SiO2/Si(111)表面Ge量子点的生长研究

Si衬底用化学方法清洗后,表面大约残余1.0 nm厚SiO2薄膜.利用原子力显微镜(AFM)和反射高能电子衍射(RHEED)来研究温度和Ge蒸发厚度对在SiO2薄膜表面生长的Ge量子点的影响.实验结果表明,当衬底温度超过500 ℃时,SiO2开始与Ge原子发生化学反应,并形成与Si(111)表面直接外延的Ge量子点.在650 ℃时,只有Ge的厚度达到0.5nm时,Ge量子点才开始形成.     

Sol-gel法制备Si基Bi_(3.15)Nd_(0.85)Ti_3O_(12)铁电薄膜

采用Sol-gel法分别在Si(100)和Si(111)衬底上制备Bi_(3.15)Nd_(0.85)Ti_3O_(12)(BNT)铁电薄膜。研究了衬底、退火温度、退火保温时间和薄膜厚度等因素对BNT铁电薄膜结晶和微观结构的影响。在500℃退火的BNT薄膜已经结晶形成层状钙钛矿相;升高退火温度(500～800℃)、延长保温时间(30～150min)、增加薄膜厚度(170～850nm),都有利于BNT薄膜晶粒长大,其中退火温度和薄膜厚度是影响晶粒长大的关键因素;每次涂覆的厚度大约是85nm。与Si(100)衬底相比,由于Si(111)与BNT薄膜具有更好的晶格匹配,因此BNT薄膜在Si(111)衬底上更容易结晶。     

SiO2层上沉积的纳米多晶硅薄膜及其特性

采用低压化学气相沉积(LPCVD)系统以高纯SiH4为气源,在p型10.16 cm<100>晶向单晶硅衬底SiO2层上制备纳米多晶硅薄膜,薄膜沉积温度为620℃,沉积薄膜厚度分别为30 nm、63 nm和98 nm.对不同薄膜厚度的纳米多晶硅薄膜分别在700℃、800℃和900℃下进行高温真空退火.通过X射线衍射(XRD)、Raman光谱、扫描电子显微镜(SEM)和原子力显微镜(AFM)对SiO2层上沉积的纳米多晶硅薄膜进行特性测试和表征,随着薄膜厚度的增加,沉积态薄膜结晶显著增强,择优取向为<111>晶向.通过HP4145B型半导体参数分析仪对沉积态掺硼纳米多晶硅薄膜电阻I-V特性测试发现,随着薄膜厚度的增加,薄膜电阻率减小,载流子迁移率增大.     

Sol-gel法制备Pb(Zr0.53Ti0.47)O3铁电薄膜

利用Sol-gel工艺在Pt/Ti/SiO2/Si衬底上制备了Pb(Zr0.53Ti0.47)O3(PZT)薄膜,研究了退火温度、保温时间和薄膜厚度对其晶相、微观结构和铁电性能的影响.在500℃退火处理的PZT薄膜开始形成钙钛矿相;在550℃退火处理的PZT薄膜基本形成钙钛矿相结构;升高退火温度(500～850℃)、延长保温时间(30～150min)、增加薄膜厚度(120～630nm)都有利于PZT晶粒的长大.在650～750℃退火的PZT薄膜具有较好的铁电性能,保温时间对PZT薄膜的铁电性能影响不大,PZT薄膜的厚度为200～300nm时可以得到比较好的铁电性能.在退火温度750℃、保温时间30min条件下退火处理厚310nm的PZT薄膜,其剩余极化值(2Pr)和矫顽电场(2Ec)分别是72μC/cm2、158kV/cm.     

Si片上PbTiO3薄膜的XPS研究

用溶胶 凝胶方法在Si上成功地制备了钙钛矿型的PbTiO3薄膜。X射线衍射结果显示 ,在热处理温度为 750～ 90 0℃范围内 ,随温度升高 ,薄膜由多晶结构转变为定向结晶。X射线光电子能谱分析发现 ,薄膜表面存在SiO2 薄层 ,其厚度大约为 0 6nm ,该薄层是在制膜过程中衬底Si通过PbTiO3薄膜扩散到表面与大气中的O2 反应而形成的。在 750℃热处理的薄膜 ,膜层中不含SiO2 ,但温度升高 ,膜层中存在SiO2 成分 ,这可能是Si在向表面扩散过程中与膜中的O反应生成的。表面SiO2 可通过Ar离子的轻微溅射而消除 ,而膜内SiO2 成分只能通过调节工艺参数来消除     

