Effect of phosphoric acid etching on the shear bond strength of two self-etch adhesives

Objective:

To evaluate the effect of optional phosphoric acid etching on the shear bond strength (SBS) of two self-etch adhesives to enamel and dentin.

Material and Methods:

Ninety-six bovine mandibular incisors were ground flat to obtain enamel and dentin substrates. A two-step self-etch adhesive (FL-Bond II) and a one-step self-etch adhesive (BeautiBond) were applied with and without a preliminary acid etching to both the enamel and dentin. The specimens were equally and randomly assigned to 4 groups per substrate (n=12) as follows: FL-Bond II etched; FL-Bond II un-etched; BeautiBond etched; BeautiBond un-etched. Composite cylinders (Filtek Z100) were bonded onto the treated tooth structure. The shear bond strength was evaluated after 24 hours of storage (37ºC, 100% humidity) with a testing machine (Ultra-tester) at a speed of 1 mm/min. The data was analyzed using a two-way ANOVA and post-hoc Tukey''s test with a significance level of p<0.05. A field emission scanning electron microscope was used for the failure mode analysis.

Results:

Both adhesives evidenced a significant decrease in the dentin SBS with the use of an optional phosphoric acid-etching step (p<0.05). Preliminary phosphoric acid etching yielded significantly higher enamel SBS for FL-Bond II (p<0.05) only, but not for BeautiBond. FL-Bond II applied to un-etched dentin demonstrated the highest mean bond strength (37.7±3.2 MPa) and BeautiBond applied to etched dentin showed the lowest mean bond strength (18.3±6.7 MPa) among all tested groups (p<0.05).

Conclusion:

The use of a preliminary acid-etching step with 37.5% phosphoric acid had a significant adverse effect on the dentin bond strength of the self-etch adhesives evaluated while providing improvement on the enamel bond strength only for FL-Bond II. This suggests that the potential benefit that may be derived from an additional etching step with phosphoric acid does not justify the risk of adversely affecting the bond strength to dentin.     

INFLUENCE OF LIGHT ENERGY DENSITY ON HEAT GENERATION DURING PHOTOACTIVATION OF DENTAL COMPOSITES WITH DIFFERENT DENTIN AND COMPOSITE THICKNESS

Objective:

The aim of this study was to determine the influence of different energy densities on the heat generated during photoactivation of Filtek Z250 (3M/ESPE) and Z100 (3M/ESPE) composite resins with different dentin and composite thickness.

Material and Methods:

The temperature increase was registered with a type-K thermocouple connected to a digital thermometer (Iopetherm 46). A chemically polymerized acrylic resin base was prepared to serve as a guide for the thermocouple and as a support for 0.5-, 1.0-, and 1.5-mm-thick bovine dentin discs. Circular elastomer molds (1.0 mm-height x 3.0-mm diameter or 2.0-mm height x 3.0-mm diameter) were adapted on the acrylic resin base to standardize the composite resin thickness. A conventional halogen light-curing unit (XL 2500, 3M/ESPE) was used with light intensity of 700 mW/cm². Energy density was calculated by the light intensity applied during a certain time with values of 28 J/cm² for Z100 and 14 J/cm² for Filtek Z250. The temperature change data were subjected to three-way ANOVA and Tukey''s test at 5% level.

Results:

The higher energy density (Z100) promoted greater temperature increase (p<0.05) than the lower energy density (Filtek Z250). For both composites and all composite thicknesses, the lowest dentin thickness (0.5 mm) yielded significantly higher (p<0.05) temperature increase than the other two dentin thicknesses. The 1-mm-thick composite resin layer yielded significantly higher (p<0.05) temperature changes for both composites and all dentin thicknesses.

Conclusions:

Temperature increase was influenced by higher energy density and dentin/composite thickness.     

Radiodensity evaluation of dental impression materials in comparison to tooth structures

In the most recent decades, several developments have been made on impression materials'' composition, but there are very few radiodensity studies in the literature. It is expected that an acceptable degree of radiodensity would enable the detection of small fragments left inside gingival sulcus or root canals.

