A novel micro-spherical CoSn2/Sn alloy composite as high capacity anode materials for Li-ion rechargeable batteries

Micro-scaled spherical CoSn₂/Sn alloy powders synthesized from oxides of Sn and Co via carbothermal reduction at 800 °C were examined for use as anode materials in Li-ion battery. The phase composition and particle morphology of the CoSn₂/Sn alloy composite powders were investigated by XRD, SEM and TEM. The prepared CoSn₂/Sn alloy composite electrode exhibits a low initial irreversible capacity of ca. 140 mAh g⁻¹, a high specific capacity of ca. 600 mAh g⁻¹ at constant current density of 50 mA g⁻¹, and a good rate capability. The stable discharge capacities of 500-515 mAh g⁻¹ and the columbic efficiencies of 95.8-98.1% were obtained at current density of 500 mA g⁻¹. The relatively large particle size of CoSn₂/Sn alloy composite powder is apparently favorable for the lowering of initial capacity loss of electrode, while the loose particle structural characteristic and the Co addition in Sn matrix should be responsible for the improvement of cycling stability of CoSn₂/Sn electrode.     

Study on the rapid synthesis of LiNi1−xCoxO2 cathode material for lithium secondary battery

LiNi_1−xCo_xO₂ (x = 0, 0.1, 0.2) cathode materials were successfully synthesized by a rheological phase reaction method with calcination time of 0.5 h at 800 °C. All obtained powders are pure phase with α-NaFeO₂ structure (R-3m space group). The samples deliver an initial discharge capacity of 182, 199 and 189 mAh g⁻¹ (25 mA g⁻¹, 4.35-3.0 V), respectively. The reaction mechanism was also discussed, which consists of a series of defect reactions. As a result of these defect reactions, the reaction of forming LiNi_1−xCo_xO₂ takes place in high speed.     

Electrochemical properties of La1−xSrxFeO3 (x = 0.2, 0.4) as negative electrode of Ni-MH batteries

La_(1−x)Sr_xFeO₃ (x = 0.2,0.4) powders were prepared by a stearic acid combustion method, and their phase structure and electrochemical properties were investigated systematically. X-ray diffraction (XRD) analysis shows that La_(1−x)Sr_xFeO₃ perovskite-type oxides consist of single-phase orthorhombic structure (x = 0.2) and rhombohedral one (x = 0.4), respectively. The electrochemical test shows that the reaction at La_(1−x)Sr_xFeO₃ oxide electrodes are reversible. The discharge capacities of La_(1−x)Sr_xFeO₃ oxide electrodes increase as the temperature rises. With the increase of the temperature from 298 K to 333 K, their initial discharge capacity mounts up from 324.4 mA h g⁻¹ to 543.0 mA h g⁻¹ (when x = 0.2) and from 147.0 mA h g⁻¹ to 501.5 mA h g⁻¹ (when x = 0.4) at the current density of 31.25 mA g⁻¹, respectively. After 20 charge-discharge cycles, they still remain perovskite-type structure. Being similar to the relationship between the discharge capacity and the temperature, the electrochemical kinetic analysis indicates that the exchange current density and proton diffusion coefficient of La_(1−x)Sr_xFeO₃ oxide electrodes increase with the increase of the temperature. Compared with La_0.8Sr_0.2FeO₃, La_0.6Sr_0.4FeO₃ electrode is a more promising candidate for electrochemical hydrogen storage because of its higher cycle capacity at various temperatures.     

Preparation and characterization of novel spinel Li4Ti5O12−xBrx anode materials

Br-doped Li₄Ti₅O₁₂ in the form of Li₄Ti₅O_12−xBr_x (0 ≤ x ≤ 0.3) compounds were successfully synthesized via solid state reaction. The structure and electrochemical properties of the spinel Li₄Ti₅O_12−xBr_x (0 ≤ x ≤ 0.3) materials were investigated. The Li₄Ti₅O_12−xBr_x (x = 0.2) presents the best discharge capacity among all the samples, and shows better reversibility and higher cyclic stability compared with pristine Li₄Ti₅O₁₂, especially at high current rates. When the discharge rate was 0.5 C, the Li₄Ti₅O_12−xBr_x (x = 0.2) sample presented the excellent discharge capacity of 172 mAh g⁻¹, which was very close to its theoretical capacity (175 mAh g⁻¹), while that of the pristine Li₄Ti₅O₁₂ was 123.2 mAh g⁻¹ only.     

