微纳米RDX颗粒级配对压装PBX性能影响

为了提高高聚物粘结炸药(PBX)的力学性能,降低其机械感度,采用溶液-水悬浮法,制备了含微纳米RDX不同颗粒级配(100/0,95/5,90/10,80/20)的PBXs。用光学显微镜观测其表观形貌,并测试了机械感度、力学性能以及爆速等性能。结果表明,微纳米RDX颗粒级配的PBX造型粉颗粒偏小、形貌规则、呈类球形。纳微米RDX颗粒级配为5/95的PBX性能最佳,撞击感度由44%降低到12%,摩擦感度由24%降低到4%;抗压强度从5.55 MPa提高到6.57 MPa,抗拉强度由0.66 MPa提高到0.77 MPa,抗剪强度由1.76 MPa提高到1.96 MPa;爆速从8033 m·s~(-1)增加到8186 m·s~(-1)。     

含发射药的粉状低爆速炸药研制

制备了含单基发射药的粉状低爆速炸药,并对其工艺进行了研究。讨论了该炸药的低爆速产生机理,研究了单基发射药的粒径、包覆剂和钝感剂的含量、炸药的密度对炸药性能的影响。测试了该炸药的低温性能、体积威力、机械感度和不同装填直径的爆速。并对该炸药在油田地质勘探中的应用效果进行了分析。结果表明,该低爆速炸药制备简单,能量和密度较高,用作震源炸药能有效地提高地震勘探的分辨率。     

高格尼能钝感浇注PBX设计及性能

通过系列浇注高聚物粘结炸药(PBX)的爆轰性能,拟合得到爆速与HMX含量的线性关系,研究了HMX颗粒特性及钝感剂含量对混合炸药机械感度的影响。结果表明,采用高品质HMX和3%的钝感剂时,混合炸药的安全性最好。在此基础上设计制备了一种组成及性能与B2273A(HMX/丁羟粘结剂90/10)接近的HMX基高固相浇注PBX炸药GO-1(HMX/丁羟粘结剂90/10)。其摩擦感度和撞击感度分别为5%和0,冲击波感度I50为17.7 mm,爆速为8587 m·s-1,格尼系数为2.80,爆轰性能、金属加速能力和安全性能优良,该炸药在枪击试验、烤燃试验中均为燃烧的低反应等级。     

含铝炸药爆热性能与破片加载特性关系探讨及验证

以浇注HMX 基含铝炸药为研究对象,构建炸药爆轰加载假设模型。探讨爆热与破片速度的关系,并使用 不同粒径设计了不同铝含量的炸药配方,测试了炸药爆速和爆热及其对全预制破片速度和穿甲率的影响。试验结果 表明：随着铝氧比和爆热的增加,破片速度和穿甲率呈现先升后降的趋势,当铝氧比和爆热分别为0.35 和6 200 kJ/kg 时,其破片速度和穿甲率分别为1 890 m/s 和89%,破片加载能力达到最大,验证了含铝炸药爆热与破片加载特性存 在数学极值关系,工程上存在最佳匹配点。     

纳米铝对DNTF压装混合炸药的爆热和热安定性影响

采用机械混合法制备了含5%纳米铝和含25%微米铝的DNTF压装混合炸药,测试了混合炸药的机械感度和爆热,同时对混合炸药的热安定性进行了分析。结果表明：与含30%微米铝的炸药对比,此炸药机械感度较低,但其爆热略低于含30%微米铝炸药;此炸药真空安定性优于含30%微米铝炸药,5s爆发点高,且其热失重率低于含微米铝炸药,说明加入纳米铝在一定程度上提高了DNTF压装混合炸药的热稳定性。     

24-二硝基苯甲醚基高爆速熔铸炸药爆轰性能表征

为了揭示2,4-二硝基苯甲醚 (DNAN)基不敏感熔铸炸药的爆轰特性,加快DNAN基熔铸炸药的应用,采用Fortran BKW代码计算了Octol炸药和不同组分DNAN基熔铸炸药的爆轰参数(爆速、爆压)。采用电测法、爆炸概率法和激光干涉测速技术分别对DNAN基配方DNAN 20/奥克托今80和Octol炸药的爆速、爆压、机械感度以及金属板驱动能力进行了试验测试。试验结果表明：该DNAN基炸药的爆速为8 436 m/s,爆压为31.23 GPa,爆轰性能优于Octol炸药;撞击感度为33%,摩擦感度为57%,机械感度低于Octol炸药;驱动金属板速度达到3 045 m/s,优于Octol炸药。该DNAN基高爆速熔铸炸药综合性能优于Octol炸药,可替代Octol炸药用于防空反导和大口径爆炸成型弹丸战斗部。     