Objective

The aim of this study was to determine the radiodensity of different impression materials, and to compare them to human and bovine enamel and dentin

Material and Methods

Twenty-five impression materials, from 5 classes, were studied: addition and condensation silicones, polyether, polysulfides and alginates. Five 1-mm-thick samples of each material and tooth structure were produced. Each sample was evaluated 3 times (N=15), being exposed to x-ray over a phosphor plate of Digora digital system, and radiodensity was obtained by the software Digora for Windows 2.5 Rev 0. An aluminum stepwedge served as a control. Data were subjected to Kruskal- Wallis and Dunn''s method (α=0.05).

Results

Different materials and respective classes had a different behavior with respect to radiodensity. Polysulfides showed high values of radiodensity, comparable to human enamel (p>0.05), but not to bovine enamel (p<0.05). Human dentin was similar only to a heavybody addition silicon material, but bovine dentin was similar to several materials. Generally, heavybody materials showed higher radiodensity than light-body ones (p<0.05).

Conclusion

Impression materials'' radiodensity are influenced by composition, and almost all of them would present a difficult detection against enamel or dentin background in radiographic examinations.     

DESENSITIZING BIOACTIVE AGENTS IMPROVES BOND STRENGTH OF INDIRECT RESIN-CEMENTED RESTORATIONS: PRELIMINARY RESULTS

Objective:

The aim of this study was to assess the bond strength of indirect composite restorations cemented with a resin-based cement associated with etch-and-rinse and self-etching primer adhesive systems to dentin treated or not with a bioactive material.

Materials and Method:

Twenty bovine incisor crowns had the buccal enamel removed and the dentin ground flat. The teeth were assigned to 4 groups (n=5): Group I: acid etching + Prime & Bond NT (Dentsply); Group II: application of a bioactive glass (Biosilicato®)+ acid etching + Prime & Bond NT; Group III: One-up Bond F (J Morita); Group IV: Biosilicato® + One-up Bond F. Indirect composite resin (Artglass, Kulzer) cylinders (6x10mm) were fabricated and cemented to the teeth with a dualcure resin-based cement (Enforce, Dentsply). After cementation, the specimens were stored in artificial saliva at 37^oC for 30 days and thereafter tested in tensile strength in a universal testing machine (EMIC) with 50 kgf load cell at a crosshead speed of 1 mm/min. Failure modes were assessed under scanning electron microscopy. Data were analyzed statistically by ANOVA and Tukey''s test (95% level of confidence).

Results:

Groups I, II and III had statistically similar results (p>0.05). Group IV had statistically significant higher bond strength means (p<0.05) than the other groups. The analysis of the debonded surfaces showed a predominance of adhesive failure mode for Group III and mixed failure mode for the other groups.

Conclusion:

The use of desensitizing agent did not affect negatively the bonding of the indirect composite restorations to dentin, independently of the tested adhesive systems.     

Evaluation of bond strength of silorane and methacrylate based restorative systems to dentin using different cavity models

Objective

The aim of this in vitro study was to evaluate the microtensile bond strength (µTBS) to dentin of two different restorative systems: silorane-based (P90), and methacrylate-based (P60), using two cavity models.

Material and Methods

Occlusal enamel of 40 human third molars was removed to expose flat dentin surface. Class I cavities with 4 mm mesial-distal width, 3 mm buccal-lingual width and 3 mm depth (C-factor=4.5) were prepared in 20 teeth, which were divided into two groups (n=10) restored with P60 and P90, bulk-filled after dentin treatment according to manufacturer''s instructions. Flat buccal dentin surfaces were prepared in the 20 remaining teeth (C-factor=0.2) and restored with resin blocks measuring 4x3x3 mm using the two restorative systems (n=10). The teeth were sectioned into samples with area between 0.85 and 1.25 mm² that were submitted to µTBS testing, using a universal testing machine (EMIC) at speed of 0.5 mm/min. Fractured specimens were analyzed under stereomicroscope and categorized according to fracture pattern. Data were analyzed using ANOVA and Tukey Kramer tests.

