Dielectric and electromagnetic wave absorption properties of reduced graphene oxide/barium aluminosilicate glass–ceramic composites

BaAl₂Si₂O₈ (BAS) glass–ceramic powders were prepared by sol–gel method. Graphene oxide (GO)/BAS mixture powders were prepared by a simple mixing process of GO and BAS. Dense and uniform reduced graphene oxide (RGO)/BAS composites were fabricated by the hot-pressing of GO/BAS, which was accompanied by the in-situ thermal reduction of GO. Microstructure, phase composition, dielectric and electromagnetic wave (EM) absorption properties of RGO/BAS were investigated. The results reveal that RGO can promote the hexacelsian-to-celsian phase transformation of BAS. In the frequency range from 8 GHz to 12 GHz, the complex permittivity of RGO/BAS increases with increasing RGO content. The composite with 1.5 wt% of RGO shows good EM absorbing ability. When the sample thickness is 2.1 mm, the minimum reflection coefficient (RC) reaches −33 dB, and the effective absorption bandwidth is more than 3.1 GHz.     

Controlled synthesis and electromagnetic wave absorption properties of core-shell Fe3O4@SiO2 nanospheres decorated graphene

Fe₃O₄/reduced graphene oxide (RGO) nanocomposite was synthesized by a simple hydrothermal method and then SiO₂ coated onto Fe₃O₄ by a modified Stӧber method. The transmission electron microscopy and field emission scanning electron microscopy characterization indicate that masses of Fe₃O₄@SiO₂ core-shell structure nanospheres attached to the RGO sheets, and that the thicknesses of SiO₂ shells are about 20–40 nm. The X-ray diffractograms and Raman spectra illustrate that the synthesized samples consist of highly crystallized cubic Fe₃O₄, amorphous SiO₂ and disorderedly stacked RGO sheets. The magnetic hysteresis loops reveal the ferromagnetic behavior of the samples at room temperature. In addition, the Fe₃O₄@SiO₂/RGO paraffin composite exhibit excellent electromagnetic wave absorption properties at room temperature in the frequency range of 2–18 GHz, which are attributed to the effective complementarities between the dielectric loss and magnetic loss. For Fe₃O₄@SiO₂/RGO-1 and Fe₃O₄@SiO₂/RGO-2 nanocomposite, the minimum reflection loss can reach −26.4 dB and −16.3 dB with the thickness of 1.5 mm, respectively. The effective absorption bandwidth of the samples can reach more than 10.0 GHz with the thickness in the range of 1.5–3.0 mm. It is demonstrated that such nanocomposite could be used as a promising candidate in electromagnetic wave absorption area.     

Fabrication of microwave absorbing CoFe2O4 coatings with robust superhydrophobicity on natural wood surfaces

A superhydrophobic wood surface with microwave absorption property was prepared based on the formation of CoFe₂O₄ nanoparticles and subsequent hydrophobization using fluorinated alkylsilane (FAS). Meanwhile, sticky epoxy resin was worked as a caking agent by adhering abundant of CoFe₂O₄ nanoparticles to wood surface. The as-prepared superhydrophobic coatings on wood maintain stable superhydrophobicity after suffering a significant abrasion. Moreover, the complex permeability and permittivity of the coated wood composites were measured in the frequency range of 2–18 GHz by vector network analysis. The microwave absorption properties were elucidated by the traditional coaxial line method. The results show that the as-prepared wood composites have excellent microwave absorption properties at the frequency of 16 GHz, and the minimum reflection loss can reach −12.3 dB. The approach presented may provide further routes for designing outdoor wood wave absorbers with a specified absorption frequency.     

