidified interface temperature and growth rate was obtained. In eutectic solidification along the γ + M₆C monovariant line, a coefficient of undercooling, the k value, was obtained.

The authors have already measured the k values of other eutectic carbides, such as γ + M₃C, austenite + M₇C₃, and γ + VC in Fe–Cr–C and Fe–V–C system. The paper also discusses the relationships between these properties of eutectic carbides.     

Interface temperature measurement of M2C and M6C eutectic carbides in the Fe–Mo–C system

The High speed cast iron, which is used for hot rolling parts, needs high fracture toughness and wear resistance. To improve these properties, the control of eutectic carbides, M₃C, M₇C₃, M₆C and MC is important by adding elements such as Cr, W, V and Mo.The aim of this study is to estimate which carbide will solidify under certain solidification conditions and compositions. This prediction criterion can be gained by measuring the interface temperature of each carbide in various samples with different solute elements, composition and growth rate.In this report, the solidified temperature of γ+M₂C and γ+M₆C eutectic carbide in the Fe–Mo–C ternary system in the composition range near to the eutectic monovariant line, was measured during the unidirectional solidification process. The relationship between solidified interface temperature and growth rate was obtained. In eutectic solidification along the γ+M₆C monovariant line, a coefficient of undercooling, the k value, was obtained.The authors have already measured the k values of other eutectic carbides, such as γ+M₃C, austenite+M₇C₃, and γ+VC in Fe–Cr–C and Fe–V–C system. The paper also discusses the relationships between these properties of eutectic carbides.     

Improvement of toughness of high chromium white cast iron: duplex ferritic-austenitic matrix

It is attempted to enhance the impact toughness of industrially used high chromium white cast iron (WCI) without sacrificing wear resistance. The microstructure is engineered by cyclic annealing to obtain features such as duplex grain matrix, where austenite envelops ferrite grain, refined M₇C₃ carbide. The newly cast and heat-treated alloy shows remarkable impact toughness i.e. 13J with improved wear resistance. The fracture micro-mechanism is studied through extensive scanning electron microscopy and it is ascertained that enhanced impact toughness results from crack arrest at duplex grain boundaries. A few other toughness enhancing features are also discussed. The results are compared with standard ASTM grade Class-III high chromium WCI and are found to be encouraging.     

烧结Cr15高铬铸铁组织与性能的研究

为研发耐磨性能优良、成本相对低廉的高铬铸铁,本文分别以亚共晶、过共晶的水雾化Cr15高铬铸铁粉末为原料,采用超固相线液相烧结工艺制备了烧结高铬铸铁(SHCCI),并对其显微组织、力学性能和冲击磨粒磨损工况下的耐磨性能进行对比研究。结果表明,烧结高铬铸铁主要由M7C3碳化物、马氏体和奥氏体组成;在亚共晶烧结高铬铸铁中,通过电解腐蚀萃取的M7C3碳化物三维形貌呈珊瑚状,沿晶界均匀分布,材料抗冲击耐磨性能优良;在过共晶烧结高铬铸铁中,优先形成的初生碳化物可能成为共晶碳化物的生长基底,形成核-壳结构的M7C3碳化物,沿晶界相互连接呈网状,严重割裂基体。亚共晶、过共晶烧结高铬铸铁的力学性能分别为:硬度HRC63.9、HRC64.3,冲击韧性7.92、3.04 J/cm^2,抗弯强度2112.65、1624.87 MPa。     

