在Gleeble-1500热模拟机上对LD7铝合金进行等温热变形实验,变形温度为300～500℃,应变速率为0.01～10s-1,研究其热变形的流变应力行为、显微组织及软化机制.结果表明LD7铝合金真应力-真应变曲线表现出动态回复特征,在应变速率ε=1.0s-1,变形温度高于420℃时,应力出现锯齿波动,表现出不连续动态再结晶特征.合金在压缩过程中主要软化机制为动态回复,同时也存在动态再结晶.变形后晶粒尺寸随变形温度升高而增大,随变形速率增加而减小.     

含钪Al-Zn-Mg合金的热变形行为和显微组织EI北大核心CSCD

采用Gleeble-1500热模拟试验机对含钪Al-Zn-Mg合金进行热压缩实验,研究了合金在不同热压缩条件下的热变形行为和显微组织。结果表明:合金的流变应力随应变速率的增大而增大,随变形温度的升高而减小。该合金热压缩变形的流变应力行为可用Zener-Hollomon参数来描述,其热变形激活能为150.25kJ/mol。在变形温度为380℃,应变速率为1s-1条件下,合金组织中存在大量的位错墙,表明发生了动态回复现象。随着变形温度的升高,当温度为500℃时,合金中出现了再结晶晶粒,说明主要软化机制逐步由动态回复转变为动态再结晶。     

GH4049合金的热变形行为及组织演变

在Gleeble-1500热模拟机上进行GH4049合金的热压缩实验,获得合金在温度为1090~1180℃、应变速率为0.1~50s-1条件下的应力-应变曲线。对峰值应力进行线性回归获得合金在不同变形条件下的材料常数,通过非线性回归建立合金的热变形本构方程。结果表明:随着变形温度升高,动态再结晶更加充分,晶粒尺寸变大;随着应变速率增加,晶粒组织趋于均匀,晶粒尺寸先减小后增大。     

轧制态7A60铝合金的热压缩显微组织及流变行为

对轧制态7A60铝合金在应变速率为0.1~0.01s-1、变形温度为250~350℃条件下热压缩的显微组织特征和流变应力进行实验研究。结果表明:随着应变速率的降低和温度的升高,材料的各向异性减弱,均匀性增强,晶粒发生明显粗化;在热变形的过程中该合金的主要软化机制为动态回复和动态再结晶,峰值应力随应变速率的增加而增大,随温度的升高而降低,在应变速率为0.01s-1时发生了明显的非连续动态再结晶行为。合金热变形的流变应力行为可用双曲正弦函数来表示,其热激活能为438.981kJ/mol。     

Cu-2.32Ni-0.57Si-0.05P合金热压缩变形研究

在Gleeble-1500D热模拟试验机上,对Cu-2.32Ni-0.57Si-0.05P合金在应变速率为0.01～5s-1、变形温度为600～800℃、最大变形程度为60%条件下,进行恒温压缩模拟实验研究.分析了实验合金在高温变形时的流变应力、应变速率及变形温度之间的关系,研究了变形温度对合金显微组织的影响.计算了合金高温热压缩变形时的应力指数n、应力参数α、结构因子A以及平均热变形激活能Q.结果表明:合金的流变应力随变形温度升高而降低,随应变速率提高而增大.热变形过程的流变应力可用双曲正弦本构关系来描述.当变形温度高于750℃时,合金流变曲线呈现出明显的动态再结晶特征,合金显微组织为完全的动态再结晶组织.合金的热加工宜在应变速率为0.1～1s-1、温度为700～800℃范围内进行.     

Mg-9Gd-3Y-0.3Zr合金高温塑性变形行为研究

以Mg-9Gd-3Y-0.3Zr合金为研究对象,采用热模拟等温压缩的试验方法,利用Arrhenius关系式,分析了合金应力与应变的关系,同时利用金相显微镜和扫描电镜,观察合金在热变形过程中组织的演变。结果表明,合金高温等温压缩变形的真应力-真应变曲线属于动态再结晶型,并且当应变速率ε一定时,温度升高,峰值流变应力下降,当温度一定时,应变速率ε增大,峰值流变应力和它所对应的应变值均提高;变形过程中随着温度的升高,合金发生不同程度的再结晶。当变形温度为623K时,组织变化以动态回复为主,变形温度提高到673K,开始出现再结晶现象,温度达到773K时得到完全再结晶组织。     

GH4706合金的热变形行为与显微组织演化

在Gleeble 3800热模拟试验机上进行GH4706合金的热压缩实验,研究了变形温度为900～1150℃、应变速率为0.001～1s-1范围内合金的热变形行为.结果表明:GH4706合金的真应力真应变曲线呈现出流变软化特征,随变形温度增加或应变速率减小,峰值应力逐渐降低,峰值应变逐渐减小.合金的本构关系可由双曲正弦函数描述,变形激活能为435.36kJ/mol,应力指数为4.13.合金的显微组织演化机制与Z参数密切相关,高Z值条件下主要发生动态回复,低Z值条件下主要发生动态再结晶与再结晶晶粒粗化.GH4706合金发生完全动态再结晶且不发生晶粒粗化的临界lnZ值为35.     

