单体组成对聚酰胺热熔胶性能影响的研究

采用二聚酸、癸二酸、乙二胺与聚醚胺合成出用于热熔胶的二聚酸型聚酰胺(PA)树脂,主要研究了上述单体组成与PA树脂基本性能,如软化点、拉伸强度、伸长率、耐低温性能以及熔融黏度等之间的关系;同时也探讨了单体组成对PA树脂剪切强度的影响.该二聚酸型聚酰胺热熔胶具有软化点高、拉伸强度和伸长率高、耐低温性能优异、成型速度快、安全...     

二聚酸型聚酰胺热熔胶的应用与改性研究进展

介绍了二聚酸型聚酰胺(PA)热熔胶在制鞋、电子电器、汽车工业及热缩套管等行业中的应用情况,详细阐述了国内外学者围绕传统二聚酸型PA热熔胶耐低温性能差、粘接强度低等问题,在化学共聚、物理共混、成本降低及助剂等方面的改性研究进展。     

二聚酸型聚酰胺热熔胶的制备及其性能研究

首先以二聚酸、乙二胺和己二胺为原料,分别合成二聚酸-乙二胺型聚酰胺热熔胶和二聚酸-己二胺型聚酰胺热熔胶。然后用聚醚二胺替代部分二元胺,再用己二酸替代部分二聚酸,通过共聚合成了改性的聚酰胺热熔胶。研究了聚醚二胺和己二酸的物质的量对聚酰胺热熔胶性能的影响。研究结果表明：(1)随聚醚二胺含量的增加,聚酰胺热熔胶的玻璃化转变温度(T_g)、硬度和拉伸强度降低;拉伸剪切强度先上升后下降,当聚醚二胺含量为20%时,拉伸剪切强度达到最大值4.2 MPa。(2)当m(二元酸)∶m(乙二胺或己二胺)∶m(聚醚二胺)=10∶6∶4时,在二元酸中掺入部分己二酸,随着己二酸含量的增加,聚酰胺热熔胶的T_g、硬度、拉伸强度和拉伸剪切强度增加。在己二酸含量为40%时,拉伸剪切强度最大值为4.2 MPa,T_g最大值为170.5℃。(3)在聚醚二胺含量为40%、己二酸含量相同时,二聚酸-乙二胺型聚酰胺热熔胶的T_g、硬度、拉伸强度和拉伸剪切强度均高于二聚酸-己二胺型聚酰胺热熔胶的性能。     

二聚酸型聚酰胺热熔胶的合成及性能研究

以哌嗪和低纯度的二聚酸为原料合成二聚酸型聚酰胺HMA(热熔胶),考察了哌嗪和二聚酸掺量等对该HMA性能的影响。采用红外光谱(FT-IR)法、差示扫描量热(DSC)法对HMA的结构、玻璃化转变温度(Tg)和软化点等进行了表征,并分析了不同样品的拉伸强度和断裂伸长率等性能。研究结果表明:合成的产物是聚酰胺;随着哌嗪或二聚酸掺量的不断增加,HMA的Tg和软化点降低、拉伸强度下降,但断裂伸长率提高。     

聚丙烯基热熔胶的制备以及对铝板剥离性能的研究

以聚丙烯(PP)为基础树脂,通过与功能性树脂共混制备了与铝板具有优异剥离性能的热熔胶。讨论了接枝树脂(PP-G-MAH)、苯乙烯类弹性体(SEBS),以及尼龙6(PA6)对热熔胶性能的影响,并比较了热熔胶在不同温度下,对不同表面状态铝板的剥离情况。结果表明,当热熔胶中含有20%PP-G-MAH时剥离强度达到最大值,苯乙烯弹性体对提高热熔胶的剥离强度有所帮助,PA6对保持热熔胶高温剥离强度有促进作用。     

