14NiCrM0106V与Q345E焊接接头组织与力学性能的研究

通过室温拉伸、弯曲、冲击、硬度试验及金相分析,对Q345E低合金钢与14NiCrM0 10 6V低合金钢混合气体保护焊焊接接头的力学性能与显微组织进行了研究.结果表明:采用ER50-6实芯焊丝焊接时,可以获得拉伸、弯曲和冲击性能均良好的焊接接头;焊缝区硬度较均匀,焊缝硬度在210～250 HV之间;焊接接头焊缝中心组织为先共析铁素体分布于柱状晶界上,晶内为针状铁素体与珠光体;Q345E侧熔合区组织为沿晶界析出块状先共析铁素体和向晶内生长的条状铁素体以及少量的珠光体和贝氏体;14NiCrMo10 6V侧熔合区和过热区组织为板条状马氏体和粒状贝氏体.     

船用5083铝合金变极性等离子焊接头组织和性能

采用变极性等离子焊接工艺实现了5mm厚船用5系铝合金立向上位置焊接,并分析了接头的组织和力学性能。力学试验显示：接头抗拉强度达到295MPa,延伸率达到10%,断裂位置在熔合线附近;焊缝区和热影响区的显微硬度均低于母材,且焊缝中心处最低。接头金相观察发现熔合线附近的焊缝为粗大的等轴晶组织,但焊缝区大部分为胞状树枝晶组织,从两侧呈对称生长并在焊缝中心处相遇,热影响区为再结晶组织。利用电子探针分析了拉伸断裂位置附近成分,发现该区域Mg含量偏低且分布不均匀,固溶强化效果下降,组织和成分的不均匀导致该区域成为接头的薄弱环节。     

7055喷射成形高强铝合金激光焊接头组织及性能

采用激光焊接对2 mm厚喷射成形的7055-T76511铝合金进行焊接试验。通过显微硬度和拉伸试验测试焊接接头的力学性能,通过光学显微镜(OM)、扫描电镜(SEM)、背散射电子衍射技术(EBSD)以及X射线衍射(XRD)分析焊接接头的微观组织。结果表明,7055铝合金激光焊接头无明显的软化区,焊缝显微硬度最低,约为130~140 HV,接头的抗拉强度372 MPa,伸长率4.1%。焊缝组织有明显的三个区(热影响区、熔合区和焊缝区)。热影响区组织是产生了部分再结晶的等轴晶粒;熔合区由于非均匀形核形成了等轴非枝晶区(non-dendritic equiaxed grain zone,EQZ),晶粒尺寸3~8μm;焊缝区靠近熔合线为柱状枝晶,中心为胞状枝晶。     

锌基合金激光焊焊接接头组织和性能的研究

通过金相显微镜、扫描电镜和能谱分析仪等分析手段,研究了锌基合金激光焊焊接接头的组织和性能。结果表明:锌基合金焊接接头熔合线明显,熔合区及热影响区很窄,组织比较均匀;焊缝中心位置的蒸发凹坑较明显。焊缝中心主要由等轴晶组成,焊缝中心与熔合线的中间区域主要由树枝状晶组成。熔合区及热影响区组织发生明显的重结晶,为细小的等轴晶,没有半熔化区晶粒组织及过热粗晶区组织出现。焊接接头的焊缝硬度最高,各区域的硬度分布为:焊缝热影响区、熔合区母材。     

6061铝合金焊接接头的组织与性能分析

通过金相技术、力学性能试验和SEM技术研究了6061-T6铝合金真空电子束焊接接头的金相组织、力学性能和断口形貌特征.结果表明:焊接接头的拉伸强度低于母材.预热和重熔可以同时降低电子束焊接接头的强度和塑性,尤其对接头的塑性影响更大.焊缝区和热影响区的硬度均低于母材,预热和重熔可以降低焊接接头的硬度.焊缝区组织主要为等轴晶和树枝柱状晶,熔合区组织主要为柱状晶.预热和重熔使得焊缝区的晶粒组织变得粗大,焊接接头的拉伸断口断面上分布的韧窝尺寸较小,且韧窝的大小接近,未发生明显的塑性流动,呈现出铸态断口特征.     

轿车用铝合金焊接接头局部力学性能分析

铝合金焊接接头是一个组织和力学性能不均匀体,准确测定不同区域的局部力学性能,对评定接头整体性能和改善焊接工艺是十分必要的.通过对轿车用5052铝合金焊接接头显微组织及硬度分析,提出了微冲压试验方法,结合ABAQUS有限元商业软件对接头局部力学性能进行了研究.在有限元反向模拟计算间接得出局部材料的本构关系,同时利用拉伸试验验证该方法的准确性.结果表明,焊接接头局部力学性能分布特征与硬度值分布特征基本相似,熔合线附近是焊接接头力学性能最薄弱的区域.     