Microstructure and properties of Ti–Nb–V–Mo-alloyed high chromium cast iron

The correlations of microstructure, hardness and fracture toughness of high chromium cast iron with the addition of alloys (titanium, vanadium, niobium and molybdenum) were investigated. The results indicated that the as-cast microstructure changed from hypereutectic, eutectic to hypoeutectic with the increase of alloy contents. Mo dissolved in austenite and increased the hardness by solid solution strengthening. TiC and NbC mainly existed in austenite and impeded the austenite dendrite development. V existed in multicomponent systems in forms of V alloy compounds (VCrFe₈ and VCr₂C₂). With the increase of alloy additions, carbides size changed gradually from refinement to coarseness, hardness and impact toughness were increased and then decreased. Compared with the fracture toughness (6 J/cm²) and hardness (50·8HRC) without any alloy addition, the toughness and hardness at 0·60 V–0·60Ti–0·60Nb–0·35Mo (wt%) additions were improved and achieved to 11 J/cm² and 58·9HRC, respectively. The synergistic roles of Ti, Nb, V and Mo influenced the solidification behaviour of alloy. The refinement of microstructure and improvement of carbides morphologies, size and distribution improved the impact toughness.     

Secondary carbide precipitation in an 18 wt%Cr-1 wt% Mo white iron

High chromium (18%) white irons solidify with a substantially austenitic matrix supersaturated with chromium and carbon. The austenite is destabilized by a hightemperature heat treatment which precipitates chromium-rich secondary carbides. In the as-cast condition the eutectic M₇Ca₃ carbides are surrounded by a thin layer of martensite and in some instances an adjacent thicker layer of lath martensite. The initial secondary carbide precipitation occurs on sub-grain boundaries during cooling of the as-cast alloy. After a short time (0.25 h) at the destabilization temperature of 1273 K, cuboidal M₂₃C₆ precipitates within the austenite matrix with the cube-cube orientation relationship. After the normal period of 4 h at 1273 K, there is a mixture of M₂₃C₆ and M₇C₃ secondary carbides and the austenite is sufficiently depleted in chromium and carbon to transform substantially to martensite on cooling to room temperature.     

Fe-Cr-C hardfacing alloys for high-temperature applications

The microstructure and phase chemistry of a Fe-34Cr-4.5C wt% hardfacing alloy has been investigated using transmission electron microscopy and microanalytical techniques. The microstructure is found to consist of large primary M₇C₃. carbides in a eutectic mixture of austenite and more M₇C₃. The results indicate that the microstructure of the undiluted alloy becomes configurationally frozen at a temperature of about 1150° C during deposition by the manual metal arc welding technique. This allows the metastable austenite phase to contain a large chromium concentration ( 16 to 17 wt %), thus imparting good corrosion and oxidation resistance. Experimental data on the partitioning of chromium, manganese and silicon between the carbide phases are discussed in the context of the high-temperature stability of the alloy.     

Effect of vanadium on cast carbide in high speed steels

Abstract

The effect of vanadium (0–4%) on the morphology and amount of eutectic and eutectoid carbides in high speed steels has been investigated using scanning electron microscopy and image analysis. It was found that vanadium promotes the formation of MC carbide and M₂C carbide, but inhibits the formation of M₆C carbide. In the vanadium free steels, the eutectic carbide consists solely of skeletal M₆C. For each steel composition, there is a critical vanadium content at which the skeletal eutectic changes to lamellar eutectic and the critical value decreases as the molybdenum content of steel increases. The effect of vanadium on the total amount of eutectic carbide differs in tungsten alloyed and molybdenum alloyed high speed steels. The δ eutectoid has a rodlike morphology in tungsten high speed steels; δ eutectoid is not present in Mo–W or molybdenum high speed steels. Increasing the vanadium content leads to an increase in the size of eutectic and eutectoid carbides.