Results

For flat surfaces, P60 obtained higher bond strength values compared with P90. However, for Class I cavities, P60 showed significant reduction in bond strength (p<0.05). No statistical difference between restorative systems was shown for Class I cavity model (p>0.05), or between Class I Cavity and Flat Surface group, considering P90 restorative system (p>0.05). Regarding fracture pattern, there was no statistical difference among groups (p=0.0713) and 56.3% of the fractures were adhesive.

Conclusion

It was concluded that methacrylate-based composite µTBS was influenced by cavity models, and the use of silorane-based composite led to similar bond strength values compared to the methacrylate-based composite in cavities with high C-factor.     

Marginal adaptation of class V composite restorations submitted to thermal and mechanical cycling

Objective:

This study evaluated the effect of the margin location and an adhesive system on the marginal adaptation of composite restorations.

Material and Methods:

Class V cavities were prepared in bovine teeth with the gingival margin on the dentin and the incisal margin on the enamel. The cavities were restored with a micro-hybrid composite resin using an etch-and-rinse [Single Bond 2 (SB)] or a self-etching adhesive [Clearfil SE Bond (CL)]. After finishing and polishing the restorations, epoxy replicas were prepared. The marginal adaptation was analyzed using scanning electronic microscopy (SEM, 500 x magnification). The higher gap width in each margin was recorded (T0). After the first evaluation, the samples were submitted to thermal cycling (2,000 cycles of 5ºC±2ºC followed by 55ºC±2ºC - T1) and mechanical cycling (100,000 cycles of 50 kN and 2 Hz - T2). Replicas of samples were rebuilt after each cycling and analyzed under SEM. The data were submitted to Mann-Whitney, Wilcoxon and Friedman testing (a=0.05).

Results:

The SB presented higher gaps in the dentin than the enamel, while there was no difference between the substrate for the CL. In the dentin, the CL showed better marginal sealing than the SB. The opposite occurred in the enamel. There were no significant differences between the baseline, thermal and mechanical cycling for any experimental condition.

Conclusions:

The outcomes of the present study showed that the adhesive system and margin location have an important effect on the marginal adaptation of composite restorations.     

EFFECT OF 2% IODINE DISINFECTING SOLUTION ON BOND STRENGTH TO DENTIN

Introduction:

Disinfection of dentin surfaces is desirable so long as it does not interfere with subsequent bonding of adhesive resins.

Objective:

To test the null hypothesis that bond strengths to dentin are not affected by previous application of an iodine disinfecting solution.

Materials and Methods:

Twenty-four extracted non-carious molars were selected. Occlusal enamel was removed producing a flat dentin substrate. Test teeth were all treated with 2% Iodine disclosing/disinfecting solution (I₂DDS) for 20 sec and rinsed for 20 sec followed by the application of self- or total- etching bonding systems, generating five adhesive groups (n=3): Single Bond;; Prime & Bond NT; Clearfil SE Bond; Opti-Bond Plus. The control groups (n=3 per adhesive) had no disclosing/disinfectant application prior to adhesive application. A 4-mm thick resin restoration was built up on each tooth for microtensile testing. Statistical analyses between experimental and control groups were performed by student''s t-test (α = 0.05).

Results:

In general, experimental groups (previously treated with I₂DDS) showed significantly lower bond strength values when compared with their respective controls (p<0.05), except for group Prime &Bond I₂ that did not significantly differ from its control (p>0.05).

Conclusion:

Acetone-base adhesive systems seem not to be affected by the application of I₂DDS prior to etching and bonding procedures.     

Effectiveness of plant-derived proanthocyanidins on demineralization on enamel and dentin under artificial cariogenic challenge

Dental caries is considered a disease of high prevalence and a constant problem in public health. Proanthocyanidins (PAs) are substances that have been the target of recent studies aiming to control or treat caries.

