| 双液淬火对9Cr2Mo钢辊皮组织与硬度的影响 |
| |
| 引用本文： | 孙国进,郜志文,崔效炎,郜可坤,孙力.双液淬火对9Cr2Mo钢辊皮组织与硬度的影响[J].金属热处理,2022,47(3):88-91. |
| |
| 作者姓名： | 孙国进 郜志文 崔效炎 郜可坤 孙力 |
| |
| 作者单位： | 1.河南工学院 材料科学与工程学院, 河南 新乡 453003;2.河南精诚汽车零部件有限公司, 河南 新乡 453000 |
| |
| 摘 要： | 探讨了双液淬火冷却工艺对9Cr2Mo钢辊皮表面组织、硬度的影响,得到了最佳双液淬火冷却工艺。结果表明,单液水冷淬火后表面组织为粗大的回火马氏体,水油双液淬火后回火马氏体晶粒明显细化,并且形成了少量的贝氏体和残留奥氏体。双液淬火处理后,辊皮外表面硬度分布为中部硬度高,边部硬度低,使辊皮的使用寿命得到了明显提高。ø750 mm的9Cr2Mo钢辊皮水油双液淬火最佳冷却工艺为入水前炉外预冷时间300 s,水冷-油冷之间预冷时间控制在60~180 s。
|
| 关 键 词： | 9Cr2Mo钢辊皮 双液淬火 硬度 组织 |
| 收稿时间： | 2021-11-12 |
Effect of dual liquid quenching on microstructure and hardness of 9Cr2Mo steel roller |
| |
| Sun Guojin,Gao Zhiwen,Cui Xiaoyan,Gao Kekun,Sun Li.Effect of dual liquid quenching on microstructure and hardness of 9Cr2Mo steel roller[J].Heat Treatment of Metals,2022,47(3):88-91. |
| |
| Authors: | Sun Guojin Gao Zhiwen Cui Xiaoyan Gao Kekun Sun Li |
| |
| Affiliation: | 1. Department of Materials Science and Engineering, Henan Institute of Technology, Xinxiang Henan 453003, China; 2. Henan Jingcheng Auto Parts Co., Ltd., Xinxiang Henan 453000, China |
| |
| Abstract: | Effect of water-oil dual liquid quenching process on microstructure and hardness of 9Cr2Mo roller were researched, and the optimum cooling process of dual liquid quenching was obtained. The results show that after single liquid quenching, the surface microstructure of the roller is coarse tempered martensite, while after water-oil dual liquid quenching, the tempered martensite is obviously refined, a small amount of bainite and retained austenite are formed, and the service life of the roller is significantly improved due to proper surface hardness distribution of the roller, which is high in the middle and low in the edge. The optimum cooling process of water-oil dual liquid quenching for 9Cr2Mo steel roller of ø750 mm is as follows: the precooling time outside the furnace before water cooling is 300 s, and the interval precooling time between water cooling and oil cooling in dual liquid quenching is controlled at 60-180 s. |
| |
| Keywords: | 9Cr2Mo steel roller dual liquid quenching process hardness microstructure |