分调控对BT20钛合金焊接接头疲劳性能的影响

通过在BT20钛合金电子束焊接过程中添加嵌料,改变接头熔合区的化学成分,研究成分的变化对其焊接接头焊缝区显微组织、显微硬度以及高周疲劳性能的影响.结果发现,成分调控在降低接头熔合区合金化程度的同时,还改变了熔合区的显微硬度分布.高周疲劳测试结果表明,成分调控BT20合金焊接接头的疲劳强度与传统焊接接头相当,比基体高;但是在780 MPa的高应力水平下,疲劳寿命随疲劳峰值应力的增加迅速降低,样品在焊缝区断裂的几率增加,表明成分调控会降低焊接接头高应力水平下的疲劳性能.     

试样尺寸对SA508-3钢焊接接头断裂韧度的影响

针对大型核容器SA508-3钢焊接接头断裂韧度进行了研究.结果表明,在大试样条件下,母材、焊缝金属及热影响区的断裂韧度存在差异,焊缝金属的断裂韧度优于热影响区,母材的断裂韧度最低.试样几何尺寸直接影响裂纹尖端的应力状态,小试样时裂纹尖端处于平面应力状态,母材、焊缝金属及热影响区全部呈韧窝断裂,表现出良好的塑性;大试样时裂纹尖端处于平面应变状态,母材断口特征转变为准解理与解理混合断裂,热影响区为典型的准解理断裂,焊缝为韧窝断裂.     

35CrMnSi钢电子束焊接头显微组织和力学性能研究

研究了35CrMnSi 钢电子束焊接头的组织和力学性能.试验结果表明:该钢电子束焊焊缝为典型的针状马氏体+残余奥氏体组织,HAZ为中温组织;2种厚度钢板焊接接头各区域的硬度值基本一致,且焊缝硬度高于热影响区的,热影响区的硬度高于母材的.经电子束焊后,2种厚度35CrMnSi钢板接头塑性比母材的塑性低,这与其显微组织有关;35CrMnSi钢电子束焊焊缝的冲击韧度低于母材.     

PM-TZM钼合金电子束焊接特性

为研究PM-TZM钼合金电子束焊接特性,对其进行了电子束焊接试验,分别对接头显微组织及力学性能进行了分析. 结果表明,PM-TZM钼合金电子束焊缝呈“钉状”几何特征,熔合线附近有链状气孔出现. 焊缝区由粗大的等轴晶及柱状晶组成,热影响区晶粒相比于母材明显长大. 接头各区域硬度值不同,焊缝区硬度与母材相当,硬度最低值出现在两侧热影响区.PM-TZM合金电子束焊接接头有较大的性能损失. 接头室温最高抗拉强度378 MPa,为母材抗拉强度的47%,1 000℃抗拉强度168 MPa. 接头拉伸断裂均发生于焊缝区,呈典型的脆性解理断裂特征.     

激光快速成形TA15钛合金氩弧焊接头组织及力学性能

对激光快速成形TA15钛合金与轧制TA15钛合金薄板进行了氩弧焊接试验,观察分析了焊接接头各区域组织特征,测试了焊接接头各区域的显微硬度以及室温拉伸性能.结果表明,激光快速成形件与轧制薄板氩弧焊焊缝凝固组织是具有粗大片状α+β组织特征外延定向生长的柱状晶.轧制件对焊接热影响敏感性强,热影响区晶粒发生严重长大现象,激光成形件靠近焊缝热影响区晶粒转变为等轴晶,距焊缝较远的热影响区仍保持柱状晶.激光成形件热影响区硬度最高,焊缝区及轧制件热影响区的硬度最低.焊接接头抗拉强度低于母材,塑性与轧制件相当,断裂位置位于轧制件热影响区.     

