FT-50S药芯焊丝工艺性能研究

研究了FT-50S药芯焊丝CO2气体保护焊在3种焊接工艺参数下的焊丝工艺性能,结果表明:小焊接参数下,FT-50S药芯焊丝发生的是短路过渡,电弧有瞬间熄弧,熔滴过渡时发生液体小桥爆炸产生大量飞溅;中等焊接参数下,发生的是大颗粒过渡,熔滴在焊丝末端长大到一定程度后重力克服表面张力过渡到熔池,产生的飞溅较小;大焊接参数下,发生的是细颗粒过渡,飞溅最小。中、大焊接参数下电弧均呈锥形,电弧稳定且扩散性好并都发生了药芯渣滴/金属熔滴分离过渡。FT-50S药芯焊丝电弧焊焊缝成形系数较大,有利于减小焊缝的热裂倾向。     

药芯焊丝电弧焊的熔滴过渡与相关技术特性

采用数码MOVIE照相技术,拍摄并电子记录了"O"形截面酸性渣系药芯焊丝电弧焊(FCAW)时的熔滴过渡行为,观察到不同工艺参数下的熔滴过渡类型有短路过渡、大颗粒过渡和细颗粒过渡;还观察到FCAW具有周向旋转、非轴向过渡、滞熔和熔滴/渣滴分离过渡等熔滴过渡特性.研究表明,药芯焊丝电弧的径向能量分布梯度小、能量密度分布较均匀,这导致了其焊缝形状系数较实芯焊丝CO2焊接增大80%以上.     

钛型渣系气保护药芯焊丝焊接参数相互关系

采用高速摄影、平板实焊等试验方法,研究了钛型渣系气保护药芯焊丝焊接参数的技术特征、电弧形态、熔滴过渡形态以及焊接工艺参数间的匹配关系.结果表明,钛型渣系气保护药芯焊丝熔滴过渡的基本形态是非轴向排斥过渡,焊丝的电弧形态属于活动、连续型,焊丝熔滴过渡受主导力控制.该工艺方法的关键参数是焊接电流和电弧电压,它们之间存在最佳数...     

碱性药芯焊丝熔滴过渡特性及工艺性分析

利用高速摄像和汉诺威弧焊分析仪,在富氩气体保护条件下,在不同的焊接参数下对3种碱性药芯焊丝样品进行了测试和分析. 结果表明,较小焊接参数时,熔滴过渡形式为粗熔滴排斥过渡,电弧稳定性差,飞溅大;随着焊接参数的增大,熔滴过渡逐渐转变为细熔滴过渡,过渡过程趋于稳定. 熔滴受到较大的排斥力以及熔体的表面张力大是造成大颗粒飞溅的主要原因,较长的渣柱对熔滴过渡具有导向作用,细化熔滴和形成稳定、较长的渣柱是改善碱性药芯焊丝工艺性的重要途径.     

钛型渣系气保护药芯焊丝研究进展北大核心

从药芯焊丝的电弧形态和熔滴过渡形态以及影响因素、焊丝的发展和改进等方面,综述了钛型渣系气保护药芯焊丝研究的某些进展。结果表明,药芯焊丝熔滴过渡的基本形态是非轴向排斥过渡,焊丝的电弧形态属于活动、连续型,焊丝熔滴过渡受主导力控制。影响气保护药芯焊丝熔滴过渡的主要因素有:药芯组成物、焊丝截面形状、焊丝直径和钢带厚度、焊接工艺参数等。提出了通过熔滴过渡指数控制焊接飞溅和通过电弧中熔滴吸收氢的总质量控制焊缝中气孔(压坑)的新思路。焊丝内在质量关键技术是熔敷金属韧性稳定性的控制,必须重视焊丝生产线装备的技术先进性因素。     

药芯焊丝电弧焊熔滴过渡与焊接飞溅

针对不同焊接参数下SQJ501型、SQJS07型和SQJ50MX型药芯焊丝电弧焊的熔滴过渡行为进行了拍照,并对焊接飞溅进行了测量,研究药芯焊丝电弧焊的熔滴过渡行为及其焊接飞溅的基本规律.试验结果表明:三种药芯焊丝随着焊接参数的增大,均依次发生短路过渡、大滴排斥过渡和细颗粒过渡.SQJ501型和SQJS0MX型药芯焊丝电孤焊电弧形态呈锥形,SQJS07型电弧形态接近于钟形.SQJ507型药芯焊丝出现细颗粒过渡的焊接参数比其他两种焊丝大.焊接工艺参数以及焊丝种类影响了熔滴过渡行为进而影响焊接飞溅,细颗粒过渡时产生的飞溅最小.     

