HSA 340高强度钢激光拼焊板焊缝组织与拉伸性能分析

选取1.5mm和2.0mm厚度的HSA340高强度钢进行激光拼焊,焊后对焊接接头进行金相检验及微观硬度测试,分析了焊缝、母材及热影响区的组织特性;对焊后试样进行拉伸试验,分析了高强度钢激光拼焊板的单拉特性,并结合拼焊板的微观组织,详细阐述了拉伸性能和焊接组织的关系。结果表明,拼焊板焊接热影响区的微观特性,决定了该区域具有良好的力学性能;提高焊缝中的针状铁素体含量,可提高试件拉伸性能;焊缝中马氏体的存在,提高了焊缝抗拉强度与硬度。     

高强度差厚激光拼焊板焊缝特性实验研究

针对激光差厚拼焊板DP600/H340LAD+Z,采用显微硬度测试方法和显微金相组织观察分析方法对其焊缝的特性进行了实验研究.测试分析了母材、焊缝及热影响区的显微硬度和微观组织特性讨论了焊缝特性对于差厚拼焊板成形性能的影响.结果表明,激光焊缝能够满足板料成形的要求.     

22MnB5/H340LA异种汽车用钢激光拼焊接头组织性能研究

对1.5 mm厚的热成形钢(22MnB5)和低合金高强钢(H340LA)进行了激光拼焊。测试了接头的杯突性能、拉伸性能和硬度。采用光学显微镜观察拼焊板接头各区域的微观组织。结果表明,采用设定的拼焊工艺获得的焊接接头杯突值(IE)较22MnB5母材下降率小于30%,破裂方向垂直于焊缝;拉伸试样断裂在H340LA母材上。22MnB5侧热影响区硬度最高,焊缝区次之。22MnB5侧的热影响区宽约0.35 mm,H340LA侧的热影响区宽约0.27 mm,焊缝宽度为1.02 mm。22MnB5侧热影响区完全淬火区由马氏体组成,不完全淬火区由马氏体+铁素体组成,焊缝组织主要为马氏体,H340LA侧的热影响区主要为铁素体和贝氏体。     

不等厚高强钢激光拼焊板焊缝组织及胀形性能分析

采用激光焊接方法,针对1.8mm厚的SAPH440与2.2mm厚的DP600高强钢实施激光拼焊.测试了不等厚拼焊板焊接接头的金相组织以及显微硬度,然后通过杯突试验对所得到的不等厚高强钢拼焊板的胀形性进行了研究,进一步与母材的胀形性相比较.结果表明,焊缝的金相组织为针状铁素体和板条马氏体,焊缝两侧硬度分布不同,焊缝处的硬度要高于母材.拼焊板的杯突值低于任何一侧母材的杯突值,焊缝的位置对不等厚拼焊板的胀形性有一定的影响,薄板所占比例越大拼焊板的胀形性越好,在胀形成形过程中焊缝向厚板侧移动.     

ST14钢激光拼焊板焊缝组织及成形性能分析

对1.5mm和0.8mm两种规格的ST14钢等厚激光拼焊板焊缝部位进行杯突试验,比较焊缝与母材杯突值;再对由这两种规格组合拼焊的不等厚激光拼焊板进行单向拉伸试验,检验拼焊板经拉伸后的断裂部位;分析焊缝区组织及其硬度变化,研究激光焊接参数变化对ST14钢拼焊板成形性能的影响.结果表明,焊缝深冲性能低于母材,焊缝杯突值受焊接速度影响,随焊接速度增加而增加;激光焊缝抗拉强度高于母材;对于1.5 mm拼焊板,提高焊接速度,加快焊缝冷却,有利于生成细小的针状铁素体,可提高激光拼焊板的成形性能;而0.8 mm板焊缝生成晶粒细小的粒状贝氏体组织,可使焊缝区材料成形性能接近母材;焊缝及其热影响区的硬度高于母材硬度.     

不等厚DC56D+Z/HC180BD+Z钢激光拼焊焊接接头性能分析

对1.5 mm厚的DC56D+Z与0.7 mm厚的HC180BD+Z两种常用汽车板材进行激光拼焊,测试了不等厚激光拼焊板的金相组织、显微硬度和力学性能。结果表明:焊缝处与基体的金相组织均为铁素体,在焊接热循环的作用下,焊缝与基体的组织形貌差异较大。焊缝两侧硬度呈非对称分布,焊缝处最高硬度达到200 HV,高于母材。接头的单向拉伸断裂发生在HC180BD+Z钢侧,强度略低于HC180BD+Z钢母材,但断后伸长率仅为HC180BD+Z钢母材的56.8%。杯突试验后,断裂位置均发生在薄板侧,随着薄板侧占比增大,其焊缝由直线型转变为抛物线型。     

