EAF steelmaking process with increasing hot metal charging ratio and improving slagging regime |
| |
| Authors: | Jian-ping Duan Xue-min Yang |
| |
| Affiliation: | a Technical Center of Shanxi Taigang Stainless Corporation Limited, Taiyuan, Shanxi 030003, China
b Institute of Process Engineering, Chinese Academy of Sciences, Beijing 100190, China |
| |
| Abstract: | A new electric arc furnace (EAF) steelmaking process with increasing hot metal charging ratio and improving slagging regime simultaneously was developed and applied in a 50 t electric arc furnace for more than a year at No.1 Steelmaking Plant of Shanxi Taigang Stainless Corporation Limited. The essential fact of the new EAF steelmaking process was to charge hot metal in two portions or steps: firstly, 35wt%-40wt% hot metal was pretreated by blowing oxygen in a specially designed reactor for decarburization and improving hot metal temperature and melting premelted slag; secondly, 30wt% hot metal was charged into EAF with high basicity refining slags from ladle furnace (LF)-vacuum degassing furnace (VD) refining process. The results show that the hot metal charging ratio can reach to about 65wt%-70wt% for the new EAF steelmaking process; meanwhile, the tap-to-tap time of a 50 t EAF can shorten by 5-10 min, the electricity consumption can decrease by 35-50 kW·h/t, the lime consumption can reduce by 10.5 kg/t of molten steel, and the content of harmful heavy metals in molten steel can be easily controlled to less than the upper limits of aimed steel specification or grade compared with the traditional EAF steelmaking process. In addition, the dephosphorization ability shows a slight strengthening, however, a small degree of lessening for desulphurization ability is observed for the new EAF steelmaking process, but the weakness of desulphurization ability cannot become an obstacle to its further application since a stronger desulphurization ability can be achieved during secondary refining of LF coupled with VD after EAF steelmaking process. |
| |
| Keywords: | electric arc furnace (EAF) charge ratio slagging refining slags lime |
| 本文献已被 ScienceDirect 等数据库收录！ |
| 点击此处可从《矿物冶金与材料学报》浏览原始摘要信息 |
|
点击此处可从《矿物冶金与材料学报》下载全文 |
|