大埔洋子湖矿山弱风化高岭土矿选矿工艺研究

以大埔洋子湖矿山中深层弱分化高岭土矿为选矿对象,通过分级试验—除砂试验—增白试验,提高了高岭土矿作为陶瓷级高岭土的品质。结果表明:分级试验—除砂试验使原矿的SiO2含量由68.96%降低到49.76%,Al2O3含量由19.25%提高到32.56%,精矿产率为16.29%;增白试验使精矿的F e2O3含量由2.04%降低到1.01%,煅烧白度由51.33%提高至77.38%。选矿后的高岭土达到陶瓷用高岭土TC-2级国家标准。选矿产生的尾砂通过筛分—脱泥—磁选—浮选得到长石精矿,其K2O+N a2O含量为11.16%,F e2O3含量为0.21%,煅烧白度为61.5%,可作为长石原料应用于陶瓷和玻璃工业。     

越南同林高岭土工艺矿物学及初步增白研究

对越南同林高岭土进行了系统的工艺矿物学研究,结果表明,试样中-0.045mm粒级产率为44.87%,淘洗率较高,说明该矿物粒度较细;煅烧试验结果表明,-0.002mm产品在900℃条件下白度较未煅烧白度低,不适合生产煅烧高岭土,但在1 250℃下煅烧后白度提高,适合作为陶瓷土使用;高梯度磁选试验研究结果表明,磁选精矿的自然白度可从磁选入料试样白度的76.28%提高到81.23%,效果不是很明显,还有待进一步研究其增白方法。     

某煤系高岭土提纯增白试验研究

以唐山开滦某煤系高岭土为原料,进行提纯增白试验研究。通过试验确定最佳工艺流程为:φ25 mm小锥角水力旋流器分级,浮选除铁和煅烧增白。结果表明:当矿浆质量分数为11%,旋流器入料压力为0.4 MPa时,高岭土中高密度杂质得到有效分离;当矿浆p H值为6.0,黄药用量为100 g/t时,浮选效果较好;将浮选精矿经950℃高温煅烧2 h后,产品白度为88.13%,产品达到高级煅烧高岭土质量要求。     

四川某煤系高岭土提纯试验研究

以四川某煤系高岭土为原料,对其进行提纯试验研究。考察磨矿时间、磁感应强度、煅烧温度等条件对提纯效果的影响,确定较优的工艺流程。结果表明,低温超导磁选和高温煅烧可显著提高煤系高岭土白度,煅烧温度过高会改变高岭石性质,降低其白度。采用"超细磨矿-三次磁选-离心-酸浸-还原煅烧"工艺流程,可获得煅烧白度分别为70.89%和83.36%的煅烧高岭土产品,除铁率分别为67.90%和70.23%,满足陶瓷用料要求,可为当地高岭土开发应用提供技术支持和理论依据。     

基于超细分级制备“双90”煅烧高岭土试验研究

以-0.038mm煤系高岭土为原料,制备"双90"优质煅烧高岭土,通过试验确定φ25 mm~φ10 mm水力旋流器组超细分级及磁选除铁、煅烧增白的工艺参数。结果表明:当矿浆质量分数为12%,旋流器组两级入料压力为0.4 MPa、0.65 MPa时,产品D90为1.98μm;当磁感应强度为1.4 T,煅烧助剂Na Cl用量为2.5%,经950℃高温煅烧2 h后,白度为91.48%,产品达到"双90"标准要求。     

煤泥伴生高岭土提纯与增白试验研究

针对河北唐山地区选煤厂浮选尾煤中煤系高岭土含量高,采用φ150 mm、φ75 mm、φ50 mm、φ10 mm的小锥角水力旋流器组提纯煤泥伴生高岭土,φ10 mm溢流产品中Al2O3含量富集到36.91%。通过磁选、化学漂白、煅烧等工艺对煤泥伴生高岭土进行增白试验,结果表明选用提纯-弱磁-高梯度磁选-化学漂白-煅烧工艺流程,产品煅烧后白度可达到92.87%,满足造纸工业用煅烧高岭土白度要求。     

某高品质煤系高岭土增白工艺研究

根据某高品质煤系高岭土的特性进行了增白工艺研究 ,研发的增白工艺流程简单、效率高 ,最终产品白度高达 93 %以上 ,完全符合了造纸涂料级煅烧高岭土对白度的要求     

煤系硬质高岭土煅烧增白研究

以陕西某地煤系高岭土为试样, 研究了煅烧过程中煅烧温度、煅烧时间、添加剂用量对白度的影响。在1 000 ℃煅烧2 h 并添加3%的锯木屑和NaCl 作增白剂, 试样煅烧白度达到了90%。探讨了添加剂的增白机理, 分析了煅烧产品的结构及性能。     

松宜煤系高岭土煅烧增白影响因素研究

以湖北松宜煤系高岭土为原料，研究了煤系高岭土煅烧过程中煅烧温度、保温时间、升温速度、添加剂等因素对煅烧产品白度的影响。在对煤系高岭土进行酸处理后，加入NaCl进行煅烧，获得了白度达85．1％的煅烧高岭土，可满足橡胶填料、中档造纸涂料等领域的应用要求，为南方煤系高岭土的开发利用提供了重要依据。     