MST/1264     

Effect of M7C3→M23C6 transformation on fracture behaviour of cast ferritic stainless steels

Abstract

The fracture behaviour of three 29 wt-%Cr ferritic steels, two containing zirconium and titanium respectively, has been investigated in the as cast condition and after annealing at 660°C for different times up to 2210 h. The fracture energy and the mode of fracture depend on both the morphology and the nature of the eutectic, which consists of carbides and ferrite. In the as cast condition, fracture is predominantly transgranular cleavage and it can be associated with the discontinuous morphology of the M₇C₃ carbides present in the eutectic as coarse particles surrounded by the eutectic ferrite. After prolonged heating, the ambient fracture energy decreases and the interdendritic mode of fracture is enhanced. This change in fracture mechanism is associated with transformation of the M₇C₃ to M₂₃ C₆ carbides. The M₂₃ C₆ carbides, unlike the coarse M₇C₃ carbides, form a continuous network within the eutectic mixture and constitute an easy path for crack propagation. The zirconium and titanium additions result in a more massive morphology of the carbides in the eutectic mixture and accelerate the M₇C₃ to M₂₃C₆ transformation during the heat treatments, enhancing the interdendritic mode of fracture both in the as cast and in the annealed condition.

MST/1734     

Analyses of the failures on shear cutting blades after trimming of ultra high-strength steel

Damages on shear cutting blades were analyzed after 50,000 strokes of trimming on an ultra high-strength steel sheet. Traditional D2 alloy and an advanced one (Cr08H) based on the composition of 1C-8Cr were quenched from 1030 °C, tempered at 180 °C and submitted to the shear cutting test. Cr08H had lower hardness, a smaller volume fraction of M₇C₃ carbides while it contained a larger volume fraction of retained austenite. And these resulted in more scratches and rounded edges because of degraded resistance to wear and local plastic deformation. In spite of higher impact toughness, Cr08H exhibited inferior resistance to chipping which was the consequence of localized brittle fracture. It could be concluded that this was caused by more transformation of austenite as well as by insufficiently hardened matrix, both of which were attributed to inappropriate conditions of the heat treatment.     

Development of microstructure during heat treatment of high carbon Cr–Mo steel

Abstract

Stainless steels containing enhanced chromium and carbon contents are particularly attractive for applications requiring improved wear and corrosion resistance. The as cast microstructure of such steels is composed mainly of ferritic matrix along with a network of interdendritic primary carbides. It has been shown that heat treatment of these steels results in microstructures that contain more than one type of carbide. A selective dissolution technique has been employed to isolate carbides from the matrix. Scanning electron microscope and X-ray diffraction studies of the as cast steels have shown that the primary carbides are essentially of M₇C₃ type, whereas in heat treated specimens both M₇C₃ (primary) and M₂₃C₆ (secondary) type carbides have been observed. The relative amounts of these carbides are found to be dependent on the heat treatment temperature. In addition, nucleation of austenite occurs above 950°C and at ～1250°C the matrix transforms entirely to austenite, which is retained completely on quenching to room temperature.     

Effect of carbon content on microstructure and corrosion behavior of hypereutectic Fe–Cr–C claddings

The aim of this study was to examine the influence of carbon content on the microstructures and corrosion characteristics. The results showed that the hypereutectic microstructure comprised primary (Cr,Fe)₇C₃ carbides and the eutectic colonies [γ-Fe + (Cr,Fe)₇C₃]. The amounts of primary (Cr,Fe)₇C₃ carbides increased from 33.81 to 86.14% when carbon content increased from 3.73 to 4.85 wt%. The corrosion resistance of the hypereutectic alloy with 4.85 wt% C was about 20 times higher than that with 3.73 wt% C. The galvanic corrosion occurred in all claddings due to difference of corrosion potential between primary carbide and austenite. The dense distribution of primary carbides could retard the austenitic matrix from selective corrosion. The austenite dissolved the Fe²⁺ ions and formed a Cr₂O₃ film under 3.5% NaCl aqueous solution.     

