Composite Ni/Al2O3 coatings and their corrosion resistance

Composite coatings Ni/Al₂O₃ were electrochemically deposited from a Watts bath. Al₂O₃ powder with particle diameter below 1 μm was codeposited with the metal. The obtained Ni/Al₂O₃ coatings contained 5-6% by weight of corundum. The structure of the coatings was examined by scanning electron microscopy (SEM). It has been found that the codeposition of Al₂O₃ particles with nickel disturbs the nickel coating's regular surface structure, increasing its microcrystallinity and surface roughness. DC and AC electrochemical tests were carried out on such coatings in a 0.5 M solution of Na₂SO₄ in order to evaluate their corrosion resistance. The potentiodynamic tests showed that the corrosion resistance of composite coating Ni/Al₂O₃ is better than that of the standard nickel coating. After 14 days of exposure the nickel coating corrodes three times faster than the Ni/Al₂O₃ coating. The electrochemical behaviour of the coatings in the corrosive solution was investigated by electrochemical impedance spectroscopy (EIS). An equivalent circuit diagram consisting of two RC electric circuits: one for electrode, nickel corrosion processes and the other for processes causing coating surface blockage, were adopted for the analysis of the impedance spectra. The changes in the charge transfer resistance determined from the impedance measurements are comparable with the changes in corrosion resistance determined from potentiodynamic measurements.     

Evaluation of hot corrosion behavior of CSZ,CSZ/micro Al2O3 and CSZ/nano Al2O3 plasma sprayed thermal barrier coatings

Hot corrosion is one of the main destructive factors in thermal barrier coatings (TBCs) which come as a result of molten salt effect on the coating–gas interface. Hot corrosion behavior of three types of plasma sprayed TBCs was evaluated: usual CSZ, layer composite of CSZ/Micro Al₂O₃ and layer composite of CSZ/Nano Al₂O₃ in which Al₂O₃ was as a topcoat on CSZ layer. Hot corrosion studies of plasma sprayed thermal barrier coatings (TBCs) were conducted in 45 wt% Na₂SO₄+55 wt% V₂O₅ molten salt at 1050 °C for 40 h. The graded microstructure of the coatings was examined using scanning electron microscope (SEM) and X-ray diffractometer (XRD) before and after hot corrosion test. The results showed that no damage and hot corrosion products was found on the surface of CSZ/Nano Al₂O₃ coating and monoclinic ZrO₂ fraction was lower in CSZ/Micro Al₂O₃ coating in comparison with usual CSZ. reaction of molten salts with stabilizers of zirconia (Y₂O₃ and CeO₂) that accompanied by formation of monoclinic zirconia, irregular shape crystals of YVO₄, CeVO₄ and semi-cubic crystals of CeO₂ as hot corrosion products, caused the degradation of CSZ coating in usual CSZ and CSZ/Micro Al₂O₃ coating.     

Effects of powder size and metallic bonding layer on corrosion behaviour of plasma-sprayed Al2O3-13% TiO2 coated mild steel in fresh tropical seawater

This study focuses on the effects of powder size and Ni–Al bonding layer on the electrochemical behaviour of plasma-sprayed Al₂O₃-13% TiO₂ coating in fresh tropical seawater. The presence of the metallic bonding layer reduces the coating porosity and increases the surface roughness for both microparticle and nanoparticle coatings. The nanoparticle exhibits better corrosion rate of 1.9×10⁻⁶ mmpy compared to the microparticle coating, with a corrosion rate of 3.05×10⁻⁶ mmpy. However, the presence of the metallic bonding layer increases the corrosion rate for both micro and nanoparticle coatings. The corrosion mechanism for the coating with and without the metallic bonding layer is discussed in detail.     

Electrochemical anticorrosion performance evaluation of Al2O3 coatings deposited by MOCVD on an industrial brass substrate

Alumina (Al₂O₃) coatings of different thickness were deposited on OT59 brass substrate (BS) using the metal organic chemical vapour deposition (MOCVD) technique to evaluate the corrosion performance by EIS measurements. The used precursor was dimethyl-aluminium-isopropoxide. Electrochemical characterizations of the deposited films were performed in a standard very aggressive acidic solution (aerated 1N H₂SO₄ at 25 °C up to 168 h of immersion time) by means of direct current method (Tafel curves) and electrochemical impedance spectroscopy (EIS). The Rutherford backscattering spectroscopy (RBS) indicated that the films are very pure with the correct Al₂O₃ stoichiometry, while the IR absorption spectra showed that the films did not contain any OH groups. The surface film morphology was investigated by atomic force microscopy (AFM) and displayed a globular texture. The films were very smooth, with a maximum root mean square roughness, for example, of 14 nm for a 0.96 μm thick coating. The EIS data confirmed, as expected, that a 2.40 μm Al₂O₃ layer ensures the best corrosion protection after 168 h of immersion in the very acidic environment used.     