Magnetic reduced graphene oxide nanocomposite as an effective electromagnetic wave absorber and its absorbing mechanism

A magnetic reduced graphene oxide (MRGO) composite consisting of graphene oxide and Fe₃O₄ particles in the range of 5–20 nm has been prepared by the one-pot hydrothermal process. RGO nanosheets provide flexible substrates for nanoparticle decoration, while Fe₃O₄ nanoparticles can also effectively prevent nanosheets to restack each other. Compared with previously literature, the synthesized RGO-Fe₃O₄ composite exhibits excellent electromagnetic wave absorption. The minimum reflection loss (R_L) value of −49.05 dB has been observed at 14.16 GHz with a thickness of 2.08 mm. The absorption bandwidth (R_L<−10 dB) corresponding to the minimum R_L is 4.60 GHz. The electromagnetic wave absorption properties of the RGO-Fe₃O₄ composite have been interpreted through the quarter-wavelength matching model.     

Controlled synthesis of Fe3O4@SnO2/RGO nanocomposite for microwave absorption enhancement

A ternary nanocomposite of Fe₃O₄@SnO₂/reduced graphene oxide (RGO) with different contents of SnO₂ nanoparticles was synthesized by a simple and efficient three-step method. The transmission electron microscopy and field emission scanning electron microscopy characterization display that plenty of Fe₃O₄@SnO₂ core–shell structure nanoparticles are well distributed on the surface of RGO sheets. The X-ray diffractograms show that the products consist of highly crystallized cubic Fe₃O₄, tetragonal SnO₂ and disorderedly stacked RGO sheets. The magnetic hysteresis measurement reveals the ferromagnetic behavior of the products at room temperature. The microwave absorption properties of paraffin containing 50 wt% products were investigated at room temperature in the frequency range of 2–18 GHz by a vector network analyzer. The electromagnetic data show that the maximum reflection loss is −45.5 dB and −29.5 dB for Fe₃O₄@SnO₂/RGO-1 and Fe₃O₄@SnO₂/RGO-2 nanocomposite, respectively. Meanwhile, the reflection loss less than −10 dB is up to 14.4 GHz and 13.8 GHz for Fe₃O₄@SnO₂/RGO-1 and Fe₃O₄@SnO₂/RGO-2 nanocomposite, respectively. It is believed that such nanocomposite could be used as promising microwave absorbers.     

Synthesis of hierarchical core-shell NiFe2O4@MnO2 composite microspheres decorated graphene nanosheet for enhanced microwave absorption performance

A ternary functional composite NiFe₂O₄@MnO₂@graphene was synthesized successfully via a facile method. The phase constitution, microstructures, morphologies and chemical compositions of the samples were investigated by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), Brunauer-Emmett-Teller (BET) and X-ray photoelectron spectroscopy (XPS). It was observed that the NiFe₂O₄ nanoparticles were coated by hierarchically MnO₂ shells and distributed on the surface of graphene. Investigations of EM wave absorption indicated that NiFe₂O₄@MnO₂@ graphene composite has the strongest reflection loss of −47.4 dB at 7.4 GHz at the matching thickness of 3 mm, compared to NiFe₂O₄ and NiFe₂O₄@MnO₂, and its maximum absorption bandwidth (<−10 dB) is 4.3 GHz (from 5.1 to 9.4 GHz). The enhanced microwave absorption performance can be attributed to the hierarchical structure of MnO₂, void space between MnO₂ and graphene, and better impedance matching of ternary composite. The above results indicate that the novel hierarchical NiFe₂O₄@MnO₂@graphene composite, with intense absorption and wide absorption bandwidth, would be a promising absorber with less EM wave interference.     

Fabrication and microwave absorption properties of magnetite nanoparticle–carbon nanotube–hollow carbon fiber composites

Absorbents with “tree-like” structures, which were composed of hollow porous carbon fibers (HPCFs) acting as “trunk” structures, carbon nanotubes (CNTs) as “branch” structures and magnetite (Fe₃O₄) nanoparticles playing the role of “fruit” structures were prepared by chemical vapor deposition technique and chemical reaction. Microwave reflection loss, permittivity and permeability of Fe₃O₄–CNTs–HPCFs composites were investigated in the frequency range of 2–18 GHz. It was proven that prepared absorbents possessed the excellent electromagnetic wave absorbing performances. The bandwidth with a reflection loss less than −15 dB covers a wide frequency range from 10.2 to 18 GHz with the thickness of 1.5–3.0 mm, and the minimum reflection loss is −50.9 dB at 14.03 GHz with a 2.5 mm thick sample layer. Microwave absorbing mechanism of the Fe₃O₄–CNTs–HPCFs composites is concluded as dielectric polarization and the synergetic interactions exist between Fe₃O₄ and CNTs–HPCFs.     