Objective

The aim of this in vitro study was to evaluate the efficacy of a treatment with grape seed extract, under cariogenic challenge, to minimize or even prevent the onset of caries in the enamel and dentin.

Material and Methods

Blocks of enamel and dentin (6.0x6.0 mm) were obtained from bovine central incisors, polished, and selected by analysis of surface microhardness (SH). The blocks were randomly divided into 3 groups (n=15), according to the following treatments: GC (control), GSE (grape seed extract), GF (fluoride – 1,000 ppm). The blocks were subjected to 6 daily pH cycles for 8 days. Within the daily cycling, the specimens were stored in buffered solution. The blocks were then analyzed for perpendicular and surface hardness and polarized light microscopy.

Results

The means were subjected to statistical analysis using the ANOVA and Fisher’s PLSD tests (p<0.05). For enamel SH, GF showed the highest hardness values. In the dentin, GF was also the one that showed higher hardness values, followed by GSE. Regarding the cross-sectional hardness values, all groups behaved similarly in both the enamel and dentin. The samples that were treated with GSE and fluoride (GF) showed statistically higher values than the control.

Conclusion

Based on the data obtained in this in vitro study, it is suggested that grape seed extract inhibits demineralization of artificial carious lesions in both the enamel and dentin, but in a different scale in each structure and in a smaller scale when compared to fluoride.     

Effect of Endodontic Irrigating Solutions on the Micro Push-out Bond Strength of a Fibre Glass Dowel

Purpose

To evaluate the effect of different endodontic irrigating solutions on the micro push-out bond strength of a fiber glass dowel.

Material and Methods

Seventy 16-mm long root segments of bovine incisors were prepared and randomly assigned to 7 groups (n=10) according to the type of irrigating solution used prior to the cementation of the intra-radicular fiber glass dowels: G1: 5.25% NaOCl + 17% EDTA; G2: 5.25% NaOCl; G3: 17% EDTA; G4: 2% chlorhexidine gel; G5: 70% alcohol; G6: 11.5% polyacrylic acid; and G7: saline (control). After treatment of intracanal dentin, the glass fibre dowels were cemented with self-adhesive resin cement (RelyX Unicem). Six slices with the thickness of 1.00 ± 0.05 mm were obtained from each tooth at the coronal, middle and apical root thirds (2 slices per third) using a low-speed saw. Micro push-out tests were performed at a crosshead speed of 0.5mm/min and the data (MPa) were analyzed statistically by ANOVA and Tukey’s and Dunnett’s tests.

Results

There were statistically significant differences (p<0.0001) among the irrigating solutions, but no significant difference (p=0.0591) was found among the root thirds. G5 presented the highest bond strength mean of all groups (p<0.0001). The use of 70% alcohol increased the adhesion values by 53% compared to the group control.

Conclusion

The use of 70% alcohol increased the bond strength of the fiber glass dowel to the dentin walls. However, the push-out bond strength between the dowel and the root dentin was not affected by the root third (coronal, middle and apical).Key words: Tensile Strength, Post and Core Technique, Root Canal Irrigants     

MARGINAL ADAPTATION AND PERFORMANCE OF BIOACTIVE DENTAL RESTORATIVE MATERIALS IN DECIDUOUS AND YOUNG PERMANENT TEETH

Objective:

The aim of this study was to investigate the adaptation of different types of restorations towards deciduous and young permanent teeth.

Materials and Methods:

Class V cavities were prepared in deciduous and young permanent teeth and filled with different materials (a conventional glass-ionomer, a resin-modified glass-ionomer, a poly-acid-modified composite resin and a conventional composite resin). Specimens were aged in artificial saliva for 1, 6, 12 and 18 months, then examined by SEM.