桥梁钢Q345焊接接头疲劳裂纹扩展速率研究

对桥梁用钢Q345焊接接头疲劳裂纹扩展性能进行了试验研究。测得对接接头的硬度分布,结果表明,焊接接头焊缝中心处的硬度值较低,在热影响区的重结晶区存在硬度最高点,而在部分重结晶区存在硬度最低点,硬度最低点为对接接头的薄弱区。通过疲劳裂纹扩展速率测试,得到其对接接头不同区域的疲劳裂纹扩展a-N曲线以及lg(da/dN)-lgΔK曲线。分析对比对接接头各区域的疲劳裂纹扩展速率lg(da/dN)-lgΔK曲线可知,在同一应力水平下,对接接头不同部位的疲劳裂纹扩展速率不同,热影响区的扩展速率较快,母材次之,焊缝金属最慢。并通过疲劳断口和焊接接头的显微组织,分析了其疲劳裂纹扩展速率不同的原因。     

A7N01铝合金焊接接头的不均匀特性

以A7N01铝合金焊接接头为分析对象,通过金相试验、显微硬度试验、拉伸试验和缺口疲劳试验分析了焊接接头微区的不均匀性．结果表明,A7N01铝合金焊接接头母材、焊缝、热影响区内的组织和硬度差别较大,焊缝硬度最低约为HV75,母材焊缝最高约为HVI10,热影响区内硬度变化较大．母材的屈服强度和抗拉强度高于焊缝和热影响区．而热影响区的断后伸长率最高．三个区域内疲劳裂纹萌生寿命差异较小,裂纹萌生寿命与总寿命之比近似为常数,疲劳总寿命差别明显,母材的疲劳总寿命最长,焊缝疲劳总寿命最短．     

旋挖钻机桅杆用16Mn碳素结构钢的双丝埋弧焊接工艺研究

采用双丝埋弧焊接工艺对旋转钻机桅杆用16Mn碳素结构钢进行了不同焊接电流、焊丝间距和焊接速度的焊接试验。研究了焊接参数对焊接接头硬度、力学性能和显微组织的影响,得到了适宜的焊接工艺参数,并提出了焊接过程的质量控制措施。结果表明,随着焊接电流的减小,焊接接头热影响区的显微硬度降低,而焊缝区的显微硬度却逐渐升高;不同焊丝间距下显微硬度峰值都在焊接热影响区,焊丝间距对焊接接头显微硬度影响不大;不同焊接速度下焊接接头焊缝区的显微硬度都要高于母材或与母材相当,热影响区的显微硬度要高于母材和焊缝区。焊缝热影响区组织为针状铁素体、片状先共析铁素体、珠光体。焊接电流为700 A、焊接速度为0.0083 m/s、焊丝间距为0.07 m时焊接接头可以获得最佳的强度和塑性,断裂位置位于母材。     

激光焊接功率对TC4钛合金微观组织和疲劳寿命的影响

使用光学显微镜和显微硬度计测试了不同功率条件下的焊缝组织和硬度;使用液压伺服疲劳试验机测试了不同功率下焊接接头的抗拉强度和疲劳寿命,分析了不同功率条件下疲劳寿命的概率分布与可靠性。结果表明:功率对焊接接头的抗拉强度和伸长率影响不大;焊缝熔合区为"网篮状"的α'针状马氏体,热影响区有少量的α'马氏体;焊缝熔合区的显微硬度高于热影响区,热影响区的显微硬度高于母材,且功率越高,硬度也越高。随着激光功率增大,同等载荷下焊接接头的疲劳寿命变长,可靠性变好。     

20g与P91异种金属焊接接头组织及其性能分析

通过对20g和P91异种金属进行埋弧自动焊试验,研究了焊接接头各区域包括母材、热影响区和焊缝的显微组织,并对焊接接头进行了硬度测试、拉伸试验和冲击试验等力学性能测试。结果表明,20g侧焊缝组织为珠光体和针状铁素体,P91侧焊缝组织是块状铁素体、珠光体以及马氏体;焊缝区的显微硬度值要明显高于两侧母材以及热影响区的显微硬度值;焊缝金属的抗拉强度要明显高于两侧母材的抗拉强度,断裂位置发生在母材20g侧;接头20g侧母材、焊缝区和P91侧母材的冲击功分别185.2、239.6和13.0 J,表明焊缝的冲击韧性明显高于两侧母材的冲击韧性,但是和焊前相比较,20g侧母材焊后冲击韧性得到大幅提高,而P91侧母材焊后冲击韧性显著降低。     

Microstructure and Fatigue Properties of Laser Welded DP590 Dual-Phase Steel Joints

