三叶形粘胶纤维对过滤纸性能的影响

对两种纤度相同的三叶形粘胶纤维和普通粘胶纤维的形态和滤水性能进行了分析,并进一步就两种粘胶纤维的用量对过滤纸物理性能和过滤性能的影响进行研究.结果表明,粘胶纤维含量低于50％时,两种纤维对过滤纸平均孔径、透气度和耐破度的影响差别不大,但含三叶形粘胶纤维的纸张厚度比含普通粘胶纤维的要大.随着三叶形粘胶纤维含量的增加,滤纸的过滤阻力降低、纳污容量增大,但过滤精度有所下降;当粘胶纤维加入量为30％时,对于含三叶形粘胶纤维和含普通粘胶纤维的两种滤纸,二者的过滤精度无显著差异,前者的纳污容量是后者的1.28倍.     

PET纤维截面形状对液体过滤材料过滤性能的影响

对3种不同截面形状（圆形、三叶形和丰字形）的PET纤维进行了形貌分析及水中分散性能研究,通过将其与阔叶木闪急浆混抄制备过滤材料,探究了PET纤维截面形状对过滤材料液体过滤性能的影响。结果表明,PET纤维含量相同时,相比于含圆形PET纤维的过滤材料,含三叶形和丰字形PET纤维的过滤材料在过滤效率、流阻、纳污容量等过滤性能方面都有不同程度的改善。三叶形纤维更有利于提高过滤材料的过滤效率,而丰字形纤维更有利于提高过滤滤材的纳污容量、降低滤材的过滤阻力。当PET纤维含量为40%时,相比于含圆形PET纤维的滤材,含三叶形和丰字形PET纤维过滤材料的纳污容量分别增加了32.1%、26.5%;对粒径14 μm颗粒的过滤效率分别提高了13.1%、6.1%。液体流量在4 L/min时,流阻分别降低了26.6 %、28.5%。     

PET纤维截面形状对过滤纸结构和性能的影响

采用5种截面形状(圆形、三角形、三叶形、十字形、丰字形)的PET纤维与植物纤维配抄过滤纸,探究PET纤维截面形状对过滤纸结构和性能的影响。结果表明,与圆形纤维相比,三角形、三叶形、十字形以及丰字形纤维对过滤纸的过滤效率没有显著影响,但容尘量都有不同程度的提高。PET纤维添加量为40%时,与圆形纤维相比,含三角形、三叶形、十字形和丰字形纤维过滤纸的容尘量分别增加了8.2 g/m~2、11.7 g/m2、9.9 g/m~2、13.8 g/m~2。其中,三叶形纤维和丰字形纤维对过滤纸的厚度和容尘量的影响较大,丰字形纤维比三角形、三叶形和十字形纤维对过滤纸的孔径和透气度具有更显著的影响。     

纤维素纳米纤维对文化用纸性能的影响

纤维素纳米纤维是由盘磨生产而得不同细小纤维含量的产品。纤维素纳米纤维在实验室和中试纸机可用作造纸的添加剂,实验室抄片研究显示:随着纤维素纳米纤维的加入,纸页的强度性能和表面性能提高,且纸页性能随着纳米纤维中细小纤维的含量增加而提高。可以通过调整一定纳米纤维含量下不同细小纤维含量而获得所需的纸页性能。在中试规模的试验中,纳米纤维在保持其他纸页性能的同时提高了纸页的灰分含量,强度性能和表面性能随着纳米纤维用量的增加而提高,对纸料的滤水性能有负面的影响。在较高的纳米纤维加入量下,纸机的运行性能良好,滤水速度下降,加入纳米纤维可提高出压榨部湿纸页的干度。     