Poly(N-ethylaniline) coatings on 304 stainless steel for corrosion protection in aqueous HCl and NaCl solutions

Poly(N-ethylaniline) (PNEA) coatings were grown by potentiodynamic synthesis technique on 304 stainless steel (SS) alloy from 0.1 M of N-ethylaniline (NEA) in 0.3 M oxalic acid solution. Characterization of adhesive and electroactive PNEA coatings was carried out by cyclic voltammetry, FT-IR spectroscopy and scanning electron microscopy (SEM) techniques. The protective properties of PNEA coatings on SS were elucidated using linear anodic potentiodynamic polarization, Tafel and electrochemical impedance spectroscopy (EIS) test techniques, in highly aggressive 0.5 M HCl and 0.5 M NaCl solutions. Linear anodic potentiodynamic polarization test results proved that PNEA coating improved the degree of protection against pitting corrosion in HCl and NaCl solutions. Tafel test results showed that PNEA coating appears to enhancement protection for SS in 0.5 M NaCl and 0.5 M HCl solutions. However, according to long-term EIS results, PNEA coating is better for the protection of SS electrodes during the long immersion period in NaCl compared to that in HCl medium.     

Vacuum thermal treated electroless NiP-TiO2 composite coatings

Composite NiP-TiO₂ layers were prepared by simultaneous electroless deposition of Ni-P and TiO₂ on steel substrate, from a solution in which TiO₂ particles were kept in suspension by stirring. Deposits were characterized for its structure, morphology and hardness. It was found that the chemical composition of Ni-P matrix has been influenced by the incorporation of TiO₂ particles. TiO₂ particle incorporation increases with increase in their bath concentrations (0.5-2.0 g/l). An improvement (up to 20%) in microhardness was observed in both as plated and vacuum heat-treated composite coatings compared to Ni-P coatings. Electroless deposited composite coatings exhibit an amorphous structure of the nickel matrix in which crystalline titanium oxide is incorporated. Vacuum heat treatment leads to the formation of a crystalline layer in which the Ni and Ni₃P crystallites appear apart from those of the TiO₂ (anatase). Potentiodynamic polarization measurements made on these deposits in 3.5 wt.% sodium chloride solution showed decrease in the corrosion resistance for the as-plated and heat-treated composite coatings.     

Electropolymerization of poly(N-ethyl aniline) on mild steel: Synthesis, characterization and corrosion protection

Poly(N-ethylaniline) (PNEA) coatings on the mild steel electrode were synthesized by electrochemical oxidation of N-ethylaniline using aqueous oxalic acid solutions as reaction medium. Electrodeposition was carried out by potentiodynamic, potentiostatic and galvanostatic synthesis techniques. Smooth, adhesive and thick PNEA coatings on mild steel could be electrosynthesized during sequential scanning of the potential region between −0.5 and 1.4 V versus SCE, with scan rate of 20 mV s⁻¹. The electrodeposited coatings were characterized by cyclic voltammetry, FT-IR and UV-vis techniques. Corrosion behavior of PNEA coated steels was investigated by linear anodic potentiodynamic polarization technique and Tafel test. Anodic potentiodynamic polarization results showed that electrodissolution current value of PNEA coated steel decreased about 90% compared to that of the uncoated steel in 0.5 M H₂SO₄ aqueous solution. Tafel plots showed also strong decrease of corrosion current for the PNEA coated electrode compared to the uncoated steel electrode in 3% NaCl as corrosive medium.     

