激光熔覆Ni-WC/Cr3C2涂层组织及性能

采用激光技术在45钢表面熔覆Ni-WC/Cr₃C₂涂层,采用SEM,XRD等手段进行熔覆层的显微组织、相组成及成分分析,并测试熔覆层的耐蚀性和耐磨性能.结果表明,Ni-WC/Cr₃C₂熔覆层底部生成方向性较强的胞状树枝晶,中上部组织为细小的树枝晶.涂层主要是由γ-(Fe, Ni),M₂₃C₆型碳化物以及未熔的WC颗粒组成.细晶强化、合金元素固溶强化以及碳化物强化的共同作用,使熔覆层的显微硬度提高至711HV0.1.熔覆层耐蚀性明显改善,腐蚀电流密度约为45钢的1/4.随着摩擦速度的增大,激光熔覆Ni-WC/Cr₃C₂涂层和45钢磨损量增加,且熔覆层的磨损量低于45钢,表明其耐磨性能明显提高.     

稀土Y2O3对6063Al激光熔覆镍基熔覆层耐磨性的影响

利用激光熔覆技术,在6063铝合金表面制备了添加有不同含量Y₂O₃的Ni60合金熔覆层,并对熔覆层进行了耐磨性试验. 通过分析熔覆层组织、熔覆层表面磨痕形貌、磨损量及摩擦系数,研究Y₂O₃含量对铝合金表面激光熔覆Ni基涂层耐磨性能的影响. 结果表明,添加5%Y₂O₃的Ni60熔覆层组织呈现明显的网状分布的枝晶和细小的等轴晶,稀土Y₂O₃可以改善铝合金表面Ni60熔覆层的组织,促进晶粒细化和成分分布均匀;添加稀土Y₂O₃的Ni60基熔覆层较Ni60熔覆层的磨损面崩损程度减小了,摩擦稳定性得到提高;随着稀土含量提高,熔覆层的磨损量减小,但Y₂O₃含量高于5%时磨损量基本不会大幅变化;5%Y₂O₃+Ni60熔覆层具有良好的磨损形貌、较低的磨损量以及较稳定的摩擦系数,其熔覆层的耐磨性是Ni60熔覆层的6.1倍,是6063Al合金基体耐磨性的20.1倍.     

H13钢表面激光熔覆NbC/Ni60复合涂层组织及高温耐磨损性能

目的 研究NbC颗粒的加入量对H13钢表面激光熔覆NbC/Ni60复合涂层的组织、硬度和耐磨性的影响。方法 将Ni60合金粉末与NbC碳化物粉末球磨混合,采用激光熔覆技术,在H13钢基体表面制备不同NbC含量(质量分数分别为0%、10%、20%、30%)增强的NbC/Ni60合金复合涂层。采用电子扫描显微镜(SEM)、X射线衍射仪对复合涂层的微观组织和物相进行分析。借助显微硬度计,研究复合涂层的截面显微硬度分布规律。采用高温摩擦磨损试验机测试复合涂层在真空400℃下的摩擦磨损性能。结果 在激光熔覆NbC/Ni60复合涂层中,物相主要由γ-(Ni, Fe)固溶体、Ni₂Si、CrB、Cr₂₃C₆、NbC组成;熔覆层以胞晶和枝晶为主,NbC含量对复合熔覆层组织及形态具有显著影响,加入少量NbC可使熔覆层组织细化;在NbC的质量分数为20%时,大量弥散的Nb C颗粒在枝晶间呈聚集趋势;在NbC的质量分数为30%时,熔覆层中NbC相呈现块状、花瓣状形貌。NbC/Ni60复合涂层的硬度显著高于H13钢基体,随着NbC含量的增加,N...     