芳纶浆粕对玻璃纤维滤纸性能的影响

用芳纶浆粕替代部分玻璃棉,与玻璃纤维混合在实验室进行抄纸,研究替代前后纸张物理性能和过滤性能的变化。研究发现:芳纶浆粕具有较大的比表面积,可以增加纤维之间的结合,从而提高玻璃纤维滤纸的强度性能;但同时芳纶浆粕分散比较困难,纤维平均直径较细,随着芳纶浆粕含量的增加,纤维絮集程度逐渐严重,透气度和孔径都有降低的趋势;在芳纶浆粕添加量5%和10%时,与纯玻纤滤纸相比,滤纸抗张强度分别增加4.3%和19.6%,纳污容量由9.00 mg·cm^-2分别上升至9.45 mg·cm^-2和9.15 mg·cm^-2,同时孔径分别下降14.2%和22.4%。     

玻璃纤维滤材厚度对液体过滤性能的影响

本研究探究了平均流量孔径接近的玻璃纤维过滤材料(简称滤材)厚度对液体过滤性能的影响。首先对短切玻璃纤维和3种玻璃棉共4种纤维原料进行了形貌分析,通过调节4种纤维原料的配比和滤材定量,制备了平均流量孔径接近而厚度不同的滤材,然后将制备的滤材在多次通过实验台上做航空液压油液体过滤性能检测。结果表明,在平均流量孔径接近的情况下,滤材相同的平均过滤比对应的污染物颗粒粒径尺寸接近。4种厚度的滤材在实验前50 min压差接近,到达终止压差时间随滤材厚度的增大而延长;纳污容量随滤材厚度的增大而提高,厚度为0. 12 mm的滤材纳污容量为38. 7 g/m~2,厚度为0. 84 mm的滤材纳污容量为82. 1 g/m~2。厚度增大到7倍,纳污容量仅为原来的2. 12倍,纳污容量增加倍数和滤材厚度增加倍数不一致,但二者存在线性关系。     

造纸工作者对聚电解质的评价

造纸工作者使用聚电解和离子型聚合物来改善絮凝作用、留着率和滤水性能。他们的目的是增加纸机的产量,改善产品的质量,在填料留着方面,降低每吨产品的填料成本,在白水澄清方面,满足排放标准或提高水的质量。 滤水性能因细小纤维被絮凝而得到改善,因为在絮凝状态下,细小纤维的流体动力表面积较小,因而流动时水力阻力也就较小。在造纸机的铜网上,可以更容易地脱去更多的水,使纸页到达压榨部     

酶对废纸浆滤水性能的改进作用

废纸浆的滤水性比原纸浆差，提高其滤水性能将有助于提高废纸的利用率，而酶对废纸浆的滤水性能有明显的改进作用。1酸能提高废纸浆的滤水性能Pommier等人首次发现，利用含纤维素酶和半纤维素酶的真菌Trichodermareesei培养液处理废纸浆后，废纸浆的滤水性能明显增加。Prasad等人研究发现，废纸浆滤水性差的主要原因是细小纤维含量和填料等比原纸浆的高，而纤维素酶和半纤维素酶能选择性地水解废纸浆中的细小纤维，增加了长纤维的含量，从而提高了废纸浆的滤水性。2酶对废纸浆德水性能的改善作用2．1不同的酶处理废纸浆利用不同的酶处理废…     

改性涤纶针织物导水透湿性能研究

将三种不同品种的改性涤纶(超柔丽、Porel、Paster)针织物与普通涤纶针织物、纯棉针织物的导水透湿性进行比较,分析不同改性方法对织物性能的影响。结果表明三叶形截面可以提高比表面积,有利于纤维回潮率的提高;中空结构增加毛细管效应,有利于改善织物导水性。     

一种新型评价纸浆滤水性能的参数──比过滤阻力

近几十年来,由于造纸抄造技术的不断发展,纸浆的滤水性能成为影响抄造过程的重要因素,但由于影响纸浆滤水性能的因素较复杂,网上纸浆的压头、有效抽吸压头、纸页定量、纸浆浓度、打浆方式、纤维长宽度、细小纤维的分布情况、浆层的湿压缩性能、纸浆在网上的温度、造纸网的结构和添加剂等都会对网上的脱水造成一定的影响。传统的打浆度（游离度）或一定条件下的静态滤水时间对评价纸浆的滤水性能都存在着一定的不足。比过滤阻力（Ｓｐｅｃｉｆｌｃｆｉｌｔｒａｔｉｏｎ ｒｅｓｉｓｔａｎｃｅ）作为一种新型的评价纸浆滤水的工具正逐步受…     