Results:

The composite resin and the polyacid-modified composite had better marginal adaptation than the glass-ionomers, though microcracks developed in the enamel of the tooth. The glass-ionomers showed inferior marginal quality and durability, but no microcracking of the enamel. The margins of the resin-modified glass-ionomer were slightly superior to the conventional glass-ionomer. Conditioning improved the adaptation of the composite resin, but the type of tooth made little or no difference to the performance of the restorative material. All materials were associated with the formation of crystals in the gaps between the filling and the tooth; the quantity and shape of these crystals varied with the material.

Conclusions:

Resin-based materials are generally better at forming sound, durable margins in deciduous and young permanent teeth than cements, but are associated with microcracks in the enamel. All fluoride-releasing materials give rise to crystalline deposits.     

EFFECT OF FLUORIDE-CONTAINING DESENSITIZING AGENTS ON THE BOND STRENGTH OF RESIN-BASED CEMENTS TO DENTIN

Objective:

The objective of this study was to evaluate the effect of desensitizing agents containing different amounts of fluoride on the shear bond strength of a dual polymerized resin cement and a resin-modified glass ionomer cement (RMGIC) to dentin.

Material and Methods:

One hundred human molars were mounted in acrylic resin blocks and prepared until the dentin surface was exposed. The specimens were treated with one of four desensitizing agents: Bifluorid 12, Fluoridin, Thermoline and PrepEze. The remaining 20 specimens served as untreated controls. All groups were further divided into 2 subgroups in which a dual polymerized resin cement (Bifix QM) or a resin-modified glass ionomer cement (AVANTO) was used. The shear bond strength (MPa) was measured using a universal testing machine at a 0.5 mm/min crosshead speed. The data were analyzed statistically with a 2-way ANOVA, Tukey HSD test and regression analysis (α=0.05). The effect of the desensitizing agents on the dentin surface was examined by scanning electron microscopy.

Results:

The fluoride-containing desensitizing agents affected the bond strength of the resin-based cements to dentin (p<0.001). PrepEze showed the highest bond strength values in all groups (p<0.001).

Conclusion:

Regression analysis showed a reverse relation between bond strength values of resin cements to dentin and the amount of fluoride in the desensitizing agent (p<0.05).     

Mechanical,antibacterial and bond strength properties of nano-titanium-enriched glass ionomer cement

The use of nanoparticles (NPs) has become a significant area of research in Dentistry.

Objective

The aim of this study was to investigate the physical, antibacterial activity and bond strength properties of conventional base, core build and restorative of glass ionomer cement (GIC) compared to GIC supplemented with titanium dioxide (TiO₂) nanopowder at 3% and 5% (w/w).

Material and Methods

Vickers microhardness was estimated with diamond indenter. Compressive and flexural strengths were analyzed in a universal testing machine. Specimens were bonded to enamel and dentine, and tested for shear bond strength in a universal testing machine. Specimens were incubated with S. mutans suspension for evaluating antibacterial activity. Surface analysis of restorative conventional and modified GIC was performed with SEM and EDS. The analyses were carried out with Kolmogorov-Smirnov, ANOVA (post-hoc), Tukey test, Kruskal-Wallis, and Mann Whitney.

Results

Conventional GIC and GIC modified with TiO₂ nanopowder for the base/liner cement and core build showed no differences for mechanical, antibacterial, and shear bond properties (p>0.05). In contrast, the supplementation of TiO₂ NPs to restorative GIC significantly improved Vickers microhardness (p<0.05), flexural and compressive strength (p<0.05), and antibacterial activity (p<0.001), without interfering with adhesion to enamel and dentin.

Conclusion

GIC supplemented with TiO₂ NPs (FX-II) is a promising material for restoration because of its potential antibacterial activity and durable restoration to withstand the mastication force.     

EFFECT OF AN ADDITIONAL HYDROPHILIC VERSUS HYDROPHOBIC COAT ON THE QUALITY OF DENTINAL SEALING PROVIDED BY TWO-STEP ETCH-AND-RINSE ADHESIVES

Objective:

To test the hypothesis that the quality of the dentinal sealing provided by two-step etch-and-rinse adhesives cannot be altered by the addition of an extra layer of the respective adhesive or the application of a more hydrophobic, non-solvated resin.