煤系高岭土化学漂白试验研究

以开滦集团林西选煤厂浮选尾煤为研究对象,对煤系高岭土采用先煅烧后漂白与先漂白后煅烧两种工艺进行漂白试验。结果表明,采用先煅烧后漂白工艺,效果更佳,最终煤系高岭土煅烧白度高达90.12%。     

大埔洋子湖矿山高岭土选矿工艺

以大埔洋子湖矿山高岭土原矿为研究对象,通过选矿试验,确定了合理的选矿工艺。原矿除砂试验后精矿产率为33.57%,SiO2含量由69.48%降低到51.08%,Al2O3含量由20.27%提高到32.13%。对精矿进行除铁增白,使Fe2O3含量由1.38%降低到0.66%,烧成白度由66.7%提高至86.1%。经过选矿后的高岭土产品达到陶瓷用高岭土TC-2级国家标准。高岭土选矿中产生的尾矿经过进一步选矿,可使其K2O+Na2O含量由6.33%提高到7.22%,Fe2O3含量由0.59%降低到0.13%,可作为长石原料应用于陶瓷工业。     

Technological characterization of kaolin tailing from small-scale mining in RN and PB states – Brazil

In small-scale mining in north-eastern Brazil, the exploitation of industrial minerals, where kaolin bearing pegmatites are mined, is common. The mineral processing of kaolin is based in mixer and classification by screen and cyclone. The overflow of cyclone is thickened and filtered by pressure filter. The product is dried for market. This work presents the results of tailings characterization. Mass balance was realized and recuperation of kaolin about 56% was identified. The feed grade of Al₂O₃ in the plant is 21.20%. The kaolin product for market sold by the company presents 37.19% Al₂O₃ and whiteness of 81.9%. The average Al₂O₃ content of the tailing is 15.55%. Minerals identified are feldspar, muscovite, tourmaline, illite and kaolinite. The −325# fraction of the tailings present Al₂O₃ grades with characteristics for market (Al₂O₃-35%) and whiteness of 79.7%. Values from 7 to 34 wt% of this −325# fraction were determined in the tailing samples analyzed; these results validate the feasibility of reprocessing the tailings for using in the ceramic industry.     

淮北煤系高岭土增白实验研究

通过磨矿、磁选、化学漂白等工艺,对淮北新蔡煤系高岭土的增白进行了系统的研究,结果表明:通过原矿→颚式破碎→对辊破碎→瓷球磨→搅拌磨→磁选→煅烧工艺,可使高岭土的白度由69.40%提高到92.61%,全Fe含量由0.71%下降到0.29%,达到各工业优级煅烧高岭土的白度标准。     

硬质高岭土矿在合成4A沸石中的应用研究

根据硬质高岭土的特点,采用了漂白、煅烧、超细磨等深加工技术,大幅度地提高了硬质高岭土的白度和细度,扩大了硬质高岭土矿的应用领域。重点介绍了用深加工后的超细高岭土粉合成4A沸石的试验研究及小批量试生产结果,最终产品达到轻工部的标准,发展前景可观。     

莱州高岭土的特征及工业应用试验

莱州高岭土杂质元素含量较高，白度较低。石英、长石含量较多，主要矿物组成为管状7A埃洛石。经淘洗、除砂、焙烧、漂白后可为工业利用。初步工业试验表明，莱州高岭土可以用作纸张涂料的原料。此为埃洛石粘土的开发应用我到了一条新的途径。     

宜昌某高岭土剥片试验

宜昌某高岭土矿高岭土含量虽达95%左右,但-2μm粒级产率仅占30%,且有10%的叠片状未剥离高岭土,层间的着色有机杂质直接煅烧难以高效脱色。为获得高品质高岭土熟料,对试样进行了剥片工艺条件研究,并对剥片前后的高岭土进行了SEM分析和熟料白度研究。结果表明,在磨矿前一次性加入与试样质量比为3%的分散剂六偏磷酸钠,搅拌磨中刚玉质中球(=1.2 mm)与小球(=0.8 mm)的体积比为0.8∶1.5,介质充填率为70%,磨矿浓度为70%,剥片转速为800 r/min,磨矿时间为180 min情况下,剥片产品-2μm粒级产率为96.62%,普遍为表面平滑、颗粒均匀的高岭土单片;剥片前后高岭土熟料的白度分别为76.84%和82.08%,剥片使熟料的白度提高了5.24个百分点。剥片后高岭土的粒度和熟料的白度均达到高档填料的质量要求。     

合浦地区高铁低品级高岭土除铁试验研究

广西合浦地区高铁低品级高岭土由于铁含量高,原矿Fe2O3+TiO2>2.5%,经淘洗后获得的-0.045mm粒级样品中的铁含量大于4%。通过试验研究表明,采用高梯度磁选、加温漂白等方法,可获得Al2O3>35%,Fe2O3<1.5%,白度大于80%的漂白精土产品。     

南方某高岭土除铁增白实验

以南方某高岭土为对象,在试样性质研究的基础上,系统考查了pH值、保险粉用量、草酸用量、矿浆浓度、温度等因素对高岭土白度的影响。结果表明:该高岭土属于砂质高岭土,影响白度的矿物主要为赤铁矿、磁铁矿和金红石;在较优的除铁增白实验条件下,获得了Fe₂O₃含量为0.46%,白度为80.82%的高岭土产品;为该高岭土矿的开发利用提供技术支撑。