CL-20/FOX-7基PBX的制备及其性能表征

为提高六硝基六氮杂异伍兹烷(CL?20)的安全性能,并保持其较高能量,以聚氨酯高聚物Estane为包覆剂,1,1?二氨基?2,2?二硝基乙烯(FOX?7)为含能降感成分,利用水悬浮包覆法制备了三种不同配比的CL?20/FOX?7基高聚物粘结炸药。采用扫描电子显微镜(SEM)、X射线衍射仪(XRD)、差示扫描量热仪(DSC)、撞击感度测试仪以及摩擦感度测试仪对样品的形貌结构、晶型、热分解特性以及样品的机械感度进行测试分析,用电测法对三种配比高聚物粘结炸药(PBX)爆速进行测试。结果表明,CL?20/FOX?7基炸药颗粒包覆效果较好,且CL?20和FOX?7均未发生转晶。三种CL?20/FOX?7基PBX表观活化能比细化CL?20分别提高了17.12,32.87 kJ·mol~(-1)和40.24 kJ·mol~(-1);活化焓(ΔH)较CL?20也明显提高;特性落高由细化CL?20的27.5 cm分别提高到58.3,56.5,54.2 cm。三种配比CL?20/FOX?7基PBX实测爆速分别为8474,8503,8577 mg·s~(-1),与PBXN?5相当,但特性落高较PBXN?5提升了48.5%以上,炸药安全性能明显提升。     

2,6-二氨基-3,5-二硝基吡啶-1-氧化物为基的耐热混合炸药性能

分别制备了以2,6-二氨基-3,5-二硝基吡啶-1-氧化物(ANPyO)为基,加入氟橡胶F2311、氟橡胶F2603及其两种混合物黏结剂和增塑剂组成的三种耐热混合炸药,进行了耐热性、感度、成型性、爆炸能量和破甲威力性能测试。结果表明,三种以ANPyO为基耐热炸药有良好的耐热性能,可以在200～250℃温度条件下使用;成型性能良好;机械感度比较接近,均低于单质ANPyO,撞击和摩擦感度最小值分别为10%和24%;爆速和破甲性能均高于以PYX基的混合炸药,爆速提高约400m.s-1,破甲深度提高约30mm。     

微/纳米HMX颗粒级配对PBX性能的影响

为了提升高聚物粘结炸药(PBX)的综合性能,通过颗粒级配的方式,将低感度的微米和纳米奥克托今(HMX)应用到压装型PBX中,采用溶液-水悬浮法制备了4种HMX基PBX造型粉,并压制成药柱。对不同微纳米颗粒级配的JO-1、JO-2、JO-3和JO-4样品(粗颗粒/微米/纳米HMX的质量比分别为100/0/0、60/35/5、60/30/10、60/25/15),观测其表面微观结构,测量组分含量、撞击感度、摩擦感度、热分解特性、抗压性能和爆速等参数,并进行对比分析和讨论。结果表明,当粗颗粒(d_(50)=100μm)/微米(d_(50)=1μm)/纳米(d_(50)=100 nm)HMX的质量比为60/30/10时,所制备的JO-3样品有最好的性能。与单一粗颗粒HMX基PBX的JO-1样品相比,JO-3样品表面更光滑,撞击感度降低了38.3%,摩擦感度降低了22.7%,自发火温度提高了5.17℃,抗压强度提高了46%,爆速提高了55 m·s~(-1),HMX基PBX的综合性能显著提升。     

TKX-50基混合炸药的爆轰及安全性能

为了研究5,5'-联四唑-1,1'-二氧二羟胺盐(TKX-50)基混合炸药的爆轰及安全性能,以F2314氟橡胶为粘结剂,采用淤浆捏合法制备了典型TKX-50基混合炸药。按照国军标(GJB-772A-1997)和自建的标准测试方法对炸药的爆轰性能(爆速、爆压、爆热、圆筒比动能)和安全性能(撞击感度、冲击波感度、热刺激感度)进行了测试,并将实测性能与PBX-9501等炸药进行了对比分析。结果表明,在爆轰性能方面,与PBX-9501相比,制备的TKX-50基混合炸药实测爆速值为9037 m·s~(-1)(密度1.860 g·cm~(-3)),但其爆热(5055 J·g~(-1))、爆压(26.4 GPa)和做功能力(1.377 kJ·g~(-1))较低。在安全性能方面,TKX-50原材料经重结晶后撞击感度可显著降低,最低撞击能由5J提高至32J,TKX-50基混合炸药的冲击波感度(L_(50)=15.1 mm)低于HMX基混合炸药(L_(50)=22.6 mm)。此外,TKX-50的热分解温度(240℃)、5 s爆发点(277℃)均低于HMX(285℃,327℃),以TKX-50为基的混合炸药在热刺激下更容易发生剧烈反应。     