Material and Methods:

full-crown preparations were acid-etched with phosphoric acid for 15 s and bonded with Adper Single Bond (3M ESPE), Excite DSC (Ivoclar/Vivadent) or Prime & Bond NT (Dentsply). The adhesives were used according to the manufacturers'' instructions (control groups) or after application to dentin they were a) covered with an extra coat of each respective system or b) coated with a non-solvated bonding agent (Adper Scotchbond Multi-Purpose Adhesive, 3M ESPE). Fluid flow rate was measured before and after dentin surfaces were acid-etched and bonded with adhesives.

Results:

None of the adhesives or experimental treatments was capable to block completely the fluid transudation across the treated dentin. Application of an extra coat of the adhesive did not reduce the fluid flow rate of adhesive-bonded dentin (p>0.05). Conversely, the application of a more hydrophobic non-solvated resin resulted in significant reductions in the fluid flow rate (p<0.05) for all tested adhesives.

Conclusions:

The quality of the dentinal sealing provided by etch-and-rinse adhesives can be significantly improved by the application of a more hydrophobic, non-solvated bonding agent.     

Bond strength to root dentin and fluid filtration test of AH Plus/gutta-percha,EndoREZ and RealSeal systems

Objectives

To investigate the bond strength and seal ability produced by AH Plus/gutta-percha, EndoREZ and RealSeal systems to root canal dentin.

Material and Methods

Sixty extracted single-root human teeth, instrumented manually to size 40, were divided into three groups (n=20) according to the sealer used; G1: AH Plus, G2: EndoREZ, and G3: RealSeal sealers. After filling using the lateral condensation technique, each sealer group was randomly divided into two subgroups according to the tests applied (n=10 for µPush-out test and n=10 for fluid filtration test). A fluid filtration method was used for quantitative evaluation of apical leakage. Four 1-mm-thick slices (cervical and medium level) were obtained from each root sample and a µPush-out test was performed. Failure modes were examined under microscopy at 40x, and a one-way ANOVA was applied to analyze the permeability. Non-parametrical statistics for related (Friedman''s and Wilcoxon''s rank tests) or unrelated samples (Kruskal-Wallis'' and Mann-Whitney''s tests) allowed for comparisons of µPush-out strength values among materials at the different levels. Statistical significance was accepted for p values <.05.

Results

There are no significant differences among fluid filtration of the three sealers. The sealer/core material does not significantly influence the µPush-out bond strength values (F=2.49; p=0.10), although statistically significant differences were detected with regard to root level (Chi²=23.93; p<0.001). AH Plus and RealSeal obtained higher bond strength to intraradicular dentin in the medium root slices.

Conclusions

There are no significant differences between the permeability and global µPush-out bond strength to root canal dentin achieved by AH Plus/gutta-percha, EndoREZ and RealSeal systems.     

Comparison of the effects of TripleGates and Gates-Glidden burs on cervical dentin thickness and root canal area by using cone beam computed tomography

The search for new instruments to promote an appropriate cervical preparation has led to the development of new rotary instruments such as TripleGates. However, to the best of the authors'' knowledge, there is no study evaluating TripleGates effect on the “risk zone” of mandibular molars.

Objectives

: The aim of this study was to evaluate the effects of a crown-down sequence of Gates-Glidden and TripleGates burs on the remaining cervical dentin thickness and the total amount of dentin removed from the root canals during the instrumentation by using cone beam computed tomography. The number of separated instruments was also evaluated.

Material and Methods

: Mesial roots of 40 mandibular first molars were divided into 2 equal groups: crown-down sequence of Gates-Glidden (#3, #2, #1) and TripleGates burs. Cervical dentin thickness and canal area were measured before and after instrumentation by using cone beam computed tomography and image analysis software. Student’s t-test was used to determine significant differences at p<0.05.