Molten salt synthesis of spherical LiNi0.5Mn1.5O4 cathode materials

This paper describes a novel simple redox process for synthesizing monodispersed MnO₂ powders and preparation of spherical LiNi_0.5Mn_1.5O₄ cathode materials by molten salt synthesis (MSS) method. Monodispersed MnO₂ powders have been synthesized by using potassium permanganate and manganese sulfate as the starting materials. By using this redox method, it was found that monodispersed MnO₂ powders with average particle size ∼5 μm can be easily obtained. Resultant MnO₂ and LiOH, Ni(OH)₂ was then used to synthesis LiNi_0.5Mn_1.5O₄ cathode materials with retention of spherical particle shape by MSS method. The discharge capacity was 129 mAh g⁻¹ in the first cycle and 127 mAh g⁻¹ after 50 cycles under an optimal synthesis condition for 12 h at 800 °C.     

Effect of synthesis condition on the structural and electrochemical properties of Li[Ni1/3Mn1/3Co1/3]O2 prepared by the metal acetates decomposition method

In order to get homogeneous layered oxide Li[Ni_1/3Mn_1/3Co_1/3]O₂ as a lithium insertion positive electrode material, we applied the metal acetates decomposition method. The oxide compounds were calcined at various temperatures, which results in greater difference in morphological (shape, particle size and specific surface area) and the electrochemical (first charge profile, reversible capacity and rate capability) differences. The Li[Ni_1/3Mn_1/3Co_1/3]O₂ powders were characterized by means of X-ray diffraction (XRD), charge/discharge cycling, cyclic voltammetry and SEM. XRD experiment revealed that the layered Li[Ni_1/3Mn_1/3Co_1/3]O₂ material can be best synthesized at temperature of 800 °C. In that synthesized temperature, the sample showed high discharge capacity of 190 mAh g⁻¹ as well as stable cycling performance at a current density of 0.2 mA cm⁻² in the voltage range 2.3-4.6 V. The reversible capacity after 100 cycles is more than 190 mAh g⁻¹ at room temperature.     

Effect of fluorine in the preparation of Li(Ni1/3Co1/3Mn1/3)O2 via hydroxide co-precipitation

Uniform and spherical Li(Ni_1/3Co_1/3Mn_1/3)O_(2−δ)F_δ powders were synthesized via NH₃ and F⁻ coordination hydroxide co-precipitation. The effect of F⁻ coordination agent on the morphology, structure and electrochemical properties of the Li(Ni_1/3Co_1/3Mn_1/3)O_(2−δ)F_δ were studied. The morphology, size, and distribution of (Ni_1/3Co_1/3Mn_1/3)(OH)_(2−δ)F_δ particle diameter were improved in a shorter reaction time through the addition of F⁻. The study suggested that the added F improves the layered characteristics of the lattice and the cyclic performance of Li(Ni_1/3Co_1/3Mn_1/3)O₂ in the voltage range of 2.8-4.6 V. The initial capacity of the Li(Ni_1/3Co_1/3Mn_1/3)O_1.96F_0.04 was 178 mAh g⁻¹, the maximum capacity was 186 mAh g⁻¹ and the capacity after 50 cycles was 179 mAh g⁻¹ in the voltage range of 2.8-4.6 V.     

Synthesis and electrochemical performance of Li2FeSiO4/carbon/carbon nano-tubes for lithium ion battery

Li₂FeSiO₄/carbon/carbon nano-tubes (Li₂FeSiO₄/C/CNTs) and Li₂FeSiO₄/carbon (Li₂FeSiO₄/C) composites were synthesized by a traditional solid-state reaction method and characterized comparatively by X-ray diffraction, scanning electron microscopy, BET surface area measurement, galvanostatic charge-discharge and AC impedance spectroscopy, respectively. The results revealed that the Li₂FeSiO₄/C/CNT composite exhibited much better rate performance in comparison with the Li₂FeSiO₄/C composite. At 0.2 C, 5 C and 10 C, the former composite electrode delivered a discharge capacity of 142 mAh g⁻¹, 95 mAh g⁻¹, 80 mAh g⁻¹, respectively, and after 100 cycles at 1 C, the discharge capacity remained 95.1% of its initial value.     

