新型中和缓蚀剂对常减压塔顶H2S-HCl-H2O腐蚀作用的影响

研究了新型中和缓蚀剂SF-121B和BZH-1在常减压蒸馏塔顶H2S-HCl-H2O腐蚀系统中的缓蚀效果,结果表明随着H2S浓度增加,腐蚀速率增加;温度升高,溶液pH值下降,腐蚀增加.中和缓蚀剂SF-121B和BZH-1的缓蚀效果优于目前工业常用的7019.SF-121B与氨水复配在保持较好缓蚀效果的同时,可减少操作成本.     

新型中和缓蚀剂对常减压塔顶HCI腐蚀作用的影响

针对石油加工过程中常减压蒸馏塔顶的HCl腐蚀，采用失重法研究了新型中和缓蚀剂SF-121B、BZH-1和SH-A在HCl-H2O环境下对碳钢的缓蚀效果，并与7019和氨水复合使用的效果进行比较。结果表明：随着HCl浓度和温度的增加，碳钢腐蚀率增加，SF-121B、BZH-1和SH-A的缓蚀效果优于7019与氨水复配使用的效果，SF-121B与氨水复配在保持较好缓蚀效果的同时能降低操作费用。     

新型中和缓蚀剂对常减压塔顶HCl腐蚀作用的影响

针对石油加工过程中常减压蒸馏塔顶的HCl腐蚀,采用失重法研究了新型中和缓蚀剂SF-121 B、BZH-1和SH-A在HCl-H2O环境下对碳钢的缓蚀效果,并与7019和氨水复合使用的效果进行比较.结果表明:随着HCl浓度和温度的增加,碳钢腐蚀率增加,SF-121B、BZH-1和SH-A的缓蚀效果优于7019与氨水复配使用的效果,SF-121B与氨水复配在保持较好缓蚀效果的同时能降低操作费用.     

羟基基团对咪唑啉衍生物在H2S/CO2体系中缓蚀性能的影响

用硬脂酸、十二羟基硬脂酸分别与二乙烯三胺、羟乙基乙二胺合成了4种咪唑啉衍生物。通过在H2S/CO2体系中采用动态腐蚀失重、接触角、AFM力曲线测试和电化学方法,研究了咪唑啉衍生物引入羟基基团后对其缓蚀性能和缓蚀剂膜的疏水性能的影响。测试结果表明,咪唑啉衍生物烷基链上引入羟基后接触角变大,粘附力升高,疏水效果更好;动态失重和电化学测试表明亲水基团和疏水基团都含有羟基时咪唑啉衍生物的缓蚀效果最好。     

新型三唑衍生物作为20g钢的H2SO4酸洗缓蚀剂作用机理的研究

采用失重法、电化学方法研究新型三唑衍生物在1mol／L H2SO4中缓蚀性能和机理,并研究该缓蚀剂在20g钢表面的吸附行为。结果表明．新型三唑绥蚀剂是一种混合型缓蚀剂,在1mol／L H2SO4溶液中缓蚀剂浓度为1000g／L时缓蚀率最高,为94．6％。Matlab拟合表明该缓蚀剂在20g钢表面的吸附行为符合Bockris-Swinkels吸附等温式。     

炼厂常减压蒸馏过程中的腐蚀与缓蚀

本文讨论常减压蒸馏过程中的腐蚀机理和缓蚀剂“581”的缓蚀机理,并通过缓蚀率的测定,表明缓蚀剂“581”不仅是乙烯裂解系统工艺循环冷却水中的新型高效缓蚀剂,而且它有可能成为炼厂常减压塔顶冷凝冷却系统的优良缓蚀剂之一。     

RH-2缓蚀阻垢剂在烷基化表面蒸发空冷2008年应用研究

分析了烷基化装置表面蒸发空冷容易结垢,故而造成垢下腐蚀的问题.并根据表面蒸发空冷的特点,对表面蒸发空冷采用注入RH-2缓蚀阻垢剂来进行防腐和缓蚀阻垢.介绍了E-2、E-6注入RH-2缓蚀阻垢剂后的设备防腐情况和技术研究.     

低碳钢自腐蚀电位与缓蚀剂吸附性能关系的探讨

在低碳钢/稀盐酸腐蚀体系中,测试了缓蚀剂六次甲基四胺(HA)对体系的缓蚀行为,并对HA和二乙基二硫代氨基甲酸钠(SDEDTC)的缓蚀行为进行了分析;从理论上导出了体系自腐蚀电位随温度变化的关系式和缓蚀剂类型的自腐蚀电位判据.研究结果表明:低碳钢缓蚀前、后自腐蚀电位的改变与温度的倒数成线性关系;HA为阳极型缓蚀剂,SDEDTC为混合型缓蚀剂,二者的吸附形式均为物理吸附,吸附热分别为-35 kJ/mol和-30 kJ/mol.     