Cr12MoV钢表面激光熔覆稀土改性铁基复合涂层的性能

采用激光熔覆技术在Cr12MoV钢表面制备CMC PMagic2L涂层,并通过添加稀土氧化物CeO₂构成改性铁基复合涂层,运用光学显微镜、扫描电镜、显微硬度计及摩擦磨损试验机等,研究了稀土氧化物CeO₂的加入对涂层组织性能的影响。结果表明,稀土氧化物CeO₂能够促进熔覆层晶粒细化,使热影响区宽度变大;CeO₂的含量越高,熔覆层硬度越大;含1%CeO₂的改性铁基复合涂层较未添加CeO₂的涂层,尽管热影响区厚度有所增加,但熔覆层平均硬度提高了22.1%,耐磨性也显著提高,磨损体积相对减小了43.66%,且熔覆层组织致密,有效地实现了模具表面强化的目的。     

激光熔覆原位合成陶瓷相增强铁基熔覆层的组织和性能

利用6 kW光纤激光器在Cr12MoV汽车模具钢表面激光熔覆含有Ti-Fe,B₄C粉末的铁基合金粉,在汽车模具钢表面直接原位合成TiC+TiB₂颗粒增强的铁基合金复合涂层.涂层与基体呈良好的冶金结合,涂层组织细小,结构致密,宏观质量较好. XRD分析结果表明,涂层组织由α-Fe,TiC,TiB₂组成. TiC,TiB₂相均匀分布于熔覆层中.由于TiC,TiB₂硬质相的形成以及激光的快速凝固冷却获得的细晶组织,使得熔覆层的显微维氏硬度有了明显提高.在距离熔覆层表面1.2 mm处显微维氏硬度高达1000 HV,有利于促进熔覆层耐磨性的提高.     

SiC/Ni基合金激光熔覆层磨损性的研究

采用扫描电子显微镜、盘销式摩擦磨损试验机等方法对45钢表面SiC／Ni基合金激光熔覆层的组织和磨损性进行了试验分析。结果表明，激光熔覆后试样从表面至心部可分为熔覆区、结合区、热影响区和基体。熔覆层显微组织以枝状晶和胞状晶为主，结合层以细晶为主，激光熔覆层与基体结合良好。磨损试验结果显示激光熔覆可显著改善钢的耐磨性，SiC／Ni基合金复合熔覆层比Ni基合金熔覆层具有更好的耐磨性；在一定成分范围内，适当提高熔覆层中SiC的含量，可提高材料的耐磨损性能。     

不锈钢表面激光熔覆原位生成Fe-Mn-Si记忆合金涂层研究

利用5 kW横流CO2激光器,在304不锈钢表面激光熔覆原位生成Fe17Mn5Si10Cr4Ni记忆合金涂层并利用金相显微镜、场发射扫描电镜、X射线衍射仪、往复摩擦仪等仪器设备对熔覆层显微组织、微区成分、摩擦磨损性能进行了分析研究。结果表明,Fe-Mn-Si记忆合金涂层自顶端到熔合界面分别由等轴晶、树枝晶、柱状树枝晶、胞状晶和平面晶组成;激光熔覆原位生成Fe-Mn-Si记忆合金涂层过程中,熔覆层内残余应力驱动诱发了γ→ε马氏体相变,相变变形可松弛熔覆层的残余应力;Fe-Mn-Si记忆合金涂层与304不锈钢基材相比,摩擦系数小、耐磨性好,磨损机制为磨粒磨损,摩擦力诱发γ→ε马氏体相变是熔覆层耐磨性得到显著提升的根本原因。     

H13钢激光熔覆TiC/Ni合金复合涂层的组织与耐磨性北大核心CSCD

为提高H13模具钢的耐磨性能,利用激光熔覆技术,在H13钢表面制备了不同Ti C含量的Ti C/Ni基合金复合涂层,通过显微组织观察、硬度测试、滑动摩擦磨损试验方法对H13钢表面激光熔覆的不同复合涂层的组织及耐磨性能进行分析测试。结果表明,Ni60+Ti C激光熔覆涂层中物相主要为γ-(Fe,Ni)、Fe3C、Cr23C6、Ni2Si及Ti C,激光熔覆层具有较高显微硬度,Ti C的加入及含量增加可使熔覆层组织细化,复合熔覆层硬度提高,Ti C含量为30%时熔覆层内平均硬度最大,为873 HV0.2;激光熔覆Ti C+Ni60复合涂层的耐磨性显著高于H13钢基体,随Ti C含量增加而先增加后降低,Ti C含量20%耐磨性较佳;H13钢基体的磨损机制主要以犁削、切削为主,激光熔覆Ti C/Ni合金复合涂层以脆性剥落机制为主。     