不同环境气压下激光沉积制备锗纳米薄膜的研究

采用脉冲激光沉积(PLD)技术,在不同环境压强下于室温Si衬底上沉积制备出了Ge纳米薄膜.用X射线衍射仪(XRD)和扫描电子显微镜(SEM)研究了环境压强对薄膜的微观结构、形貌以及膜厚的影响规律.结果表明:所制备的纳米薄膜中Ge均为晶态;随着环境压强的增大,薄膜表面由常规的量子点镶嵌结构演变为类网状结构;膜厚随着环境压强的增大而减小.     

Ge基GaAs薄膜和InAs量子点MBE生长研究

采用分子束外延(MBE)法,在优化Ge衬底退火工艺的基础上,通过对比在(001)面偏<111>方向分别为0°、2°、4°和6°的Ge衬底上生长的GaAs薄膜,发现当Ge衬底的偏角为6°时有利于高质量GaAs薄膜的生长;通过改变迁移增强外延(MEE)的生长温度,发现在GaAs成核温度为375℃时,可在6°偏角的Ge衬底上获得质量最好的GaAs薄膜。通过摸索GaAs/Ge衬底上InAs量子点的生长工艺,实现了高效的InAs量子点光致发光,其性能接近GaAs衬底上直接生长的InAs量子点的水平。     

热循环退火对InAs/Si(211)薄膜结构和电学性能的影响

InAs作为III-V族化合物半导体材料,可以应用于磁阻和霍尔元器件、量子点激光器元件、太阳能电池和红外探测器元件等方面,具有广泛的研究和应用前景.本文以Si(211)为衬底,采用热壁外延(hot wall epitaxy,HWE)技术制备了InAs薄膜,研究热循环退火(thermal cycle annealing,TCA)次数对InAs/Si(211)薄膜结构及电学性能的影响.热壁外延制备InAs薄膜的衬底温度为400℃,生长时间为4 h,不同的热循环退火次数为2、4、6、8、10.X射线衍射(XRD)测试表明:利用HWE技术在Si(211)衬底表面成功制备了闪锌矿结构的InAs薄膜,且沿(111)取向择优生长;TCA能够明显增强Si(211)衬底表面生长的InAs薄膜的择优取向.扫描电子显微镜(SEM)及原子力显微镜(AFM)测试分析表明:随着TCA次数增加到6次,InAs/Si(211)薄膜表面由于晶粒细化作用变得均匀平整,表面粗糙度从69.63 nm降低到56.43 nm,此时霍尔迁移率达到2.67×10~3cm~2/(V·s);过多的退火次数(≥8次)又会使薄膜表面的晶粒过大、缺陷增多,导致薄膜性能下降.     

Ge/Si量子点生长的研究进展

回顾了近年来在Ge/Si量子点生长方面的研究进展.主要讨论了为了提高量子点空间分布有序性、增大量子点的密度、减小量子点的尺寸及改善其分布均匀性而采取的各种方法,如图形衬底辅助生长、表面原子掺杂及利用超薄SiO2层辅助生长等,以及Ge量子点的演变及组分变化.     

Si(111)衬底上离子束溅射沉积法生长β-FeSi2薄膜的研究

采用离子束溅射Fe靶的方法在500～800℃的Si(111)衬底上制备出不同种类的铁硅化合物.当衬底温度为700℃时得到厚度为500nm的单相的β-FeSi2薄膜,高分辨透射电镜证实该β-FeSi2薄膜为局部外延,薄膜和Si衬底之间界面明显,没有中间层.     