Results

: No significant differences (p>0.05) were observed between the instruments, regarding the root canal area and dentin wall thickness.

Conclusion

: Both tested instruments used for cervical preparation were safe to be used in the mesial root canal of mandibular molars.     

INFLUENCE OF CROWN SHAPE ON ROOT COVERAGE THERAPY

Objectives:

The aim of this study was to evaluate the influence of the crown shape on the outcomes of root coverage procedures.

Material and methods:

Eighty patients with Miller class I gingival recessions in maxillary canines or premolars were selected. The recession areas were treated using the subepithelial connective tissue grafting. The following clinical parameters were analyzed: crown length (CL) and width (CW), recession height and width, probing depth, clinical attachment level, width and thickness of the keratinized tissue and percentage of root coverage achieved. These measurements were recorded at baseline and 6 months after the surgical procedure. The CW/CL ratio was calculated for each tooth and the median obtained (0.83). Patients were then ranked into two groups, according to the shape of the tooth with gingival recession: Group A – square crown shape (CW/CL values above 0.83) and Group B – long and narrow crown shape (CW/CL values below 0.83).

Results:

No statistically significant differences (p>0.05) were found between groups in any of the clinical parameters at baseline. After 6 months, both groups presented improved clinical outcomes for all parameters analyzed compared to baseline (p>0.05). The mean percentages and standard deviations of root coverage achieved in Group A and Group B was 91.37 (16.75) and 85.49 (23.55), respectively (p>0.05).

Conclusions:

Crown shape did not influence the root coverage obtained with the subepithelial connective tissue graft technique.     

Long-term degradation of resin-based cements in substances present in the oral environment: influence of activation mode

Indirect restorations in contact with free gingival margins or principally within the gingival sulcus, where the presence of organic acids produced by oral biofilm is higher, may present faster degradation of the resin-based cement pellicle.

Objectives:

To investigate the degradation of four resin-based cements: Rely X ARC (R), Variolink II (V), enforce (E) and All Cem (A), after immersion in distilled water (DW), lactic acid (LA) and artificial saliva (AS) and to analyze the influence of the activation mode on this response.

Material and Methods:

Two activation modes were evaluated: chemical (Ch) and dual (D). In the dual activation, a two-millimeter thick ceramic disk (IPS empress System) was interposed between the specimen and light-curing unit tip. Specimens were desiccated, immersed in distilled water, artificial saliva and lactic acid 0.1 M at 37ºC for 180 days, weighed daily for the first 7 days, and after 14, 21, 28, 90 and 180 days and were desiccated again. Sorption and solubility (µg/mm³) were calculated based on ISO 4049. The data were submitted to multifactor analysis of variance (MANOVA) and Tukey''s HSD test for media comparisons (α=0.05).

Results:

Sorption was higher after immersion in LA (p<0.05) and increased significantly with time (p<0.05). Sorption was influenced by the activation mode: Ch>D (p<0.05). The lowest solubility was presented by R (p<0.05).

Conclusions:

Lactic acid increased the degradation of resin-based cements. Moreover, the physical component of activation, i.e., light-activation, contributed to a low degradation of resin-based cements.     

Tensile bond strength of indirect composites luted with three new self-adhesive resin cements to dentin

Objective

The aims of this study were to evaluate the tensile bond strengths between indirect composites and dentin of 3 recently developed self-adhesive resin cements and to determine mode of failure by SEM.

Material and Methods

Exposed dentin surfaces of 70 mandibular third molars were used. Teeth were randomly divided into 7 groups: Group 1 (control group): direct composite resin restoration (Alert) with etch-and-rinse adhesive system (Bond 1 primer/adhesive), Group 2: indirect composite restoration (Estenia) luted with a resin cement (Cement-It) combined with the same etch-and-rinse adhesive, Group 3: direct composite resin restoration with self-etch adhesive system (Nano-Bond), Group 4: indirect composite restoration luted with the resin cement combined with the same self-etch adhesive, Groups 5-7: indirect composite restoration luted with self-adhesive resin cements (RelyX Unicem, Maxcem, and Embrace WetBond, respectively) onto the non-pretreated dentin surfaces. Tensile bond strengths of groups were tested with a universal testing machine at a constant speed of 1 mm/min using a 50 kgf load cell. Results were statistically analyzed by the Student''s t-test. The failure modes of all groups were also evaluated.

