强流脉冲电子束对3Cr2W8V微摩擦磨损性能的影响

分别制备了常规热处理、强流脉冲电子束直接处理和强流脉冲电子束合金化Al处理的3Cr2W8V模具钢试样,使用金相显微镜、表面粗糙度测试仪,硬度测试仪对处理层的显微结构、表面粗糙度及截面硬度进行分析,采用HSR-2M微摩擦磨损试验机对处理层摩擦磨损性能进行测试。结果表明:试样原始表面粗糙度的大小对处理后粗糙度的影响较大;电子束处理后截面硬度均有所提高,其中3Cr2W8V电子束合金化Al的峰值硬度相对于原始样品升高了10%,而3Cr2W8V电子束直接照射样品的峰值硬度相对于原始样品升高了24%～33%;经电子束照射后的试样在微摩擦实验中摩擦系数均出现突然增大现象,增大后的摩擦系数与原始样品相当。3Cr2W8V电子束合金化Al样品、3Cr2W8V电子束直接照射样品的磨损量相对于原始样品分别下降22.7%、72.7%。     

Microstructure and mechanical propertiesof spray-deposited Al-Si-Fe-Cu-Mg alloy containing Mn

Al-20Si-5Fe-3Cu-1Mg alloy was synthesized by the spray atomization and deposition technique. The microstructure and mechanical properties of the spray deposited hypereutectic Al-Si alloy were studied using optical microscopy, scanning electron microscopy, X-ray diffraction, TEM (Transmission Electron Microscope) and HREM (High-resolution Electron Microscope), DSC (Differential Scanning Calorimetry), microhardness measurement, and tensile tests. The effects of Mn on the microstructural evolution of the high-silicon aluminum alloy after extrusion and heat treatment have been examined. The results show that two kinds of phases, i. e. S (Al2CuMg) and σ(Al5Cu6,Mg2), precipitated from matrix and improved the tensile strength of the alloy efficiently at both the ambient and elevated temperatures (300℃). The tensile test results indicate that the spray-deposited Al-20Si-5Fe-3Cu-1Mg alloy has better strength than the powder metallurgy processed Al-20Si-3Cu-1Mg alloy at elevated temperature.     

Microstructural evolution and mechanical properties of aging high nitrogen austenitic stainless steels

The microstructural evolution of 18Cr18Mn2Mo0.77N high nitrogen austenitic stainless steel in aging treatment was investigated by optical microscopy (OM), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The results show that hexagonal intergranular and cellular Cr2N with a=0.478 nm and c=0.444 nm and body-centered cubic intermetallic χ phase with a=0.892 nm precipitate gradually in the isothermal aging treatment. The matrix nitrogen depletion due to the intergranular Cr2N pre...     

训练及热循环对CuZnAl合金马氏体形态的影响

本文研究了ＣｕＺｎＡｌ形状记忆合金在训练后以及热循环后热弹性马氏体的形态；分析了马氏体形态对该合金的双程记忆效应的影响。     

激光熔覆铜基合金涂层中的液相分离行为

为了研究铜基合金激光熔覆中的液相分离行为,根据液相分离理论在ZL104铝合金表面成功制备了具有液相分离特性的铜基合金涂层,并采用扫描电镜等对涂层中液相分离形成的分离相(硬质强化相)的形态特征与分布规律进行了观察,研究了不同分离相的形成机制与液相分离行为.研究表明,涂层中的分离相通常呈弥散分布和偏聚2种典型形态.熔池温度较高时分离相表现出"富Mo核心 包围相"的2层复合结构,呈边缘粗糙的不规则近球状形貌,这是由异质形核诱发的液相分离所形成的;温度稍低时强的表面能约束则是影响液相分离的主要因素,并使分离相呈光滑球状形态.当表面能过高时在对流等因素作用下分离相问会发生严重的碰撞凝并,最终形成大块偏聚体.     

粗镁直接熔炼AZ91D的力学性能及断口分析

为了研究粗镁直接熔炼AZ91D镁合金锭不同位置上的夹杂分布情况,对AZ91D镁合金锭的三个不同取样位置进行了拉伸及冲击试验,通过扫描电子显微镜对拉伸和冲击断口进行了组织形貌上的观察与分析.结果表明:合金锭中间部分的力学性能要明显优于两侧部分,夹杂含量相对于两侧要低; 粗镁直接熔炼的AZ91D镁合金拉伸与冲击断口形貌呈河流状,为脆性断裂.粗镁直接熔炼的合金产生的夹杂物中的主要元素为C、O、Si,并含有少量Fe、K、Ca、S、Cl、Cr等元素; 在夹杂物周围容易出现二次裂纹,夹杂物的数量和种类直接影响着合金的力学性能.     