纸浆纤维表面性能及其分析方法研究进展

构成纸张的基本结构单元是纤维素纤维,纤维性能对于纸张的抄造过程以及纸张的性能都起着关键性的作用。其中,纤维表面性能是纤维的一项非常重要的性能,影响着纤维与各种化学助剂的相互作用以及纤维间的结合性能,进而影响纸机的运行性能以及成纸的物理性能。本文主要综述了近几年关于纤维表面化学组成、表面电荷特性、表面能以及比表面积对纤维性能以及纤维成纸特征影响机制的研究成果,对纤维表面性能的分析方法进行了总结。     

P-RC APMP浆不同筛分级分的纤维特性和成纸性能

以杨木P-RC APMP浆为实验对象,测定经Bauer-McNett纸浆纤维筛分仪筛分后各个级分纤维的含量、纤维特性（纤维形态、表面电荷、比容积和比表面积）、纤维间结合性能以及手抄片的物理强度性能。结果表明,P-RC APMP浆中纤维尺寸分布很不均匀,含有大量的细小纤维组分。随着筛分仪筛网目数的增加,筛分得到的纤维级分的纤维长度和粗度逐渐减小,纤维表面暴露的电荷量逐渐增加,纤维的比表面积逐渐变大,而纤维自身的强度逐渐降低,手抄片的强度性能和纤维间的结合能力逐渐增加。     

The effect of specific surface area of macro fibers on energy absorption capacity of concrete

Energy absorption capacity is the salient property of concrete. Reinforcement of concrete with macro fibers is one of the techniques that has led to enhancement of this important feature of concrete. However, the effect of specific surface area of melt-spun polypropylene macro fibers has hardly been studied so far. In this work, the effect of this parameter on mechanical behavior of fiber reinforced concrete (FRC) was investigated. Diameter of macro fibers was varied by changing the melt feeding rate and fiber draw ratio. Changes in fibers diameter affect fibers specific surface area, which in turn influences the adhesion of fibers to the matrix in FRCs. In order to evaluate the FRCs behavior, bending tests were conducted and the area under load-displacement curves was studied. It was found that increase in specific surface area of fibers results in considerable increase in energy absorption capacity of the FRCs. Concrete reinforced with the larger diameter fibers exhibited 6× energy absorption capacity than the reference sample. This was found to be in line with the 14× energy absorption capacity of sample which was reinforced by smaller diameter fibers. This was attributed to the increase in total contact area between the finer fibers and the matrix as a direct consequence of the increase in number of fibers for a given fiber volume fraction.     

聚苯硫醚纤维表面低温等离子体改性

采用空气辉光低温等离子体技术对聚苯硫醚(PPS)纤维进行表面改性,利用XPS、SEM等方法探讨了改性前后纤维表面形态结构和组成的变化。实验发现通过等离子体处理后纤维亲水性有明显提高,XPS分析表明,其原因是经等离子体处理后,纤维表面被刻蚀并且增加了含硫极性基团。     

PSA和PPS耐高温纤维的结构与性能研究

通过红外光谱仪和X-射线衍射仪测定芳砜纶(PSA)纤维和聚苯硫醚(PPS)纤维的微观结构,用热分析仪测定两者的热分解温度,通过Instron电子强伸度仪测定两者受热前后的力学性能,并对两者结构与性能的差异进行比较。结果表明:PPS纤维的结构较PSA纤维稳定,结晶度高于PSA纤维;PSA纤维和PPS纤维的热分解温度分别为435.6℃和480℃,两种纤维均具有优异的耐热性能;PPS纤维的断裂强度和伸长均显著高于PSA纤维,两种纤维经高温处理后,强力损失均较小,经300℃处理200h后,强力仍保持90%左右。     