Effect of Al2O3 particle size on preparation and properties of ZTA ceramics formed by gelcasting

Zirconia-toughened alumina (ZTA) ceramics were prepared using three different kinds of Al₂O₃ powders (marked PW-A average particle size: 7.53 μm, marked PW-B average particle size: 1.76 μm, marked PW-C average particle size: 0.61 μm) by gelcasting. Effect of Al₂O₃ particle size on zeta potential, dispersant dosage and solid volume fractions of ZTA suspensions as well as the mechanical properties of ZTA green bodies and ceramics were investigated. The optimum dosages of dispersant for ZTA suspensions prepared by PW-A, PW-B and PW-C are 0.4 wt%, 0.5 wt% and 0.7 wt%, respectively. The highest solid volume fractions of ZTA suspensions can reach 62 vol% (SP-A), 60 vol% (SP-B) and 52 vol% (SP-C), respectively. The green bodies show a bending strength as high as 20 MPa, which can meet the requirement of machining. The Al₂O₃ powder with fine particle size is beneficial to the improvement of mechanical properties. The ZTA ceramics prepared by PW-B Al₂O₃ powder show the highest bending strength (680 MPa) and toughness (7.49 MPa m^1/2).     

The influence of gun transverse speed on electrochemical behaviour of thermally sprayed Cr3C2-NiCr coatings in 0.5 M H2SO4 solution

In the present study, different types of 75% Cr₃C₂-25% NiCr coatings were applied on a steel substrate by means of high velocity oxygen fuel spraying (HVOF), and studied using ac and dc electrochemical measurements in an aerated and unstirred 0.5 M H₂SO₄ solution. Structural characterization was determined before and after electrochemical tests. Differences between all sprayed systems are related to the gun transverse speed and number of deposited layers, which strongly affected the electrochemical characteristics of the coated steels. The coating obtained with a higher torch speed showed better resistance against corrosion. The electrochemical impedance results were analyzed using an equivalent circuit where porosity of the coatings and substrate oxidation were considered.     

Effect of Ti amount on wear and corrosion properties of Ti-doped Al2O3 nanocomposite ceramic coated CP titanium implant material

Al₂O₃ and Ti-doped Al₂O₃ nanocomposite ceramic coatings were prepared by using a sol-gel dip-coating process. Corrosion and wear resistance of Al₂O₃ ceramic coatings in relation to Ti amount were carried out using pin-on-disk tribotester, potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). Surface characterizations before and after the corrosion and wear tests were investigated by the scanning electron microscope (SEM) and X-ray diffraction (XRD) and hardness analysis. The results of corrosion and wear tests exhibited that the corrosion and wear resistance of nanocomposite ceramic coatings became better than uncoated samples. Also, corrosion and wear resistance of nanocomposite ceramic coatings improved with Ti doping content increased.     

Effect of electroless nickel interlayer on the electrochemical behavior of single layer CrN, TiN, TiAlN coatings and nanolayered TiAlN/CrN multilayer coatings prepared by reactive dc magnetron sputtering

The electrochemical behavior of single layer TiN, CrN, TiAlN and multilayer TiAlN/CrN coatings, deposited on steel substrates using a multi-target reactive direct current (dc) magnetron sputtering process, was studied in 3.5% NaCl solution. The total thickness of the coatings was about 1.5 μm. About 0.5 μm thick chromium interlayer was used to improve adhesion of the coatings. With an aim to improve the corrosion resistance, an additional interlayer of approximately 5 μm thick electroless nickel (EN) was deposited on the substrate. Potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) were used to study the corrosion behavior of the coatings. Scanning electron microscopy and energy dispersive X-ray analysis were used to characterize the corroded samples. The potentiodynamic polarization tests showed lower corrosion current density and higher polarization resistance (R_p) for the coatings with EN interlayer. For example, the corrosion current density of TiN coated steel was decreased by a factor of 10 by incorporating 5 μm thick EN interlayer. Similarly, multilayer coatings of TiAlN/CrN with EN interlayer showed about 30 times improved corrosion resistance as compared to the multilayers without EN interlayer. The porosity values were calculated from the potentiodynamic polarization data. The Nyquist and the Bode plots obtained from the EIS data were fitted by appropriate equivalent circuits. The pore resistance (R_pore), the charge transfer resistance (R_ct), the coating capacitance (Q_coat) and the double layer capacitance (Q_dl) of the coatings were obtained from the equivalent circuit. Multilayer coatings showed higher R_pore and R_ct values as compared to the single layer coatings. Similarly, the Q_coat and Q_dl values decreased from uncoated substrate to the multilayer coatings, indicating a decrease in the defect density by the addition of EN interlayer. These studies were confirmed by examining the corroded samples under scanning electron microscopy.     