Structural and optical properties of AlxOy/Pt/AlxOy multilayer absorber

We report on the microstructure and optical properties of Al_xO_y–Pt–Al_xO_y interference-type multilayer films, deposited by electron beam (e-beam) deposition onto corning 1737 glass, silicon (1 1 1) and copper substrates. The structural properties were investigated by Rutherford backscattering spectrometry, X-ray diffraction, scanning electron microscopy, energy dispersive X-ray spectroscopy and atomic force microscopy. The optical properties were extracted from specular reflection/transmission, diffuse reflectance and emissometer measurements. The stratification of the coatings consists of a semi-transparent middle Pt layer sandwiched between two layers of Al_xO_y. The top and bottom Al_xO_y layers were non-stoichiometric with no crystalline phases present. The Pt layer is in the fcc crystalline phase with a broad size distribution and spheroidal shape in and between the rims of Al_xO_y. The surface roughness of the stack was found to be comparable to the inter-particle distance. The optical calculations confirm a high solar absorptance of ∼0.94 and a low thermal emittance of ∼0.06 for the multilayer stack, which is attributed not only to the optimized nature of the multilayer interference stacks, but also to the specific surface morphology and texture of the coatings. These optical characteristics validate the spectral selectivity of the Al_xO_y–Pt–Al_xO_y interference-type multilayer stack for use in high temperature solar-thermal applications.     

Synthesis of a new perovskite Pb(Li14Nb34)O3

A high-pressure technique was adopted to obtain perovskite-type $\text{Pb(Li}{}_{\mathrm{<mtext>1</mtext><mtext>4</mtext>}}\text{Nb}{}_{\mathrm{<mtext>3</mtext><mtext>4</mtext>}}\text{)}\text{O}{}_3$. A new perovskite $\text{Pb(Li}{}_{\mathrm{<mtext>1</mtext><mtext>4</mtext>}}\text{Nb}{}_{\mathrm{<mtext>3</mtext><mtext>4</mtext>}}\text{)}\text{O}{}_3$ was characterized to have a cubic symmetry with $\text{a}{}_{\mathrm{<mtext>o</mtext>}}\text{= 4.069}\text{A}\text{?}$; Li and Nb ions in the B-site of perovskite lattice may be in a random arrangement.     

Bulk crystalline BaPb34Bi14O3: A ceramic superconductor

The preparation conditions of the high T_C ceramic superconductor Ba(Pb,Bi)O₃ is correlated with the superconducting transition. Transition onsets of all materials are similar, but transition widths and transition completeness is strongly dependent on firing temperature. Only materials prepared over a narrow temperature range, resulting in a nearly ideal weight loss, have a complete and narrow transition.     

Optimization of AlxOy/Pt/AlxOy multilayer spectrally selective coatings for solar-thermal applications

Spectrally selective Al_xO_y/Pt/Al_xO_y multilayer absorber coatings were deposited onto corning 1737 glass, Si (111) and copper substrates using electron beam (e-beam) vacuum evaporator at room temperature. The employment of ellipsometric measurements and optical simulation was proposed as an effective method to optimize and deposit multilayer solar absorber coatings. The optical constants (n and k) measured using spectroscopic ellipsometry, showed that both Al_xO_y layers, which used in the coatings, were dielectric in nature and the Pt layer was semi-transparent. The optimized multilayer coatings exhibited high solar absorptance α ∼ 0.94 ± 0.01 and low thermal emittance ? ∼ 0.06 ± 0.01 at 82 °C. The Rutherford backscattering spectroscopy (RBS) data of Al_xO_y/Pt/Al_xO_y multilayer absorber indicated the Al_xO_y layers present in the coating were nearly stoichiometry. The scanning electron microscope analysis (SEM) result indicated that the average diameter and inter-particles distance of Pt grains were statistically about 146 ± 0.17 nm and 6-10 ± 0.2 nm respectively.     

Electrostriction in Pb (Zn13Nb23)O3

The electrostriction in $\text{Pb (Zn}{}_{\mathrm{<mtext>1</mtext><mtext>3</mtext>}}\text{Nb}{}_{\mathrm{<mtext>2</mtext><mtext>3</mtext>}}\text{)}\text{O}{}_3$ crystals has been investigated using a strain gauge method. In the ferroelectric phase below 140 C, the strain vs the electric field shows a hysteresis, which is ascribed to the effect of ferroelectric domains. A quadratic relation holds between the strain x and the electric polarization P as x = QP² above about 170 C in the paraelectric phase. Values of the electrostrictive Q coefficients are determined from the measurements near 190 C, as Q₁₁ = 1.6·10^?2m⁴/C², Q₁₂ = ?0.86·10^?2m⁴/C², and Q₄₄ = 0.85·10^?2m⁴/C².     