膳食纤维与水的相互作用与其组分和

以40种不同来源的膳食纤维粉体作为研究对象,在测定其水合性质（持水力、膨胀力）、吸湿性质（初始吸湿速率、吸湿平衡时间、最大吸湿率）、膳食纤维组分含量（总膳食纤维、水溶性膳食纤维与水不溶性膳食纤维）和颗粒结构（粒径、径距、比表面积、孔容、孔径）的基础上,利用相关性分析了膳食纤维和水的相互作用对组分和颗粒结构的依赖性。结果发现：① 膳食纤维粉的持水力与膨胀力呈显著正相关,但水合性质与吸湿性质之间的相关不显著。② 组成是影响膳食纤维粉水合性质的主要因素;而颗粒结构对水合性质的影响相对较弱,颗粒大小越均一,膳食纤维粉的持水力越高。③ 就吸湿性质而言,其与组成和颗粒结构的相关都不显著。     

CPAM-膨润土双元体系在新型硅酸钙加填纸上的应用

比较分析了CPAM-膨润土双元微粒助留体系对新型硅酸钙(FACS)和研磨碳酸钙(Gcc)加填浆料的留着、滤水及纸张性能的影响.实验结果表明,CPAM-膨润土双元体系应用于FACS加填纸中时,CPAM需求量高于GCC加填的;膨润土用量为0.1％时,CPAM用量的增加,能改善FACS加填纸料的留着性能,但对其滤水性能却有不利影响;CPAM用量为0.08％时,随着膨润土用量的增加,FACS加填纸料Zeta电位的下降比GCC加填的更快;膨润土的用量低于0.2％时,膨润土用量的增加对纸料的首程留着率和滤水性能都有利.CPAM用量为o.08％、膨润土用量为0.1％时,FACS加填纸白度与GCC加填纸张相当,但是不透明度比GCC加填纸高;FACS加填纸的抗张指数比GCC加填纸低11.2％,撕裂指数比GCC加填纸低21.0％;FACS加填纸张的松厚度比GCC加填纸高41.7％.加填纸张的扫描电镜对比发现,FACS能够较好地填充在纤维之间的缝隙中,可以看到纤维与填料之间有较好的交织.     

蒸汽爆破压力对西兰花老茎膳食纤维品质及理化特性的影响

为明确西兰花老茎膳食纤维改性工艺中适宜蒸汽爆破压力参数的选择,选取蒸汽爆破压力参数0.5、1.0、1.5、1.8、2.0 MPa,研究不同蒸汽爆破压力对西兰花老茎膳食纤维品质及理化特性的影响。结果表明:经0.5 MPa处理粉体的色泽最好,膨胀力最大,为3.56 mL/g,但持油力最小;经1.0 MPa处理粉体的可溶性膳食纤维含量最高,达8.89%,且松密度最大,达0.337 g/mL,经1.5 MPa处理粉体的比表面积最大,但可溶性膳食纤维含量和持水力最小;经1.8 MPa处理粉体的DPPH自由基清除能力最强,达95.89%,较对照提高约2倍;经2.0 MPa处理粉体的堆积密度、持油力和亚硝酸根吸附量最大,但色泽最差。经0.5、1.5和1.8 MPa处理的粉体适宜作为功能配料添加到食品中或吸附于食品表面,经1 MPa处理的粉体适宜胶囊剂等产品加工,经2.0 MPa处理的粉体更利于片剂产品生产。     

等离子体及生物酶对滤嘴用醋酸纤维的改性

为了寻找较环保的卷烟降焦减害方法,分别利用低温等离子体、纤维素酶以及低温等离子体和纤维素酶协同对滤嘴用醋酸纤维进行表面改性处理,提高了纤维的比表面积、吸附作用和截滤性能。测试了纤维的马克隆值、减量率和K/S值,并用SEM观测了纤维纵向的形态变化。结果表明,滤嘴用醋酸纤维经低温等离子体和生物酶协同作用后,纤维表面明显粗糙化,滤嘴用醋酸纤维的比表面积增大,吸附作用和截滤性能增强,其改性效果比等离子体和生物酶单独作用时更好。