钛型渣系气保护药芯焊丝研究进展

从药芯焊丝的电弧形态和熔滴过渡形态以及影响因素、焊丝的发展和改进等方面,综述了钛型渣系气保护药芯焊丝研究的某些进展.结果表明,药芯焊丝熔滴过渡的基本形态是非轴向排斥过渡,焊丝的电弧形态属于活动、连续型,焊丝熔滴过渡受主导力控制.影响气保护药芯焊丝熔滴过渡的主要因素有:药芯组成物、焊丝截面形状、焊丝直径和钢带厚度、焊接工艺参数等.提出了通过熔滴过渡指数控制焊接飞溅和通过电弧中熔滴吸收氢的总质量控制焊缝中气孔(压坑)的新思路.焊丝内在质量关键技术是熔敷金属韧性稳定性的控制,必须重视焊丝生产线装备的技术先进性因素.     

钛型气保护药芯焊丝的电弧行为、冶金特性及其工艺质量

本文分析了钛型渣系气保护药芯焊丝的电弧行为和化学冶金过程,探讨了药芯焊丝的焊接飞溅及焊缝中气孔工艺质量问题。结果表明,药芯焊丝熔滴过渡的基本形态是非轴向排斥过渡,焊丝的电弧形态属于活动、连续型,焊丝熔滴过渡受主导力控制。焊丝的焊接化学冶金过程是分区连续进行的。药芯焊丝熔滴过渡中伴随渣柱,以及渣柱直接进入熔池现象,可能导致焊接化学冶金反应不完全和;台金过程的新变化。药芯焊丝的焊接飞溅主要发生在非轴向排斥过渡的熔滴与焊丝之间的缩颈处,提出通过熔滴过渡指数控制焊接飞溅新观点。当气体从焊缝金属中逸出被阻止于焊缝中或被困于熔渣下面,就分别形成了气孔和表面压坑,提出了通过电弧中熔滴吸收氢的总重量控制焊缝中气孔的新思路。     

碱性渣系气体保护药芯焊丝立向上焊接工艺

采用平板对接立向上焊接、焊接电弧物理观察等试验方法，观察了碱性渣系气体保护药芯焊丝熔滴过渡和电弧特性，研究了立向上焊焊缝成形机理及影响因素。结果表明，碱性焊丝立向上焊时，粗熔滴非轴向过渡和集中、活动型电弧特性使熔滴过渡的定向性很差，熔滴飞溅增大；碱性熔渣的流动性大，凝固速度慢，对熔池的扶托作用差，熔池的形状较难控制，焊缝成形相对困难。采用合理的、最佳匹配的焊接参数和有效的操作技术和运丝方式是获得满意立向上焊缝的必要条件。     

药芯焊丝电弧焊“滞熔”现象影响因素的研究

针对当前药芯焊丝应用及研究中存在的问题，用数码照相技术研究了CO2保护气氛下药芯焊丝电弧焊所特有的“滞熔”现象，主要从药芯焊丝渣系、焊接参数、焊丝截面方面对“滞熔”形成原因进行了探讨。实验结果表明，酸性、碱性、金属型三种渣系药芯焊丝均存在不同程度的滞熔现象；在相同焊接参数下，金属型药芯焊丝滞熔程度最小，酸性渣系与碱性渣系相比，小参数下药芯滞熔程度较小，随着焊接参数的增大，酸碱性渣系药芯焊丝的滞熔程度区别不大。     

电弧电压变化量分析熔滴过渡特征的研究

利用焊接过程中熔滴还没有发生短路瞬间的电弧电压变化量△U，可以区分药芯焊丝气体保护焊(FCAW)熔滴过渡特征．绘制了一定焊接条件下的金属过渡模式图，为最终确定FCAW的最佳工艺参数(焊接电流、电弧电压等)提供指导，可实施长时间在践监控熔滴过渡过程。     

水下湿法焊接浅水环境下FCAW电弧静特性

为了研究水下湿法焊接浅水环境下FCAW电弧特性,在自制的能够模拟不同水深的高压舱焊接系统内进行了一系列试验.并用编写的Lab View程序在采集到的电弧电压和焊接电流数据中选取焊接时较稳定的数据绘制电弧静特性曲线,对比分析了在相同的焊接工艺参数下常压空气中平板工件焊接和在浅水环境下水下湿法FCAW的电弧静特性,同时研究...     