Structural and electrochemical behaviors of metastable Li2/3[Ni1/3Mn2/3]O2 modified by metal element substitution

Layered metastable lithium manganese oxides, Li_2/3[Ni_1/3−xMn_2/3−yM_x+y]O₂ (x = y = 1/36 for M = Al, Co, and Fe and x = 2/36, y = 0 for M = Mg) were prepared by the ion exchange of Li for Na in P2-Na_2/3[Ni_1/3−xMn_2/3−yM_x+y]O₂ precursors. The Al and Co doping produced the T^#2 structure with the space group Cmca. On the other hand, the Fe and Mg doped samples had the O6 structure with space group R-3m. Electron diffraction revealed the 1:2 type ordering within the Ni_1/3−xMn_2/3−yM_x+yO₂ slab. It was found that the stacking sequence and electrochemical performance of the Li cells containing T^#2-Li_2/3[Ni_1/3Mn_2/3]O₂ were affected by the doping with small amounts of Al, Co, Fe, and Mg. The discharge capacity of the Al doped sample was around 200 mAh g⁻¹ in the voltage range between 2.0 and 4.7 V at the current density of 14.4 mA g⁻¹ along with a good capacity retention. Moreover, for the Al and Co doped and undoped oxides, the irreversible phase transition of the T^#2 into the O2 structure was observed during the initial lithium deintercalation.     

Synthesis of spinel LiMn2O4 with manganese carbonate prepared by micro-emulsion method

Micro-spherical particle of MnCO₃ has been successfully synthesized in CTAB-C₈H₁₈-C₄H₉OH-H₂O micro-emulsion system. Mn₂O₃ decomposed from the MnCO₃ is mixed with Li₂CO₃ and sintered at 800 °C for 12 h, and the pure spinel LiMn₂O₄ in sub-micrometer size is obtained. The LiMn₂O₄ has initial discharge specific capacity of 124 mAh g⁻¹ at discharge current of 120 mA g⁻¹ between 3 and 4.2 V, and retains 118 mAh g⁻¹ after 110 cycles. High-rate capability test shows that even at a current density of 16 C, capacity about 103 mAh g⁻¹ is delivered, whose power is 57 times of that at 0.2 C. The capacity loss rate at 55 °C is 0.27% per cycle.     

Synthesis and electrochemical characterization of mesoporous CoxNi1−x layered double hydroxides as electrode materials for supercapacitors

A novel nanostructured mesoporous Co_xNi_1−x layered double hydroxides (Co_xNi_1−x LDHs), which both Co(OH)₂ and Ni(OH)₂ exhibit, has been successfully synthesized by a chemical co-precipitation route using polyethylene glycol as the structure-directing reagent. Structural and morphological characterizations were performed using powder X-ray diffraction (XRD) and field emission scanning electron microscopy (FESEM). The component and thermal stability of the sample were measured by energy dispersed X-ray spectrometry (EDS), FT-IR and thermal analyses, including thermogravimetry (TG) and differential thermal analysis (DTA). Cyclic voltammogram and galvanostatic charge-discharge testified that the Co_xNi_1−x LDH has a specific capacitance of 1809 F g⁻¹ at a current density of 1 A g⁻¹ and remains at about 90.2% of the initial value after 1000 cycles at a current density of 10 A g⁻¹. The relationship between the chemical composition and the capacitance is discussed.     

Study on phase structure and electrochemical properties of Ml1−xMgxNi2.80Co0.50Mn0.10Al0.10 (x = 0.08, 0.12, 0.20, 0.24, 0.28) hydrogen storage alloys

Phase structure and electrochemical properties of the Ml_1−xMg_xNi_2.80Co_0.50Mn_0.10Al_0.10 (x = 0.08, 0.12, 0.20, 0.24, 0.28) (Ml = La-rich mixed lanthanide) alloys were studied. X-ray diffraction (XRD) analysis and Rietveld refinement show that the alloys consist mainly of LaNi₅ and (La,Mg)Ni₃ phase. Due to variation in phases of the alloys, the maximum discharge capacity, the high rate dischargeability (HRD), and the low temperature dischargeability increase first and then decrease. The maximum discharge capacity increases from 322 mAh g⁻¹ (x = 0.08) to 375 mAh g⁻¹ (x = 0.12), and then decreases to 351 mAh g⁻¹ (x = 0.28) with increasing x. As the case of x = 0.20, HRD at 1200 mA g⁻¹ and discharge capacity at 233 K reaches 41.7% and 256 mAh g⁻¹, respectively. The cycling stability is improved by substituting La with Ml and B-site multi-alloying, and the capacity retention of Ml_0.72Mg_0.28Ni_2.80Co_0.50Mn_0.10Al_0.10 at the 200th cycle is 71%.     