In this paper, cold-rolled DP590 dual-phase steel sheets with 1.5 mm thickness were butt-welded by a fiber laser, and the evolution and effect on microhardness, tensile property and fatigue property of the welded joint microstructure were studied. The results showed that the base metal is composed of ferrite and martensite, with the martensite dispersed in the ferrite matrix in an island manner. The microstructure of the weld zone was lath-shaped martensite that can be refined further by increasing the welding speed, while the heat-affected zone was composed of ferrite and tempered martensite. The microhardness increased with increasing welding speed, and the hardness reached its highest value—393.8 HV—when the welding speed was 5 m/min. Static tensile fracture of the welded joints always occurred in the base metal, and the elongation at break was more than 16%. The conditional fatigue limits of the base metal and the weld joints were 354.2 and 233.6 MPa, respectively, under tension–tension fatigue tests with a stress rate of 0.1. After observation of the fatigue fracture morphology, it was evident that the fatigue crack of the base metal had sprouted into the surface pits and that its expansion would be accelerated under the action of a secondary crack. The fatigue source of the welded joint was generated in the weld zone and expanded along the martensite, forming a large number of fatigue striations. Transient breaking, which occurred in the heat-affected zone of the joint as a result of the formation of a large number of dimples, reflected the obvious characteristics of ductile fracture.     

Microstructure and mechanical properties of E36 steel joint welded by underwater wet welding

The microstructure and mechanical properties of E36 steel joint welded by underwater welding using flux-cored wire are comprehensively investigated. The welding depth, welding current and welding voltage is 4 m, 130 A and 32 V, respectively. The weld metal is ferrite which varies in size, with carbide particles distributed on it, while the microstructure of HAZ is mixture of martensite of different size and some tempered structure. The microhardness of the weld metal is 190 HV. Almost all the tensile specimens fracture in weld metal and the average tensile strength of joint is 390 MPa, which is equal to 80% that of base metal. The tensile fracture morphology of joint presents obviously the characterization of brittle fracture, which displays the features of cleavage fracture and intergranular fracture.     

高温钛合金Ti55/Ti60真空电子束焊接

对 Ti55 与 Ti60 合金薄板进行了电子束焊接,研究了电子束焊接工艺参数对接头组织及力学性能的影响.结果表明,焊缝区形成大量针片状的α' 马氏体,焊缝中心为粗大的柱状晶.焊接工艺参数对焊缝组织和接头抗拉强度有一定影响,接头室温抗拉强度高于母材,600℃时接头抗拉强度与 Ti60 母材相当,抗弯强度达到母材的 80% 左右,冲击韧度能够达到母材的 90% 以上,断裂发生在热影响区处,为韧性断裂.

Abstract：

Ti55 and Ti60 titanium alloy sheets were welded by electron beam, and the influences of parameters on microstmcture and mechanical properties of welding joints were studied. The results show that weld zone is characterized by acicular α' martensite plate,and weld center is formed by coarse columnar crystals. Welding parameters can affect microstructure and tensile strength to a certain extent. At room temperature, the tensile strength of joint is higher than that of base metal. At a higher temperature of 600 ℃, tensile strength of joint is about equal to that of Ti60, and bending strength can be up to 80% of that of base metal, even impact toughness also can be larger than 90% of base metal. Failure occurs in heat-affected zone, and the fracture mode shows toughness characteristic.     

700MPa级低合金高强钢低匹配焊接接头组织和性能研究

按照低匹配设计原则,采用熔化极气体保护焊对屈服强度为700 MPa级的低合金高强钢进行了焊接。采用光学显微镜、扫描电镜和力学性能试验研究了焊接接头的组织和性能。结果表明,焊缝区组织主要为针状铁素体和少量先共析铁素体,粗晶热影响区组织为上贝氏体;焊缝区显微硬度明显低于母材,焊缝区-40℃时的冲击韧度(AKV)为58 J,抗拉强度达到了母材抗拉强度的92.4%,焊接接头的综合力学性能良好。     

TC4厚壁管全位置PAW工艺及接头性能分析

介绍了一种适合TC4钛合金厚壁管的等离子弧焊接新工艺,通过对工艺参数分区控制和优化匹配,实现了钛合金管道全位置优质焊接.采用光学显微镜、扫描电镜以及显微维氏硬度仪分别对特征位置焊接接头的显微组织、断口形貌以及显微硬度进行表征.结果表明,特征位置接头焊缝区及热影响区显微组织均主要由网篮状α'相、针状α相以及粗大β相组成;接头拉伸性能良好,拉伸试样均断裂于母材处;冲击试样的断裂形式为韧性断裂;焊缝区及热影响区硬化区的硬度值高于母材.     