45钢表面激光熔覆铁基合金涂层显微组织与性能

采用激光熔覆技术在45钢表面制备铁基合金涂层,分析了激光熔覆层的微观组织,测试了其显微硬度及摩擦磨损性能.结果表明:激光熔覆区为细小的树枝晶,组织均匀致密,并有硬质点弥散分布,使得表面硬度和耐磨性大幅度提高.     

H13钢激光熔覆TiC/Ni合金复合涂层的组织与耐磨性

为提高H13模具钢的耐磨性能,利用激光熔覆技术,在H13钢表面制备了不同Ti C含量的Ti C/Ni基合金复合涂层,通过显微组织观察、硬度测试、滑动摩擦磨损试验方法对H13钢表面激光熔覆的不同复合涂层的组织及耐磨性能进行分析测试。结果表明,Ni60+Ti C激光熔覆涂层中物相主要为γ-(Fe,Ni)、Fe3C、Cr23C6、Ni2Si及Ti C,激光熔覆层具有较高显微硬度,Ti C的加入及含量增加可使熔覆层组织细化,复合熔覆层硬度提高,Ti C含量为30%时熔覆层内平均硬度最大,为873 HV0.2;激光熔覆Ti C+Ni60复合涂层的耐磨性显著高于H13钢基体,随Ti C含量增加而先增加后降低,Ti C含量20%耐磨性较佳;H13钢基体的磨损机制主要以犁削、切削为主,激光熔覆Ti C/Ni合金复合涂层以脆性剥落机制为主。     

激光熔覆Cu包SiCp/Ni35覆层组织及磨损性能

目的研究Cu包SiC_p/Ni35激光熔覆层的显微组织、物相及其在25℃和600℃下的摩擦机理。方法采用化学镀的方法在SiC_p表面包覆一层Cu,并用激光熔覆的方法在H13钢表面制备了Cu包SiC_p增强Ni35熔覆层。用XRD、OM、SEM和EDS对熔覆层的物相、组织和成分进行了分析,用显微硬度计测试了熔覆层的显微硬度,用高温磨损试验机测试了熔覆层在常温、高温下的耐磨性能。结果熔覆层由基相γ-Ni(Fe)固溶体、增强相M7C3以及硼化物、硅化物和石墨构成。熔覆层的显微硬度和常温摩擦性能较H13钢显著提高,而其高温摩擦性能较H13钢基体提高较少。结论 SiC_p化学包覆Cu能减缓激光熔覆过程中SiC_p的分解,但分解速度还是过快。常温磨损时,高硬度碳化物和硅化物的覆层提高了材料的耐磨性能。高温下模具钢表面形成致密的氧化物薄膜,起到减磨降摩的作用,而高温下覆层无法形成致密氧化膜,导致其耐磨性能弱于常温。     

Effect of compositions on the microstructure and properties of plasma clad NiAl coating

NiAl intermetallic coating was in-situ synthesized by the plasma cladding process. The effect of atomic ratio of Ni to Al atoms 1 (coating 1), 2 (coating 2) and 3 (coating 3) on the microstructure and mechanical properties of plasma clad was studied by combining microstructural analysis and wear-resistant test. The obtained results indicated that the microstructure of the synthesized NiAl coating was compact and uniform in addition to few porosities and the NiAl coating well metallurgically bonded with the substrate. Coating 1 is mainly composed of NiAl and the solid solution γ-(Fe,Ni) phases. Coating 2 contains of NiAl, Ni₃Al and γ-(Fe,Ni). Coating 3 is mainly composed of Ni₃Al, γ-(Fe,Ni) and NiAl. Coating 3 has excellent wear-resistance property owing to high hardness and low friction coefficient. Ni3Al phase has great influence on wear-resistance property of coating 3. The main wear mechanism of coating 1 is multi-plastic deformation wear and adhesion wear. Grain abrasion is the main wear mechanism of coating 3. The main wear mechanism of coating 2 is grain abrasion and partly adhesive wear.     