氨基膦酸化合物缓蚀性能的量子化学研究

运用量子化学密度泛函(DFT)中B3LYP方法,在6-31G*基组水平上,对6种氨基膦酸化合物的缓蚀性能和分子结构进行研究,讨论了量子化学计算结果和缓蚀性能的关系,结果表明:分子的轨道能量和化合物中苯环的亲电Fukui指数和缓蚀性能有很好的相关性,说明氨基膦酸的缓蚀性能主要与苯环的得电子能力有关,此类化合物的缓蚀性能主要因为苯环和金属之间形成反馈π键。     

CO2/H2S对油气田常用钢材腐蚀规律及防腐技术研究进展

CO2和H2S腐蚀是石油天然气工业中常见的腐蚀类型之一,它们溶于水后,pH值呈现弱酸性,对管道设备等会产生腐蚀,但当两种气体同时存在时,对钢材的腐蚀呈现复杂多样性。针对两种气体同时存在时腐蚀的多变性,本文总结归纳了在CO2和H2S共存条件下的腐蚀机理、影响因素及缓蚀行为,旨在为油田防腐及选材提供参考依据,更好的延长管道使用寿命。     

超级13Cr马氏体不锈钢在CO_2 及H_2 S/CO_2 环境中的腐蚀行为

在模拟油田腐蚀环境中,通过高温、高压、CO2和H2S/CO2腐蚀实验及电化学测试,研究超级13Cr马氏体不锈钢的腐蚀行为.结果表明:在CO2腐蚀环境中,随着温度的升高,超级13Cr的均匀腐蚀速率呈稍微上升的趋势,点蚀轻微;在H2S、CO2共存条件下,超级13Cr的均匀腐蚀速率变化不大,点蚀严重,当Cl-的质量浓度为160g.L-1时,其最大点蚀深度可达28μm.超级13Cr的点蚀电位明显高于普通13Cr的点蚀电位,温度升高、Cl-的质量浓度增大和H2S气体的存在降低了超级13Cr的点蚀电位,而CO2对超级13Cr的点蚀电位影响不大;在N2、CO2环境中,超级13Cr的回复电位都在钝化区间,且回复电位较高,具有良好的再钝化能力.H2S气体的存在同样使超级13Cr的回复电位和点蚀电位显著降低.     

乙醇胺为主体的CO_2吸收剂的复配研究

以改善乙醇胺(MEA)水溶液吸收负荷、吸收速率、再生程度和防腐蚀等性能为目标,对以MEA为主体的复配吸收剂的性能进行了研究。结果表明,在MEA水溶液中加入哌嗪(PZ)或者2-氨基-2-甲基-1-丙醇(AMP)能提高MEA水溶液吸收CO2的负荷、平均吸收速率和再生性能。在溶液中加入少量氧化膜型缓蚀剂能有效抑制吸收剂溶液对碳钢的腐蚀,吸收剂溶液对碳钢的腐蚀速率从无缓蚀剂条件下的1.96 g/(m2.h)可降低到0.2 g/(m2.h)左右,极大地改善了吸收剂溶液的防腐蚀性能,对碳钢材料起到了较好的保护作用,缓蚀效果为偏钒酸钠铬酸钾重铬酸钾亚硝酸钠硝酸钠磷酸钠亚硫酸钠。     

硫化氢质量浓度和温度对碳钢在NACE溶液中腐蚀行为的影响

采用动电位极化曲线和电化学阻抗谱等电化学实验方法以及扫描电镜和能谱等表面分析技术对20#碳钢在不同H2S质量浓度(0,95.61,103.22,224.16 mg.L-1)、不同温度(25,35,45℃)下的NACE溶液(含CO2)中腐蚀行为进行了研究,同时对该环境下腐蚀产物的形成机制进行了探讨.发现在含有CO2的NACE溶液中,加入少量H2S,能加剧碳钢腐蚀,加速阳极铁的溶解和阴极氢气的析出.随着H2S质量浓度的增加,腐蚀电流密度增大,碳钢腐蚀加剧.温度升高,腐蚀极化电阻变小,腐蚀也会加剧.腐蚀试样外层絮状腐蚀产物主要是铁碳化物,接近基体表面的腐蚀产物主要是铁硫化物.     

Influence of chromium on the initial corrosion behavior of low alloy steels in the CO2-O2-H2S-SO2 wet-dry corrosion environment of cargo oil tankers

The influence of Cr on the initial corrosion behavior of low-alloy steels exposed to a CO2–O2–H2S–SO2wet–dry corrosion envi-ronment was investigated using weight-loss measurements, scanning electron microscopy, N2 adsorption tests, X-ray diffraction analysis, and electrochemical impedance spectroscopy. The results show that the corrosion rate increases with increasing Cr content in samples subjected to corrosion for 21 d. However, the rust grain size decreases, its specific surface area increases, and it becomes more compact and denser with increasing Cr content, which indicates the enhanced protectivity of the rust. The results of charge transfer resistance (Rct) calculations indicate that higher Cr contents can accelerate the corrosion during the first 7 d and promote the formation of the enhanced protective inner rust after 14 d; the formed protective inner rust is responsible for the greater corrosion resistance during long-term exposure.     