焊接速度对30CrMnSiNi2A钢电子束焊接头组织和力学性能的影响

30CrMnSiNi2A钢由于其出色的质强比成为制造飞机起落架、襟翼的重要材料。电子束焊的焊接速度对工程应用中30CrMnSiNi2A钢的微观结构和机械性能产生极大影响。接头微观组织从热影响区细小等轴的回火索氏体与马氏体混合组织,转变为焊缝区域的树枝状板条马氏体晶粒。显微硬度由母材向焊缝中心逐渐增高,焊缝区域显微硬度最高可达690HV0.2,约为母材的两倍;拉伸强度最高为842MPa,达到母材强度的96.9%。此外随着焊接速度的提高,晶粒尺寸减小,显微硬度随之提高;但HAGB和渗碳体数量的下降对接头强度不利,使得接头抗拉强度随焊接速度提高而下降,不同焊接速度下接头断裂模式均为脆性断裂。     

热处理对TC17(α+β)/TC17(β)线性摩擦焊接头组织及力学性能的影响

针对热处理前后TC17(α+β)/TC17(β)钛合金线性摩擦焊接头组织和性能进行了对比分析. 结果表明,焊态时焊缝区组织发生动态回复和再结晶,两侧的热力影响区组织均被不同程度地拉长,热处理后焊缝中的亚稳相分解析出弥散的α和β相,TC17(α+β)侧热力影响区的初生α相有所长大. 焊态接头焊缝区显微硬度比母材低,接头的抗拉强度和屈服强度略低于母材,分别达到母材的91.9%,96.2%,接头拉伸性能试件断裂位置均在焊缝区;经过热处理,母材显微硬度未发生明显变化,焊缝区显微硬度显著提高,接头抗拉强度和屈服强度达到与母材相当,与焊态相比分别提高11.9%,8.2%,接头拉伸性能试件断于母材区.     

低活化铁素体/马氏体钢厚板光纤激光焊接接头组织及力学性能分析

针对核聚变反应堆试验包层模块(TBM)中使用的CLF-1低活化铁素体/马氏体钢进行焊接试验,采用15 kW光纤激光,实现了17.5 mm厚CLF-1钢的穿透焊接,得到了正反表面成形良好、无明显缺陷的焊接接头,并对接头显微组织及力学性能进行了分析研究. 结果表明,焊缝区主要为粗大的板条马氏体;熔合线附近热影响区为细小的板条马氏体和少量贝氏体;不完全淬火区为经焊接热循环作用下二次回火的回火索氏体及马氏体双相组织;接头室温及550 ℃高温抗拉强度较高,均断裂于母材;焊缝显微硬度高于母材,且热影响区无明显软化;接头冲击韧性良好. 接头综合力学性能良好.     

TC21+TC4-DT线性摩擦焊接头组织与力学性能试验

针对高强TC21和中强TC4-DT异种钛合金进行线性摩擦焊工艺研究,对接头进行不同热处理,接头微观组织和力学性能进行试验分析. 结果表明,TC21 + TC4-DT线性摩擦焊接头飞边成形良好,飞边表面光滑根部无明显缺陷存在;焊态条件下焊缝组织为典型的魏氏组织结构特征,热处理后焊缝组织析出弥散的针状α相,随着热处理温度的升高析出的针状α相逐渐长大粗化,致使接头冲击和断裂性能先上升后下降;接头拉伸性能与TC4-DT母材相当;700℃/3 h热处理接头、母材高周疲劳性能试验结果表明,接头的疲劳极限达到558 MPa,与TC4-DT基体相当,焊缝组织细化是提高接头疲劳极限的重要原因.