Microwave absorbing properties of a thermally reduced graphene oxide/nitrile butadiene rubber composite

Reduced graphene oxide (RGO) with a layered and porous structure was synthesized by thermal exfoliation of graphite oxide. Synthesized RGO is very light weight and flaky. The formation of RGO was studied using Fourier transform infrared and Raman spectroscopies, X-ray diffraction and scanning electron microscopy. Composites were prepared by dispersing 2%, 4% and 10% by weight of the synthesized RGO into nitrile butadiene rubber (NBR) matrix. Microwave absorption properties of RGO/NBR composites were investigated by measuring their complex permittivity and permeability by using waveguide method. Simulation studies show that 10 wt.% of graphene oxide in NBR matrix exhibits high values of reflection loss (>10 dB) over a wide frequency range 7.5–12 GHz and maximum loss is 57 dB at 9.6 GHz at a thickness of 3 mm.     

Double-layer electromagnetic wave absorber based on barium titanate/carbon nanotube nanocomposites

The electromagnetic wave absorption properties of double-layer barium titanate/carbon nanotube (BTO/CNT) nanocomposites were evaluated. The BTO/CNT nanomaterials were characterized using X-ray diffraction, X-ray photoelectron spectroscopy, transmission electron microscopy, and field emission scanning electron microscopy. The reflection loss (R.L.) of the samples was calculated based on the measured complex permittivity and permeability. The minimum R.L. of single-layer BTO/CNT 30 wt% nanocomposites sample with a thickness of 1.1 mm reached ~−30.3 dB (over 99.9% absorption) at 13.8 GHz, and the bandwidth of the reflection loss less than −10 dB (over 90% absorption) was 1.5 GHz. The double-layer composites consist of BTO/CNT 30 wt% (absorption layer) with thickness of 1.0 mm and BTO 30 wt% (matching layer) with thickness of 0.3 mm showed a minimum R.L. of ~−63.7 dB (over 99.9999% absorption) at 13.7 GHz, and the bandwidth of the reflection loss less than −10 dB was 1.7 GHz. Wider response bandwidth, >1.7 GHz also can be achieved with different designs of double-layer absorbers. The R.L. significantly improved and wider response bandwidth can be obtained with double-layer composites. The capability to modulate the absorption and bandwidth of these samples to suit various applications in different frequency bands indicates that these nanocomposites could be an excellent electromagnetic wave absorber.     

Electromagnetic wave absorption properties of graphene modified with carbon nanotube/poly(dimethyl siloxane) composites

By using a catalytic growth procedure, carbon nanotubes (CNTs) are in situ formed on reduced graphene oxide (RGO) sheet at 600 °C. CNTs growing on RGO planes through covalent C–C bond possess lower interfacial contact electrical resistance. As a hybrid structure, the CNTs/graphene (CNT/G) are well dispersed into poly (dimethyl siloxane). The hybrid combining electrically lossy CNTs and RGO, which disperses in electrically insulating matrix, constructs an electromagnetic wave (EM) absorbing material with ternary hierarchical architecture. The interfacial polarization in heterogeneous interface plays an important role in absorbing EM power. When the filler loading is 5 wt.% and thickness of absorber is 2.75 mm, the minimum value of reflection coefficient and the corresponding frequency are −55 dB and 10.1 GHz, and the effective absorption bandwidth reaches 3.5 GHz. Therefore, combining the CNTs and graphene sheet into three-dimensional structures produces CNT/G hybrids that can be considered as an effective route to design light weight and high-performance EM absorbing material, while the effective EM absorption frequency can be designed.     