Preparation of nanocrystalline Sr3Al2O6 powders via citric acid precursor

Sr₃Al₂O₆ was synthesized via citric acid precursor. The effects of the molar ratio of citric acid to total metal cations concentration (CA/M) on the formation of Sr₃Al₂O₆ were investigated. Increasing the CA/M promoted the formation of Sr₃Al₂O₆. Single-phase and well-crystallized Sr₃Al₂O₆ was obtained from the CA/M = 1, CA/M = 2 and CA/M = 4 precursor at temperature 1200 °C, 1100 °C and 900 °C, respectively. Differential thermal analysis and thermogravimetric (DTA/TG), X-ray diffractometry (XRD) and field emission scanning electron microscopy (FESEM) were used to characterize the precursors and the derived oxide powders. Sr₃Al₂O₆ nanoparticles with a diameter of about 50-70 nm were obtained.     

Deposition behavior and characteristics of hydroxyapatite coatings on Al2O3, Ti,and Ti6Al4V formed by a chemical bath method

A simple chemical bath method was used to deposit hydroxyapatite (HA) coatings on Al₂O₃, Ti, and Ti6Al4V substrates at ambient pressure by heating to 65–95 °C in an aqueous solution prepared with Ca(NO₃)₂·4H₂O, KH₂PO₄, KOH, and EDTA. The deposition behavior, morphology, thickness, and phase of the coatings were investigated using scanning electron microscopy and X-ray diffractometry. The bonding strength of the coatings was measured using an epoxy resin method. The HA coatings deposited on the three kinds of substrates were fairly dense and uniform and exhibited good crystallinity without any additional heat treatment. A coating thickness of 1–1.8 μm was obtained for the samples coated once. By repeating the coating process three times, the thickness could be increased to 4.5 μm on the Al₂O₃ substrate. The bonding strength of these coatings was 18 MPa.     

Electrochemical corrosion characterization of Al-Ni alloys in a dilute sodium chloride solution

The aim of this study is to characterize the electrochemical corrosion resistance of Al-Ni alloy samples which were directionally solidified under upward unsteady state heat flow conditions. Electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization techniques were used to analyze the corrosion resistance in a dilute 0.05 M NaCl solution at 25 °C. Equivalent circuit analyses were also conducted. It was found that microstructural features such as the dendritic arrangement and the distribution of Al₃Ni intermetallic particles have important roles on both the resulting pitting potential and the general corrosion resistance of Al-Ni alloys.     

Corrosion protection of carbon steel by thin films of poly(3-alkyl thiophenes) in 0.5 M H2SO4

Poly(3-octyl thiophene) (P3OT) and poly(3-hexylthiophene) (P3HT) dissolved in toluene were deposited onto 1018 carbon steel and corroded in 0.5 M H₂SO₄. P3OT and P3HT films were chemically deposited by drop casting onto 1018-type carbon steel with two surface finishing, i.e. abraded with 600-emery paper and with alumina (Al₂O₃) particles of 1.0 μm in diameter (mirror finish). Their corrosion resistance was estimated by using potentiodynamic polarization curves, linear polarization resistance (LPR), and electrochemical impedance spectroscopy, EIS, techniques. In all cases, polymeric films protected the substrate against corrosion, but the protection was improved if the surface was polished with Al₂O₃ particles of 1.0 μm in diameter. The polymer which gave the best protection was P3HT because the amount of defects was much lower than that for the P3OT films. The polymers did not act only as a barrier layer against aggressive environment, but they improved the passive film properties by decreasing the critical current necessary to passivate the substrate, increasing the pitting potential and broadening the passive interval.     

Electrochemical synthesis of poly(N-methylaniline) on an iron electrode and its corrosion performance

Synthesis of poly(N-methylaniline) (PNMA) on pure iron and Pt electrodes was carried out from aqueous 0.3 M oxalic acid solution containing 0.1 M N-methylaniline (NMA) by potentiodynamic and galvanostatic techniques. It was found that when compared to polyaniline (PAni) and its ring- and N-ethyl-substituted derivatives, PNMA can be electrosynthesized with lower upper scanning potential (upper potential limit, E_upp) of 0.8 V vs. saturated calomel electrode (SCE) on an Fe electrode. PNMA coatings were characterized by electrochemical, scanning electron microscopy (SEM) and FTIR techniques. Linear anodic potentiodynamic polarization results proved that increasing the acidity of the polymerization solution causes more effective protection against corrosion in 0.5 M H₂SO₄ medium for PNMA. Moreover, PNMA exhibited similar protective properties with PAni under the same corrosion test conditions. Tafel test results reveal that the PNMA coating appears to enhance protection for iron in 0.5 M NaCl and 0.1 M HCl solutions. According to EIS results, the PNMA coating is able to offer protection to Fe electrodes in NaCl compared to that in HCl medium over a long immersion period.     