β21S钛合金高温变形行为研究

在Gleeble-1500热模拟试验机上对β21S钛合金进行了高温恒应变速率压缩实验,研究其在变形温度为750～1100℃,应变速率为0.01～1s-1条件下的流变应力及微观组织变化规律,计算了变形激活能及应力指数,并给出了流变应力的计算模型.结果表明:合金的流变应力随应变速率的增大而增大,在恒应变速率下,其应力水平随温度的升高而降低;在较低温度和高应变速率变形时,合金仅发生回复现象,随着温度的升高和应变速率的降低,有部分再结晶发生且再结晶程度逐渐增大;计算得出实验条件下的变形激活能和应力指数分别为211.04kJ/mol和4.0129.     

含Sc超高强Al-Zn-Cu-Mg-Zr合金的热变形行为和微观组织

采用热模拟实验对含Sc超高强Al-Zn-Cu-Mg-Zr合金在应变速率为0.001～10s-1、变形温度为380～470℃的条件下进行了热压缩实验.研究了实验合金的流变应力行为和微观组织演变.结果表明:流变应力随变形温度升高而下降;随应变速率增加峰值应力也相应增加.随变形温度升高和应变速率降低,合金动态再结晶的程度加深,亚晶尺寸变大.含Sc超高强Al-Zn-Cu-Mg-Zr合金,形成了Al3Sc弥散相,该相可强烈抑制再结晶.合金主要软化机制为动态回复伴随动态再结晶.     

Ti-5Mo-5V-1Cr-3Al合金的热压缩变形行为研究EI北大核心CSCD

采用恒应变速率热压缩模拟实验,对Ti-5Mo-5V-1Cr-3A1（简称1Cr）钛合金在应变速率0.001～1s-1、变形温度700～900℃条件下进行研究.结果表明：该材料的流变应力对温度与应变速率敏感：当变形温度为700～800℃时,真应力-真应变曲线呈现动态再结晶单曲线特征;当变形温度为800～900℃时,低应变速率（0.001s-1）的真应力-真应变曲线呈现动态再结晶多应力峰值曲线特征,高应变速率（0.01～1s-1）的真应力-真应变曲线呈现动态回复曲线特征.1Cr合金在等温压缩变形时的流变行为可用包含Zener-Holomon参数的Arrhenius本构方程描述,变形激活能为456kJ/mol.金相结果显示,材料在热压缩过程中的动态行为除了与变形速率、变形温度等加工参数相关外,也与相应温度、变形速率下材料的组织及相结构有关.合金在低应变速率0.001s 1下热压缩变形时,在接近相变点或以上（800～900℃）温度范围内仍呈现动态再结晶行为,这与材料在此阶段发生的应变诱发马氏体转变密切相关,马氏体相的析出促使材料在热变形时趋向于发生动态再结晶行为.     

From Industry 4.0 to Research 4.0. Development of High Performance Fibers in the Light of Digitization

We associate a variety of innovations with the term ＂Industry 4.0＂. The pioneer of many 4.0 modifications forms the basisfor the trend towards the integrated di...     

Roman iron and steel: A review

ABSTRACT

The production of ferrous metal increased during the Roman Late Republican period, Principate and Empire. The direct bloomery process was used to extract the metal from its ores using slag-tapping and slag-pit furnaces. The fuel was charcoal and an air blast was introduced by bellows-operated tuyères. Iron formed as a bloom, often as a spongy mass of metal, which contained impurities from the smelting process, including unreacted ore, fuel, slag and fragments from the furnace walls, while the metal was often inhomogeneous with varied carbon contents. Blooms were either smithed directly into bars or ingots or they were broken up, which also allowed the removal of gross impurities and a selection of pieces with similar properties to be made. These could then be forge-welded together and formed into characteristically shaped ingots. Making steel in the furnace seems to have been achieved: it depended on the ore and the furnace and conditions within it. Surface carburization was also carried out. Iron and steel were used extensively in construction and for tools and weapons. Fire welding was often used to add pieces of steel to make the edges of tools and weapons, which could be heat-treated by quenching to harden them.     