变质处理对ZG85Cr12MoNi组织和性能的影响

ＺＧ８５Ｃｒ１２ＭｏＮｉ是一种耐磨性能优良的合金钢，但其组织中共晶碳化物量较多，脆性较大，应用于承受冲击的工况下易发生断裂，为提高其抗断裂能力，研究了钾、钠、稀土和钛复合变质处理对其组织和性能的影响。结果表明，ＺＧ８５Ｃｒ１２ＭｏＮｉ经钾、钠、稀土和钛复合变质处理后，组织细化，共晶碳化物由条块状变成团球状且分布均匀，冲击韧性和断裂韧性大幅度提高，热疲劳性能也明显改善；作轧机导卫板用使用安全，寿命比高铬铸铁和高镍铬合金分别提高３００％和３５．６％。     

Effect of multicomponent modifier on microstructure and mechanical properties of high Ni–Cr–Mo cast iron

Abstract

The microstructure and mechanical properties of high Ni–Cr–Mo indefinite chilled cast iron with the addition of a newly developed multicomponent modifier consisting of mixed rare earths, Si–Ca alloy and Bi–Sb alloy have been investigated through optical microscopy, X-ray diffraction and scanning electron microscopy, along with hardness, impact toughness and wear resistance measurements. After the addition of the modifier, the grain sizes of the primary austenite and eutectic carbides are found to be greatly refined, and the typically highly continuous net-like carbides become less interconnected but rather appear more blocky shaped. Such microstructure changes lead to mechanical property improvement in the cast specimen, with its hardness increased from 43 to 50 HRC, impact toughness from 6·3 to 7·8 J cm^?2 and ?20% increase in abrasive wear resistance.     

Structure and abrasive wear resistance of R6M5 steel-tungsten carbide composite coatings

Features of the structure formation, composition, and abrasive wear resistance of R6M5 steel-tungsten carbide (R6M5-WC) composite coatings have been studied as dependent on the WC content. The introduction of ～20 wt % WC into the hardening composition leads to an increase in the fraction of M₆C carbide (in the form of eutectic inclusions with average size ～5.9 μm at grain boundaries and dispersed ～0.25 μm particles in the volume of grains), while a large proportion of metastable austenite (～88 vol %) is still retained. The R6M5-WC coatings exhibit high abrasive wear resistance, which is ensured by the γ → α′ martensite transformation during friction and a muiltimodal size distribution of hardening particles.     

Microstructural study and wear behavior of ductile iron surface alloyed by Inconel 617

In this research, microstructure and wear behavior of Ni-based alloy is discussed in detail. Using tungsten inert gas welding process, coating of nearly 1–2 mm thickness was deposited on ductile iron. Optical and scanning electron microscopy, as well as X-ray diffraction analysis and electron probe microanalysis were used to characterize the microstructure of the surface alloyed layer. Micro-hardness and wear resistance of the alloyed layer was also studied. Results showed that the microstructure of the alloyed layer consisted of M₂₃C₆ carbides embedded in Ni-rich solid solution dendrites. The partial melted zone (PMZ) had eutectic ledeburit plus martensite microstructure, while the heat affected zone (HAZ) had only a martensite structure. It was also noticed that hardness and wear resistance of the alloyed layer was considerably higher than that of the substrate. Improvement of wear resistance is attributed to the solution strengthening effect of alloying elements and also the presence of hard carbides such as M₂₃C₆. Based on worn surface analysis, the dominant wear mechanisms of alloyed layer were found to be oxidation and delamination.     

Effects of Mo on microstructure of as-cast 28 wt.% Cr–2.6 wt.% C–(0–10) wt.% Mo irons

