Improving the dielectric performance of poly(vinylidene fluoride)/polyaniline nanorod composites by stretch‐induced crystal transition |
| |
| Authors: | Shuangmin Yu Gengchao Wang |
| |
| Affiliation: | School of Materials Science and Engineering, Shanghai Key Laboratory of Advanced Polymeric Materials, Key Laboratory for Ultrafine Materials of the Ministry of Education, East China University of Science and Technology, Shanghai, P. R. China |
| |
| Abstract: | The introduction of conductive polyaniline (PANI) can significantly improve the dielectric constant of polymer‐based materials. However, there is a drawback of high dielectric loss. Herein, a simple and efficient stretching process was applied to improve the dielectric performance of poly(vinylidene fluoride)/PANI (PVDF/PANI) nanorod films through the stretch‐induced crystal transition from non‐polar α‐crystal to polar β‐crystal in PVDF and the oriented distribution of PANI nanorods. XRD, DSC and Fourier transform IR analyses indicate that the stretched PVDF and stretched PVDF/PANI films possess a high content of β‐crystal at the stretching temperature of 135 °C under a stretching ratio of 200%–400%. Furthermore, the stretched PVDF/PANI film with 10 wt% PANI displays a high dielectric constant of 338 at 100 Hz, which is increased by 20% compared to non‐stretched PVDF/PANI film (281). More importantly, the corresponding dielectric loss is reduced from 0.31 for the non‐stretched film to 0.17 for the stretched film. © 2018 Society of Chemical Industry |
| |
| Keywords: | poly(vinylidene fluoride) polyaniline stretch‐induced crystal transition dielectric materials |
|
|