Preparation and Properties of PBXs Based on FOX-7 in Controlled Fragmentation Warhead Application（英）

Polymer bonded explosive(PBX)formulations were successfully prepared in the laboratory scale containing 1,1-diamino-2,2-dinitroethene(FOX-7)and hexogen(RDX)as brisant high explosives and different binder types of polyurethane(PU)based on glycidyl azide polymer(GAP) and hydroxyl-terminated polybutadiene(HTPB) as an energetic and inert polymeric binder respectively.Casting technique was used for the preparation of different PBX formulations based on FOX-7/RDX and PU(GAP/HTPB)with 14% binder.The sensitivity to different initial impulses and performance characteristics of the explosive and lethal zone of the tested controlled fragmentation warhead by the fragmentation warhead assessment test(arena test)were studied,in which the arena test was carried out with a controlled fragmentation warhead made from Ck45 steel,with dimensions(100 mm length,30 mm outer diameter and 3 mm thickness).Results show that PBXGF4 has lower sensitivity to impact and heat than those of PBXGR4 by 188.4% and 3.2% respectively.Its friction sensitivity is the same as that of PBXGR4.It has better performance,in which detonation velocity increases by 2.1% and brisance increases by 0.5% when compared with those of PBXGR4.It was concluded that PBXGF4 which based on FOX-7 bonded with PU/GAP matrix has good characteristics as PBX,specially in the sensitivity to impact and can be applied for replacing PBXs based on RDX in the advanced PBXs for low sensitive fragmentation warheads.     

不同粘结体系对PBX炸药能量输出特性的影响

粘结剂作为PBX炸药中重要的添加剂,对炸药的力学性能、能量特性等都有很大的影响.为研究不同粘结体系对PBX炸药水下爆炸能量特性的影响,首先对不同粘结体系炸药配方进行优化设计,然后进行不同粘结体系PBX炸药的水下爆炸试验.试验结果表明:与HTPB惰性粘结体系炸药相比,含能粘结体系应用于PBX炸药后,比冲击波能提高了12%~23%;但是由于含能粘结体系力学和工艺性能的限制,使得炸药固含量降低,降低了炸药的气泡能.总的来看,TEGDN、GAP、HTPB粘结体系的PBX炸药总能量分别达到了2.01、1.99、2.15倍TNT当量.     

ETPE黏结剂对RDX-Al体系的包覆研究

为了研究以3,3-双叠氮甲基氧杂环丁烷(BAMO)与3-叠氮甲基-3-甲基氧杂环丁烷(AMMO)为基合成的含能热塑性弹性体(ETPE,数均分子量在20000左右)作黏结剂对黑索今(RDX)-铝粉(Al)体系炸药造型粉感度的影响,对ETPE,RDX和Al粉三者的接触角进行了测定,由接触角结果计算出ETPE与RDX和Al粉...     

3,4-二硝基吡唑的性能表征及应用

为了探究3,4-二硝基吡唑(DNP)替代TNT作为新型熔铸炸药载体的可行性,采用光学显微镜、傅里叶红外变换光谱仪、紫外可见分光光度计及DTA/TG热分析仪器对其结构进行了表征,利用氧弹量热仪、电测法分别测试了DNP爆热、爆速,并应用VLW程序计算了TNT/CL-20,DNP/CL-20混合炸药的爆轰参数。结果表明,DNP热分解过程主要分为吡唑环断裂和硝基脱环、自催化加速反应两个阶段,热分解表观活化能为131 k J·mol-1;DNP爆热、爆速分别为4326 k J·Kg~(-1)、7633 m·s~(-1),计算得出DNP/CL-20混合炸药爆轰性能明显优于TNT/CL-20混合炸药,当DNP/CL-20=2∶3(质量比)时,计算爆压为39.4 GPa,爆速为8961 m·s~(-1)。     

GAP 应用研究进展

为研制高能量、高性能的混合炸药,引入聚叠氮缩水甘油醚(GAP)作为含能粘结剂。在分析GAP物理、化学性能的基础上,总结前人在 GAP 固化体系力学性能研究和 GAP 在推进剂和混合炸药中的应用等方面的工作。结果表明：引入适当的高聚物与GAP发生共聚,可改善GAP粘接体系的力学性能;将GAP引入混合炸药中,可有效提高混合炸药的能量和改善混合炸药的力学性能。     