电子束焊接钼板的组织及性能研究

采用电子束焊接方法对16 mm厚的钼板进行焊接,利用光学显微镜、扫描电镜等手段分析了电子束焊接接头的显微组织及断口形貌,并利用维氏硬度仪和拉伸试验机检测了接头区域硬度和接头强度。结果表明,采用电子束焊接钼板获得的焊缝呈"钉子"状,焊缝热影响区窄,焊缝中间为粗大的等轴晶,熔合合区域为柱状晶。焊缝接头各区域硬度值有差异,母材区硬度最小。热处理后硬度值有变化,热处理温度在1000℃以上时,硬度值有所降低,焊接接头不同厚度处力学性能不一致,1100℃热处理接头强度最高在焊缝底部。焊接接头断裂全部在焊缝处,断口为解理断裂。     

焊后热处理对6063铝合金激光填丝焊接头组织与性能的影响

采用激光填丝焊对6063铝合金进行焊接,并对焊接接头进行人工时效和固溶+人工时效的热处理。通过光学显微镜、扫描电镜观察及拉伸试验,对焊后经不同热处理的焊接接头组织和性能进行研究。结果表明:未热处理的焊接接头抗拉强度为196 MPa,焊缝内部为铸态组织,弥散分布着Mg₂Si强化相,熔合线附近存在向焊缝内部生长的粗大柱状晶,焊缝内部为细小的树枝晶,焊缝中心为等轴晶;经时效处理后,焊接接头组织不均匀性和强化相的分布得到改善,焊接接头抗拉强度提高27 MPa;经固溶+时效处理的焊接接头抗拉强度提高64 MPa,焊缝组织、熔合区及热影响区组织得到显著细化。焊接接头均为韧脆混合断裂;时效处理的断口韧窝大小差异较大,韧窝较深;固溶+时效处理后的断口韧窝大小均匀,韧窝尺寸较大较深,韧窝数量更多。     

BS600MCJ4低合金高强钢焊接接头组织与力学性能研究

通过拉伸、弯曲、冲击、硬度、金相分析等试验对BS600MCJ4低合金高强钢焊接接头的力学性能和组织形态进行了研究。结果表明,采用ER70-G焊丝焊接时,BS600MCJ4焊接接头具有良好的拉伸、弯曲和冲击性能;其焊缝组织为有少量先共析铁素体、少量无碳贝氏体从晶界伸向晶内,晶内为针状铁素体,个别部位有粒状贝氏体。熔合区及粗晶区组织为粒状贝氏体和少量针状铁素体。正火区组织为索氏体和粒状贝氏体。BS600MCJ4焊接接头的硬度值在243~330 HV之间,焊缝处硬度最高,但与热影响区和母材相差不大,热影响区软化不明显。     

铝锂合金1420交流CMT焊接工艺及接头性能研究

采用交流CMT焊接方法对1420铝锂合金薄板进行了焊接试验,使用光学显微镜观察了焊接接头不同部位的显微组织,测试了接头横截面不同位置沿水平方向的显微硬度,并通过拉伸试验测定了焊接接头的力学性能。结果表明,焊缝成形良好,表面有少量气孔;焊缝区组织较母材粗大,熔合线附近出现了细晶区,未出现热裂纹;焊缝区域的显微硬度均低于母材,接头有软化现象;接头的抗拉强度和屈服强度均比母材低,熔合线附近是焊接接头的薄弱区域。     

喷射成形7055铝合金FSW焊工艺与性能

采用搅拌摩擦焊接方法对厚度为4 mm的喷射成形7055铝合金板进行焊接试验.分析了焊接速度和旋转频率对接头力学性能的影响,对焊缝的显微组织和断口进行了微观分析.结果表明,当焊接工艺参数选择合适时,可得到外形美观,无缺陷的焊缝.另外焊接接头力学性能与焊接工艺参数存在一定的关系,在旋转频率为1 000r/min,且焊接速度为100 mm/min时,可以获得较好的焊接性能,抗拉强度可以达到455MP,断裂形式为韧性和脆性的混合型断裂;焊缝中存在3个组织变化区,其中焊核区内是细小均匀的等轴晶;焊缝显微硬度的最低值出现在前进侧,说明前进侧是焊缝的薄弱环节.     

超声振动对6061-T4铝合金搅拌摩擦焊接头组织和性能的影响

利用自主研制的试验装置,通过工具头将超声振动能量施加在搅拌头前方的待焊工件上,研究了超声振动能量对减少焊接缺陷、改善搅拌摩擦焊接头组织和力学性能的影响.对6 mm厚度6061-T4铝合金板进行了超声振动强化搅拌摩擦焊工艺试验,并与相同工艺条件下的常规搅拌摩擦焊进行了对比.结果表明,超声振动能够减小焊速/转速比较大时的焊缝内部隧道型缺陷,增大材料对接混合区宽度和焊核区体积,细化焊核区和热力影响区微观组织,提高接头抗拉强度和焊核区显微硬度.     

铝合金电流强化激光焊接焊缝组织及性能

采用电流强化激光焊接方法对3.0 mm厚的2219-T6铝合金板材进行堆焊,研究了电流对激光焊缝宏观和微观组织、气孔缺陷以及力学性能的影响.试验发现,引入电流后,焊缝区的晶粒发生明显细化,促使粗大的柱状晶转变为细小的等轴晶;而且消除了激光焊缝中央存在的羽毛状晶.与激光焊接相比,电流强化激光焊接焊缝中的气孔明显减少,接头...     