Ethanol steam reforming reactions over Al2O3 · SiO2-supported Ni-La catalysts

Nickel-based catalysts supported on Al₂O₃ · SiO₂ were prepared with modification of the second metal involving La, Co, Cu, Zr or Y, of which the catalytic behaviors were assessed in the ethanol steam reforming reaction. Activity test indicated that addition of La resulted in higher selectivity of hydrogen and lower selectivity of carbon monoxide, compared with Co-doped nickel catalyst. Influences of lanthanum amounts on catalytic performance were studied over 30NixLa/Al₂O₃ · SiO₂ (x = 5, 10, 15), and characterizations by XRD, TPR and XPS indicated that low amount of lanthanum additives (5%) was superior to inhibit the crystal growth of nickel as well as beneficial to the reduction of nickel oxide. Finally 100 h test for the optimal catalyst 30Ni5La/Al₂O₃ · SiO₂ indicated its good long-term stability to provide high hydrogen selectivity and low carbon monoxide formation, as well as good resistance to coke deposition at low temperature.     

Phase diagram of the Al2O3-HfO2-Y2O3 system

The phase diagram of the Al₂O₃-HfO₂-Y₂O₃ system was first constructed in the temperature range 1200-2800 °C. The phase transformations in the system are completed in eutectic reactions. No ternary compounds or regions of appreciable solid solution were found in the components or binaries in this system. Four new ternary and three new quasibinary eutectics were found. The minimum melting temperature is 1755 °C and it corresponds to the ternary eutectic Al₂O₃ + HfO₂ + Y₃Al₅O₁₂. The solidus surface projection, the schematic of the alloy crystallization path and the vertical sections present the complete phase diagram of the Al₂O₃-HfO₂-Y₂O₃ system.     

Corrosion inhibition of mild steel by natural product compound

Corrosion inhibition of mild steel in H₃PO₄ containing chloride or sulphate ions have been studied using different electrochemical techniques. The corrosion and hydrogen evolution of mild steel alloy in 2 M H₃PO₄ acid containing 0.5 M NaCl can be effectively inhibited by addition of natural product compound, Thymol (IPMP), of different concentrations. However, in 2 M H₃PO₄ containing 0.5 M Na₂SO₄ corrosion cannot be effectively inhibited. The results of electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization measurements confirm the synergistic effects which describe the increase in the effectiveness of a corrosion inhibitor in the presence of Cl⁻ ions in the corrosive medium. At any temperature, an increase in it leads to an increase of the corrosion rate and hydrogen evolution on mild steel. Polarization and EIS results are in good agreement with each other. The obtained results were confirmed by surface examination using scanning electron microscope.     

Synthesis and electrochemical characteristics of Al2O3-coated LiNi1/3Co1/3Mn1/3O2 cathode materials for lithium ion batteries

LiNi_1/3Co_1/3Mn_1/3O₂ cathode materials have been coated with Al₂O₃ nano-particles using sol-gel processing to improve its electrochemical properties. The X-ray diffraction (XRD) pattern of the as-prepared Al₂O₃ nano-particles was indexed to the cubic structure of the γ-Al₂O₃ phase and had an average size of ∼4 nm. The XRD showed that the structure of LiNi_1/3Co_1/3Mn_1/3O₂ was not affected by the Al₂O₃ coating. However, the Al₂O₃ coatings on LiNi_1/3Co_1/3Mn_1/3O₂ improved the cyclic life performance and rate capability without decreasing its initial discharge capacity. These electrochemical properties were also compared with those of LiAlO₂-coated LiNi_1/3Co_1/3Mn_1/3O₂ cathode material. The electrochemical impedance spectroscopy (EIS) was studied to understand the enhanced electrochemical properties of the Al₂O₃-coated LiNi_1/3Co_1/3Mn_1/3O₂ compared to uncoated LiNi_1/3Co_1/3Mn_1/3O₂.