Cr12MoV钢表面激光熔覆Ni/Ni-WC梯度涂层的组织与耐磨性能

利用脉冲Nd:YAG激光器在Cr12MoV模具钢表面熔覆了Ni/Ni-WC梯度涂层,通过X射线衍射仪、扫描电镜及能谱仪、高速往复摩擦磨损试验机以及白光干涉仪研究了梯度涂层的物相组成、耐磨性能和磨损形貌。结果表明:梯度涂层Ni60A+35%WC耐磨层物相主要由γ-(Ni, Fe)固溶体、WSi₂相以及多种碳化物等硬质相组成。梯度涂层间以及涂层与基体间没有裂纹和气孔等缺陷生成,在界面处表现为良好的冶金结合。Ni60A+35%WC耐磨层平均显微硬度约为基体的1.7倍,Ni/Ni-WC耐磨涂层的磨损机理主要为疲劳磨损和磨粒磨损,基体的磨损机理主要为粘着磨损和磨粒磨损。     

低合金钢表面Fe基B4C耐磨涂层组织与性能

目的在低合金结构钢表面制备一层高硬度、高耐磨的铁基陶瓷颗粒增强层,并研究熔覆层的微观结构及性能。方法利用等离子熔敷技术,在16Mn钢基体上熔敷Fe58合金粉与B_4C陶瓷粉的混合粉末。结果在16Mn钢表面成功制备了高硬度、高耐磨的铁基陶瓷颗粒增强层,陶瓷颗粒增强层致密、均匀、无气孔、无裂纹,且与基体结合良好。XRD及SEM结果表明,熔覆层生成了细小、均匀的碳、硼化物增强相,熔覆层与基体的相容性好,界面呈冶金结合,熔覆层的增强相主要有Fe2B、FeB、Cr7BC4、Cr7C3及B_4C相,Fe与B的化合物Fe2B、FeB呈链状沿晶界分布在(Fe,Ni)固溶体上,并与(Fe,Ni)固溶体在晶界形成网状结构。铬的碳、硼化物Cr7BC4和Cr7C3及未完全反应的B_4C陶瓷相,则呈不规则块状和点状在晶内弥散分布。熔覆层断面的显微硬度及表面磨粒磨损测试结果表明,熔覆层断面的显微硬度分布均匀,平均硬度可达11.9GPa,是16Mn钢基体的7.95倍,耐磨粒磨损性能是基体的7倍以上。结论晶内弥散分布的B_4C、Cr7BC4和Cr7C3硬质相与晶界成链状分布的Fe2B、FeB共同作用,使熔覆层的硬度、耐磨性明显提高。     

等离子熔覆-注射B4C铁基熔覆层组织耐磨性研究

目的采用等离子熔覆-注射工艺在Q235基体上制备B4C铁基熔覆层并研究其耐磨性。方法通过OM,SEM,EDS等分析熔覆层及界面的组织特征,并进行耐磨性测试。结果当B4C质量占主体熔覆材料质量的18%时,注射熔覆层表面比较平整,无裂纹。注射熔覆层组织致密,界面呈现平直的亮白色过渡层,稀释率小,与基体形成了良好的冶金结合。B4C陶瓷颗粒表面溶解会形成Fe,Cr等元素的硼化物。等离子熔覆-注射B4C熔覆层的耐磨性是42CrMo的22倍,是16Mn钢的41倍。结论等离子熔覆-注射B4C工艺能够增强B4C与熔覆层之间的结合力,提高熔覆层的硬度和耐磨性。     

电火花沉积 Fe 基涂层的组织及耐磨性能

通过电火花沉积技术在P20模具钢表面制备了Fe基涂层,利用SEM,XRD及摩擦磨损试验机等分析了涂层的组织结构、显微硬度及耐磨性能。结果表明:电火花沉积Fe基涂层组织均匀、致密;涂层中靠近界面处的组织为柱状枝晶,而涂层中上部组织为超细晶粒。涂层的平均硬度为637.1HV0.1,相比基体提高了1倍;涂层耐磨性优于基体,涂层中弥散分布的Cr7C3,CrB及Fe3C等硬质是Fe基涂层硬度及耐磨性提高的主要原因。涂层的磨损机理主要为磨粒磨损的微切削和疲劳磨损。     