二聚酸型聚酯酰胺热熔胶的合成

研究了以涤纶树脂、二聚酸等为主要原料,通过共缩聚反应制备聚酯酰胺热熔胶的方法,探讨了 配比及反应条件等对热熔胶性能的影响。结果表明:所制得的聚酯酰胺热熔胶不仅成本低,性能也能满足服 装、粘合衬工业的要求,而且对涤纶废料的开发利用及环境保护意义重大。     

EEA热熔胶的研究

本文研究了EEA体系热熔胶中主要组成物EEA树脂 ,增粘树脂和蜡类对热熔胶高温熔融粘度和剪切强度的影响     

低熔点聚酰胺的合成与应用研究进展

综述了近年来低熔点聚酰胺(PA)的合成方法及其下游应用的研究进展。在PA中掺入无机金属盐共混后,金属盐的金属离子可与PA的酰胺基团产生络合作用,降低其结晶度和熔点。不同结构单元的尼龙盐混合后进行熔融或溶液缩聚;多种二元酸与多种二元胺直接进行熔融聚合;以二聚酸替代二元酸与二元胺或多元胺直接进行熔融聚合是目前工业生产低熔点PA最常用的方法。己内酰胺与聚醚、聚酯、聚醇等通过多步法活性阴离子聚合或者水解开环聚合可制备低熔点PA,但熔点下降有限。低熔点PA主要应用于热熔胶、热粘合纤维以及工程塑料等领域,与国外产品相比,国内低熔点PA产品的品种、质量及应用仍有较大差距,研究和探索低熔点PA的合成工艺及其下游应用具有重要的现实意义和经济价值。     

行业动态

二聚酸是生产聚酰胺树脂的重要原料,国内产量很低,每年都需大量进口。随着粘合剂、涂料和油墨工业的发展,非尼龙聚酰胺树脂的用量会迅速扩大。预计2000年,生产汽车涂料需聚酰胺树脂约4000t,再加上其它涂料对聚酰胺树脂的需求,涂料工业对聚酰胺树脂的需求量将超过7000t。 聚酰胶树脂还可用于生产热熔胶和环氧树脂粘合剂。目前,国内热熔胶和环氧树脂粘合剂产量分别为3000t/a和7000t/a,2000年产量将分别达到2万t。因此,生产粘合剂对聚酰胺树脂的用量也将会快速增加,预计2000年可达2500t。再考虑到油墨工业等对聚酰胺树脂的需求,2000年国内对非尼龙聚酰胺树脂的总需求量将超过1.3万t。如果完全靠国内生产来满足市场需求,生产非尼龙聚酰胺树脂约需二聚酸5000t～6000t。再加上二聚酸在其     

反应型聚氨酯热熔胶主要性能影响因素研究

采用二苯基甲烷二异氰酸酯(MDI)、不同的低聚物二醇及增黏剂等原料制备了反应型聚氨酯热熔胶。研究了低聚物二醇种类、分子量以及增黏树脂EVA用量对反应型聚氨酯热熔胶的黏度、开放时间、初粘强度和终粘强度的影响。结果表明,相对分子质量为2 000的聚己二酸丁二醇酯二醇(PBA)较适合作为合成聚氨酯热熔胶的低聚物二醇,随着低聚物二醇结晶性的增强、分子量的增加,以及增黏树脂EVA用量的提高,聚氨酯热熔胶的黏度增大、开放时间缩短、初粘强度提高。但是终粘强度则是随着增黏树脂用量的增多而先升高后降低,在增黏树脂添加量10%时最高。     

Lower purity dimer acid based polyamides used as hot melt adhesives: synthesis and properties