Electrochemical performance of flowerlike CaSnO3 as high capacity anode material for lithium-ion batteries

Nanosized CaSnO₃ is synthesized by a hydrothermal process and characterized by X-ray diffraction (XRD), Raman spectroscopy, and scanning electron microscopy (SEM). The SEM observation shows the sample has a porous flowerlike morphology. The electrochemical results exhibit that the stable and reversible capacity of 547 mAh g⁻¹ is obtained after 50 cycles at 60 mA g⁻¹ (0.1 C) and the corresponding charge capacity is determined to be 316 mAh g⁻¹ at the current density of 2.5 C. Cyclic voltammetry and electrochemical impedance spectroscopy data are analyzed to complement the galvanostatic results. The observed excellent performance is attributed to the porous structure and large surface area of flowerlike CaSnO₃.     

Mesoporous polyaniline or polypyrrole/anatase TiO2 nanocomposite as anode materials for lithium-ion batteries

A functional composite as anode materials for lithium-ion batteries, which contains highly dispersed TiO₂ nanocrystals in polyaniline matrix and well-defined mesopores, is fabricated by employing a novel one-step approach. The as-prepared mesoporous polyaniline/anatase TiO₂ nanocomposite has a high specific surface area of 224 m² g⁻¹ and a predominant pore size of 3.6 nm. The electrochemical performance of the as-prepared composite as anode material is investigated by cyclic voltammograms and galvanostatic method. The results demonstrate that the polyaniline/anatase nanocomposite provides larger initial discharge capacity of 233 mAh g⁻¹ and good cycle stability at the high current density of 2000 mA g⁻¹. After 70th cycles, the discharge capacity is maintained at 140 mAh g⁻¹. The excellent electrochemical performance of the polyaniline/TiO₂ nanocomposite is mainly attributed to its special structure. Furthermore, it is accessible to extend the novel strategy to other polymer/TiO₂ composites, and the mesoporous polypyrrole/anatase TiO₂ is also successfully fabricated.     

Submicron-sized cube-like α-Fe2O3 agglomerates as an anode material for Li-ion batteries

Submicron-sized cube-like α-Fe₂O₃ agglomerates were successfully fabricated via hydrothermal technique. The material showed a high reversible capacity of 900.2 mAh g⁻¹ and excellent capacity retention of 88.9% after 35 cycles at a current density of 40 mA g⁻¹. The initial columbic efficiencies of the as-prepared powder were 82.65 and 80.57% at current densities of 40 and 80 mA g⁻¹, respectively, which is higher than that of other α-Fe₂O₃ electrodes reported so far. We believe that the small crystal size and the high structure stability are responsible for the drastic improvement in initial coulombic efficiency and reversibility.     

Comparison of AlPO4- and Co3(PO4)2-coated LiNi0.8Co0.2O2 cathode materials for Li-ion battery

Electrochemical and thermal properties of Co₃(PO₄)₂- and AlPO₄-coated LiNi_0.8Co_0.2O₂ cathode materials were compared. AlPO₄-coated LiNi_0.8Co_0.2O₂ cathodes exhibited an original specific capacity of 170.8 mAh g⁻¹ and had a capacity retention (89.1% of its initial capacity) between 4.35 and 3.0 V after 60 cycles at 150 mA g⁻¹. Co₃(PO₄)₂-coated LiNi_0.8Co_0.2O₂ cathodes exhibited an original specific capacity of 177.6 mAh g⁻¹ and excellent capacity retention (91.8% of its initial capacity), which was attributed to a lithium-reactive Co₃(PO₄)₂ coating. The Co₃(PO₄)₂ coating material could react with LiOH and Li₂CO₃ impurities during annealing to form an olivine Li_xCoPO₄ phase on the bulk surface, which minimized any side reactions with electrolytes and the dissolution of Ni⁴⁺ ions compared to the AlPO₄-coated cathode. Differential scanning calorimetry results showed Co₃(PO₄)₂-coated LiNi_0.8Co_0.2O₂ cathode material had a much improved onset temperature of the oxygen evolution of about 218 °C, and a much lower amount of exothermic-heat release compared to the AlPO₄-coated sample.     