低温时效对AZ81-4%Gd镁合金组织和性能的影响

为了研究低温时效对AZ81-4%Gd镁合金组织和性能的影响,对经过固溶处理后的该合金在150 ℃下进行不同时间的时效处理,采用x-射线衍射仪(XRD)、扫描电子显微镜(SEM)、能谱分析(EDS)以及硬度测试等技术,分析了经过不同时间时效后合金的显微组织和力学性能,并用金属学理论分析了合金组织和性能变化的原因.结果表明,合金在低温时效时,β-Mg₁₇Al₁₂相以连续和非连续两种方式析出,两种β-Mg₁₇Al₁₂相形貌不同.分析认为,β相的析出方式及形貌与其形核长大机理有关.在实验范围内,合金硬度随着时效时间的延长而逐渐增大.     

脉冲电流对Ti-6Al-4V合金显微组织及力学性能的影响

采用组织观察、性能检测、断口分析等方法研究了脉冲电流对Ti-6Al-4V合金显微组织及力学性能的影响。结果表明,脉冲电流使试样瞬间急速升温、产生较高的热压应力,并发生α→β相变,随后试样快速降温冷却发生β→α′相变。由于急速升温和快速冷却,新相的形核率增加且无充足时间长大,使合金的显微组织细化,而相变和组织细化导致了合金力学性能提高和电阻率变化。适当优化电脉冲处理工艺参数可使Ti-6Al-4V合金的综合力学性能明显提高。通过测量电阻变化可间接表征电脉冲处理后材料微观组织结构的变化程度。     

Ce对Al-Zn-Mg-Cu-Sc合金组织和力学性能的影响

为了研究Ce元素对T6态Al-7.5Zn-2Mg-2.3Cu-0.1Sc合金显微组织和力学性能的影响,通过改变合金中Ce元素的添加量,采用光学显微镜、扫描电子显微镜和电子万能实验机对合金的显微组织、拉伸断口形貌和力学性能进行了研究.结果表明,加入质量分数为0.2%的Ce元素可以显著细化Al-7.5Zn-2Mg-2.3Cu-0.1Sc合金的铸态和T6态显微组织.在合金的T6处理过程中随着时效时间的增加,合金硬度和抗拉强度均先增加后降低,合金的硬度和抗拉强度峰值分别为216 HB和681.7 MPa,合金最高屈服强度为638.2 MPa.合金拉伸断口呈韧脆混合断裂特征.     

Solidification structures of high niobium containing TiAl alloys

To understand the effect of alloy stoichiometry on the microstructural development and mechanical behavior of γ-TiAlbased materials, it is necessary to have a determination of the phase relationships for the TiAl alloy system near the γ phase field.Cast structures and phases of Ti-(43-47)Al-8Nb-(1-2)Mn (at%) alloys have been studied by using scanning electron microscope and X-ray diffraction. Their solidification path and microstructure development during the solidification were analyzed. The experimental results show that the alloys with different Al contents form different macrostructures and microstructural morphologies. This indicates that the solidification paths are different with different Al contents. The alloy with 43Al forms equiaxed grain structure, and the solidification path is as follows: L → L β→β→α β→α β cores →α2 γ B2 cores. Whereas the alloy with 47Al forms columnar grain structure, and the solidification path is as follows: L → L β→α β L →α γ β cores →α2 γ B2 cores. The β phase is their primary solid phase and can be retained to ambient temperature. The alloy with 43Al solidifies completely into β phase. The peritectic reactions L β→α and L α→γ appear when the Al content increases to 47Al.     