Hot melt polyamides exhibit high adhesive strength. The polyamides synthesized from dimer fatty acids and diamines can present low crystallinity and a broad range of melting temperatures. In this work, polyamides with different compositions of dimer fatty acids, piperazine, ethylenediamine, sebacic acid and stearic acid and different content of secondary diamine (piperazine) and primary diamine (ethylenediamine) were synthesized. Polyamides with higher purity of dimer acids showed greater molecular weight, adhesion performance and a better mechanical resistance evaluated in stress/strain test. Softening point increased with increase in monomers content. By differential scanning calorimetry analysis, it was observed that polyamides with low percentage of monomer content show only one narrow melting peak in 100 °C. The increase in the acids monomer content leads to a larger temperature range of melting peak. The use of dimer fatty acid with a low content of monomers (up to 6%) in the polyamides synthesis promotes the formation of hot melt adhesives with good adhesion performances. The lowest monomer content leads to an increase in molecular weight, viscosity and mechanical properties of polyamide. Increase in the content of primary amines in polyamides increases crystallinity, viscosity and mechanical properties due to the higher number of hydrogen bonds formed by amide groups.     

Cross-linking reactions on polyamides by bis- and tris(maleimide)s

12 bis- and tris(maleimide)s were synthesized and characterized and their reactions with polyamides in the melt were examined. It was found that the double bonds of the maleimides react with terminal amino groups of the polyamides to form elastomeric networks. The chemical and physical properties of these elastomers were examined. Mixtures of bis- and tris(maleimide)s with amino-terminated polyamides can be applied as hot melt adhesives with high tensile and shear strength, with high thermal stability and high chemical resistance.     

Polyamides from carboxystearic acid

A series of polyamide and copolyamide resins were prepared from carboxystearic acid or methyl carboxystearate, with ethylenediamine, hexamethylenediamine, adipic acid, or caprolactam as coreactants. None of the product formulations appeared suitable for use in hot melt adhesives. More promising were the liquid, reactive polyamides made from carboxystearic acid and polyamines. These products gave excellent adhesion value in scouting tests when used as one component in 2-component epoxy adhesives and coatings. In other applications, C-19 polyamides had enhanced solubility and low melting characteristics to make them attractive as modifiers.     

用涤纶下脚料生产聚酯热熔胶

介绍了以涤给下脚料为主要原料，再配以其他的二元酸，二元醇制备聚酯热熔胶的反应原理，生产方法及工艺过程。对生产聚酯热熔胶的各种主要原料及其在热熔胶中所起作用作了较为详细的叙述，并介绍了辅助原料（催化剂，抗氧剂，增白剂等）的使用，另外，就涤纶的醇解，二元酸的酯化以及产品的缩聚等过程中相关操作工艺也作了详细的描述。     

SIS、SEBS产品及其在热熔胶中的应用

介绍了SIS、SEBS产品的性能及其热熔胶应用特点,研究了增粘树脂、增塑剂及其对SIS热熔压敏胶性能的影响,以及蜡对SIS、SEBS热熔胶的影响,提供了SIS、SEBS热熔(压敏)胶的基础性配方。     

我国湿固化聚氨酯热熔胶的研究现状和趋势

对聚氨酯热熔胶的分类和湿固化聚氨酯热熔胶的定义做了简明的阐述。分别从合成方法、改性和应用等方面对国内湿固化聚氨酯热熔胶的研究现状进行了综述。最后,对我国湿固化聚氨酯热熔胶的研究趋势进行了展望。     

Filled melt adhesives based on dimerized fatty acid polyamide derivatives

Melt adhesives based on filled polyamides prepared from a dimerized fatty acid and aliphatic polyamines have been developed. It has been shown that the incorporation of various fillers significantly improves the service behavior of these melt adhesives.     

环保型热熔胶研究进展

综述了可生物降解的热熔型胶粘剂、反应型热熔胶、压敏型热熔胶、水基型热熔胶等环保型热熔胶的制备、粘接性能及其应用。     

聚乙烯与铝材的粘结研究

本文通过聚乙烯本性改性、表面改性以及粘合剂的选择,探讨了聚乙烯与铝材的粘结,发现通过表面改性或／和使用热交、可以使铝材和聚乙烯达到优良的粘结,在实际上可获得应用。