Effect of H2S concentration on the corrosion behavior of pipeline steel under the coexistence of H2S and CO2

The effect of H2S concentration on H2S/CO2 corrosion of API-X60 steel was studied by scanning electron microscopy, a weight-loss method, potentiodynamic polarization tests, and the electrochemical impedance spectroscopy technique. It is found that the cor-rosion process of the steel in an environment where H2S and CO2 coexist at different H2S concentrations is related to the morphological structure and stability of the corrosion product film. With the addition of a small amount of H2S, the size of the anode reaction region is de-creased due to constant adsorption and separation of more FeS sediment or more FeHS＋ions on the surface of the steel. Meanwhile, the dou-ble-layer capacitance is diminished with increasing anion adsorption capacity. Therefore, the corrosion process is inhibited. The general cor-rosion rate of the steel rapidly decreases after the addition of a small amount of H2S under the coexistence of H2S and CO2. With a further increase in H2S concentration, certain parts of the corrosion product film become loose and even fall off. Thus, the protection provided by the corrosion product film worsens, and the corrosion rate tends to increase.     

2．25Cr1Mo钢在硫化氢溶液中的应力腐蚀开裂研究

本文用楔形张开加载（WOL）预裂纹试样进行了2．25Cr1Mo材料在硫化氢水溶液中的抗应力腐蚀试验,研究了2．25Cr1Mo钢在不同浓度硫化氢溶液中的抗应力腐蚀性能。试验测定了2．25Cr1Mo钢在500ppm,1000ppm H2S溶液下的应力腐蚀临界应力强度因子Ksoc和应力腐蚀裂纹扩展速率da／dt。结果表明,随着H2S浓度的升高,2．25Cr1Mo钢的应力腐蚀临界应力强度因子Ksoc下降,应力腐蚀裂纹扩展速率da／dt增大,抗应力腐蚀的寿命缩短。     

工业纯钛和00Cr25Ni22Mo2不锈钢的缝隙腐蚀

采用在不同温度及不同介质中化学浸泡法和电化学测试方法,对工业纯钛和００Ｃｒ２５Ｎｉ２２Ｍｏ２不锈钢之间产生的缝隙腐蚀行为进行研究。结果表明：在有缝隙的情况下,００Ｃｒ２５Ｎｉ２２Ｍｏ２不锈钢在氧化性介质中的缝隙腐蚀速率明显大于在还原性介质中的缝隙腐蚀速率;工业纯钛则恰恰相反。温度对缝隙腐蚀有较大影响,随温度升高,００Ｃｒ２５Ｎｉ２２Ｍｏ２不锈钢的缝隙腐蚀加重并伴有点蚀产生;工业纯钛在１（ｍｏｌ·Ｌ－１）Ｈ２ＳＯ４溶液中,随温度升高缝隙腐蚀速率增加明显,高于８３℃伴有点蚀产生。电化学实验表明,存在缝隙情况下,在２５℃１（ｍｏｌ·Ｌ－１）Ｈ２ＳＯ４溶液中,工业纯钛的维钝电流密度小于００Ｃｒ２５Ｎｉ２２Ｍｏ２不锈钢的维钝电流密度,工业纯钛的击穿电位比００Ｃｒ２５Ｎｉ２２Ｍｏ２不锈钢的高约８００ｍＶ;而在８５℃,工业纯钛的维钝电流密度大于００Ｃｒ２５Ｎｉ２２Ｍｏ２不锈钢的,而且工业纯钛的击穿电位下降明显,两者的击穿电位十分接近     

阻锈剂改善碳化混凝土再碱化效果研究

采用电化学测试技术和仪器分析方法研究了2种阻锈剂在混凝土中的迁移,利用电化学测试方法评估阻锈剂在模拟体系中的缓蚀效果,结合阻锈剂的缓蚀作用,研究了阻锈剂改善再碱化修复碳化钢筋混凝土结构效果的可行性．结果表明：在3A／m^2恒电流密度形成的电场作用下阻锈剂通过30mm厚的混凝土速率明显高于未通电情况下的,说明电场作用对阻锈剂的迁移扩散过程起到了促进作用;在模拟体系中,随着乙醇胺及二乙醇胺浓度的增大,其缓蚀效果也逐步提高,相同浓度下二乙醇胺缓蚀效果更好,在二乙醇胺浓度为0．08mol／L时对Q235钢筋缓蚀率为93．24％;再碱化后在相同的弛豫时间内,采用添加二乙醇胺的碳酸钠电解液进行再碱化的样品腐蚀电位明显正移,腐蚀电流密度变小,阻锈剂能够改善再碱化的修复效果．     

抑制CO2/H2S腐蚀的气液双相新型缓蚀剂的制备及评价

通过合成咪唑啉、噻唑类衍生物,将其与低分子量的有机胺及表面活性剂进行复配得到复配缓蚀剂.用静态挂片失重法研究它们的缓蚀效率.结果表明该复配物对抑制CO2/?H2S的气液两相的腐蚀有良好的效果.并通过极化曲线等手段研究了该缓蚀剂的缓蚀机理.