Certification Institutions Expected to Update and Transfer Information on Present Standards

Standards are the basis for production enterprises to organize production, ex-factory inspection, trade (delivery) and technical exchanges, product certification, quality arbitration and supervision.……     

The Research of Anti-Wear Properties of Organomolybdenum Compounds in the Engine Oils

A four-ball tester was used to evaluate the anti-wear performance of three kinds of organomolybdemun compounds in the engine oils, i. e., molybdenum dialkyldithiophosphate (MoDDP), molybdenum dialkyldithiocarbamate ( MoDTC), and sulphur and phosphorus freeorganomolybdeum (Molybdate). The results indicate that a low concentration of MoDDP doesn' t improve the anti-wear properties of the commercial engine oils, but a high concentration of MoDDP can obviously improve the anti-wear properties and the load-carrying capacity of the engine oils. MoDTC doesn' t improve the antiwear properties of the engine oils, but worsens the anti-wear properties of the oils. Signifi can timprove ment of frictional and wear characteristics is obtained with Molybdate added in the commercial engine oils and the formulated oils.     

Synthesis of Alumina-Zirconia Nanocomposites by Solgel Process

Al₂O₃-ZrO₂ nanocomposites were developed starting with the solgel process. Composite alumina-zirconia nanopowders were synthesized from metallorganic precursors (Aluminium secondary butoxide and zirconium Iso propoxide) using the solgel process. The parameters affecting the synthesis—solvent, concentration of precursor, R/H ratio (i.e., dilution of water in solvent)—were varied as also the temperature and pH. BET and TEM were used to measure nanosize. Diffuse reflectance spectroscopy and also qualitative optical absorption led to identical particle size estimate. The variation of process parameters was used to study the effect and interdependence of process parameters. Artificial Neural Networks was used to rigorously analyze the process. Although this led to confirmation of interdependence of parameters, the presence of a single overwhelming solvent variable was also established. Then the optimal process was used to synthesize more nanopowder. To produce bulk nanocomposite the nanopowders were sintered by varying the temperature and time period. The sintered lithoids were probed with a vickers hardness tester to measure elastic modulus, hardness, and fracture toughness. The results showed high elastic modulus, modest hardness, and very high fracture toughness.     

Friction Stir Processing Strategies for Uniform Distribution of Reinforcement in a Surface Composite

Friction stir processing (FSP) is an important technique for preparing surface composites. Fabricating defect-free surface composites with uniform particle distribution by FSP is a challenging task. In this study, silicon carbide particles reinforced AA5083 alloy surface composites was fabricated using different FSP strategies including variation in process parameters, dual-tool processing and tool offset overlapping. Material flow of the processed material with reinforcement particles demonstrated that the distribution of particles was influenced by the stirring action of the probe as well as the extrusion of the plasticized material due to the movement of the tool. Process parameters, particularly rotational speed, showed a dominant influence on the distribution of silicon carbide particles.     

Optimum-Simulation von Ernteprozessen

Zusammenfassung Bei der Gestaltung von Ernteprozessen — beispielsweise des Prozesses Mähdrusch, Körnertransport und -abnahme — als transportverbundene Fließarbeitsverfahren mit mindestens zwei verschiedenen Arbeitsmitteln gibt es einen großen Optimierungsspielraum. Solche Prozesse sind mehrstufige Bedienungsprozesse mit gemischter Anordnung der Bedienungseinrichtungen. Außerdem besitzen sie stark ausgeprägte räumliche Aspekte. Es wird vor allem gezeigt, welche Merkmale solcher Prozesse in Simulationsmodellen abgebildet sein müssen, welche Zielgrößen in Abhängigkeit von welchen Einflußgrößen unter Berücksichtigung welcher Prozeßbedingungen ermittelt werden sollten und wie der Bewertungsprozeß zur Ermittlung der gewünschten Informationen gestaltet werden muß.     

Certification Becomes Important for the I Quality; and Safety Supervision of the Chinese Liquor Sector

The end of 2007, over 200 unit products of more than 80 Chinese firms have passed the quality grade certification for liquor products. These products involve distilled spirits, beer, wine, yellow wine, fruit syrup wine and others, and cover over 80% of the national top-branded liquor products.……     

Deposition and Coating Properties on CVD Tungsten

Surface characterization and microstructure studies are performed on chemical vapor deposited (CVD) tungsten coating. There is about 2 μm thickness diffusion layer of tungsten in the molybdenum substrate. The thermal shock test shows tungsten coating has good adhesion with molybdenum substrate, but the elements of oxygen and carbon in the tungsten coating have the bad affection to the adhesion. The result of high-temperature diffusion experiment is the diffusion rate from molybdenum substrate to tungsten coating is faster.     

Instructions & Forms for Authors

Journal of Materials Sciences ＆ Technology is a monthly journal for the rapid dissemination of new, impor- rant results in material and related fields. Submission Electronic files of MS Word and PDF are acceptable. Please visit http：//www.jmst.org and submit online.