| 疏水磁性碳酸钙的制备及其除油特性EI北大核心CSCD |
| |
| 引用本文： | 林仕宏,叶宝芳,王永净.疏水磁性碳酸钙的制备及其除油特性EI北大核心CSCD[J].材料工程,2022,50(1):138-144. |
| |
| 作者姓名： | 林仕宏 叶宝芳 王永净 |
| |
| 作者单位： | 1.福州大学 环境与资源学院, 福州 3501002 厦门大学 近海海洋环境科学国家重点实验室, 福建 厦门 361101 |
| |
| 基金项目： | 国家自然科学基金(21577018);福建省自然科学基金(2016 J01223)。 |
| |
| 摘 要： | 以硬脂酸为疏水改性剂,将其与Fe_(3)O_(4)纳米颗粒和市售CaCO_(3)共混,分别以不同的原料质量比,制备疏水磁性碳酸钙HMC-1和HMC-2,并将HMC-2负载在PU海绵上用以提高其实用性能。采用X射线粉末衍射仪、红外光谱仪、差示扫描量热仪、接触角/表界面张力测量仪对合成样品的物相、表面有机官能团、热稳定性及疏水性能进行系列表征分析。结果表明,HMC-2比HMC-1,具有更稳定的疏水性能,除油前后水接触角基本保持不变,约为150°,除油后该材料没有出现类似HMC-1的铁渗出现象。将HMC-2负载在PU海绵上后,改性PU海绵在3 s内可去除98%的油,重复吸油20次仍能达到95%以上的除油率,吸油倍率(吸附油质量/吸附剂质量)大于100。
|
| 关 键 词： | 碳酸钙 四氧化三铁 除油 磁性 |
| 收稿时间： | 2020-02-03 |
Preparation of hydrophobic magnetic calcium carbonate and its oil removal properties |
| |
| LIN Shihong,YE Baofang,WANG Yongjing.Preparation of hydrophobic magnetic calcium carbonate and its oil removal properties[J].Journal of Materials Engineering,2022,50(1):138-144. |
| |
| Authors: | LIN Shihong YE Baofang WANG Yongjing |
| |
| Affiliation: | 1.College of Environment and Resources, Fuzhou University, Fuzhou 350100, China2 State Key Laboratory of Marine Environmental Science, Xiamen University, Xiamen 361101, Fujian, China |
| |
| Abstract: | The hydrophobic magnetic materials of HMC-1 and HMC-2 were obtained by blending synthesized Fe3O4 nanoparticles and commercial CaCO3 powder with stearic acid solution,which is used as hydrophobic modifier.HMC-2 was loaded on the PU sponge for the further improvement of the applicability.The structural properties of the two materials were detected by X-ray powder diffractometer and infrared spectrometer.Thermal stability of HMC-2 was analysed by differential scanning calorimeter.The hydrophobic properties of the samples were determined by contact angle meter.The results show that HMC-2 has more stable hydrophobic properties than HMC-1.HMC-2 exhibits more stable hydrophobic performance.The contact angle remains nearly unchanged(about 150°)after oil removal.HMC-2 shows no release of Fe(Ⅲ)ions,which has taken place during the oil removal experiment using HMC-1.PU sponge loaded with HMC-2 can remove 98%oil in 3 s.The oil removal rate remains 95%,after 20 times of repeated oil absorption.The mass ratio of oil adsorption/adsorbent is larger than 100. |
| |
| Keywords: | CaCO3 Fe3O4 oil removal magnetism |