Microstructures of as-cast 28 wt.% Cr–2.6 wt.% C irons containing (0–10) wt.% Mo with the Cr/C ratio of about 10 were studied and related to hardness. The experimental irons were cast into dry sand molds. Microstructural investigation was performed by light microscopy, X-ray diffractometry, scanning electron microscopy, transmission electron microscopy and energy-dispersive X-ray spectrometry. It was found that the iron with about 10 wt.% Mo was eutectic/peritectic, whereas the others with less Mo content were hypoeutectic. The matrix in all irons was austenite, partly transformed to martensite during cooling. Mo addition promoted the formation of M₂₃C₆ and M₆C. At 1 wt.% Mo, multiple eutectic carbides including M₇C₃, M₂₃C₆ and M₆C were observed. M₂₃C₆ existed as a transition zone between eutectic M₇C₃ and M₆C, indicating a carbide transition as M₇C₃(M_2.3C) → M₂₃C₆(M_3.8C) → M₆C. At 6 wt.% Mo, multiple eutectic carbides including M₇C₃ and M₂₃C₆ were observed together with fine cellular/lamellar M₆C aggregates. In the iron with 10 wt.% Mo, only eutectic/peritectic M₂₃C₆ and M₆C were found without M₇C₃. Mo distribution to all carbides has been determined to be increased from ca. 0.4 to 0.7 in mass fraction as the Mo content in the irons was increased. On the other hand, Cr distribution to all carbides is quite constant as ca. 0.6 in mass fraction. Mo addition increased Vickers macro-hardness of the irons from 495 up to 674 HV₃₀. High Mo content as solid-solution in the matrix and the formation of M₆C or M₂₃C₆ aggregates were the main reasons for hardness increase, indicating potentially improved wear performance of the irons with Mo addition.     

The effect of the reduction of carbon content on the toughness of high chromium white irons in the as-cast state

Three high chromium white cast irons were examined in the as-cast state to determine the effect of the carbon content on the fracture toughness. The plane strain fracture toughness K _Ic and the fracture strength were measured for each alloy. X-ray mapping was used to identify the phases on the fracture surfaces. Scanning electron fractography and optical microscopy were used to determine the volume fraction of each phase on the fracture surfaces. It was found that most fracture occurred in the eutectic carbides, but that for the alloys with a reduced volume fraction of eutectic carbides, a small amount of crack propagation occurred in the austenitic dendrites. This change in crack path correlated with an increase in fracture toughness. The Ritchie-Knott-Rice model of brittle fracture was applied. It was found to sensibly predict the critical length for fracture for each alloy. Deep etching was employed to examine the distribution of eutectic carbides. It was found that the eutectic carbides formed a continuous network in each case.     

Effect of K/Na on microstructure of high-speed steel used for rolls

In the present work, the effect of K/Na on microstructure of high-speed steel (HSS) used for rolls was investigated utilizing Hi-scope video microscope (HSVM) and electron probe microanalyser (EPMA). As-cast microstructure of the alloy is mainly composed of pearlite matrix, M₇C₃, M₂C and MC eutectic carbides. The carbides are connected or placed next to each other to form a network along grain boundaries. After K/Na modification, the morphology, size and distribution of carbides change greatly. The carbide network tends to break, and all carbides are refined and distributed homogeneously in the matrix. The mechanism of K/Na modification on microstructure of the alloy is also discussed.     

Non-equilibrium synthesis of Fe-Cr-C-W alloy by laser cladding

Synthesis of Fe-Cr-C-W alloy using the laser cladding technique offered an opportunity to produce a novel wear-resistant material with fine and uniform microstructure. Use of preheating during laser cladding Fe-Cr-C-W provided crack-free clads. The preheating temperature was very critical to eliminate cracks in the clad. Different complex types of carbide were observed in this research. Overall laser process parameters such as power density or specific energy as well as preheating temperature affected the characteristics of the carbide precipitates in the matrix. The increase of solid solubility and high cooling rate resulted in good metallurgical characteristics. Mostly M₆C or M₂₃C₆ type carbides were observed. Usually diamond-shaped M₆C carbides showed good tribological characteristics. In general, increasing the power density brought an increase of average hardness, while decreasing the power density brought a decrease of wear scar width. The laser-clad Fe-Cr-C-W alloy showed better wear properties than laser-clad Fe-Cr-Mn-C and several times smaller scar width as compared to Stellite 6 hard-facing during line-contact wear testing.