Results

The indirect composite restorations luted with the self-adhesive resin cements (groups 5-7) showed better results compared to the other groups (p<0.05). Group 4 showed the weakest bond strength (p>0.05). The surfaces of all debonded specimens showed evidence of both adhesive and cohesive failure.

Conclusion

The new universal self-adhesive resins may be considered an alternative for luting indirect composite restorations onto non-pretreated dentin surfaces.     

EFFECT OF FLUORIDATED VARNISH AND SILVER DIAMINE FLUORIDE SOLUTION ON ENAMEL DEMINERALIZATION: pH-CYCLING STUDY

Objective:

In the present investigation, the anticariogenic effect of fluoride released by two products commonly applied in infants was evaluated.

Methods:

Bovine sound enamel blocks were randomly allocated to each one of the treatment groups: control (C), varnish (V) and diamine silver fluoride solution (D). The blocks were submitted to pH cycles in an oven at 37°C. Next, surface and cross-sectional microhardness were assessed to calculate the percentage loss of surface microhardness (%SML) and the mineral loss (∆Z). The fluoride present in enamel was also determined.

Results:

F/Px10^-3(ANOVA, p<0.05) in the 1^stlayer of enamel before pH-cycling were (C, V and D): 1.61^a; 21.59^band 3.98^c. The %SMH (Kruskal-Wallis, p<0.05) were: - 64.0^a, -45.2^band -53.1^c. %∆Z values (ANOVA, p<0.05) were: -18.7^a, -7.7^band -17.3^a.

Conclusion:

The data suggested that the fluoride released by varnish showed greater interaction with sound enamel and provided less mineral loss when compared with silver diamine solution.     

The combined use of Er,Cr:YSGG laser and fluoride to prevent root dentin demineralization

The use of erbium lasers to prevent caries in enamel has shown positive results. However, it is not known if Er,Cr:YSGG laser can also be used to increase acid resistance of root dentine, which is another dental tissue susceptible to the action of cariogenic bacteria.

Objective

To analyze the effects of the Er,Cr:YSGG laser (λ=2.78 μm, 20 Hz) irradiation associated with 2% neutral sodium fluoride (NaF) to prevent root dentin demineralization.

Material and Methods

One hundred human root dentin samples were divided into 10 groups (G) and treated as follows: G1: no treatment; G2: NaF; G3: laser (4.64 J/cm²) with water cooling (WC=5.4 mL/min); G4: laser (4.64 J/cm²) without WC; G5: laser (8.92 J/cm²) with WC; G6: laser (8.92 J/cm²) without WC; G7: laser (4.64 J/cm²) with WC and NaF; G8: laser (4.64 J/cm²) without WC and NaF; G9: laser (8.92 J/cm²) with WC and NaF; G10: laser (8.92 J/cm²) without WC and NaF. The NaF gel was applied alone or after 4 min of irradiation. After 14 days of acid challenge, the samples were sectioned and the Knoop microhardness (KHN) test was done at different depths (30, 60, 90 and 120 μm) from the outer dentin surface. Data were analyzed by one-way ANOVA and Fisher''s test (α=5%).

Results

The results showed that G8 and G10 presented higher KHN than the G1 for the depths of 30 and 60 μm, indicating an increase of the acid resistance of the dentin in up to 35% (p<0.05).

Conclusions

The use of Er,Cr:YSGG laser irradiation at 4.64 J/ cm² and 8.92 J/cm² without water cooling and associated with 2% NaF can increase the acid resistance of human root dentin.