TiO2 nanotube arrays annealed in CO exhibiting high performance for lithium ion intercalation

Anatase titania nanotube arrays were fabricated by means of anodization of Ti foil and annealed at 400 °C in respective CO and N₂ gases for 3 h. Electrochemical impendence spectroscopy study showed that CO annealed arrays possessed a noticeably lower charge-transfer resistance as compared with arrays annealed in N₂ gas under otherwise the same conditions. TiO₂ nanotube arrays annealed in CO possessed much improved lithium ion intercalation capacity and rate capability than N₂ annealed samples. At a high charge/discharge current density of 320 mA g⁻¹, the initial discharge capacity in CO annealed arrays was found to be as high as 223 mAh g⁻¹, 30% higher than N₂ annealed arrays, ∼164 mAh g⁻¹. After 50 charge/discharge cycles, the discharge capacity in CO annealed arrays remained at ∼179 mAh g⁻¹. The improved intercalation capacity and rate capability could be attributed to the presence of surface defects like Ti-C species and Ti³⁺ groups with oxygen vacancies, which not only improved the charge-transfer conductivity of the arrays but also possibly promoted phase transition.     

Enhanced electrochemical properties of LiFePO4/C synthesized with two kinds of carbon sources,PEG-4000 (organic) and Super p (inorganic)

Olivine structured LiFePO₄/C cathode was synthesized via a freeze-drying route and followed by microwave heating with two kinds of carbon sources: PEG-4000 (organic) and Super p (inorganic). XRD patterns indicate that the as-prepared sample has an olivine structure and carbon modification does not affect the structure of the sample. Image of SEM shows a uniform and optimized particles size, which greatly improves the electrochemical properties. TEM result reveals the amorphous carbon around the surface of the particles. At a low rate of 0.1 C, the LiFePO₄/C sample presents a high discharge capacity of 157.8 mAh g⁻¹ which is near the theoretical capacity (170 mAh g⁻¹), and it still attains to 149.1 mAh g⁻¹ after 200 cycles. It also exhibits an excellent rate capacity with high discharge capacities of 143.2 mAh g⁻¹, 137.5 mAh g⁻¹, 123.7 mAh g⁻¹ and 101.6 mAh g⁻¹ at 0.5 C, 1.0 C, 2.0 C and 5.0 C, respectively. EIS results indicate that the charge transfer resistance of LiFePO₄ decreases greatly after carbon coating.     

Synthesis of sawtooth-like Li4Ti5O12 nanosheets as anode materials for Li-ion batteries

Hierarchical layered hydrous lithium titanate and Li₄Ti₅O₁₂ microspheres assembled by nanosheets have been successfully synthesized via a hydrothermal process and subsequent thermal treatment. The electrochemical properties of the two samples have been investigated by galvanostatic methods. The former, with the obvious layered structure and a large surface area, delivers a reversible capacity of 180 mA h g⁻¹ after 200 cycles at 200 mA g⁻¹. As for Li₄Ti₅O₁₂, with the intriguing and unique sawtooth-like morphology, it presents exceptional high rate performance and excellent cycling stability. Up to 132 mA h g⁻¹ is obtained after 200 cycles at 10,000 mA g⁻¹ (57 C), proving itself promising for high-rate applications.     

Spray-drying synthesized LiNi0.6Co0.2Mn0.2O2 and its electrochemical performance as cathode materials for lithium ion batteries

Layered LiNi_0.6Co_0.2Mn_0.2O₂ materials were synthesized at different sintering temperatures using spray-drying precursor with molar ratio of Li/Me = 1.04 (Me = transition metals). The influences of sintering temperature on crystal structure, morphology and electrochemical performance of LiNi_0.6Co_0.2Mn_0.2O₂ materials have been characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and charge-discharge test. As a result, material synthesized at 850 °C has excellent electrochemical performance, delivering an initial discharge capacity of 173.1 mAh g^− 1 between 2.8 and 4.3 V at a current density of 16 mA g^− 1 and exhibiting good cycling performance.