大面积等离子束表面冶金铁基涂层的成形机理及组织结构

采用等离子束表面冶金技术,通过多道搭接方式在低碳钢基体上制备大面积铁基复合超厚涂层。基于大面积涂层成形的特点,探讨搭接率与涂层厚度等的变化规律,并利用扫描电镜、X射线衍射仪、金相显微镜、显微硬度计及磨损试验分析测试了涂层的相组成、组织及性能。结果表明:表面冶金涂层厚度可达3.0 mm,无裂纹、气孔等缺陷;组织为γ-(Fe,Ni)枝晶、M23C6、CrB及原位合成的TiC陶瓷颗粒,与基体呈良好的冶金结合。由于颗粒强化、细晶强化和弥散强化等多种强化作用,大面积Fe基超厚涂层具有良好的耐磨性能。     

42CrMo钢表面激光熔覆颗粒增强Co基涂层的组织与性能

为改进矿用截齿的耐磨性能,使用激光熔覆技术在截齿用42CrMo钢基体表面制备Co基复合涂层,并分析涂层的微观组织、硬度和耐磨性。结果表明,熔覆层形貌良好且与基体呈冶金结合。在激光作用下,WC颗粒发生溶解并与多种元素发生反应,熔覆层主要由γ-(Co, Fe)和碳化物组成。熔覆层组织呈梯度变化,过渡区组织为平面晶、枝状晶和柱状晶,熔覆区组织则为等轴枝晶和均匀分布的富W、Ti的碳化物颗粒。熔覆层平均显微硬度为995 HV,远高于基体(328 HV),同时热影响区的硬度也大幅提高。在相同的磨损条件下,熔覆层摩擦因数较低,体积磨损量仅为基体的13.5%。在摩擦过程中,弥散分布的细小碳化物颗粒逐渐凸起并起到承担载荷和抵抗磨损的作用,使熔覆层具有良好的耐磨性,磨损机制为轻微磨粒磨损。激光熔覆技术制备的颗粒增强Co基涂层,组织致密,性能良好,能显著地提高42CrMo钢的表面硬度和耐磨性。     

Characterization on laser clad nickel based alloy coating on pure copper

Nickel based alloy coating has been successfully deposited onto pure copper surface by laser cladding with coaxial powder feeding. Coating with thickness in the region of 1.5 mm can be obtained by depositing two layers of overlapping laser clad tracks. The microstructure observation from optical microscopy and scanning electron microscopy indicated that the coating was free of cracks and pores, and soundly bonded with the substrate. The X-ray diffraction analysis results showed that the coating was mainly composed of γ-(Ni, Cr, Mo, W) solid solution, some carbides and silicides. The average hardness of the coating was about HV_0.1 360, which was about 5 times that of the pure copper. The dry sliding wear tests showed the wear resistance of copper was significantly improved after laser clad nickel based alloy coating.     

等离子熔敷TiC/γ-(Fe,Ni)复合涂层组织与耐磨性

为了提高奥氏体不锈钢的耐磨性能,扩大其应用范围,以Ti-C-Fe-Ni混合合金粉末为原料,利用等离子熔敷技术在1Cr18Ni9Ti奥氏体不锈钢表面原位合成了TiC增强耐磨复合涂层。分析了涂层的显微组织结构,测试了涂层沿层深方向的硬度分布,评价了涂层在室温干滑动磨损试验条件下的摩擦磨损性能,结果表明:等离子熔敷TiC金属陶瓷增强复合涂层显微组织细小均匀,由花瓣状和少量颗粒状TiC初生相均匀分布在TiC/γ-(Fe,Ni)共晶基体上组成,涂层与不锈钢基材之间形成了完全冶金结合,涂层平均显微硬度约790 HV,涂层在室温干滑动磨损试验条件下表现出良好的耐磨性及较低的摩擦系数。