SPCC冷轧钢光纤激光拼焊工艺及焊缝组织研究

采用数控光纤激光焊接机,对1.2mm+2.5 mmSPCC冷轧板进行不等厚拼焊,研究了焦点位置、激光功率与焊接速度、保护气体等工艺参数对焊缝形成、熔深的影响,优化工艺参数可以获得深而窄、均匀美观的焊缝;焊后对焊接接头进行金相分析和拉伸、杯突试验.结果表明,热影响区组织细小、性能优良,焊缝冷却后出现错位马氏体和针状铁素体组织,提高了焊缝的硬度和韧性,拉伸断裂位置位于母材,表明焊接接头的力学性能优于母材.     

DP590激光拼焊板焊接性能和成形性

激光拼焊板作为车身轻量化的重要技术,在汽车行业中应用前景广阔。研究了1.6 mm和2.0 mm规格的DP590激光拼焊板的焊接接头力学性能,并对其成形性能进行了分析。结果表明,焊接接头强度高于母材强度,但其延展性低于母材;焊缝区的显微硬度分布均匀,热影响区不存在明显的软化点;杯突试验中焊接接头开裂位置均在母材上,断口为韧性断裂,焊缝质量良好。     

B170P1差厚高强钢激光焊接工艺与力学性能分析

选取1.0mm和1.5mm厚的B170P1高强度钢为研究对象,采用不同激光焊接工艺参数对其进行激光拼焊,焊后对焊接接头进行金相检验及显微硬度测试,分析了母材、焊缝及热影响区的微观组织特性;对焊后试样进行拉伸试验,研究了激光焊接工艺对力学性能的影响.结果表明,焊接功率的增加造成焊缝中粒状贝氏体数量增多,材料韧性变差;焊接速度大时焊缝中晶界铁素体以条状居多,焊接速度小时焊缝中主要是块状铁素体;激光热输入较小时,晶粒尺寸随热输入的增加增长迅速,调节热输入大小可抑制晶粒增长.     

06Cr25Ni20奥氏体不锈钢钢管焊接接头的组织和性能

通过拉伸和维氏硬度测试以及金相分析,对8 mm厚的06Cr25Ni20奥氏体不锈钢钢管焊接接头的显微组织和力学性能进行研究。结果表明:采用?2.5 mm H0Cr26Ni21焊丝进行TIG打底焊、?4 mm A402焊条进行SWAW填充焊和盖面焊的焊接接头性能良好,焊缝区和热影响区硬度都略高于母材;焊缝组织为奥氏体+少量铁素体组织,热影响区为粗大奥氏体组织;拉伸断裂于母材区域,为韧性断裂;并且焊接接头的抗拉强度高于母材抗拉强度,能达到560MPa。     

130mm铝合金扫描激光填丝焊接头微区组织和性能

针对船用130 mm 5A06铝合金厚壁结构件的扫描激光填丝焊接头,对其焊缝（weld metal,WM）、热影响区（heat affected zone,HAZ）及母材（base metal,BM）的显微组织进行研究,并通过维氏硬度和微型剪切试验研究了接头各区力学性能差异.结果表明,5A06铝合金单激光焊缝以等轴晶为主,填丝焊焊缝以柱状晶为主,HAZ和BM晶粒比WM粗,母材及热影响区为轧制的纤维状组织;由于焊接热循环作用,接头热影响区硬度略高于母材,抗剪强度二者差别不大,单激光焊缝硬度和抗剪强度略高于填丝层.总体而言,焊缝区强度低塑性好,母材及热影响区强度高塑性低.     

Effect of Laser Welding Process Parameters on Microstructure and Mechanical Properties on Butt Joint of New Hot-Rolled Nano-scale Precipitation-Strengthened Steel

A 4 kW fiber laser was chosen to weld the new hot-rolled nano-scale precipitation-strengthened steel with a thickness of 4.5 mm. The effect of laser power, defocusing distance, and welding speed on the welded joint appearance was examined, and the microstructure and mechanical properties on the typical butt joints were investigated. Results showed that increasing laser welding power may cause faster downward flow of molten metal to produce greater root humping. With the welding speed increasing, the average welding seam （WS） width decreased, and the average WS and heat-affected zone （HAZ） hardness increased. The microstructures of WS, fusion line, and coarse grain heat-affected zone were lath martensite, but the growth direction of the original austenite grain boundaries was significantly different. The microstructures of fine grain heat-affected zone were ferrite and martensite, and the microstructure of mixed grain heat- affected zone contained ferrite, massive M/A island, and a small amount of martensite. The micro-hardness values of WS, HAZ, and base metal （BM） were 358, 302, and 265 HV, respectively. The butt joint fracture at the BM far from the WS and the welded joint tensile strength are observed to follow proportional relationship with hardness.     