The effect of GO loading on electromagnetic wave absorption properties of Fe3O4/reduced graphene oxide hybrids

Ideal electromagnetic absorbing materials with lightweight and high efficiency have broad application outlook in military and civil fields. In this work, a 3D nanostructure material by hybridizing Fe₃O₄ nanocrystals and reduced graphene oxide (Fe₃O₄/rGO) were synthesized through an environmental-friendly one-pot solvothermal method. The effect of GO loading on electromagnetic (EM) wave absorption characteristic of Fe₃O₄/rGO was investigated. The introduction of rGO sheets not only prevented Fe₃O₄ from agglomerating, also improved the absorption performance of Fe₃O₄/rGO hybrids. With an appropriate addition, Fe₃O₄/rGO obtained a minimum reflection loss (RL) of −22.7 dB and the absorption bandwidth was 3.13 GHz (90% absorption).     

Facile synthesis of Co0.5Zn0.5Fe2O4 nanoparticles decorated reduced graphene oxide hybrid nanocomposites with enhanced electromagnetic wave absorption properties

Herein, reduced graphene oxide/cobalt-zinc ferrite (RGO/Co_0.5Zn_0.5Fe₂O₄) hybrid nanocomposites were fabricated by a facile hydrothermal strategy. Results revealed that the contents of RGO could affect the micromorphology, electromagnetic parameters and electromagnetic wave absorption properties. As the contents of RGO increased in the as-synthesized hybrid nanocomposites, the dispersibility of the particles was improved. Meanwhile, numerously ferromagnetic Co_0.5Zn_0.5Fe₂O₄ particles were evenly anchored on the wrinkled surfaces of flaky RGO. Besides, the obtained hybrid nanocomposites exhibited superior electromagnetic absorption in both X and Ku bands, which was achieved by adjusting the RGO contents and matching thicknesses. Significantly, when the content of RGO was 7.4 wt%, the binary nanocomposites showed the optimal reflection loss of -73.9 dB at a thickness of 2.2 mm and broadest effective absorption bandwidth of 6.0 GHz (12.0–18.0 GHz) at a thin thickness of merely 2.0 mm. The enhanced electromagnetic absorption performance was primarily attributed to the multiple polarization effects, improved conduction loss caused by electron migration, and magnetic loss derived from ferromagnetic Co_0.5Zn_0.5Fe₂O₄ nanoparticles. Our results could provide inspiration for manufacturing graphene-based hybrid nanocomposites as high-efficient electromagnetic wave absorbers.     

Highly efficient synthesis of graphene/MnO2 hybrids and their application for ultrafast oxidative decomposition of methylene blue

A highly efficient method has been reported to fabricate the reduced graphene oxide/MnO₂ (RGO/MnO₂) hybrid materials, a kind of catalysts for oxidative decomposition of methylene blue (MB). The pristine suspension of graphene oxide/manganese sulfate (GO/MnSO₄) produced by the modified Hummers method is in situ transformed into GO/MnO₂ composites in combination with KMnO₄, and then further into RGO/MnO₂ composites by means of glucose-reduction. It is found that MnO₂ nanoparticles with the size of 20–30 nm are uniformly distributed in the structure of RGO. A series of composites with different mass ratios of RGO to MnO₂ has been proved superior catalytic activities, much higher than that of the bare MnO₂ for decomposition of MB dye in the presence of H₂O₂. Typically, 50 mL of MB (50 mg L⁻¹) can be completely decolorized and nearly 66% mineralized at 50 °C in 5 min with 10 mg of the RGO/MnO₂ hybrid. According to the adsorption–oxidation–desorption mechanism, the high activity of RGO/MnO₂ composites for decomposition of MB is closely related to the positive synergistic effect of RGO and MnO₂ with the assistance of H₂O₂.     