Friction stir welding of AZ31 magnesium alloy

Friction stir welding (FSW) is an new solid-phase joining technology which has more advantages over fusion welding methods in welding of aluminum and other non-ferrous metals. The effects of welding parameters on mechanical properties and microstructure during friction stir welding of AZ31 magnesium alloy were studied in this paper. Microstructures and mechanical properties of the joints were investigated by means of optical microscopy, scanning electric microscopy ( SEM ) , micro-hardness analysis, and tensile test. Experimental results show that the magnesium alloy can be successfully welded by FSW method, and the ultimate tensile strength (UTS) of FSW joint reaches up to 90 percent of base metal. The microstructures of welded joints exhibit the variation from dynamically recrystallized fine grains to greatly deformed grains. Hardness in nugget zone was found lower than the base metal but not too obvious.     

Mechanical and corrosion properties of 445J2 ultra pure ferritic stainless steel joint

The microstructure, mechanical and corrosion resistance properties of 445J2 ultra pure ferritic stainless steel thin plate joints conducted by the pulsed current gas tungsten arc welding (PCGTAW) were discussed in this paper. In order to avoid weld defects, the appropriate welding process was adjusted. The joints were subjected to optical microscopy, transverse static tensile, plastic deformation, intergranular corrosion and electrochemistry corrosion tests. The results indicated that the weld zone (WZ) is characterized with columnar grains and equiaxed grains and the heat-affected zone (HAZ) shows coarse ferrite grains due to the rapid solidification of thin plate welding. The PCGTAW joint exhibited acceptable mechanical properties and equivalent corrosion resistance properties as the base metal.     

含钪与不含钪铝镁钪合金焊接接头的组织与性能

分别采用Al-Mg-Zr和Al-Mg-Zr-Sc合金焊丝为填充材料,对2 mm厚的Al-Mg-Sc合金薄板进行惰性气体保护焊接,然后对两种焊接接头的显微组织和力学性能进行对比研究。结果表明:采用两种焊丝焊接的Al-Mg-Sc合金薄板的焊接接头强度系数均大于0.9。但采用Al-Mg-Zr-Sc合金焊丝为填充材料时,焊缝晶粒组织明显细化,熔合区形成的细小等轴晶层提高了基材与焊缝填充材料的结合力,焊接接头的屈服强度比采用Al-Mg-Zr合金焊丝为填充材料时提高了100 MPa,显著提高了Al-Mg-Sc合金焊接构件的许用强度,因此焊接Al-Mg-Sc板材更宜采用Al-Mg-Sc-Zr焊丝。     

Enhancement of AZ80 joints using ultrasonic vibration-assisted welding process

Ultrasonic vibration-assisted welding process was developed to improve the microstructures and mechanical properties of AZ80 Mg alloy joints. Results show that the ultrasonic vibration-assisted welding process has a significant effect on the morphology and size of both β-Mg₁₇Al₁₂ precipitated phases and α-Mg grains. With ultrasonic vibration treatment, the primary α-Mg grains are transformed from coarse dendrites to nearly fine equiaxed grains, and the β-Mg₁₇Al₁₂ phases at α-Mg boundaries are refined and become discontinuous, owing to the cavitation effects and acoustic streaming effects induced by ultrasonic vibration. The mechanical properties of AZ80 Mg alloy joints under the ultrasonic vibration-assisted process are obviously improved. And the influence mechanisms of the ultrasonic vibration-assisted welding process on joints are discussed in detail.     

镁合金 TIG 焊接接头组织和力学性能分析

应用交流TIG焊对镁合金板材进行焊接,对焊接接头进行组织观察和力学性能测试.结果表明,焊缝区为细小的等轴晶粒,热影响区晶粒粗大,拉伸断裂多发生在晶粒粗大的热影响区.     

2219-O铝合金的搅拌摩擦焊接

对2219-O铝合金进行了搅拌摩擦焊接,采用光学显微镜分析了接头的微观组织,采用拉伸试验方法评价了接头的力学性能.微观分析表明,在热机循环的共同作用下,焊核区(WNZ)发生了动态再结晶,形成了细小的等轴晶粒,并且沉淀相的数量较其它各区有所增加;热机影响区(TMAZ)晶粒被拉长、弯曲,发生了动态回复和部分再结晶,晶粒内部开始有新的晶粒生成;热影响区(HAZ)的晶粒发生粗化.力学性能测试结果表明,当转速为800r/min,焊接速度为200～400 mm/min时,接头与母材等强度,断裂发生在母材区;当焊接速度大于400mm/min时,接头的抗拉强度很低,断裂发生在缺陷处.     

厚大螺母与镀锌薄钢板环凸焊接头组织与性能

通过大量试验,探讨了厚大螺母与镀锌薄板环凸焊接头的组织与性能,结果表明：当接头具有良好的性能时,结合面存在的微区熔化并凝固的细小等轴晶,其接头的连接机制属于微区熔化和固态塑性变形＋动态再结晶的混合连接模式。