Y25焊接构架吊杆吊座焊接工艺分析

在Y25系列货车转向架的焊接生产中,2个吊杆吊座之间的焊接距离仅有35mm,由于焊接热影响区较近,易出现焊接裂纹。利用不同的焊接工艺参数进行了焊接工艺评定,研究了接头的宏观形貌、金相组织及接头的硬度分布,并最终制定了适合于焊接生产的焊接工艺参数。     

10Ni3CrMoV钢CO2激光多层焊的接头组织与性能

与传统电弧焊相比,激光焊接厚板优势明显。采用纯激光焊和激光电弧复合焊等多道焊接技术实现了28 mm厚10Ni3CrMoV钢的高效焊接,采用光学显微镜分析焊缝、热影响区和焊缝重叠区的组织,激光复合焊缝组织主要为针状铁素体,纯激光焊缝、粗晶区和细晶区组织主要为板条马氏体,激光复合焊缝重叠区组织为粒状贝氏体+马氏体,纯激光焊缝和激光复合焊缝重叠区组织为马氏体+少量粒状贝氏体。测试了焊接接头的力学性能,结果表明,激光复合焊缝金属的冲击韧性较高,焊接接头的抗拉强度和屈服强度与母材相当,延伸率略小于母材,焊接接头的最大硬度小于360 HV,弯曲性能合格。     

Lap joining of titanium alloy using laser welding and resistance seam welding combined process

Titanium alloy lap joints were performed by combined laser welding and resistance seam welding process. The welding characteristics of this combined process were investigated compared with that of laser welding. The experimental results indicate that the combined process welded joint has larger weld width at the lap surface. The joint tensile shear force of combined process is 2.5 times that of laser welding. There are some pores around the lap surface in laser welded joint, and most pores can be eliminated by resistance seam welding process. Metallographic examinations of combined process welded joint reveal that the microstructure in heat-affected zone (HAZ) and weld zone has the acicular martensite morphology, which causes that the microhardness in HAZ and weld zone increases compared with the base metal, and the microhardness in weld zone is highest.     

AM60变形镁合金薄板激光焊接接头的组织与性能

以AM60变形镁合金薄板为研究对象，分析C02激光焊后接头的组织和性能，探讨镁合金激光焊接的工艺特点。结果表明：在合适的工艺参数下，能获得表面成型良好、变形小的焊接接头。金相观察分析发现接头中热影响区不明显，焊缝区组织致密，晶粒细小，晶界上均匀分布着脆性相（Mg17A112），但内部易产生气孔、裂纹等微观缺陷。硬度测试结果显示，焊缝硬度略高，母材和热影响区硬度相当。在本实验条件下采用C02激光焊能实现AM60镁合金的焊接，抗拉强度可达母材的94％，断口表现为混合断裂。     

X80管线钢及其接头的低温韧性和显微组织

分别利用示波冲击韧性试验、硬度试验和光学显微镜、透射电镜研究了X80管线钢及其焊管接头的力学性能和显微组织。试验结果表明，X80钢及其焊管接头具有良好的韧性，其中焊缝的韧性最高，焊接热影响区粗晶区因受焊接热效应引起晶粒粗化和形成脆性组织，故韧性最低。试验钢由针状铁素体和少量块状铁素体组成，焊缝为典型的针状铁素体组织，焊接热影响区粗晶区以粒状贝氏体为主。焊接热影响区熔合线附近的硬度值最高，越远离熔合线硬度值越低，并逐渐接近母材的硬度值。     

D406A钢的光纤激光-电弧复合焊接性能

对低合金超高强度钢(D406A)进行了光纤激光-电弧复合焊接,在最佳工艺参数条件下,研究了装配间隙对D406A焊接性能的影响.结果表明,装配间隙的最佳范围为0.6~1.0 mm.另外在最佳工艺条件下,对焊缝形状、焊接接头组织、硬度及力学性能进行了研究.结果表明,焊缝金属可以分为电弧区、激光-电弧复合区及激光区,并且激光区与电弧区相比组织细小;3个区域的硬度分布最高值均出现在热影响区(HAZ);经热处理后,焊接接头力学性能基本与母材相同.     

双丝埋弧焊接头性能研究

在16Mn钢板上进行双丝自动埋弧焊工艺试验,得到了不同焊接速度下的焊件.对不同工艺参数下得到的焊接接头试样进行了拉伸试验、硬度测试以及金属显微组织观察,并计算了双丝自动埋弧焊时的熔敷率.结果表明:采用双丝埋弧焊得到的焊缝外形美观;金属熔敷率与焊接速度成反比;随着焊接速度的降低焊接线能量相应的增大,较长的高温停留时间会促...