硼铝金属化炸药的制备及性能表征（英）

以奥克托今(HMX)为基,加入氧化剂高氯酸铵(AP)、硼铝复合粉和粘结剂端羟基聚丁二烯(HTPB),设计和制备硼铝金属化炸药.用扫描电子显微镜(SEM)观测了硼粉、铝粉及硼铝复合粉的外观形貌;用热重-差示扫描量热(TG-DSC)分析了奥克托今(HMX)和高氯酸铵(AP)对硼铝粉热氧化特性的影响,对硼铝粉的反应动力学机理进行了深入了解;为掌握金属化炸药对各种外界能量刺激的安全性以及传播爆轰波的能力, 测试了硼铝金属化炸药的撞击感度、摩擦感度、电火花感度、雷管起爆感度和起爆特性.结果表明,硼铝复合粉中,球形Al粉的表面有许多小颗粒的硼粉;在室温~1000 ℃范围和N2气氛下,虽然压力对HMX和AP的热分解峰温有影响,但是,Al粉和B粉仅发生部分氧化,不能燃烧;硼铝金属化炸药的撞击感度为60%~80%,摩擦感度均为100%,电火花感度为3.83~6.40 kV,可以用8#工业雷管直接起爆,表明无粘结剂的硼铝金属化炸药感度较高,使用钝化HMX和AP后其感度明显降低,添加聚氨酯粘结剂后其感度进一步下降,当聚氨酯粘结剂含量为20%时,HMX基硼铝金属化炸药的撞击感度小于10%,摩擦感度小于30%,显示能满足混合炸药制备及加工工艺的安全要求;此外,直径Φ50 mm的硼铝金属化炸药可以用8#工业雷管直接起爆,能稳定传播爆轰波,表现出较强的后效做功能力.     

PBT/A3 基RDX 含铝炸药爆炸能量特性研究

为掌握PBT/A3 粘结剂体系对含铝炸药爆炸能量的影响特性,以PBT/A3 粘结剂体系为研究对象,复合 RDX 和Al 粉设计PBT/A3 基RDX 含铝炸药配方。测试炸药复合体系密度、爆速、爆热等性能,并与相同条件HTPB 基RDX 含铝炸药进行对比,探讨PBT/A3 粘结剂对炸药密度及爆炸本征能量爆速和爆热影响;开展PBT/A3 基含铝 炸药冲击波超压性能测试,对其近/远场冲击波能量释放特性进行分析和讨论。研究结果表明：较于HTPB 基RDX 含铝炸药,PBT/A3 粘结剂对复合体系装药密度提升9.1%,爆速和爆热分别提升1.45%和11.47%,能量密度提升较 为明显;PBT/A3 基炸药近场超压当量为1.6 倍,远场超压当量为1.69 倍,PBT/A3 含能粘结剂体系的引入改善了复 合体系氧平衡,有利于Al 粉充分燃烧提高其远场能量释放。     

浇注六硝基六氮杂异伍兹烷基混合炸药驱动性能

为研究浇注六硝基六氮杂异伍兹烷（CL-20）基混合炸药的金属驱动特性,制备了CL-20∶端羟基聚丁二烯（HTPB)∶Al-Zn配比为84∶11∶5的浇注CL-20基炸药试样GWL. 测试GWL密度、爆速、爆压、机械感度以及快速烤燃、慢速烤燃和枪弹撞击3项不敏感特性,发现其炸药密度为1.78 g/cm³、爆速为8 750 m/s、爆压为33.21 GPa,不敏感试验反应等级均为燃烧,机械感度也符合炸药使用要求。采用50 mm标准圆筒试验测试了GWL炸药试样的做功能力,发现GWL炸药试样驱动圆筒在41 mm特征点上的速度为1 730 m/s. 应用有限元分析软件Autodyn时圆筒试验过程进行数值模拟计算,通过对比试验结果与数值模拟结果,得到GWL炸药的JWL状态方程;设计CL-20∶HTPB配比为89∶11的无金属粉炸药试样GC,在相同试验条件下测试了GC的机械感度与爆炸驱动能力,结果表明GC与GWL两种炸药试样驱动能力相当,但是GC炸药的机械感度高于GWL炸药。采用Autodyn软件建模对比研究了GWL炸药与C-1炸药和LX-14炸药的驱动能力,结果显示：GWL炸药驱动破片的终速比LX-14炸药高2.6%;其驱动性能优良,是一种高能低感度的新型CL-20基浇注炸药。