Sensitivity model for prediction of bead geometry in underwater wet flux cored arc welding

To investigate influence of welding parameters on weld bead geometry in underwater wet flux cored arc welding (FCAW), orthogonal experiments of underwater wet FCAW were conducted in the hyperbaric chamber at water depth from 0.2 m to 60 m and mathematical models were developed by multiple curvilinear regression method from the experimental data. Sensitivity analysis was then performed to predict the bead geometry and evaluate the influence of welding parameters. The results reveal that water depth has a greater influence on bead geometry than other welding parameters when welding at a water depth less than 10 m. At a water depth deeper than 10 m, a change in travel speed affects the bead geometry more strongly than other welding parameters.     

Study on arc characteristics and behavior of metal transfer in pulse current flux-cored arc welding of mild steel

The variation in arc characteristics and behavior of metal transfer with the change in pulse parameters has been studied by high speed video camera during pulse current flux cored arc weld deposition. A comparative study of similar nature has also been carried out during flux-cored arc weld deposition in globular and spray transfer modes. The effect of pulse parameters has been studied by considering their mean current and arc voltage. The arc characteristics studied by its root diameter, projected diameter and length, and the behavior of metal transfer noted by the metal transfer model and the droplet diameter have been found to vary significantly with the pulse parameters. The observation may help in understanding the arc characteristics with respect to the variation in pulse parameters which may be beneficial in using pulse current FCAW to produce desired weld quality.     

双丝间接电弧焊的电弧形态

用高速摄像系统及示波器对双丝间接电弧气体保护焊的电弧形态进行了研究.结果表明,双丝间接电弧气体保护焊在两丝端部形成电弧,其电弧本质仍然是气体放电的一种表现形式.焊接电流、电弧电压及两焊丝交点与工件间距离对电弧形态产生较大的影响,随焊接电流的变化,电弧形态会发生不同程度的集中与分散的变化;电压越大电弧越明亮电弧的形体也越大;两丝交点与工件间距离越小,电弧越集中并且变得短而亮.燃烧过程中电弧电压随时间而周期性变化,相应的电弧形态也随着时间发生周期性变化,电弧电压与电弧形态间有很好的对应关系.     

不锈钢活性剂等离子弧焊焊接电弧

针对活性剂等离子弧焊焊接过程,对焊接电弧外形的变化,焊接电弧电压与活性剂之间的关系进行了研究,采用红外热像伪着色法测定了活性剂等离子弧焊焊接电弧温度场,并建立了活性剂等离子弧焊焊接电弧热流密度径向分布模型.研究结果表明,活性剂等离子弧焊焊接电弧收缩,弧尾翼消失,尾焰加大,电弧穿透力增强,电弧电压升高;活性剂等离子弧焊焊接电弧的温度分布比较紧凑,温度场外形窄,温度分布范围较集中,电弧径向温度梯度较大;电弧径向温度分布呈现正态Gauss分布模式;使用活性剂后的焊接接头性能与未使用活性剂焊接接头相当.     

Effects of flux composition on the element transfer and mechanical properties of weld metal in submerged arc welding

Submerged arc welding was performed using metal-cored wires and fluxes with different compositions. The effects of wire/flux combination on the chemical composition, tensile strength, and impact toughness of the weld metal were investigated and interpreted in terms of element transfer between the slag and the weld metal, i.e., Δ quantity. Both carbon and manganese show negative Δ quantity in most combinations, indicating the transfer of the elements from the weld metal to the slag during welding. The amount of transfer, however, is different depending on the flux composition. More basic fluxes yield less negative Δ C and Δ Mn through the reduction of oxygen content in the weld metal and presumably higher Mn activity in the slag, respectively. The transfer of silicon, however, is influenced by Al₂O₃, TiO₂ and ZrO₂ contents in the flux. Δ Si becomes less negative and reaches a positive value of 0.044 as the oxides contents increase. This is because Al, Ti, and Zr could replace Si in the SiO₂ network, leaving more Si free to transfer from the slag to the weld metal. Accordingly, the Pcm index of weld metals calculated from chemical compositions varies from 0.153 to 0.196 depending on the wire/flux combination, and it almost has a linear relationship with the tensile strength of the weld metal.     

弧偏吹对埋弧焊接质量的影响和焊接工艺改进措施

为避免埋弧焊接过程中产生未熔合、未焊透和条状夹渣等危害性缺陷。提高埋弧焊接质量。探讨了直流弧焊电源埋弧焊接时弧偏吹现象的产生机理．分析阐述了埋弧焊接过程中条状缺陷的形成原因、弧偏吹产生的条件及弧偏吹对埋弧焊接质量的影响，并以此为指导。改进对接焊缝和熔透T形焊缝的埋弧焊接工艺。经推广应用．效果理想，经济效益显著。