Effects of laser heat treatment on salt spray corrosion of 1Cr5Mo heat resistant steel welding joints

The surface of 1Cr5 Mo heat-resistant steel welding joint was processed with CO2 laser, and the corrosion behaviors before and after laser heat treatment(LHT) were investigated in the salt spray corrosion environments. The microstructures, phases, residual stresses and retained austenite content of 1Cr5 Mo steel welding joint before and after LHT were analyzed with optical microscope and X-ray diffraction, respectively. The cracking morphologies and chemical compositions of corrosion products after salt spray corrosion were analyzed with field emission scanning electron microscopy(FESEM) and energy disperse spectroscopy(EDS), respectively, the polarization curves were measured on a PS-268 A type electrochemical workstation, and the mechanism of corrosion resistance by LHT was investigated as well. The results show that the passive film of original sample is destroyed owing to the corrosive media penetrating into the subsurface, resulting in the redox reaction. The content of residual austenite in the surface and the self-corrosion potential are increased by LHT, which is contributed to improving the capability of salt spray corrosion resistance.     

Mechanism of α-Cr precipitation and crystallographic relationships between α-Cr and δ phases in Inconel 718 alloy after long-time thermal exposure

To study the precipitation mechanism of α-Cr phase in Inconel 718 alloy, the samples after long-time aging at 650 and 677℃ were examined by microstructural observations and chemical phase analysis methods. Combining the thermodynamics and kinetics calcula-tion results, α-Cr always precipitates in the vicinity of δ phase, because δ phase rejects Cr into theγ-matrix when growing. The selected area diffraction patterns confirm that the crystallographic relationships of α-Cr with δ phase are (010) δ//(-110)α -Cr and [100] δ//[111] δ-Cr. A graphic model is also presented to show the crystallographic relation between α-Cr and δ phases.     

Effects of mechanical alloying parameters on the microstructures of nanocrystalline Cu-5 wt% Cr alloy

Nanocrystalline Cu-5 wt%Cr alloy powders were fabricated by mechanical alloying (MA). The effects of MA processing parameters on the crystallite size, solid solubility, and microstructures of the Cu-5 wt%Cr alloys were investigated including type and size distribution of the grinding medium and ball-to-powder weight ratio (BPR). The results show that the crystallites were refined effectively and solid solubility of Cr in Cu was extended when heavier ball and higher BPR were adopted. The maximum solubility is extended up to 5.6 at% (namely 4.6 wt%) Cr in Cu by use of a combination of large and small size WC-Co balls with BPR of 30:1. A Cu-5 wt%Cr supersaturated solid solution alloy bulk is obtained by spark plasma sintering the as-milled powders at 900 ℃ for 5 min.     

Microstructure and wear resistance of in situ NbC particles reinforced Ni-based alloy composite coating by laser cladding

The in situ synthesized NbC particles reinforced Ni-based alloy composite coating was produced by laser cladding a precursor mixture of Ni-based alloy powder,graphite and niobium powders on a steel substrate.The microstructure,phase composition and wear property of the composite coating were investigated by means of scanning electron microscopy(SEM),X-ray diffraction(XRD)and dry sliding wear test.The experiment results show that the composite coating is homogeneous and free from cracks,and about 0.8 mm thick.The microstructure of the composite coating is mainly composed of NbC particles,CrB type chromium borides,γ-Ni primary dendrites,and interdendritic eutectics.CrB phases often nucleate and grow on the surface of NbC particles or in their close vicinity.NbC particles are formed via in situ reaction between niobium and graphite in the molten pool during the laser cladding process and they are commonly precipitated in three kinds of morphologies,such as quadrangle,cluster,and flower-like shape.Compared with the pure Ni-based alloy coating,the microhardness of the composite coating is increased about 38%,giving a high average hardness of HV0.21000,and the wear rate of the composite coating is decreased by about 32%,respectively.These are attributed to the presence of in situ synthesized NbC particles and their well distribution in the coating.     

一种高硬度铸造镁合金

设计了一种成分（质量分数/%）为Mg-8Zn-6Al-3Cu-3Ca-1.5Mn-1Si的合金,利用金相显微镜、扫描电镜、X射线衍射和维氏硬度计研究了自然冷却、快速冷却及时效处理对合金显微组织和硬度的影响.Mg-8Zn-6Al-3Cu-3Ca-1.5Mn-1Si合金慢冷组织主要由α-Mg、Mg2Cu6Al5、CaMgSi、Mg2Zn3等相构成,没有出现Mg17Al12相.合金经快冷后,抑制了第二相从基体中的析出;时效10 h后,CaMgSi相以细小的块状相均匀析出.合金具有较高的硬度值,在时效时间10 h时最大HV值达到111.     