One-step microwave-assisted synthesis of Sb2O3/reduced graphene oxide composites as advanced anode materials for sodium-ion batteries

Sb₂O₃/reduced graphene oxide (RGO) composites were prepared through a facile microwave-assisted reduction of graphite oxide in SbCl₃ precursor solution, and investigated as anode material for sodium-ion batteries (SIBs). The experimental results show that a maximum specific capacity of 503 mA h g⁻¹ is achieved after 50 galvanostatic charge/discharge cycles at a current density of 100 mA g⁻¹ by optimizing the RGO content in the composites and an excellent rate performance is also obtained due to the synergistic effect between Sb₂O₃ and RGO. The high capacity, superior rate capability and excellent cycling performance of Sb₂O₃/RGO composites demonstrate their excellent sodium-ion storage ability and show their great potential as electrode materials for SIBs.     

Dielectric and microwave absorption properties of polymer derived SiCN ceramics annealed in N2 atmosphere

Porous SiCN ceramics were successfully fabricated by pyrolysis of a kind of polysilazane. The effects of annealing temperature on the microstructure evolution, direct-current electrical conductivity, dielectric properties, and microwave absorption properties of SiCN in the frequency range 8.2–12.4 GHz (X-band) were investigated. With the increase of annealing temperature, SiC, Si₃N₄ and free carbon nanodomains are gradually formed in the SiCN. Both the SiC and free carbon nanodomains lead to the increases of the complex relative permittivity and loss tangent of SiCN. With the increase of the annealing temperature, the average real permittivity, imaginary permittivity and loss tangent increase from 4.4, 0.2 and 0.05 to 13.8, 6.3 and 0.46, respectively. The minimum reflection coefficient and the frequency bandwidth below −10 dB for SiCN annealed at 1500 °C are −53 dB and 3.02 GHz, indicating good microwave absorption properties.     

Controllable synthesis of porous CxNy nanofibers with enhanced electromagnetic wave absorption property

Porous C_xN_y nanofibers are controllably synthesized by a simple two-step method. The prepared samples possess uniform micropores and a chemical composition of C_0.73 N_0.27 with a surface area of 329 m² g⁻¹. The obtained C_xN_y nanofibers exhibit remarkable electromagnetic (EM) wave absorption properties when compared with conventional one-dimensional carbon materials. The minimum reflection loss (RL) reaches −36 dB at 2.7 GHz when the ratio of the C_xN_y absorbent added in paraffin matrix is only 1:3. The bandwidth of the RL below −10 dB covers 7.7 GHz (8.1–15.8 GHz) at the sample thickness of 2.5 mm. A possible EM wave loss mechanism was proposed in detail. The multiple reflection and dielectric loss could govern the excellent EM absorption leading the product to a probable application in stealth materials.     

Cation distribution and magnetic analysis of wideband microwave absorptive CoxNi1−xFe2O4 ferrites

Co_xNi_1−xFe₂O₄ ferrites (x=0, 0.2, 0.4, 0.4, 0.6, 0.8 and 1) were prepared by a sol-gel auto-combustion method. The samples were structurally characterized by X-ray diffractometry (XRD), field emission scanning electron microscopy (FE-SEM), energy dispersive X-ray analysis (EDX), and Fourier transform infrared spectroscopy (FTIR). The XRD patterns confirmed single phase formation of spinel structure. Cation distribution estimated from XRD data suggested the mixed spinel structure of ferrite. The EDX analysis was in good agreement with the nominal composition. The results of FTIR analysis indicated that the functional groups of Co-Ni spinel ferrite were formed during the combustion process. According to FE-SEM micrographs, by addition of cobalt ion the average particle size of substituted nickel ferrite was gradually became smaller from 450 nm to 280 nm. Magnetic measurement using vibrating sample magnetometer (VSM) showed an increase in saturation magnetization and coercivity by Co²⁺ substitution in nickel ferrite. For Co_0.8Ni_0.2Fe₂O₄ sample, M_s and H_c reaches as high as 93 emu/g and 420 Oe, respectively. The reflection loss properties of the nanocomposites were investigated in the frequency range of 8–12 GHz, using vector network analyzer (VNA). Cobalt substitution could enhance reflection loss of NiFe₂O₄ ferrite. The maximum reflection loss value of the Co²⁺ substituted Ni ferrite was ~ −26 dB (i.e. over 99% absorption) at 9.7 GHz with bandwidth of 4 GHz (RL<– 10 dB) through the entire frequency range of X-band.     