Magnetic,electrical and thermal studies on the V1−xMox02

The monoclinic-to-tetragonal structure transition of oxides V_1?xMo_x0₂ with $\text{0≤}\text{x}\text{≤0.20}$ has been studied by means of DTA, X-ray diffraction, magnetic susceptibility (powder samples) and electrical conductivity (single crystals) measurements within the temperature region 80 K to 400 K. A linear decrease of the transition temperature of 11 K per atom % Mo was observed. The magnetic susceptibility of the low temperature phase was found to be temperature independent paramagnetic for all preparations. Electrical conductivity measurements on the same phase showed crystals with $\text{x}\text{? 0.04}$ to be semiconducting, while a metallic behavior was observed in the region $\text{0.10 ?}\text{x}\text{? 0.14}$.     

n-PbTep+−Pb1−xSnxTe heterojunctions prepared by a modified hot wall technique

$\text{n-PbTe}\text{p}{}^{\mathrm{+}}\text{?}\text{Pb}{}_{\mathrm{1?x}}\text{Sn}{}_{\mathrm{x}}\text{Te}$ heterojunctions with a long wavelength spectral cutoff (λ_c ≈ 6 μm) were prepared using the double-channel hot wall technique. The electrical and photoelectrical properties of the heterojunctions at 77, 197 and 300 K were investigated. Detectors with R_oA equal to 170 Ω cm² and a quantum efficiency of 25–40% were obtained. Reasons for the shift of the long wavelength spectral cutoff of the heterojunctions towards shorter wavelengths are given.     

Reactive plasma deposited SixCyHz films

Si_xC_yH_z films have been prepared at 200°C by reactive plasma deposition from SiH₄ and CH₄ diluted in helium in a tubular reactor. These films have a ratio s (equal to $\text{Si}\text{(}\text{Si+C}\text{))}$ ranging from 0.2 to 0.8, a refractive index ranging from 1.96 to 2.6 and an optical energy band gap in the range 2.7-2.2 eV. The total quantity of hydrogen in the film is 40% when s=0.5. Infrared analysis shows that these films have large fractions of homonuclear bonds and that this material is best described as a polymer. Mass spectrometric measurements of the gaseous products formed in the SiH₄-CH₄-He plasma have been performed and the results are related to the composition of the deposited layers.     

Core-current-enhanced domain-wall pinning in nanocrystalline Fe/sub 73.5/Cu/sub 1/Nb/sub 3/Si/sub 15.5/B/sub 7/ ribbon

We have studied the influence of surface fields H/sub p/ (generated by either direct or alternating core current) on soft magnetic properties of amorphous and nanocrystalline Fe/sub 73.5/Cu/sub 1/Nb/sub 3/Si/sub 15.5/B/sub 7/ ribbon. While in an amorphous ribbon the coercive field H/sub c/ decreases with H/sub p/, in the same optimally annealed ribbon (H/sub c/=1.3 A/m, M/sub m//spl ap/M/sub s/) H/sub c/ increases with H/sub p/ for all the explored types of H/sub p/ (static and dynamic with different phases with respect to that of the magnetizing field H). The unexpected increase of H/sub c/ in nanocrystalline ribbon is associated with the influence of H/sub p/ on the surface and main (inner) domain structure. Here, we develop a model that takes into account this influence and explains the experimental results.     

Interfacial microstructure of NiSix/HfO2/SiOx/Si gate stacks

Integration of NiSi_x based fully silicided metal gates with HfO₂ high-k gate dielectrics offers promise for further scaling of complementary metal-oxide- semiconductor devices. A combination of high resolution transmission electron microscopy and small probe electron energy loss spectroscopy (EELS) and energy dispersive X-ray analysis has been applied to study interfacial reactions in the undoped gate stack. NiSi was found to be polycrystalline with the grain size decreasing from top to bottom of NiSi_x film. Ni content varies near the NiSi/HfO_x interface whereby both Ni-rich and monosilicide phases were observed. Spatially non-uniform distribution of oxygen along NiSi_x/HfO₂ interface was observed by dark field Scanning Transmission Electron Microscopy and EELS. Interfacial roughness of NiSi_x/HfO_x was found higher than that of poly-Si/HfO₂, likely due to compositional non-uniformity of NiSi_x. No intermixing between Hf, Ni and Si beyond interfacial roughness was observed.