工具钢表面激光熔覆Co基合金涂层的组织及性能

通过送粉式激光熔覆在碳素工具钢(T10钢)表面制备了Co基合金熔覆涂层。利用扫描电子显微镜(SEM)和X射线衍射仪(XRD)分析其微观结构和相组成。结果表明:熔覆层中主要有γ-Co相以及其他相,包括Cr23C6、Co7W6和CrNi。从熔池与基体界面到熔覆层表面存在不同的凝固形态,依次为平面晶(在界面处)、胞状晶和树枝晶。微观组织较细的树枝晶强化了熔覆层,因而激光熔覆层的显微硬度增加,耐腐蚀性提高。     

Composition and Morphology of Zn-Co Alloy Coatings Deposited by Means of Pulse Plating Containing Reverse Current

The influence of bath constituents and pulse parameters on cobalt content, surface morphologies and grain size of Zn-Co alloy deposits was studied using a pulse plating technique with a square- wave current containing reverse pulse, It is found that Zn-Co alloy coatings obtained from the bath with the cobalt ion concentration over 60 wt% have a higher cobalt content in deposits. The results of pulse plating show that the average current density and reverse anodic current density amongst the variables investigated have very strong effects on the cobalt content in the Zn-Co alloy deposits. It is possible to electrodeposit Zn-Co alloy coatings with 10-90 wt% cobalt by modulating pulse parameters. The grain size, surface appearance and internal stress in the deposit were improved significantly by introducing the reverse current.     

过共品铸造Al-Si—Cu—Mg—Fe合金组织性能研究

通过正交试验和单因素试验,考察了Cu、Mg、Zn、Ni和Fe对Al—18Si过共晶铝硅合金室温及高温（350℃）力学性能的影响规律,利用光学金相显微镜（OM）、扫描电镜（SEM）、能谱分析仪（EDX）对合金中富Cu相、富Fe相的组织组成进行了分析．结果表明：Cu、Mg是提高AI-18Si过共晶铝硅舍金室温及高温强度的主要因素;Zn含量增加明显降低合金350℃时的高温强度,改善合金的室温和高温延伸率;Fe降低合金的室温强度,显著提高合金的高温强度;当Cr：Fe=0．35：1,Mn：Cr=2：1,含铁0．8％～1．2％时,Al-18Si-4．0Cu-0．7Mg-0．2Zn-1.0Ni-（0．8～1．2）Fe合金力学性能σb（25℃））310MPa,延伸率受（25℃）≥0．75%,σb（350℃）〉130MPa,延伸率δs（35℃）〉1．5％;合金中富铜相主要以块状Al。Cu相和白灰色花卉状A15Si。cu2Mg8相存在,富铁相主要以三叶草状、树枝状和棒状Al5Si（Cr,Mn,Fe）相存在．     

时效态Al-Zn-Mg-Cu-Zr-Sc合金的组织与疲劳性能

为了研究时效处理对Al-7.2Zn-2.5Mg-1.5Cu-0.08Zr-0.12Sc合金的组织与疲劳性能的影响,利用透射电子显微镜对合金的显微组织进行了观察分析,并针对不同时效状态的合金进行了低周疲劳实验.结果表明,经过150℃×6 h时效处理后,合金晶内析出相较少,晶界无析出相;经过150℃×36 h时效处理后,合金晶内析出相较为细小,并呈弥散分布,同时晶界析出断续分布的平衡相,并存在晶界无析出带;经过150℃×48 h时效处理后,合金的析出相均已长大,且晶界无析出带发生宽化.经过150℃×36 h时效处理后的合金,表现出了较高的循环变形抗力与较长的低周疲劳寿命;不同时效状态合金的塑性应变幅、弹性应变幅与载荷反向周次之间,以及循环应力幅与塑性应变幅之间均呈线性关系.     

20#钢表面镍基添Y2O3激光熔覆层及其高温磨损行为

采用激光熔覆法,在20#钢表面制备出添Y2O3的镍基合金粉末的熔覆涂层．分析了熔覆层的相组成、高温耐磨性能;观察了熔覆层显微形貌．结果表明：所制得的熔覆层组织均一、致密,与基体形成了良好的冶金结合．添加Y2O3的熔覆层硬度提高到基体的3．9倍,高温耐磨率仅是基体的1／4．熔覆层耐磨能力增强的主要原因是熔覆层与基体良好的冶金结合,镍基合金良好性能,组织细化以及硼化物、硼碳化物等析出相的强化作用．