Hollow polyaniline/Fe3O4 microsphere composites: Preparation,characterization, and applications in microwave absorption

Hollow polyaniline/Fe₃O₄ microsphere composites with electromagnetic properties were successfully prepared by decorating the surface of hollow polyaniline/sulfonated polystyrene microspheres with various amounts of Fe₃O₄ magnetic nanoparticles using sulfonated polystyrene (SPS) as hard templates and then removing the templates with tetrahydrofuran (THF). The synthesized hollow microsphere composites were characterized by FT-IR, UV/Vis spectrophotometry, SEM, XRD, elemental analysis, TGA, and measurement of their magnetic parameters. Experimental results indicated that the microspheres were well-defined in size (1.50–1.80 μm) and shape, and that they were superparamagnetic with maximum saturation magnetization values of 3.88 emu/g with a 12.37 wt% content of Fe₃O₄ magnetic nanoparticles. Measurements of the electromagnetic parameters of the samples showed that the maximum bandwidth was 8.0 GHz over ?10 dB of reflection loss in the 2–18 GHz range when the Fe₃O₄ content in the hollow polyaniline/Fe₃O₄ microsphere composites was 7.33 wt%.     

Using Al2O3 defect levels to enhance the photoelectrocatalytic activity of SnS2 nanosheets

Hexagonal SnS₂ nanosheets and Al₂O₃/SnS₂ composites were fabricated via a one-step hydrothermal synthesis method. The investigation indicates that hexagonal SnS₂ with diameters of 100–200 nm are well dispersed on the surface of Al₂O₃. The band gap of SnS₂ after coupling with 11 wt%-Al₂O₃ is reduced by 0.042 eV compared with the pure SnS_2. The composite with 11 wt%-Al₂O₃ shows the highest photocurrent density of 37 μA/cm² at 0.49 V (vs. Ag/AgCl) under visible light (λ>420 nm), which is approximately 1.2 times that of the pure SnS₂ nanosheets. Photoelectrocatalytic measurements demonstrate that an appropriate amount of Al₂O₃ can enhance the photoelectrocatalytic efficiency of SnS₂. The 11 wt%-Al₂O₃/SnS₂ composite (AOSS-11) can degrade 85.9% MB after 3 h under visible light illumination at an applied potential of 0.49 V (vs. Ag/AgCl). The highly effective photoelectrocatalytic activity of the Al₂O₃/SnS₂ composite is attributed to the efficient separation of photoinduced electron-hole pairs based on the defect levels. This work may provide a new design idea for constructing the effective SnS₂-based photocatalysts with other defective semiconductors.     

Flexible polymer composites with enhanced wave absorption properties based on beta-manganese dioxide nanorods and PVDF

Beta-manganese dioxide (β-MnO₂) nanorods have been fabricated on a large scale by a simple hydrothermal process in a wild condition. Several characterizations such as XRD, SEM, TEM and FESEM have been employed. The wave absorption properties of β-MnO₂/PVDF nanocomposites have been investigated. The results indicated that the β-MnO₂/PVDF nanocomposites exhibit enhanced wave absorption properties. The minimum reflection loss of the β-MnO₂/PVDF nanocomposite reaches − 30.1 dB (> 99.9% attenuation) at 8.16 GHz with a filler loading of 40 wt.%, and the frequency bandwidth less than –10 dB is from 7.12 to 9.20 GHz. The main microwave absorbing mechanism has been also discussed.